CN106280820A - A kind of fluorine silicon acrylate paint - Google Patents
A kind of fluorine silicon acrylate paint Download PDFInfo
- Publication number
- CN106280820A CN106280820A CN201610596579.1A CN201610596579A CN106280820A CN 106280820 A CN106280820 A CN 106280820A CN 201610596579 A CN201610596579 A CN 201610596579A CN 106280820 A CN106280820 A CN 106280820A
- Authority
- CN
- China
- Prior art keywords
- fluorine silicon
- acrylate
- silicon acrylate
- parts
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fluorine silicon acrylate paint, be made up of following composition by weight: fluorine silicon acrylate 30 45 parts, filler 30 45 parts, solvent 10 25 parts, auxiliary agent 5 15 parts, bioantifouling agent 5 10 parts.Chemically modified and physical modification two angles are set out, chemically angle is set out the acrylate resin coating of copolymerization fluorine silicon, and add the bioantifouling agent to marine environment nonhazardous effect from physical angle, obtain preferable resistance to soiling, be particularly suited for marine antifouling coating.
Description
Technical field
The present invention relates to coating, specifically refer to a kind of fluorine silicon acrylate paint.
Background technology
Acrylate resin coating is because of the ultraviolet aging resistance of its excellence, film property, the advantage such as environment friendly and pollution-free, the most
Through being widely used in every field, its modification is become the focus of research.Ship or underwater installation in ocean all can
Be stained by halobiontic, for they performance, service life etc. cause negative impact.Marine antifouling coating meet the tendency and
Raw.The marine antifouling coating of present stage to reach antifouling effect, and main by two approach, the first is killed, passed through toxicity
Material directly kills the absorption marine organisms on surface, and existing poisoning type marine antifouling coating is owing to depositing marine environment after release
At potential hazard, the most disabled or limit the use of, environmentally friendly bioantifouling agent replaces.It two is that low-surface-energy is antifouling,
Prevent marine organisms at surface enrichment by hydro-oleophobicity surface coating, mainly have organosilicon and the big class of Organic fluoride two.At present
Prior art about the antifouling aspect of ocean low-surface-energy is a lot, but organosilicon, Organic fluoride, acrylate and bioantifouling agent
Not, resistance to soiling is further improved four technology combined.
Summary of the invention
The problem to be solved in the present invention is to provide a kind of fluorine silicon acrylate paint, and soil resistance is good, it is adaptable to ocean is prevented
Dirt, has resistance to soiling good, pollutes few feature.
In order to solve above-mentioned technical problem, the present invention adopts the following technical scheme that a kind of fluorine silicon acrylate paint, by
Following composition by weight forms: fluorine silicon acrylate 30-45 part, filler 30-45 part, solvent 10-25 part, auxiliary agent 5-15
Part, bioantifouling agent 5-10 part.
As preferably, described auxiliary agent is one or more groups in defoamer, levelling agent, thickening agent, wetting dispersing agent
Close.
As preferably, described solvent is the one in dimethyl phthalate, butyl acetate, ethylenediamine or many
Plant combination.
As preferably, described filler be in zeolite, organobentonite, titanium dioxide, Kaolin, mica powder any one or
Person's multiple combination.
As preferably, described bioantifouling agent is the one in capsaicin, osthole, elatol and protease
Or multiple combination.
As preferably, the polymerization of described fluorine silicon acrylate is as follows: by fluoro-acrylate monomer, siliceous third
Acrylic monomer and acrylate main monomer add in solvent, add initiator and are polymerized, and polymerization gained resin is fluorine-containing
Si acrylate resin.Wherein fluoro-acrylate monomer be methacrylic acid ten trifluoro monooctyl ester, ethylacrylic acid ten trifluoro monooctyl ester,
At least one in methyl base acrylic acid ten fluorine butyl ester.Wherein silyl acrylate monomer is vinyl silane triisopropoxide, second
At least one in thiazolinyl triethoxysilane.Wherein acrylate main monomer is acrylic acid methyl ester., ethyl acrylate, acrylic acid
In butyl ester, 2-EHA, methoxyethyl acrylate, ethoxyethyl acrylate, methoxyethyl butyl ester
At least one.Wherein initiator is dibenzoyl peroxide, azodiisobutyronitrile, potassium peroxydisulfate, Ammonium Persulfate 98.5, hydrogen oxide-Asia
One in iron salt, any two kinds or the most two or more mixture.
After using technique scheme, present invention have the advantage that chemically modified and physical modification two angles go out
Sending out, chemically angle is set out the acrylate resin coating of copolymerization fluorine silicon, and adds nontoxic to marine environment from physical angle
The bioantifouling agent of evil effect, obtains preferable resistance to soiling, is particularly suited for marine antifouling coating.
Detailed description of the invention
Embodiment 1
A kind of fluorine silicon acrylate paint, includes following raw materials according by weight: fluorine silicon acrylate 30 parts, boiling
20 parts of stone, organobentonite 25 parts, butyl acetate 15 parts, auxiliary agent 5 parts, capsaicin 5 parts.
Embodiment 2
A kind of fluorine silicon acrylate paint, includes following raw materials according by weight: fluorine silicon acrylate 45 parts, titanium
15 parts of white lead, mica powder 15 parts, dimethyl phthalate 7 parts, butyl acetate 8 parts, auxiliary agent 5 parts, osthole 5 parts.
Embodiment 3
A kind of fluorine silicon acrylate paint, includes following raw materials according by weight: fluorine silicon acrylate 40 parts, high
30 parts of ridge soil, solvent 10 parts, ethylenediamine 10 parts, elatol 10 parts.
Embodiment 4
A kind of fluorine silicon acrylate paint, includes following raw materials according by weight: fluorine silicon acrylate 35 parts, boiling
10 parts of stone, organobentonite 10 parts, titanium dioxide 10 parts, dimethyl phthalate 15 parts, auxiliary agent 12 parts, proteinase 8 part.
Additionally needing explanation, the fluorine silicon acrylate polymerization methods in 4 embodiments is identical, and concrete mode is:
Fluoro-acrylate monomer, silyl acrylate monomer and acrylate main monomer are added in solvent, adds initiator and gather
Closing, polymerization gained resin is fluorine silicon acrylate.Wherein fluoro-acrylate monomer is that methacrylic acid ten trifluoro is pungent
At least one in ester, ethylacrylic acid ten trifluoro monooctyl ester, methyl base acrylic acid ten fluorine butyl ester.Wherein silyl acrylate monomer is
At least one in vinyl silane triisopropoxide, VTES.Wherein acrylate main monomer is propylene
Acid methyl ester, ethyl acrylate, butyl acrylate, 2-EHA, methoxyethyl acrylate, ethioxy second
At least one in ester, methoxyethyl butyl ester.Wherein initiator is dibenzoyl peroxide, azodiisobutyronitrile, over cure
One in acid potassium, Ammonium Persulfate 98.5, hydrogen oxide-ferrous salt, any two kinds or the most two or more mixture.
With reference to national standard " anti-fouling paint model shallow sea soak test method " (GB/T 5370-2007), the inspection present invention is real
Execute the example antifouling usefulness in sea area, Shanghai.(seeing table 1) shown in the board experiment result of sea area, natural sea area link plate 12 months
After, the biodeterioration on embodiment surface is substantially less than blank model and commercially available lacquer coat plate, shows that bioantifouling agent tool is good
Good anti-fouling effect.
Table 1
In addition to above preferred embodiment, the present invention also has other embodiment, and those skilled in the art can be according to this
Invention is variously modified, and without departing from the spirit of the present invention, all should belong to model defined in claims of the present invention
Enclose.
Claims (6)
1. a fluorine silicon acrylate paint, is characterized in that, is made up of following composition by weight: fluorine silicon acrylate
30-45 part, filler 30-45 part, solvent 10-25 part, auxiliary agent 5-15 part, bioantifouling agent 5-10 part.
Fluorine silicon acrylate paint the most according to claim 1, is characterized in that: described auxiliary agent be defoamer, levelling agent,
One or more combinations in thickening agent, wetting dispersing agent.
Fluorine silicon acrylate paint the most according to claim 1, is characterized in that: described solvent is phthalic acid two
One or more combinations in methyl ester, butyl acetate, ethylenediamine.
Fluorine silicon acrylate paint the most according to claim 1, is characterized in that: described filler is zeolite, organic swelling
Any one or multiple combination in soil, titanium dioxide, Kaolin, mica powder.
Fluorine silicon acrylate paint the most according to claim 1, is characterized in that: described bioantifouling agent is Fructus Capsici
One or more combinations in element, osthole, elatol and protease.
Fluorine silicon acrylate paint the most according to claim 1, is characterized in that, described fluorine silicon acrylate
Polymerization is as follows: fluoro-acrylate monomer, silyl acrylate monomer and acrylate main monomer is added in solvent, adds
Initiator is polymerized, and polymerization gained resin is fluorine silicon acrylate.