CN106274246A - The method of manufacturing technology of a kind of tea element artware and product - Google Patents
The method of manufacturing technology of a kind of tea element artware and product Download PDFInfo
- Publication number
- CN106274246A CN106274246A CN201610709543.XA CN201610709543A CN106274246A CN 106274246 A CN106274246 A CN 106274246A CN 201610709543 A CN201610709543 A CN 201610709543A CN 106274246 A CN106274246 A CN 106274246A
- Authority
- CN
- China
- Prior art keywords
- raw material
- tea
- main body
- element main
- artware
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of method of manufacturing technology of tea element artware, processing step is as follows: the raw-material preparation of element main body of (1) tea: in pruning Camellia sinensis two spring or the three spring months or autumn or branch and leaf in winter, tea branch and leaf pruning obtained wither, then stack and complete to half-fermented, knead crushed after being dried, obtain described tea element main body raw material.(2) preparation of raw material composite: for the intensity of reinforcing material, by above-mentioned tea element main body raw material, plant fiber material or Carbon fibe raw material or metallic fiber raw material, Moulding powder raw material mix homogeneously, obtain described raw material composite；(3) described raw material composite is preheated；(4) by preheated described raw material composite, add thermocompression forming in heating die cavity, obtain described tea element artware.
Description
Technical field
The present invention relates to artware, tea branch and leaf discarded after more specifically referring to, pornographic movie, stalky tea unqualified with tea, pruning are
Main raw material(s) manufactures method of manufacturing technology and the product of a kind of tea element artware.
Background technology
The series such as current tea artware such as tea picture, tea suspension member, tea goods of furniture for display rather than for use.Or use the processing method manufacture of tea cake formula,
Employing raw tea material makes, and loosely organized, easy-weathering peels off and goes mouldy, and durability is very poor.Made artware, after a procedure because of wind
Changing mouldy discarded, nobody can bring and drink, and causes a large amount of waste.Traditional handicraft softens at Folium Camelliae sinensis high-temperature humidifying, presses
Finished product drying link after system, there is also power consumption height, the situation that cost is big.
The summary of the invention purpose of the present invention be contemplated to provide a kind of Folium Camelliae sinensis used in Tea Production unqualified or
It is Folium Camelliae sinensis pornographic movie, stalky tea, and the tea branch and leaf etc. discarded after pruning manufacture the system of tea artware for the main material that manufactures
Make process and product.This tea element artware had both reached high rigidity, high water proofing property, high anti-mildew requirement, met again life
State environmental requirement, tea perfume (or spice) overflows.
The technical scheme is that
A kind of method of manufacturing technology of tea element artware, processing step is as follows:
(1) the raw-material preparation of tea element main body:
Method one: by unqualified for Folium Camelliae sinensis pulverizing, or Folium Camelliae sinensis is unqualified, pornographic movie, stalky tea mix after pulverizing, and obtains described tea element main body
Raw material；Or
Method two: further, obtains the most cheap tea element main body raw material with the following method:
In pruning Camellia sinensis two spring or the three spring months or autumn or branch and leaf in winter, tea branch and leaf pruning obtained wither, then
Stack and complete to half-fermented, knead crushed after being dried, obtain described tea element main body raw material.
(2) preparation of raw material composite:
Method one:
Above-mentioned tea element main body raw material is mixed homogeneously with Moulding powder raw material, obtains mixing compositions；Or
Method two:
Further, for the intensity of reinforcing material, by above-mentioned tea element main body raw material, plant fiber material or Carbon fibe raw material
Or metallic fiber raw material, Moulding powder raw material mix homogeneously, obtain described raw material composite；
(3) described raw material composite is preheated；
(4) by preheated described raw material composite, add thermocompression forming in heating die cavity, obtain described tea element technique
Product.
Described Moulding powder raw material is containing curing agent component or stabilizer component or resistance to water component or the mould of plasticizing component
Molding powder raw material, or be containing curing agent component, stabilizer component, resistance to water component, the Moulding powder raw material of plasticizing component blending constituent.
A kind of tea element artware, uses above-mentioned method of manufacturing technology to make.
Above-mentioned employing tea is unqualified, pornographic movie, stalky tea, tea branch and leaf discarded after pruning are main raw material(s), manufactures a kind of tea
The method of manufacturing technology of element artware and product, obtain the most positive technological progress:
The first, the tea branch and leaf owing to using Folium Camelliae sinensis unqualified or to obtain after Folium Camelliae sinensis pornographic movie, stalky tea, or pruning are main raw material(s),
Carry out manufacturing process product, it is achieved that twice laid.After in Tea Production, tea dust, Folium Camelliae sinensis pornographic movie, stalky tea separate, general process side
Method is all discarded or undersells as the general raw material of industry, and the tea branch and leaf after pruning go out of use burning especially, are applied to work
In the production of skill product, it is achieved that twice laid, it is manufactured into artware, substantially increases tea dust, Folium Camelliae sinensis pornographic movie, stalky tea, and
The added value of the tea branch and leaf obtained after pruning.
The second, above-mentioned employing Folium Camelliae sinensis is unqualified, Folium Camelliae sinensis pornographic movie, stalky tea, and the tea branch and leaf obtained after pruning manufacture for main
The tea element artware that material manufactures, the tea branch and leaf obtained after being mainly composed of tea dust, Folium Camelliae sinensis pornographic movie, stalky tea, and pruning
Easily degraded, compared with the artware of other materials manufacture, can produce the biggest ecological, environmental protective benefit.
3rd, owing to have employed, Folium Camelliae sinensis is unqualified, Folium Camelliae sinensis pornographic movie, stalky tea, and the tea branch and leaf obtained after pruning are main system
Producing material material, carrys out manufacturing process product, and the notable functional technical effect of generation is: artware, with the fragrance of tea, has abundant
Tea culture propagates succession characteristic element, can be welcome by market.
4th, this tea element artware is compared with tea cake formula tea artware, reaches high rigidity, high water proofing property, high mildew-resistant
Change, the requirement of weather resistance, have good durability, and profile is the most attractive in appearance.
Embodiment
It is exemplified below:
Embodiment 1:
(1) the raw-material preparation of tea element main body:
Method one: by unqualified for Folium Camelliae sinensis pulverizing, or Folium Camelliae sinensis is unqualified, pornographic movie, stalky tea mix after pulverizing, and obtains described tea element main body
Raw material；
Method two: obtain the most cheap tea element main body raw material with the following method:
In pruning two spring or the three spring months or autumn or branch and leaf in winter, tea branch and leaf pruning obtained wither, and then stack
Complete to half-fermented, knead crushed after being dried, obtain described tea element main body raw material.
(2) preparation of raw material composite:
Method one:
Above-mentioned tea element main body raw material is mixed homogeneously with melamino-formaldehyde (melamine) Moulding powder raw material, obtains described former material
Feed composition, the mass ratio of tea element main body raw material and melamino-formaldehyde (melamine) Moulding powder raw material is (3～8): (4～
10)；
Method two:
For the intensity of reinforcing material, by fine to above-mentioned tea element main body raw material, plant fiber material or Carbon fibe raw material or metal
Dimension raw material, melamino-formaldehyde (melamine) Moulding powder raw material mix homogeneously, obtain described raw material composite, and tea element main body is former
Material, plant fiber material or Carbon fibe raw material or metallic fiber raw material, the matter of melamino-formaldehyde (melamine) Moulding powder raw material
Amount ratio is (3～8): (0.5～2): (4～10)；
(3) described raw material composite is preheated；
(4) by preheated described raw material composite, add thermocompression forming in heating die cavity, obtain described tea element technique
Product.
The temperature upper limit preheating described raw material composite is 130 DEG C.
Described raw material composite is carried out the temperature range of thermocompression forming be 140～150 DEG C, pressure limit be 5～
40MPa。
Embodiment 2:
(1) the raw-material preparation of tea element main body:
Method one: by unqualified for Folium Camelliae sinensis pulverizing, or Folium Camelliae sinensis is unqualified, pornographic movie, stalky tea mix after pulverizing, and obtains described tea element main body
Raw material；
Method two: obtain the most cheap tea element main body raw material with the following method:
In pruning two spring or the three spring months or autumn or branch and leaf in winter, tea branch and leaf pruning obtained carry out severe and wither, then
Stack and complete to half-fermented, knead crushed after being dried, obtain described tea element main body raw material.
(2) preparation of raw material composite:
Method one:
Above-mentioned tea element main body raw material is mixed homogeneously with urea aldehyde Moulding powder raw material, obtains raw material composite, tea element master
Body raw material is (3～8) with the mass ratio of urea aldehyde Moulding powder raw material: (4～10)；
Method two:
For the intensity of reinforcing material, by fine to above-mentioned tea element main body raw material, plant fiber material or Carbon fibe raw material or metal
Dimension raw material, urine aldehyde Moulding powder raw material mix homogeneously, obtain described raw material composite, tea element main body raw material, Plant fiber
The mass ratio of raw material or Carbon fibe raw material or metallic fiber raw material, urea aldehyde Moulding powder raw material is (3～8): (0.5～2): (4～
10)；
(3) described raw material composite is preheated；
(4) by preheated described raw material composite, add thermocompression forming in heating die cavity, obtain described tea element technique
Product.
The temperature upper limit preheating described raw material composite is 130 DEG C.
Described raw material composite is carried out the temperature range of thermocompression forming be 140～150 DEG C, pressure limit be 5～
40MPa。
Claims (4)
1. a method of manufacturing technology for tea element artware, its technical characteristic is that processing step is as follows:
(1) the raw-material preparation of tea element main body:
Method one: by unqualified for Folium Camelliae sinensis pulverizing, or Folium Camelliae sinensis is unqualified, pornographic movie, stalky tea mix after pulverizing, and obtains described tea element main body
Raw material；Or
Method two: further, obtains the most cheap tea element main body raw material with the following method:
In pruning Camellia sinensis two spring or the three spring months or autumn or branch and leaf in winter, tea branch and leaf pruning obtained wither, then
Stack and complete to half-fermented, knead crushed after being dried, obtain described tea element main body raw material;
(2) preparation of raw material composite:
Method one:
Above-mentioned tea element main body raw material is mixed homogeneously with Moulding powder raw material, obtains described raw material composite；Or
Method two:
Further, for the intensity of reinforcing material, by above-mentioned tea element main body raw material, plant fiber material or Carbon fibe raw material
Or metallic fiber raw material, Moulding powder raw material mix homogeneously, obtain described raw material composite；
(3) described raw material composite is preheated；
(4) by preheated described raw material composite, add thermocompression forming in heating die cavity, obtain described tea element technique
Product.
The method of manufacturing technology of a kind of tea element artware the most according to claim 1, it technology is characterized in that described molding
Powder raw material is the Moulding powder raw material containing curing agent component or stabilizer component or resistance to water component or plasticizing component, or for containing
There is the Moulding powder raw material of curing agent component, stabilizer component, resistance to water component, plasticizing component blending constituent.
The method of manufacturing technology of a kind of tea element artware the most according to claim 1 and 2, it technology is characterized in that described
In raw material composite, tea element main body raw material is (3～8) with the mass ratio of Moulding powder raw material: (4～10) or tea unit
Element main body raw material, the mass ratio of plant fiber material or Carbon fibe raw material or metallic fiber raw material, Moulding powder raw material be (3～
8): (0.5～2): (4～10).
4. a tea element artware, it technology is characterized in that the method for manufacturing technology system used described in claim 1 or 2 or 3
Make.