CN106274772A - A kind of automobile grills - Google Patents
A kind of automobile grills Download PDFInfo
- Publication number
- CN106274772A CN106274772A CN201610713157.8A CN201610713157A CN106274772A CN 106274772 A CN106274772 A CN 106274772A CN 201610713157 A CN201610713157 A CN 201610713157A CN 106274772 A CN106274772 A CN 106274772A
- Authority
- CN
- China
- Prior art keywords
- flase floor
- parts
- avris
- air filter
- automobile grills
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The open a kind of automobile grills of the present invention, including flase floor and Air Filter, the avris in described flase floor front is provided with raised line, described raised line fixes with flase floor, described flase floor is that hollow out is arranged, the hollow part of described flase floor is provided with vertical bar, described vertical bar fixes with flase floor, the middle part of described flase floor is provided with nameplate base, described nameplate base be internally provided with screwed hole, the middle part of described flase floor is provided with skeleton, the avris at described flase floor back is provided with fixing seat, described Air Filter is fixed on flase floor back, the avris of described Air Filter is provided with clamping plate, the avris of described clamping plate is provided with the seat that is screwed, the described seat that is screwed fits with flase floor；This automobile grills have installation easily, fastening is stable and the advantage of dust-proof air ventilation, flase floor hardness is big, intensity is high and durability degree is long for it.
Description
Technical field
Present invention relates particularly to a kind of automobile grills.
Background technology
Generally, vehicle is provided with for being filled with the cooling of the heat of cooling interior arrangement in inhalation vehicle from car by cold air
Putting, such as radiator grid, it is arranged on the front side of engine room to be introduced in engine room from car by cold air.Always with
Come, it is known that existing grid is bad in order to improve the burning caused by the sub-cooled of electromotor, radiator etc., and can adjust
In importing enging cabin via the traveling wind such as front grid being arranged on vehicle front, electromotor is dispelled the heat.
It addition, rainwater, the water splashed from road surface, snowmelt etc. flow into the running air inlet that traveling wind is passed through, and
Situation about being attached on grid surface is quite a few.The water being attached on this grid surface can make damper component freeze each other when cold
Knot, therefore exists and causes grid ventilation blocking to cause the bad this problems such as engine overheat, furthermore, the dust mistake on highway
Greatly, the grid air vent of some vehicles is excessive, causes dust in air to enter in enging cabin, causes cabin to be contaminated, enter
And affect the running of electromotor, and cause blackout difficulty when changing the most again because of its structure, and existing grid weight is big and
Structure is insecure, easily causes accident.
Therefore, there is installation difficulty, structure and fasten stable not and lack dust-proof air ventilation in current existing automobile grills
Problem, flase floor hardness is little, insufficient strength is high and durability degree is short for it.
Summary of the invention
The technical problem to be solved in the present invention be to provide a kind of install easily, fastening is stable and the automobile lattice of dust-proof air ventilation
Grid, and hardness is big, intensity is high and the flase floor of durability degree length.
For solving the problems referred to above, the present invention adopts the following technical scheme that
A kind of automobile grills, including flase floor and Air Filter, the avris in described flase floor front is provided with raised line, described convex
Bar fixes with flase floor, and described flase floor is that hollow out is arranged, and the hollow part of described flase floor is provided with vertical bar, described vertical bar with
Flase floor fixes, and the middle part of described flase floor is provided with nameplate base, described nameplate base be internally provided with screwed hole, described lattice
The middle part of screen is provided with skeleton, and the avris at described flase floor back is provided with fixing seat, and described Air Filter is fixed on flase floor
Back, the avris of described Air Filter is provided with clamping plate, and the avris of described clamping plate is provided with the seat that is screwed, described in be screwed seat
Fit with flase floor.
Further, described flase floor is made up of the material of following parts by weight proportioning, including bisphenol A-type unsaturated polyester (UP)
100-140 part, adjacent benzene-type beta-unsaturated esters 80-120 part, metaphenylene unsaturated polyester ester group resin 90-130 part, glass dregs 30-50
Part, Pulvis Talci 20-30 part, calcite 20-30 part, calcium carbonate 20-30 part, carbon fiber 20-40 part, fibre glass roving 50-70
Part, nikel powder 20-36 part, citrate 12-22 part, pyrophosphate 14-28 part, thiosulfate 12-18 part and boric acid 20-40
Part.
Further, described vertical bar is provided with one or more, beneficially reinforced grille plate.
Further, described vertical bar is formed in one with flase floor.
Further, described fixing seat is provided with more than one, and beneficially flase floor fixes with automobile.
Further, described fixing seat is formed in one with flase floor.
Further, described Air Filter is detachable setting, after being conducive to dismounting clears up the dust on Air Filter.
Further, described in the seat that is screwed be provided with more than one, beneficially Air Filter fixes with flase floor.
The preparation method of a kind of flase floor, comprises the following steps:
1) bisphenol A-type unsaturated polyester (UP) 100-140 part, adjacent benzene-type beta-unsaturated esters 80-120 part and metaphenylene unsaturated polyester are taken
Ester base resin 90-130 part is added in reactor, makes it melt by pyroreaction, and makes above-mentioned material merge uniformly, system
Obtain glue, standby；
2) take Pulvis Talci 20-30 part, calcite 20-30 part and calcium carbonate 20-30 part repeatedly to be ground, by upper by ball mill
State material and grind to form the powder of 50 mesh, then at the uniform velocity stirred with the speed of 50 turns per minute by blender, prepare mixed-powder,
Standby；
3) take glass dregs 30-50 part and put into smelting furnace, prepare glass melt by high-temperature fusion, standby；
4) by step 2) prepare filler and step 3) prepare glass melt and carbon fiber 20-40 part add step to
1) in the glue prepared, then stirred with the speed of 200 turns per minute by blender, prepare mixed glue solution, standby；
5) take fibre glass roving 50-70 part prepare the skeleton of flase floor and fix in a mold, then by step 4) system
The mixed glue solution obtained carries out being cast into molding by mould, and die sinking prepares flase floor blank, standby；
6) the flase floor blank that step 5 prepares is carried out surface sanding and polishing by buffing machine so that flase floor blank table
Face is smooth, standby；
7) nikel powder 20-36 part, citrate 12-22 part, pyrophosphate 14-28 part, thiosulfate 12-18 part and boron are taken
Acid 20-40 part mixing, is then stirred by stirring rod, prepares electroplating solution, standby；
8) by step 6) flase floor for preparing is suspended in electroplating solution, and by the method for the rack plating surface to flase floor
Carry out nickel plating, to obtain final product.
The invention has the beneficial effects as follows: owing to being provided with vertical bar, it is possible to reinforced grille plate, Air Filter can be fixed simultaneously,
Owing to being provided with nameplate base, it is possible to the mark of holding vehicles, owing to being provided with skeleton, it is possible to the intensity of enhanced grid plate, due to
Being provided with fixed plate, beneficially flase floor fixes with automobile, owing to being provided with Air Filter, is conducive to the ash in air filtering
Dirt, places in the cabin that dust enters automobile, and affects the operating in cabin, and meanwhile, flase floor uses the material system in the application
Become, have that hardness is big, intensity is high and the advantage of durability degree length.
Accompanying drawing explanation
Fig. 1 is the front view of a kind of automobile grills of the present invention；
Fig. 2 is the structure figure of a kind of automobile grills of the present invention.
Detailed description of the invention
Embodiment one:
Refering to shown in Fig. 1-2, a kind of automobile grills, including flase floor 1 and Air Filter 8, the avris in described flase floor 1 front
Being provided with raised line 2, described raised line 2 fixes with flase floor 1, and described flase floor 1 is arranged for hollow out, the hollow out of described flase floor 1
Place is provided with vertical bar 3, and described vertical bar 3 fixes with flase floor 1, and the middle part of described flase floor 1 is provided with nameplate base 4, described inscription
Board seat 4 be internally provided with screwed hole 5, the middle part of described flase floor 1 is provided with skeleton 6, and the avris at described flase floor 1 back sets
Being equipped with fixing seat 7, described Air Filter 8 is fixed on flase floor 1 back, and the avris of described Air Filter 8 is provided with clamping plate 9, described folder
The avris of plate 9 is provided with the seat 10 that is screwed, described in the seat 10 that is screwed fit with flase floor 1.
Described flase floor 1 is made up of the material of following parts by weight proportioning, including bisphenol A-type unsaturated polyester (UP) 140 parts, neighbour
Benzene-type beta-unsaturated esters 80 parts, metaphenylene unsaturated polyester ester group resin 90-part, glass dregs 30 parts, Pulvis Talci 20 parts, calcite 20
Part, calcium carbonate 20 parts, 20 parts of carbon fiber, fibre glass roving 50 parts, nikel powder 20 parts, citrate 12 parts, pyrophosphate 14 parts,
Thiosulfate 12 parts and boric acid 20 parts.
Described vertical bar 3 is provided with one or more, beneficially reinforced grille plate 1.
Described vertical bar 3 is formed in one with flase floor 1.
Described fixing seat 7 is provided with more than one, and beneficially flase floor 1 fixes with automobile.
Described fixing seat 7 is formed in one with flase floor 1.
Described Air Filter 8 is detachable setting, after being conducive to dismounting clears up the dust on Air Filter 8.
The described seat 10 that is screwed is provided with more than one, and beneficially Air Filter 8 fixes with flase floor 1.
The preparation method of a kind of flase floor, comprises the following steps:
1) bisphenol A-type unsaturated polyester (UP) 140 parts, adjacent benzene-type beta-unsaturated esters 80 parts and metaphenylene unsaturated polyester ester group resin are taken
90 parts are added in reactor, make it melt by pyroreaction, and make above-mentioned material merge uniformly, prepare glue, standby；
2) take Pulvis Talci 20 parts, 20 parts of calcite and calcium carbonate 20 parts repeatedly to be ground by ball mill, above-mentioned material is ground
Wear into the powder of 50 mesh, then at the uniform velocity stirred with the speed of 50 turns per minute by blender, prepare mixed-powder, standby；
3) take glass dregs 30 parts and put into smelting furnace, prepare glass melt by high-temperature fusion, standby；
4) by step 2) prepare filler and step 3) prepare glass melt and 20 parts of carbon fiber add step 1 to)
In the glue prepared, then stirred with the speed of 200 turns per minute by blender, prepare mixed glue solution, standby；
5) take the skeleton of 50 parts of prepared flase floors of fibre glass roving and fix in a mold, then by step 4) prepare
Mixed glue solution carries out being cast into molding by mould, and die sinking prepares flase floor blank, standby；
6) the flase floor blank that step 5 prepares is carried out surface sanding and polishing by buffing machine so that flase floor blank table
Face is smooth, standby；
7) nikel powder 20 parts, citrate 12 parts, pyrophosphate 14 parts, thiosulfate 12 parts and boric acid 20 parts mixing are taken,
Then stirred by stirring rod, prepare electroplating solution, standby；
8) by step 6) flase floor for preparing is suspended in electroplating solution, and by the method for the rack plating surface to flase floor
Carry out nickel plating, to obtain final product.
Embodiment two:
Refering to shown in Fig. 1-2, a kind of automobile grills, including flase floor 1 and Air Filter 8, the avris in described flase floor 1 front
Being provided with raised line 2, described raised line 2 fixes with flase floor 1, and described flase floor 1 is arranged for hollow out, the hollow out of described flase floor 1
Place is provided with vertical bar 3, and described vertical bar 3 fixes with flase floor 1, and the middle part of described flase floor 1 is provided with nameplate base 4, described inscription
Board seat 4 be internally provided with screwed hole 5, the middle part of described flase floor 1 is provided with skeleton 6, and the avris at described flase floor 1 back sets
Being equipped with fixing seat 7, described Air Filter 8 is fixed on flase floor 1 back, and the avris of described Air Filter 8 is provided with clamping plate 9, described folder
The avris of plate 9 is provided with the seat 10 that is screwed, described in the seat 10 that is screwed fit with flase floor 1.
Described flase floor 1 is made up of the material of following parts by weight proportioning, including bisphenol A-type unsaturated polyester (UP) 100 parts, neighbour
Benzene-type beta-unsaturated esters 120 parts, metaphenylene unsaturated polyester ester group resin 130 parts, glass dregs 50 parts, Pulvis Talci 30 parts, calcite 30
Part, calcium carbonate 30 parts, 40 parts of carbon fiber, fibre glass roving 70 parts, nikel powder 36 parts, citrate 22 parts, pyrophosphate 28 parts,
Thiosulfate 18 parts and boric acid 40 parts.
Described vertical bar 3 is provided with one or more, beneficially reinforced grille plate 1.
Described vertical bar 3 is formed in one with flase floor 1.
Described fixing seat 7 is provided with more than one, and beneficially flase floor 1 fixes with automobile.
Described fixing seat 7 is formed in one with flase floor 1.
Described Air Filter 8 is detachable setting, after being conducive to dismounting clears up the dust on Air Filter 8.
The described seat 10 that is screwed is provided with more than one, and beneficially Air Filter 8 fixes with flase floor 1.
The preparation method of a kind of flase floor, comprises the following steps:
1) bisphenol A-type unsaturated polyester (UP) 100 parts, adjacent benzene-type beta-unsaturated esters 120 parts and metaphenylene unsaturated polyester ester group tree are taken
130 parts of fat adds in reactor, makes it melt by pyroreaction, and makes above-mentioned material merge uniformly, prepares glue, standby
With；
2) take Pulvis Talci 30 parts, 30 parts of calcite and calcium carbonate 30 parts repeatedly to be ground by ball mill, above-mentioned material is ground
Wear into the powder of 50 mesh, then at the uniform velocity stirred with the speed of 50 turns per minute by blender, prepare mixed-powder, standby；
3) take glass dregs 50 parts and put into smelting furnace, prepare glass melt by high-temperature fusion, standby；
4) by step 2) prepare filler and step 3) prepare glass melt and 40 parts of carbon fiber add step 1 to)
In the glue prepared, then stirred with the speed of 200 turns per minute by blender, prepare mixed glue solution, standby；
5) take the skeleton of 70 parts of prepared flase floors of fibre glass roving and fix in a mold, then by step 4) prepare
Mixed glue solution carries out being cast into molding by mould, and die sinking prepares flase floor blank, standby；
6) the flase floor blank that step 5 prepares is carried out surface sanding and polishing by buffing machine so that flase floor blank table
Face is smooth, standby；
7) nikel powder 36 parts, citrate 22 parts, pyrophosphate 28 parts, thiosulfate 18 parts and boric acid 40 parts mixing are taken,
Then stirred by stirring rod, prepare electroplating solution, standby；
8) by step 6) flase floor for preparing is suspended in electroplating solution, and by the method for the rack plating surface to flase floor
Carry out nickel plating, to obtain final product.
Embodiment three:
Refering to shown in Fig. 1-2, a kind of automobile grills, including flase floor 1 and Air Filter 8, the avris in described flase floor 1 front
Being provided with raised line 2, described raised line 2 fixes with flase floor 1, and described flase floor 1 is arranged for hollow out, the hollow out of described flase floor 1
Place is provided with vertical bar 3, and described vertical bar 3 fixes with flase floor 1, and the middle part of described flase floor 1 is provided with nameplate base 4, described inscription
Board seat 4 be internally provided with screwed hole 5, the middle part of described flase floor 1 is provided with skeleton 6, and the avris at described flase floor 1 back sets
Being equipped with fixing seat 7, described Air Filter 8 is fixed on flase floor 1 back, and the avris of described Air Filter 8 is provided with clamping plate 9, described folder
The avris of plate 9 is provided with the seat 10 that is screwed, described in the seat 10 that is screwed fit with flase floor 1.
Described flase floor 1 is made up of the material of following parts by weight proportioning, including bisphenol A-type unsaturated polyester (UP) 120 parts, neighbour
Benzene-type beta-unsaturated esters 100 parts, metaphenylene unsaturated polyester ester group resin 110 parts, glass dregs 40 parts, Pulvis Talci 25 parts, calcite 25
Part, calcium carbonate 25 parts, 30 parts of carbon fiber, fibre glass roving 60 parts, nikel powder 28 parts, citrate 18 parts, pyrophosphate 21 parts,
Thiosulfate 15 parts and boric acid 30 parts.
Described vertical bar 3 is provided with one or more, beneficially reinforced grille plate 1.
Described vertical bar 3 is formed in one with flase floor 1.
Described fixing seat 7 is provided with more than one, and beneficially flase floor 1 fixes with automobile.
Described fixing seat 7 is formed in one with flase floor 1.
Described Air Filter 8 is detachable setting, after being conducive to dismounting clears up the dust on Air Filter 8.
The described seat 10 that is screwed is provided with more than one, and beneficially Air Filter 8 fixes with flase floor 1.
The preparation method of a kind of flase floor, comprises the following steps:
1) bisphenol A-type unsaturated polyester (UP) 120 parts, adjacent benzene-type beta-unsaturated esters 100 parts and metaphenylene unsaturated polyester ester group tree are taken
110 parts of fat adds in reactor, makes it melt by pyroreaction, and makes above-mentioned material merge uniformly, prepares glue, standby
With；
2) take Pulvis Talci 25 parts, 25 parts of calcite and calcium carbonate 25 parts repeatedly to be ground by ball mill, above-mentioned material is ground
Wear into the powder of 50 mesh, then at the uniform velocity stirred with the speed of 50 turns per minute by blender, prepare mixed-powder, standby；
3) take glass dregs 40 parts and put into smelting furnace, prepare glass melt by high-temperature fusion, standby；
4) by step 2) prepare filler and step 3) prepare glass melt and 30 parts of carbon fiber add step 1 to)
In the glue prepared, then stirred with the speed of 200 turns per minute by blender, prepare mixed glue solution, standby；
5) take the skeleton of 60 parts of prepared flase floors of fibre glass roving and fix in a mold, then by step 4) prepare
Mixed glue solution carries out being cast into molding by mould, and die sinking prepares flase floor blank, standby；
6) the flase floor blank that step 5 prepares is carried out surface sanding and polishing by buffing machine so that flase floor blank table
Face is smooth, standby；
7) nikel powder 28 parts, citrate 18 parts, pyrophosphate 21 parts, thiosulfate 15 parts and boric acid 30 parts mixing are taken,
Then stirred by stirring rod, prepare electroplating solution, standby；
8) by step 6) flase floor for preparing is suspended in electroplating solution, and by the method for the rack plating surface to flase floor
Carry out nickel plating, to obtain final product.
Experimental example:
Choose common flase floor with special flase floor compared with the flase floor of the present invention, and according to hardness, intensity
With durability degree foundation as a comparison, analyze the situation of three groups of flase floors, and draw best flase floor.
Hardness: enable to structure more firm, is unlikely to deform；
Intensity: the resistance that automobile advance runs into can be born；
Durability degree: service life is long.
With common flase floor be matched group one, special flase floor be matched group two and the present invention flase floor for comparison
Group three, concrete data are as shown in the table:
Contrasting three groups of materials, the flase floor effect obtaining the present invention is best, has hardness big, strong compared with two groups of matched groups
The advantage that degree is high and durability degree is good.
The invention has the beneficial effects as follows: owing to being provided with vertical bar, it is possible to reinforced grille plate, Air Filter can be fixed simultaneously,
Owing to being provided with nameplate base, it is possible to the mark of holding vehicles, owing to being provided with skeleton, it is possible to the intensity of enhanced grid plate, due to
Being provided with fixed plate, beneficially flase floor fixes with automobile, owing to being provided with Air Filter, is conducive to the ash in air filtering
Dirt, places in the cabin that dust enters automobile, and affects the operating in cabin, and meanwhile, flase floor uses the material system in the application
Become, have that hardness is big, intensity is high and the advantage of durability degree length.
The above, the only detailed description of the invention of the present invention, but protection scope of the present invention is not limited thereto, and any
The change expected without creative work or replacement, all should contain and be as the criterion at scope.
Claims (8)
1. an automobile grills, it is characterised in that: including flase floor and Air Filter, the avris in described flase floor front is provided with convex
Bar, described raised line fixes with flase floor, and described flase floor is that hollow out is arranged, and the hollow part of described flase floor is provided with vertical bar,
Described vertical bar fixes with flase floor, and the middle part of described flase floor is provided with nameplate base, described nameplate base be internally provided with spiral shell
Pit, the middle part of described flase floor is provided with skeleton, and the avris at described flase floor back is provided with fixing seat, and described Air Filter is solid
Being scheduled on flase floor back, the avris of described Air Filter is provided with clamping plate, and the avris of described clamping plate is provided with the seat that is screwed, described
The seat that is screwed fits with flase floor.
2. removed the automobile grills as described in claim 2, it is characterised in that: described flase floor is by the material of following parts by weight proportioning
Material is made, including bisphenol A-type unsaturated polyester (UP) 100-140 part, adjacent benzene-type beta-unsaturated esters 80-120 part, metaphenylene unsaturated polyester (UP)
Base resin 90-130 part, glass dregs 30-50 part, Pulvis Talci 20-30 part, calcite 20-30 part, calcium carbonate 20-30 part, carbon fiber
20-40 part, fibre glass roving 50-70 part, nikel powder 20-36 part, citrate 12-22 part, pyrophosphate 14-28 part, sulfur generation
Sulfate 12-18 part and boric acid 20-40 part.
3. removed the automobile grills as described in claim 3, it is characterised in that: described vertical bar is provided with one or more.
4. removed the automobile grills as described in claim 4, it is characterised in that: described vertical bar is formed in one with flase floor.
5. removed the automobile grills as described in claim 5, it is characterised in that: described fixing seat is provided with more than one.
6. removed the automobile grills as described in claim 6, it is characterised in that: described fixing seat is formed in one with flase floor.
7. removed the automobile grills as described in claim 7, it is characterised in that: described Air Filter is detachable setting.
8. removed the automobile grills as described in claim 8, it is characterised in that the seat that is screwed described in: is provided with more than one.