CN106279880A - A kind of PE Foam bag for product packaging and preparation method thereof - Google Patents
A kind of PE Foam bag for product packaging and preparation method thereof Download PDFInfo
- Publication number
- CN106279880A CN106279880A CN201610654015.9A CN201610654015A CN106279880A CN 106279880 A CN106279880 A CN 106279880A CN 201610654015 A CN201610654015 A CN 201610654015A CN 106279880 A CN106279880 A CN 106279880A
- Authority
- CN
- China
- Prior art keywords
- parts
- foam
- bag
- product packaging
- kaolin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of PE Foam bag for product packaging and preparation method thereof, the described PE Foam bag for product packaging includes the raw material of following parts by weight: PE Foam 125 160 parts, polyphosphoric acid amine 2.5 6 parts, polyoxyethylenated alcohol sodium sulfate 8 16 parts, sodium laurylsulfate 6 13 parts, ethyoxyl cocoalkyl amines 7 11 parts, tricresyl phosphate 49 parts, sodium alginate 37 parts, dibenzylatiooluene 26 parts, nano aluminium oxide 6 10 parts, Kaolin 9 14 parts, viscose rayon 6 11 parts, Pulvis Talci 7 13 parts, calcium carbonate 5 10 parts, bamboo fiber 8 16 parts, white carbon 7 14 parts.The good flame retardation effect of the PE Foam bag in the present invention, the most also has good water proof moisture effect, thus makes its serviceability be greatly enhanced.
Description
Technical field
The invention belongs to field of packaging material, particularly to a kind of PE Foam bag for product packaging and preparation thereof
Method.
Background technology
PE Foam, cotton also known as polyethylene foam, non-crosslinked hole-closing structure, is the packaging material of a kind of novel environment friendly, by low
Density polyethylene fat produces countless separated foams through physical blowing and constitutes.Overcome common foamed glue frangible, deformation, restorative
The shortcoming of difference, has that water proof is moistureproof, shockproof, sound insulation, insulation, plasticity is good, toughness is strong, reconstituted circularly, environmental protection, crashworthiness power are strong
Etc. plurality of advantages, also there is good chemical resistance.And PE Foam has recuperability, of many uses, therefore it is a kind of
The preferable substitute of conventional packaging material.But the fire resistance of tradition PE Foam bag is poor, and water proof moisture effect is the most undesirable, thus
Make its application be very limited, and can not get preferable using effect.
Summary of the invention
It is an object of the invention to provide a kind of PE Foam bag for product packaging and preparation method thereof, described for product
The PE Foam bag of packaging has good fire resistance and water proof moisture effect.
For achieving the above object, the present invention provides following technical scheme:
A kind of PE Foam bag for product packaging, it includes the raw material of following parts by weight: PE Foam 125-160 part,
Polyphosphoric acid amine 2.5-6 part, polyoxyethylenated alcohol sodium sulfate 8-16 part, sodium laurylsulfate 6-13 part, ethyoxyl cocos nucifera oil alkane
Base amine 7-11 part, tricresyl phosphate 4-9 part, sodium alginate 3-7 part, dibenzylatiooluene 2-6 part, nano aluminium oxide 6-10
Part, Kaolin 9-14 part, viscose rayon 6-11 part, Pulvis Talci 7-13 part, calcium carbonate 5-10 part, bamboo fiber 8-16 part, Linesless charcoal
Black 7-14 part.
Preferably, the described PE Foam bag for product packaging includes the raw material of following parts by weight: PE Foam 140
Part, polyphosphoric acid amine 4 parts, polyoxyethylenated alcohol sodium sulfate 10 parts, sodium laurylsulfate 7 parts, ethyoxyl cocoalkyl amines 9
Part, tricresyl phosphate 6 parts, sodium alginate 5 parts, dibenzylatiooluene 5 parts, nano aluminium oxide 8 parts, Kaolin 12 parts, viscous
Glue fiber 9 parts, Pulvis Talci 8 parts, calcium carbonate 8 parts, bamboo fiber 10 parts, white carbon 9 parts.
Preferably, the described PE Foam bag for product packaging includes the raw material of following parts by weight: PE Foam 150
Part, polyphosphoric acid amine 4.5 parts, polyoxyethylenated alcohol sodium sulfate 8 parts, sodium laurylsulfate 10 parts, ethyoxyl cocoalkyl amines 9
Part, tricresyl phosphate 9 parts, sodium alginate 6 parts, dibenzylatiooluene 3.5 parts, nano aluminium oxide 6 parts, Kaolin 10 parts,
Viscose rayon 7 parts, Pulvis Talci 11 parts, calcium carbonate 8 parts, bamboo fiber 12 parts, white carbon 12 parts.
Preferably, the described PE Foam bag for product packaging includes the raw material of following parts by weight: PE Foam 132
Part, polyphosphoric acid amine 4 parts, polyoxyethylenated alcohol sodium sulfate 15 parts, sodium laurylsulfate 7 parts, ethyoxyl cocoalkyl amines 11
Part, tricresyl phosphate 6 parts, sodium alginate 6 parts, dibenzylatiooluene 3.5 parts, nano aluminium oxide 8 parts, Kaolin 13 parts,
Viscose rayon 9 parts, Pulvis Talci 8 parts, calcium carbonate 7 parts, bamboo fiber 11 parts, white carbon 9 parts.
The preparation method of the described PE Foam bag for product packaging, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) first PE Foam is ground into powder, is subsequently adding dibenzylatiooluene, nano aluminium oxide, polyphosphoric acid amine, phosphorus
Acid front three phenyl ester and ethyoxyl cocoalkyl amines, after mix homogeneously, microwave frequency be 2400MHz-2500MHz, power 800W
Microwave oven in process 25-30min, obtain the first material；
(3) by Kaolin, white carbon, Pulvis Talci, calcium carbonate, polyoxyethylenated alcohol sodium sulfate, sodium laurylsulfate
With sodium alginate mix, add suitable quantity of water, after mix homogeneously under the conditions of ultrasonic frequency 80kHz, power 100W ultrasonic place
Reason 18-20min, obtains the second material；
(4) the first material and the second material are mixed, add viscose rayon, bamboo fiber simultaneously, be warming up to 110-120
DEG C insulated and stirred 12-16min, is then cooled to room temperature, more extruded machine is extruded, obtains stock shapes；
(5) utilize folding brake that the stock shapes in step (4) is carried out fold handling, finally utilize automatic bag-mfg. machine to make
Bag.
Compared with prior art, the invention has the beneficial effects as follows:
The present invention is by adding polyphosphoric acid amine, polyoxyethylenated alcohol sodium sulfate, ethyoxyl cocos nucifera oil alkane in PE Foam
The raw materials such as base amine, nano aluminium oxide, Kaolin and viscose rayon so that the good flame retardation effect of PE Foam bag, the most also have good
Good water proof moisture effect, thus make its serviceability be greatly enhanced, and application is wider.
Detailed description of the invention
Describe technical scheme in detail below in conjunction with embodiment, but protection domain is not limited thereto.
Embodiment one:
A kind of PE Foam bag for product packaging, it includes the raw material of following parts by weight: PE Foam 128 parts, poly-phosphorus
Acid amide 4.6 parts, polyoxyethylenated alcohol sodium sulfate 11 parts, sodium laurylsulfate 8 parts, ethyoxyl cocoalkyl amines 8 parts, phosphoric acid
Front three phenyl ester 5 parts, sodium alginate 4.2 parts, dibenzylatiooluene 3 parts, nano aluminium oxide 9 parts, Kaolin 9 parts, viscose rayon 7
Part, Pulvis Talci 12 parts, calcium carbonate 9 parts, bamboo fiber 12 parts, white carbon 9 parts.
The preparation method of the described PE Foam bag for product packaging, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) first PE Foam is ground into powder, is subsequently adding dibenzylatiooluene, nano aluminium oxide, polyphosphoric acid amine, phosphorus
Acid front three phenyl ester and ethyoxyl cocoalkyl amines, after mix homogeneously, microwave frequency be 2400MHz-2500MHz, power 800W
Microwave oven in process 25-30min, obtain the first material；
(3) by Kaolin, white carbon, Pulvis Talci, calcium carbonate, polyoxyethylenated alcohol sodium sulfate, sodium laurylsulfate
With sodium alginate mix, add suitable quantity of water, after mix homogeneously under the conditions of ultrasonic frequency 80kHz, power 100W ultrasonic place
Reason 18-20min, obtains the second material；
(4) the first material and the second material are mixed, add viscose rayon, bamboo fiber simultaneously, be warming up to 110-120
DEG C insulated and stirred 12-16min, is then cooled to room temperature, more extruded machine is extruded, obtains stock shapes；
(5) utilize folding brake that the stock shapes in step (4) is carried out fold handling, finally utilize automatic bag-mfg. machine to make
Bag.
Embodiment two:
A kind of PE Foam bag for product packaging, it includes the raw material of following parts by weight: PE Foam 145 parts, poly-phosphorus
Acid amide 6 parts, polyoxyethylenated alcohol sodium sulfate 13 parts, sodium laurylsulfate 9 parts, ethyoxyl cocoalkyl amines 10 parts, phosphoric acid
Front three phenyl ester 8 parts, sodium alginate 4.5 parts, dibenzylatiooluene 5 parts, nano aluminium oxide 7 parts, Kaolin 11 parts, viscose rayon
9 parts, Pulvis Talci 8 parts, calcium carbonate 8 parts, bamboo fiber 9 parts, white carbon 9 parts.
The preparation method of the described PE Foam bag for product packaging, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) first PE Foam is ground into powder, is subsequently adding dibenzylatiooluene, nano aluminium oxide, polyphosphoric acid amine, phosphorus
Acid front three phenyl ester and ethyoxyl cocoalkyl amines, after mix homogeneously, microwave frequency be 2400MHz-2500MHz, power 800W
Microwave oven in process 25-30min, obtain the first material；
(3) by Kaolin, white carbon, Pulvis Talci, calcium carbonate, polyoxyethylenated alcohol sodium sulfate, sodium laurylsulfate
With sodium alginate mix, add suitable quantity of water, after mix homogeneously under the conditions of ultrasonic frequency 80kHz, power 100W ultrasonic place
Reason 18-20min, obtains the second material；
(4) the first material and the second material are mixed, add viscose rayon, bamboo fiber simultaneously, be warming up to 110-120
DEG C insulated and stirred 12-16min, is then cooled to room temperature, more extruded machine is extruded, obtains stock shapes；
(5) utilize folding brake that the stock shapes in step (4) is carried out fold handling, finally utilize automatic bag-mfg. machine to make
Bag.
Embodiment three:
A kind of PE Foam bag for product packaging, it includes the raw material of following parts by weight: PE Foam 140 parts, poly-phosphorus
Acid amide 4 parts, polyoxyethylenated alcohol sodium sulfate 10 parts, sodium laurylsulfate 7 parts, ethyoxyl cocoalkyl amines 9 parts, tricresyl phosphate
Toluene ester 6 parts, sodium alginate 5 parts, dibenzylatiooluene 5 parts, nano aluminium oxide 8 parts, Kaolin 12 parts, viscose rayon 9 parts,
Pulvis Talci 8 parts, calcium carbonate 8 parts, bamboo fiber 10 parts, white carbon 9 parts.
The preparation method of the described PE Foam bag for product packaging, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) first PE Foam is ground into powder, is subsequently adding dibenzylatiooluene, nano aluminium oxide, polyphosphoric acid amine, phosphorus
Acid front three phenyl ester and ethyoxyl cocoalkyl amines, after mix homogeneously, microwave frequency be 2400MHz-2500MHz, power 800W
Microwave oven in process 25-30min, obtain the first material；
(3) by Kaolin, white carbon, Pulvis Talci, calcium carbonate, polyoxyethylenated alcohol sodium sulfate, sodium laurylsulfate
With sodium alginate mix, add suitable quantity of water, after mix homogeneously under the conditions of ultrasonic frequency 80kHz, power 100W ultrasonic place
Reason 18-20min, obtains the second material；
(4) the first material and the second material are mixed, add viscose rayon, bamboo fiber simultaneously, be warming up to 110-120
DEG C insulated and stirred 12-16min, is then cooled to room temperature, more extruded machine is extruded, obtains stock shapes；
(5) utilize folding brake that the stock shapes in step (4) is carried out fold handling, finally utilize automatic bag-mfg. machine to make
Bag.
Embodiment four:
A kind of PE Foam bag for product packaging, it includes the raw material of following parts by weight: PE Foam 150 parts, poly-phosphorus
Acid amide 4.5 parts, polyoxyethylenated alcohol sodium sulfate 8 parts, sodium laurylsulfate 10 parts, ethyoxyl cocoalkyl amines 9 parts, phosphoric acid
Front three phenyl ester 9 parts, sodium alginate 6 parts, dibenzylatiooluene 3.5 parts, nano aluminium oxide 6 parts, Kaolin 10 parts, viscose rayon
7 parts, Pulvis Talci 11 parts, calcium carbonate 8 parts, bamboo fiber 12 parts, white carbon 12 parts.
The preparation method of the described PE Foam bag for product packaging, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) first PE Foam is ground into powder, is subsequently adding dibenzylatiooluene, nano aluminium oxide, polyphosphoric acid amine, phosphorus
Acid front three phenyl ester and ethyoxyl cocoalkyl amines, after mix homogeneously, microwave frequency be 2400MHz-2500MHz, power 800W
Microwave oven in process 25-30min, obtain the first material；
(3) by Kaolin, white carbon, Pulvis Talci, calcium carbonate, polyoxyethylenated alcohol sodium sulfate, sodium laurylsulfate
With sodium alginate mix, add suitable quantity of water, after mix homogeneously under the conditions of ultrasonic frequency 80kHz, power 100W ultrasonic place
Reason 18-20min, obtains the second material；
(4) the first material and the second material are mixed, add viscose rayon, bamboo fiber simultaneously, be warming up to 110-120
DEG C insulated and stirred 12-16min, is then cooled to room temperature, more extruded machine is extruded, obtains stock shapes；
(5) utilize folding brake that the stock shapes in step (4) is carried out fold handling, finally utilize automatic bag-mfg. machine to make
Bag.
Embodiment five:
A kind of PE Foam bag for product packaging, it includes the raw material of following parts by weight: PE Foam 132 parts, poly-phosphorus
Acid amide 4 parts, polyoxyethylenated alcohol sodium sulfate 15 parts, sodium laurylsulfate 7 parts, ethyoxyl cocoalkyl amines 11 parts, phosphoric acid
Front three phenyl ester 6 parts, sodium alginate 6 parts, dibenzylatiooluene 3.5 parts, nano aluminium oxide 8 parts, Kaolin 13 parts, viscose rayon
9 parts, Pulvis Talci 8 parts, calcium carbonate 7 parts, bamboo fiber 11 parts, white carbon 9 parts.
The preparation method of the described PE Foam bag for product packaging, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) first PE Foam is ground into powder, is subsequently adding dibenzylatiooluene, nano aluminium oxide, polyphosphoric acid amine, phosphorus
Acid front three phenyl ester and ethyoxyl cocoalkyl amines, after mix homogeneously, microwave frequency be 2400MHz-2500MHz, power 800W
Microwave oven in process 25-30min, obtain the first material；
(3) by Kaolin, white carbon, Pulvis Talci, calcium carbonate, polyoxyethylenated alcohol sodium sulfate, sodium laurylsulfate
With sodium alginate mix, add suitable quantity of water, after mix homogeneously under the conditions of ultrasonic frequency 80kHz, power 100W ultrasonic place
Reason 18-20min, obtains the second material；
(4) the first material and the second material are mixed, add viscose rayon, bamboo fiber simultaneously, be warming up to 110-120
DEG C insulated and stirred 12-16min, is then cooled to room temperature, more extruded machine is extruded, obtains stock shapes；
(5) utilize folding brake that the stock shapes in step (4) is carried out fold handling, finally utilize automatic bag-mfg. machine to make
Bag.
Embodiment six:
A kind of PE Foam bag for product packaging, it includes the raw material of following parts by weight: PE Foam 148 parts, poly-phosphorus
Acid amide 3.6 parts, polyoxyethylenated alcohol sodium sulfate 14 parts, sodium laurylsulfate 7 parts, ethyoxyl cocoalkyl amines 8 parts, phosphoric acid
Front three phenyl ester 6.5 parts, sodium alginate 4.7 parts, dibenzylatiooluene 4.6 parts, nano aluminium oxide 8 parts, Kaolin 11 parts, viscose glue
Fiber 9 parts, Pulvis Talci 7 parts, calcium carbonate 5 parts, bamboo fiber 15 parts, white carbon 8.5 parts.
The preparation method of the described PE Foam bag for product packaging, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) first PE Foam is ground into powder, is subsequently adding dibenzylatiooluene, nano aluminium oxide, polyphosphoric acid amine, phosphorus
Acid front three phenyl ester and ethyoxyl cocoalkyl amines, after mix homogeneously, microwave frequency be 2400MHz-2500MHz, power 800W
Microwave oven in process 25-30min, obtain the first material；
(3) by Kaolin, white carbon, Pulvis Talci, calcium carbonate, polyoxyethylenated alcohol sodium sulfate, sodium laurylsulfate
With sodium alginate mix, add suitable quantity of water, after mix homogeneously under the conditions of ultrasonic frequency 80kHz, power 100W ultrasonic place
Reason 18-20min, obtains the second material；
(4) the first material and the second material are mixed, add viscose rayon, bamboo fiber simultaneously, be warming up to 110-120
DEG C insulated and stirred 12-16min, is then cooled to room temperature, more extruded machine is extruded, obtains stock shapes；
(5) utilize folding brake that the stock shapes in step (4) is carried out fold handling, finally utilize automatic bag-mfg. machine to make
Bag.
Embodiment seven:
A kind of PE Foam bag for product packaging, it includes the raw material of following parts by weight: PE Foam 155 parts, poly-phosphorus
Acid amide 4.8 parts, polyoxyethylenated alcohol sodium sulfate 13 parts, sodium laurylsulfate 7 parts, ethyoxyl cocoalkyl amines 10 parts, phosphorus
Acid front three phenyl ester 7 parts, sodium alginate 4 parts, dibenzylatiooluene 4 parts, nano aluminium oxide 7 parts, Kaolin 11 parts, viscose rayon
9 parts, Pulvis Talci 12 parts, calcium carbonate 8 parts, bamboo fiber 12 parts, white carbon 11 parts.
The preparation method of the described PE Foam bag for product packaging, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) first PE Foam is ground into powder, is subsequently adding dibenzylatiooluene, nano aluminium oxide, polyphosphoric acid amine, phosphorus
Acid front three phenyl ester and ethyoxyl cocoalkyl amines, after mix homogeneously, microwave frequency be 2400MHz-2500MHz, power 800W
Microwave oven in process 25-30min, obtain the first material；
(3) by Kaolin, white carbon, Pulvis Talci, calcium carbonate, polyoxyethylenated alcohol sodium sulfate, sodium laurylsulfate
With sodium alginate mix, add suitable quantity of water, after mix homogeneously under the conditions of ultrasonic frequency 80kHz, power 100W ultrasonic place
Reason 18-20min, obtains the second material；
(4) the first material and the second material are mixed, add viscose rayon, bamboo fiber simultaneously, be warming up to 110-120
DEG C insulated and stirred 12-16min, is then cooled to room temperature, more extruded machine is extruded, obtains stock shapes；
(5) utilize folding brake that the stock shapes in step (4) is carried out fold handling, finally utilize automatic bag-mfg. machine to make
Bag.
Embodiment eight:
A kind of PE Foam bag for product packaging, it includes the raw material of following parts by weight: PE Foam 140 parts, poly-phosphorus
Acid amide 6 parts, polyoxyethylenated alcohol sodium sulfate 12 parts, sodium laurylsulfate 8 parts, ethyoxyl cocoalkyl amines 9 parts, tricresyl phosphate
Toluene ester 9 parts, sodium alginate 4.5 parts, dibenzylatiooluene 2.8 parts, nano aluminium oxide 7.6 parts, Kaolin 10 parts, viscose glue is fine
Tie up 10 parts, Pulvis Talci 8 parts, calcium carbonate 9 parts, bamboo fiber 8 parts, white carbon 13 parts.
The preparation method of the described PE Foam bag for product packaging, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) first PE Foam is ground into powder, is subsequently adding dibenzylatiooluene, nano aluminium oxide, polyphosphoric acid amine, phosphorus
Acid front three phenyl ester and ethyoxyl cocoalkyl amines, after mix homogeneously, microwave frequency be 2400MHz-2500MHz, power 800W
Microwave oven in process 25-30min, obtain the first material；
(3) by Kaolin, white carbon, Pulvis Talci, calcium carbonate, polyoxyethylenated alcohol sodium sulfate, sodium laurylsulfate
With sodium alginate mix, add suitable quantity of water, after mix homogeneously under the conditions of ultrasonic frequency 80kHz, power 100W ultrasonic place
Reason 18-20min, obtains the second material；
(4) the first material and the second material are mixed, add viscose rayon, bamboo fiber simultaneously, be warming up to 110-120
DEG C insulated and stirred 12-16min, is then cooled to room temperature, more extruded machine is extruded, obtains stock shapes；
(5) utilize folding brake that the stock shapes in step (4) is carried out fold handling, finally utilize automatic bag-mfg. machine to make
Bag.
Finally illustrating, above example is only in order to illustrate technical scheme and unrestricted, although with reference to relatively
The present invention has been described in detail by good embodiment, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent, and without deviating from objective and the scope of the technical program, it all should be contained in the present invention
Right in the middle of.
Claims (5)
1. the PE Foam bag for product packaging, it is characterised in that include the raw material of following parts by weight: PE Foam 125-
160 parts, polyphosphoric acid amine 2.5-6 part, polyoxyethylenated alcohol sodium sulfate 8-16 part, sodium laurylsulfate 6-13 part, ethyoxyl
Cocoalkyl amines 7-11 part, tricresyl phosphate 4-9 part, sodium alginate 3-7 part, dibenzylatiooluene 2-6 part is nano oxidized
Aluminum 6-10 part, Kaolin 9-14 part, viscose rayon 6-11 part, Pulvis Talci 7-13 part, calcium carbonate 5-10 part, bamboo fiber 8-16
Part, white carbon 7-14 part.
PE Foam bag for product packaging the most according to claim 1, it is characterised in that include following parts by weight
Raw material: PE Foam 140 parts, polyphosphoric acid amine 4 parts, polyoxyethylenated alcohol sodium sulfate 10 parts, sodium laurylsulfate 7 parts, ethoxy
Base cocoalkyl amines 9 parts, tricresyl phosphate 6 parts, sodium alginate 5 parts, dibenzylatiooluene 5 parts, nano aluminium oxide 8 parts,
Kaolin 12 parts, viscose rayon 9 parts, Pulvis Talci 8 parts, calcium carbonate 8 parts, bamboo fiber 10 parts, white carbon 9 parts.
PE Foam bag for product packaging the most according to claim 1, it is characterised in that include following parts by weight
Raw material: PE Foam 150 parts, polyphosphoric acid amine 4.5 parts, polyoxyethylenated alcohol sodium sulfate 8 parts, sodium laurylsulfate 10 parts, second
Epoxide cocoalkyl amines 9 parts, tricresyl phosphate 9 parts, sodium alginate 6 parts, dibenzylatiooluene 3.5 parts, nano aluminium oxide 6
Part, Kaolin 10 parts, viscose rayon 7 parts, Pulvis Talci 11 parts, calcium carbonate 8 parts, bamboo fiber 12 parts, white carbon 12 parts.
PE Foam bag for product packaging the most according to claim 1, it is characterised in that include following parts by weight
Raw material: PE Foam 132 parts, polyphosphoric acid amine 4 parts, polyoxyethylenated alcohol sodium sulfate 15 parts, sodium laurylsulfate 7 parts, ethoxy
Base cocoalkyl amines 11 parts, tricresyl phosphate 6 parts, sodium alginate 6 parts, dibenzylatiooluene 3.5 parts, nano aluminium oxide 8
Part, Kaolin 13 parts, viscose rayon 9 parts, Pulvis Talci 8 parts, calcium carbonate 7 parts, bamboo fiber 11 parts, white carbon 9 parts.
5., according to the preparation method of the PE Foam bag for product packaging according to any one of claim 1-4, its feature exists
In, comprise the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) first PE Foam is ground into powder, is subsequently adding dibenzylatiooluene, nano aluminium oxide, polyphosphoric acid amine, tricresyl phosphate
Toluene ester and ethyoxyl cocoalkyl amines, after mix homogeneously, microwave frequency be 2400MHz-2500MHz, power 800W micro-
Process 25-30min in ripple stove, obtain the first material；
(3) by Kaolin, white carbon, Pulvis Talci, calcium carbonate, polyoxyethylenated alcohol sodium sulfate, sodium laurylsulfate and sea
Sodium alginate mix, add suitable quantity of water, after mix homogeneously under the conditions of ultrasonic frequency 80kHz, power 100W supersound process 18-
20min, obtains the second material；
(4) the first material and the second material are mixed, add viscose rayon, bamboo fiber simultaneously, be warming up to 110-120 DEG C of guarantor
Temperature stirring 12-16min, is then cooled to room temperature, more extruded machine is extruded, obtains stock shapes；
(5) utilize folding brake that the stock shapes in step (4) is carried out fold handling, finally utilize automatic bag-mfg. machine to make bag.