CN106273977A - A kind of high-barrier composite membrane being applied to thermal insulation board - Google Patents
A kind of high-barrier composite membrane being applied to thermal insulation board Download PDFInfo
- Publication number
- CN106273977A CN106273977A CN201610719147.5A CN201610719147A CN106273977A CN 106273977 A CN106273977 A CN 106273977A CN 201610719147 A CN201610719147 A CN 201610719147A CN 106273977 A CN106273977 A CN 106273977A
- Authority
- CN
- China
- Prior art keywords
- microns
- vmpet
- thickness
- thin layer
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-barrier composite membrane being applied to thermal insulation board, sequentially sealed formed by a VMPET thin layer, VMPET12 thin layer, the 2nd VMPET thin layer, PE hot sealing layer, a described VMPET thin film layer thickness is 10 14 microns, VMPET12 thin film layer thickness is 12 microns, 2nd VMPET thin film layer thickness is 10 14 microns, and the thickness of PE hot sealing layer is 40 80 microns.Described PET hot sealing layer, a VMPET thin layer or PE hot sealing layer are provided with laser anti-counterfeit stricture of vagina.Packaging film of the present invention is sequentially sealed formed by a VMPET thin layer, VMPET12 thin layer, the 2nd VMPET thin layer, PE hot sealing layer, not only has good heat-proof quality, and has shading, prevents the performances such as ultraviolet irradiation.
Description
Technical field
The present invention relates to the packaging film of thermal insulation board, be specifically related to a kind of high-barrier composite membrane being applied to thermal insulation board.
Background technology
Compound soft dress film has very important status at electronic product such as the use on thermal insulation board, electric refrigerator etc..Electronics
Product category is various, and different products is different to the requirement of packaging material, such as shading, hinders wet, resistance oxygen, mouldability, some
Electronic product product require heat insulation, resistance to rupture, but currently used in many composite membranes seem not enough at heat insulation aspect.
Market, in the urgent need to a kind of composite, can keep good tear-resistant performance, and have good obstruct
Property, thermal insulation etc..
Summary of the invention
The technical problem to be solved is that the thermal isolation film heat-proof quality used on existing thermal insulation board is poor, impact
The normal use of thermal insulation board, present invention aim at providing a kind of high-barrier composite membrane being applied to thermal insulation board, uses VMPET
Film, PE film etc. are complex as a whole film, the problem solving to apply the heat-insulating problem difference of thermal isolation film on thermal insulation board.
The present invention is achieved through the following technical solutions:
A kind of high-barrier composite membrane being applied to thermal insulation board, by a VMPET thin layer, VMPET12 thin layer, the 2nd VMPET
Thin layer, PE hot sealing layer sequentially seal and form, and a described VMPET thin film layer thickness is 10 14 microns, VMPET12 thin layer
Thickness is 12 microns, and the 2nd VMPET thin film layer thickness is 10 14 microns, and the thickness of PE hot sealing layer is 40 80 microns, described
PET hot sealing layer, a VMPET thin layer or PE hot sealing layer are provided with laser anti-counterfeit stricture of vagina.
Wherein a VMPET thin layer, the 2nd VMPET thin layer are identical structure.VMPET, aluminizes for polyester aluminizer
Film, the characteristic of existing plastic sheeting, there is again the characteristic of metal.The effect that film surface is aluminized is shading, resisting ultraviolet radiation,
Both extended the shelf-life of content, and improve again the brightness of thin film, instead of aluminium foil to a certain extent, it may have inexpensive,
Attractive in appearance and preferable barrier property, therefore, aluminizer application in composite packaging is quite varied, is currently mainly applied to cookies
Deng be dried, puffed food packaging and some medicine, cosmetics outer package on.
Further, in order to preferably realize the present invention, a described VMPET thin film layer thickness is 10 microns, VMPET12
Thin film layer thickness is 12 microns, and the 2nd VMPET thin film layer thickness is 10 microns, and the thickness of PE hot sealing layer is 40 microns.
Further, in order to preferably realize the present invention, a described VMPET thin film layer thickness is 12 microns, VMPET12
Thin film layer thickness is 12 microns, and the 2nd VMPET thin film layer thickness is 12 microns, and the thickness of PE hot sealing layer is 50 microns.
Further, in order to preferably realize the present invention, a described VMPET thin film layer thickness is 13 microns, VMPET12
Thin film layer thickness is 12 microns, and the 2nd VMPET thin film layer thickness is 13 microns, and the thickness of PE hot sealing layer is 70 microns.
Further, in order to preferably realize the present invention, a described VMPET thin film layer thickness is 14 microns, VMPET12
Thin film layer thickness is 12 microns, and the 2nd VMPET thin film layer thickness is 14 microns, and the thickness of PE hot sealing layer is 80 microns.
The present invention compared with prior art, has such advantages as and beneficial effect:
Packaging film of the present invention is by a VMPET thin layer, VMPET12 thin layer, the 2nd VMPET thin layer, PE hot sealing layer sequentially
Heat-sealing forms, and not only has good heat-proof quality, and has shading, prevents the performances such as ultraviolet irradiation.
Accompanying drawing explanation
Accompanying drawing described herein is used for providing being further appreciated by the embodiment of the present invention, constitutes of the application
Point, it is not intended that the restriction to the embodiment of the present invention.In the accompanying drawings:
Fig. 1 is present configuration schematic diagram.
Labelling and corresponding parts title in accompanying drawing:
1-the oneth VMPET thin layer, 2-VMPET12 thin layer, 3-the 2nd VMPET thin layer;101-PE hot sealing layer.
Detailed description of the invention
For making the object, technical solutions and advantages of the present invention clearer, below in conjunction with embodiment and accompanying drawing, to this
Invention is described in further detail, and the exemplary embodiment of the present invention and explanation thereof are only used for explaining the present invention, do not make
For limitation of the invention.
Embodiment 1:
As it is shown in figure 1, a kind of high-barrier composite membrane being applied to thermal insulation board of the present invention, by a VMPET thin layer 1, VMPET12
Thin layer the 2, the 2nd VMPET thin layer 3, PE hot sealing layer 4 sequentially seal and form, and described VMPET thin layer 1 thickness is 10
14 microns, VMPET12 thin layer 2 thickness is 12 microns, and the 2nd VMPET thin layer 3 thickness is 10 14 microns, PE hot sealing layer 4
Thickness be 40 80 microns.It is provided with polyurethane binder between mutual each adjacent bed.
In a further embodiment, described PET hot sealing layer the 4, the oneth VMPET thin layer 1 or PE hot sealing layer 4 is provided with laser
False proof stricture of vagina.
In a further embodiment, described VMPET thin layer 1 thickness is 10 microns, VMPET12 thin layer 2 thickness
Being 12 microns, the 2nd VMPET thin layer 3 thickness is 10 microns, and the thickness of PE hot sealing layer 4 is 40 microns.
In a further embodiment, described VMPET thin layer 1 thickness is 12 microns, VMPET12 thin layer 2 thickness
Being 12 microns, the 2nd VMPET thin layer 3 thickness is 12 microns, and the thickness of PE hot sealing layer 4 is 50 microns.
In a further embodiment, described VMPET thin layer 1 thickness is 13 microns, VMPET12 thin layer 2 thickness
Being 12 microns, the 2nd VMPET thin layer 3 thickness is 13 microns, and the thickness of PE hot sealing layer 4 is 70 microns.
In a further embodiment, described VMPET thin layer 1 thickness is 14 microns, VMPET12 thin layer 2 thickness
Being 12 microns, the 2nd VMPET thin layer 3 thickness is 14 microns, and the thickness of PE hot sealing layer 4 is 80 microns.
Above-described detailed description of the invention, has been carried out the purpose of the present invention, technical scheme and beneficial effect further
Describe in detail, be it should be understood that the detailed description of the invention that the foregoing is only the present invention, be not intended to limit the present invention
Protection domain, all within the spirit and principles in the present invention, any modification, equivalent substitution and improvement etc. done, all should comprise
Within protection scope of the present invention.
Claims (5)
1. the high-barrier composite membrane being applied to thermal insulation board, it is characterised in that: by a VMPET thin layer (1), VMPET12
Thin layer (2), the 2nd VMPET thin layer (3), PE hot sealing layer (4) sequentially seal and form, and a described VMPET thin layer (1) is thick
Degree is 10 14 microns, and VMPET12 thin layer (2) thickness is 12 microns, and the 2nd VMPET thin layer (3) thickness is 10 14 micro-
Rice, the thickness of PE hot sealing layer (4) is 40 80 microns, described PET hot sealing layer (4), a VMPET thin layer (1) or PE heat-sealing
Layer (4) is provided with laser anti-counterfeit stricture of vagina.
A kind of high-barrier composite membrane being applied to thermal insulation board the most according to claim 1, it is characterised in that: described first
VMPET thin layer (1) thickness is 10 microns, and VMPET12 thin layer (2) thickness is 9 microns, the 2nd VMPET thin layer (3) thickness
Being 10 microns, the thickness of PE hot sealing layer (4) is 40 microns.
A kind of high-barrier composite membrane being applied to thermal insulation board the most according to claim 1, it is characterised in that: described first
VMPET thin layer (1) thickness is 12 microns, and VMPET12 thin layer (2) thickness is 9.5 microns, and the 2nd VMPET thin layer (3) is thick
Degree is 14 microns, and the thickness of PE hot sealing layer (4) is 50 microns.
A kind of high-barrier composite membrane being applied to thermal insulation board the most according to claim 1, it is characterised in that: described first
VMPET thin layer (1) thickness is 13 microns, and VMPET12 thin layer (2) thickness is 12 microns, and the 2nd VMPET thin layer (3) is thick
Degree is 13 microns, and the thickness of PE hot sealing layer (4) is 70 microns.
A kind of high-barrier composite membrane being applied to thermal insulation board the most according to claim 1, it is characterised in that: described first
VMPET thin layer (1) thickness is 14 microns, and VMPET12 thin layer (2) thickness is 12 microns, and the 2nd VMPET thin layer (3) is thick
Degree is 14 microns, and the thickness of PE hot sealing layer (4) is 80 microns.