CN106277917A - A kind of concrete Anchor Agent - Google Patents
A kind of concrete Anchor Agent Download PDFInfo
- Publication number
- CN106277917A CN106277917A CN201610714018.7A CN201610714018A CN106277917A CN 106277917 A CN106277917 A CN 106277917A CN 201610714018 A CN201610714018 A CN 201610714018A CN 106277917 A CN106277917 A CN 106277917A
- Authority
- CN
- China
- Prior art keywords
- anchor agent
- concrete anchor
- preservative
- polyvinyl alcohol
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of concrete Anchor Agent, be made up of high-end elastic emulsion, aqueous epoxy emulsion, polyvinyl alcohol glue, preservative, tap water.The concrete Anchor Agent of the present invention has protective value to reinforcing bar; the reinforcing bar of corrosion can be played repairing barrier propterty; and it is durable in use; old concrete basic unit there is good adaptability; extra high adhesion strength and flexibility can be produced; can be in moist environment construction, this product has the performances such as higher cementability, crack resistance, water proofing property, uvioresistant, and processed coating surface does not haves crack or lamination.
Description
Technical field
The invention belongs to chemistry painting industry field, particularly relate to a kind of concrete Anchor Agent.
Background technology
Ground or the breakage of highway pavement, armored concrete order many units in charge of construction headache exposed under corrosive environment,
The exposed economic loss that causes of reinforcing bar, but air can be caused dirty if directly brushing organic coating immediately above at exposed reinforcing bar
Dye economic waste is also big, if directly batch scraping cement on damaged ground easily combine two skins of bad appearance, and also some car
The dusting that storehouse, road cause because strength of cement is low, is easy to fall from dusting pull-up if doing surface layer directly above.City now
Concrete Anchor Agent common on face, its product quality is uneven, is mixing with mortar concrete, is having in the short time
Preferably adhesive effect, arises that loose concrete, falls block phenomenon, have impact on the adhesive property of coating after some months.
Summary of the invention
In sum, for solving the problems referred to above, the invention provides a kind of concrete Anchor Agent that can overcome disadvantages mentioned above.
The technical scheme is that a kind of concrete Anchor Agent, in percentage by weight, composed of the following components:
High-end elastic emulsion 20～30%
Aqueous epoxy emulsion 30～40%
Polyvinyl alcohol glue 5～10%
Preservative 0.2～1.0%
Tap water 30～40%.
Further, described polyvinyl alcohol glue in use, needs first to add preservative at Xiang Shuili, then by polyvinyl alcohol
It is slowly added under high velocity agitation in the water added with preservative, the solution becoming concentration to be 20% with water dissolution.
Beneficial effects of the present invention: the concrete Anchor Agent of the present invention has protective value to reinforcing bar, the steel to corrosion
Muscle can play repairing barrier propterty, and durable in use, and old concrete basic unit is had good adaptability, can produce extra high viscous
Knotting strength and flexibility, can be in moist environment construction, and this product has higher cementability, crack resistance, water proofing property, uvioresistant
Etc. performance, processed coating surface does not haves crack or lamination.
Detailed description of the invention
The present invention being expanded on further below in conjunction with specific embodiment, raw material used in following example, as without especially
Illustrate, be commercially available.
Embodiment 1
A kind of concrete Anchor Agent, in percentage by weight, composed of the following components:
High-end elastic emulsion 6,159 25%
The aqueous epoxy emulsion 2,217 39% that bonding force is stronger
Polyvinyl alcohol glue 5%
Preservative 215 0.2%
Tap water 30.8%.
This case has stronger bonding force after testing, and bonding coefficient reaches 8.0MP, and resistance to compression coefficient reaches 0.0095, anti-
Compressive Strength reaches 100 MP, requires the harshest to bonding ground, and as long as no greasy dirt, ground does not has dust, does not has open fire with regard to energy
Construction, old concrete ground, rough highway can use.
Embodiment 2
A kind of concrete Anchor Agent, in percentage by weight, composed of the following components:
High-end elastic emulsion 6,159 20%
The aqueous epoxy emulsion 2,217 38% that bonding force is stronger
Polyvinyl alcohol glue 24-88P 7%
Preservative 215 0.4%
Tap water 34.6%.
This case has stronger bonding force after testing, and bonding coefficient reaches 8.0MP, and resistance to compression coefficient reaches 0.0095, anti-
Compressive Strength reaches 100 MP, requires the harshest to bonding ground, and as long as no greasy dirt, ground does not has dust, does not has open fire with regard to energy
Construction, old concrete ground, rough highway can use.
Embodiment 3
A kind of concrete Anchor Agent, in percentage by weight, composed of the following components:
High-end elastic emulsion 6,159 30%
The aqueous epoxy emulsion 2,217 37% that bonding force is stronger
Polyvinyl alcohol glue 24-88P 7%
Preservative 215 0.3%
Tap water 34.7%.
Concrete Anchor Agent obtained by above example, polyvinyl alcohol glue used in use, needs before dissolving
In water, first add preservative, be slowly added to polyvinyl alcohol under high velocity agitation the water added with preservative becomes with water dissolution
The solution of 20%.By the time it is completely dissolved out after the bubbles such as rear static a period of time disappear and is then added in above-mentioned material.By above-mentioned material
It is sequentially added into and is sufficiently stirred for, after stirring, be finished product.
On clean ground, in the case of not having open fire, concrete Anchor Agent is first sprayed, then at concrete during use
Anchor Agent volatilization during this period of time hasten stir with great Sha fine sand cement after add by a certain percentage concrete anchoring
Agent is mixed uniformly can not dry powder, directly criticizes and scrapes on the ground being sprayed with concrete Anchor Agent.According to circumstances can criticize and scrape one to two
All over.
This case has stronger bonding force after testing, and bonding coefficient reaches 8.0MP, and resistance to compression coefficient reaches 0.0095, anti-
Compressive Strength reaches 100 MP, requires the harshest to bonding ground, and as long as no greasy dirt, ground does not has dust, does not has open fire with regard to energy
Construction, old concrete ground, rough highway can use.
Although, the present invention is described in detail the most with a general description of the specific embodiments, but
On the basis of the present invention, can make some modifications or improvements it, this will be apparent to those skilled in the art.Cause
This, these modifications or improvements without departing from theon the basis of the spirit of the present invention, belong to the scope of protection of present invention.
Claims (5)
1. a concrete Anchor Agent, it is characterised in that in percentage by weight, composed of the following components:
High-end elastic emulsion 20～30%
Aqueous epoxy emulsion 30～40%
Polyvinyl alcohol glue 5～10%
Preservative 0.2～1.0%
Tap water 30～40%.
A kind of concrete Anchor Agent the most according to claim 1, it is characterised in that described polyvinyl alcohol glue is using
Time, need first to add preservative at Xiang Shuili, then polyvinyl alcohol be slowly added in the water added with preservative under high velocity agitation,
The solution becoming concentration to be 20% with water dissolution.
A kind of concrete Anchor Agent the most according to claim 1, it is characterised in that its weight percentages of components is:
High-end elastic emulsion 25%
Aqueous epoxy emulsion 39%
Polyvinyl alcohol glue 5%
Preservative 0.2%
Tap water 30.8%.
A kind of concrete Anchor Agent the most according to claim 1, it is characterised in that its weight percentages of components is:
High-end elastic emulsion 20%
Aqueous epoxy emulsion 38%
Polyvinyl alcohol glue 7%
Preservative 0.4%
Tap water 34.6%.
A kind of concrete Anchor Agent the most according to claim 1, it is characterised in that its weight percentages of components is:
High-end elastic emulsion 30%
Aqueous epoxy emulsion 37%
Polyvinyl alcohol glue 7%
Preservative 0.3%
Tap water 34.7%.