CN106278132A - A kind of preparation method of meerschaum thermal insulation board - Google Patents
A kind of preparation method of meerschaum thermal insulation board Download PDFInfo
- Publication number
- CN106278132A CN106278132A CN201510315331.9A CN201510315331A CN106278132A CN 106278132 A CN106278132 A CN 106278132A CN 201510315331 A CN201510315331 A CN 201510315331A CN 106278132 A CN106278132 A CN 106278132A
- Authority
- CN
- China
- Prior art keywords
- meerschaum
- preparation
- thermal insulation
- insulation board
- carbon fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The preparation method of a kind of meerschaum thermal insulation board belongs to building material field, in order to improve its effect of heat insulation.The technical program mainly includes the steps such as mixing, molding, compound, hardening, shaping, and in described composite steps, the THICKNESS CONTROL of carbon fiber is at 2mm；In described cure step, temperature controls at 120 degrees Celsius.The preparation method of a kind of meerschaum thermal insulation board that the present invention provides, by using above-mentioned preparation method, can be by meerschaum together with carbon fiber both nonmetallic materials efficient combination, it is not necessary to the media material effects such as adhesive, reduce cost.Meanwhile, both functions are carried out efficient combination, further increase its heat-resisting effect, there is good performance.It is effectively increased its structural strength, is beneficial to construction, beneficially life-time service, there is the longer life-span.This preparation method process is simple, and effect is good.
Description
Technical field
The invention belongs to building material field, be specifically related to the preparation method of a kind of meerschaum thermal insulation board.
Background technology
Meerschaum has sound insulation, heat insulation and fire protecting performance, is a kind of excellent construction material.In use find, general
The performance of logical meerschaum thermal insulation board the most increasingly can not meet the demand of reality, needs design and development of new structure
The thermal insulation board with meerschaum as matrix.
Summary of the invention
The technical problem to be solved is to provide the preparation method of a kind of meerschaum thermal insulation board, in order to improve its every
Thermal effect.
For solving above-mentioned technical problem, the technical solution adopted in the present invention is: the preparation side of a kind of meerschaum thermal insulation board
Method, it is characterised in that mainly include the following steps that,
1) mixing, adds water in sepiolite powder, stirs, and forms meerschaum slurry；
2) molding, pours meerschaum slurry into mould, forms certain size；
3) compound, lay one layer of carbon fiber on meerschaum slurry surface；
4) hardening, drying of heating；
5) shaping, removes overlap to the meerschaum thermal insulation board of hardening, polishes smooth；
In described composite steps, the THICKNESS CONTROL of carbon fiber is at 2mm；
In described cure step, temperature controls at 120 degrees Celsius.
The preparation method of a kind of meerschaum thermal insulation board that the present invention provides, by using above-mentioned preparation method, can be by Hai Pao
Stone is together with carbon fiber both nonmetallic materials efficient combination, it is not necessary to the media material effects such as adhesive, reduces
Cost.Meanwhile, both functions are carried out efficient combination, further increase its heat-resisting effect, have good
Performance.It is effectively increased its structural strength, is beneficial to construction, beneficially life-time service, there is the longer life-span.This is prepared
Procedure is simple, and effect is good.
Detailed description of the invention
The preparation method of a kind of meerschaum thermal insulation board, mainly includes the following steps that,
1) mixing, adds water in sepiolite powder, stirs, and forms meerschaum slurry；
2) molding, pours meerschaum slurry into mould, forms certain size；
3) compound, lay one layer of carbon fiber on meerschaum slurry surface, the THICKNESS CONTROL of carbon fiber is at 2mm；
4) hardening, drying of heating, temperature controls at 120 degrees Celsius；
5) shaping, removes overlap to the meerschaum thermal insulation board of hardening, polishes smooth.
The preparation method of a kind of meerschaum thermal insulation board that the present invention provides, by using above-mentioned preparation method, can be by
Meerschaum is together with carbon fiber both nonmetallic materials efficient combination, it is not necessary to the media materials such as adhesive are made
With, reduce cost.Meanwhile, both functions are carried out efficient combination, further increase its heat-resisting effect,
There is good performance.It is effectively increased its structural strength, is beneficial to construction, beneficially life-time service, has longer
Life-span.
Claims (3)
1. the preparation method of a meerschaum thermal insulation board, it is characterised in that: mainly include the following steps that,
1) mixing, adds water in sepiolite powder, stirs, and forms meerschaum slurry；
2) molding, pours meerschaum slurry into mould, forms certain size；
3) compound, lay one layer of carbon fiber on meerschaum slurry surface；
4) hardening, drying of heating；
5) shaping, removes overlap to the meerschaum thermal insulation board of hardening, polishes smooth.
The preparation method of a kind of meerschaum thermal insulation board the most according to claim 1, it is characterised in that: described multiple
Closing in step, the THICKNESS CONTROL of carbon fiber is at 2mm.
The preparation method of a kind of meerschaum thermal insulation board the most according to claim 1, it is characterised in that: described firmly
Changing in step, temperature controls at 120 degrees Celsius.