CN106273968A - A kind of double-face leather fabric - Google Patents
A kind of double-face leather fabric Download PDFInfo
- Publication number
- CN106273968A CN106273968A CN201610617286.7A CN201610617286A CN106273968A CN 106273968 A CN106273968 A CN 106273968A CN 201610617286 A CN201610617286 A CN 201610617286A CN 106273968 A CN106273968 A CN 106273968A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyurethane resin
- agent
- mass ratio
- constituent mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of double-face leather fabric, including PU leather skin and batt, described PU leather skin is made up of polymeric surface layer, polymeric base layer and polymer base coat three part, and described polymer base coat penetrates in described batt.The present invention is compared with traditional processing technology, and fabric has good elasticity and voluptuousness, and polymer base coat and batt are tightly combined water-fastness, and one formula being capable of fabric produces, and reduces cost, improves production efficiency.
Description
[technical field]
The present invention relates to a kind of garment material field, be specifically related to a kind of double-face leather fabric.
[background technology]
In order to increase warmth retention property and the dicoration of fabric, people have invented Glove suede and have been combined all kinds of man-made hair or Glove suede and scald
Gold product is combined all kinds of man-made hair.Man-made hair includes two-layer, and one is batt, and one is base fabric.Traditional artificial fur is to use warp knit
Glove suede forms with the laminating of the base fabric of all kinds of man-made hairs by the way of glue or the fusion of sponge flame.Cloth in existing production line
Because batt absorbs water, so first doing leather layer, then batt is combined with base fabric synthetic leather, it is impossible to one through current
Road formula produces, it is proposed that a kind of double-face leather fabric.
[summary of the invention]
The purpose of the present invention solves the problems of the prior art exactly, proposes a kind of double-face leather fabric, it is possible to realize face
One formula of material produces, and reduces cost, improves production efficiency and fabric has good elastic voluptuousness.
For achieving the above object, the present invention proposes a kind of double-face leather fabric, including PU leather skin and batt, described
PU leather skin is made up of polymeric surface layer, polymeric base layer and polymer base coat three part, and described polymer base coat penetrates into
In described batt.
As preferably, described polymeric surface layer includes that following components and each constituent mass ratio are: polyether-polyurethane resin
50～90 parts, polyurethane resin 20～50 parts, dimethylformamide 160～240 parts, Masterbatch 3～8 parts, silicon system waterproofing agent 0.1
～0.6 part；Described polymeric base layer includes that following components and each constituent mass ratio are: polyether-polyurethane resin 80～120 parts,
N-Methyl pyrrolidone 20～50 parts, butanone 13～30 parts, dimethyl acetylamide 80～120 parts, microsphere foaming agent 3～8 parts, color
Master batch 1.5～2.5 parts, the ultra-fine fine particle calcium carbonate of nanometer 0.5～1.5 parts, water-based thickener 0.5～1.5 parts；Described polymer base coat includes
Following components and each constituent mass ratio be: polyurethane resin 45～75 parts, dimethylformamide 80～120 parts, firming agent 2.5
～6 parts, accelerator 1.5～2.5 parts, silicon system waterproofing agent 0.1～0.6 part.
As preferably, described polymeric surface layer includes that following components and each constituent mass ratio are: polyether-polyurethane resin
60～80 parts, polyurethane resin 25～45 parts, dimethylformamide 180～220 parts, Masterbatch 4～6 parts, silicon system waterproofing agent 0.2
～0.4 part；Described polymeric base layer includes that following components and each constituent mass ratio are: polyether-polyurethane resin 90～110 parts,
N-Methyl pyrrolidone 25～45 parts, butanone 17～23 parts, dimethyl acetylamide 90～110 parts, microsphere foaming agent 4～6 parts, color
Master batch 1.7～2.3 parts, the ultra-fine fine particle calcium carbonate of nanometer 0.8～1.2 parts, water-based thickener 0.8～1.2 parts；Described polymer base coat includes
Following components and each constituent mass ratio be: polyurethane resin 52～68 parts, dimethylformamide 90～110 parts, firming agent 3.4
～4.6 parts, accelerator 1.7～2.3 parts, silicon system waterproofing agent 0.34～0.46.
As preferably, each constituent mass ratio of described polymeric surface layer is: polyether-polyurethane resin 70 parts, polyurethane tree
30 parts of fat, dimethylformamide 200 parts, Masterbatch 5 parts, silicon system waterproofing agent 0.3 part；Each constituent mass of described polymeric base layer
Ratio is: polyether-polyurethane resin 100 parts, N-Methyl pyrrolidone 30 parts, butanone 20 parts, dimethyl acetylamide 100 parts, microsphere
Foaming agent 5 parts, Masterbatch 2 parts, the ultra-fine fine particle calcium carbonate of nanometer 1 part, water-based thickener 1 part；Described polymer base coat each constituent mass ratio
Example is: polyurethane resin 60 parts, dimethylformamide 100 parts, 4 parts of firming agent, accelerator 2 parts, silicon system waterproofing agent 0.4 part.
As preferably, each constituent mass ratio of described polymeric surface layer is: polyether-polyurethane resin 80 parts, polyurethane tree
25 parts of fat, dimethylformamide 180 parts, Masterbatch 6 parts, silicon system waterproofing agent 0.5 part；Each constituent mass of described polymeric base layer
Ratio is: polyether-polyurethane resin 100 parts, N-Methyl pyrrolidone 25 parts, butanone 25 parts, dimethyl acetylamide 90 parts, microsphere
Foaming agent 6 parts, Masterbatch 3 parts, the ultra-fine fine particle calcium carbonate of nanometer 1 part, water-based thickener 1 part；Described polymer base coat each constituent mass ratio
Example is: polyurethane resin 70 parts, dimethylformamide 90 parts, 3 parts of firming agent, accelerator 2 parts, silicon system waterproofing agent 0.6 part.
As preferably, each constituent mass ratio of described polymeric surface layer is: polyether-polyurethane resin 60 parts, polyurethane tree
45 parts of fat, dimethylformamide 220 parts, Masterbatch 4 parts, silicon system waterproofing agent 0.1 part；Each constituent mass of described polymeric base layer
Ratio is: polyether-polyurethane resin 107 parts, N-Methyl pyrrolidone 43 parts, butanone 18 parts, dimethyl acetylamide 109 parts, microsphere
Foaming agent 4 parts, Masterbatch 1.8 parts, the ultra-fine fine particle calcium carbonate of nanometer 1.2 parts, water-based thickener 0.8 part；The each component of described polymer base coat
Mass ratio is: polyurethane resin 53 parts, dimethylformamide 108 parts, 4.6 parts of firming agent, and accelerator 1.5 parts, silicon system is waterproof
Agent 0.2 part.
As preferably, the silicon system waterproofing agent in described polymeric surface layer uses Dow corning company Z-6689 waterproofing agent；
Described microsphere foaming agent uses the microsphere foaming agent of Beijing Hu Jin Science and Technology Ltd.；Water-based thickener uses Wuhuization to lead to technology
The V-2100 high efficiency water thickening agent of application company limited；Firming agent uses the NJ-1 epoxy resin of Wuxi light chemical company admittedly
Agent；Accelerator uses the unsaturated polyester resin accelerator cobalt iso-octoate of Tai Chang Resins Corporation；Silicon system in polymer base coat
Waterproofing agent is also adopted by Dow corning company Z-6689 waterproofing agent.
Beneficial effects of the present invention: the present invention is compared with traditional processing technology, and fabric has good elasticity and voluptuousness, poly-
Compound bottom and batt are tightly combined water-fastness, and one formula being capable of fabric produces, and reduces cost, improves production effect
Rate.
[detailed description of the invention]
The present invention proposes a kind of double-face leather fabric, and including PU leather skin and batt, described PU leather skin is by being polymerized
Thing top layer, polymeric base layer and polymer base coat three part composition, described polymer base coat penetrates in described batt.Described
Polymeric surface layer includes that following components and each constituent mass ratio are: polyether-polyurethane resin 50～90 parts, polyurethane resin 20
～50 parts, dimethylformamide 160～240 parts, Masterbatch 3～8 parts, silicon system waterproofing agent 0.1～0.6 part；Described polymer base
Layer includes that following components and each constituent mass ratio are: polyether-polyurethane resin 80～120 parts, N-Methyl pyrrolidone 20～50
Part, butanone 13～30 parts, dimethyl acetylamide 80～120 parts, microsphere foaming agent 3～8 parts, Masterbatch 1.5～2.5 parts, nanometer
Ultra-fine fine particle calcium carbonate 0.5～1.5 parts, water-based thickener 0.5～1.5 parts；Described polymer base coat includes following components and each component matter
Amount ratio is: polyurethane resin 45～75 parts, dimethylformamide 80～120 parts, firming agent 2.5～6 parts, accelerator 1.5～
2.5 parts, silicon system waterproofing agent 2.5～6 parts.Silicon system waterproofing agent in described polymeric surface layer uses Dow corning company Z-6689
Waterproofing agent；Described microsphere foaming agent uses the microsphere foaming agent of Beijing Hu Jin Science and Technology Ltd.；Water-based thickener uses Wuhu
Change logical technology and apply the V-2100 high efficiency water thickening agent of company limited；Firming agent uses the NJ-1 ring of Wuxi light chemical company
Epoxy resins firming agent；Accelerator uses the unsaturated polyester resin accelerator cobalt iso-octoate of Tai Chang Resins Corporation；Polymer base coat
In silicon system waterproofing agent be also adopted by Dow corning company Z-6689 waterproofing agent.
The specific embodiment of the present invention is:
Embodiment 1:
Each constituent mass ratio of polymeric surface layer is: polyether-polyurethane resin 70 parts, polyurethane resin 30 parts, dimethyl
Methanamide 200 parts, Masterbatch 5 parts, silicon system waterproofing agent 0.3 part；Each constituent mass ratio of polymeric base layer is: polyether-polyurethane
Resin 100 parts, N-Methyl pyrrolidone 30 parts, butanone 20 parts, dimethyl acetylamide 100 parts, microsphere foaming agent 5 parts, Masterbatch 2
Part, the ultra-fine fine particle calcium carbonate of nanometer 1 part, water-based thickener 1 part；Polymer base coat each constituent mass ratio is: polyurethane resin 60 parts, two
Methylformamide 100 parts, 4 parts of firming agent, accelerator 2 parts, silicon system waterproofing agent 0.4 part.
Embodiment 2:
Each constituent mass ratio of polymeric surface layer is: polyether-polyurethane resin 80 parts, polyurethane resin 25 parts, dimethyl
Methanamide 180 parts, Masterbatch 6 parts, silicon system waterproofing agent 0.5 part；Each constituent mass ratio of described polymeric base layer is: polyethers gathers
Urethane resin 100 parts, N-Methyl pyrrolidone 25 parts, butanone 25 parts, dimethyl acetylamide 90 parts, microsphere foaming agent 6 parts, color masterbatch
Grain 3 parts, the ultra-fine fine particle calcium carbonate of nanometer 1 part, water-based thickener 1 part；Described polymer base coat each constituent mass ratio is: polyurethane resin
70 parts, dimethylformamide 90 parts, 3 parts of firming agent, accelerator 2 parts, silicon system waterproofing agent 0.6 part.
Embodiment 3:
Each constituent mass ratio of polymeric surface layer is: polyether-polyurethane resin 60 parts, polyurethane resin 45 parts, dimethyl
Methanamide 220 parts, Masterbatch 4 parts, silicon system waterproofing agent 0.1 part；Each constituent mass ratio of described polymeric base layer is: polyethers gathers
Urethane resin 107 parts, N-Methyl pyrrolidone 43 parts, butanone 18 parts, dimethyl acetylamide 109 parts, microsphere foaming agent 4 parts, color
Master batch 1.8 parts, the ultra-fine fine particle calcium carbonate of nanometer 1.2 parts, water-based thickener 0.8 part；Described polymer base coat each constituent mass ratio is: poly-
Urethane resin 53 parts, dimethylformamide 108 parts, 4.6 parts of firming agent, accelerator 1.5 parts, silicon system waterproofing agent 0.2 part.
Above-described embodiment is the description of the invention, is not limitation of the invention, any to simple transformation of the present invention after
Scheme belong to protection scope of the present invention.
Claims (7)
1. a double-face leather fabric, it is characterised in that: including PU leather skin and batt, described PU leather skin is by polymer
Top layer, polymeric base layer and polymer base coat three part composition, described polymer base coat penetrates in described batt.
2. a kind of double-face leather fabric as claimed in claim 1, it is characterised in that: described polymeric surface layer includes following components
And each constituent mass ratio is: polyether-polyurethane resin 50～90 parts, polyurethane resin 20～50 parts, dimethylformamide 160
～240 parts, Masterbatch 3～8 parts, silicon system waterproofing agent 0.1～0.6 part；Described polymeric base layer includes following components and each component
Mass ratio is: polyether-polyurethane resin 80～120 parts, N-Methyl pyrrolidone 20～50 parts, butanone 13～30 parts, dimethyl
Acetamide 80～120 parts, microsphere foaming agent 3～8 parts, Masterbatch 1.5～2.5 parts, the ultra-fine fine particle calcium carbonate of nanometer 0.5～1.5 parts, aqueous
Thickening agent 0.5～1.5 parts；Described polymer base coat includes that following components and each constituent mass ratio are: polyurethane resin 45～
75 parts, dimethylformamide 80～120 parts, firming agent 2.5～6 parts, accelerator 1.5～2.5 parts, silicon system waterproofing agent 0.1～0.6
Part.
3. a kind of double-face leather fabric as claimed in claim 2, it is characterised in that: described polymeric surface layer includes following components
And each constituent mass ratio is: polyether-polyurethane resin 60～80 parts, polyurethane resin 25～45 parts, dimethylformamide 180
～220 parts, Masterbatch 4～6 parts, silicon system waterproofing agent 0.2～0.4 part；Described polymeric base layer includes following components and each component
Mass ratio is: polyether-polyurethane resin 90～110 parts, N-Methyl pyrrolidone 25～45 parts, butanone 17～23 parts,
Dimethyl acetylamide 90～110 parts, microsphere foaming agent 4～6 parts, Masterbatch 1.7～2.3 parts, the ultra-fine fine particle calcium carbonate of nanometer 0.8～
1.2 parts, water-based thickener 0.8～1.2 parts；Described polymer base coat includes that following components and each constituent mass ratio are: poly-ammonia
Ester resin 52～68 parts, dimethylformamide 90～110 parts, firming agent 3.4～4.6 parts, accelerator 1.7～2.3 parts, silicon system prevents
Water preparation 0.34～0.46 part.
4. a kind of double-face leather fabric as claimed in claim 2, it is characterised in that: each constituent mass of described polymeric surface layer
Ratio is: polyether-polyurethane resin 70 parts, polyurethane resin 30 parts, dimethylformamide 200 parts, and Masterbatch 5 parts, silicon system is waterproof
Agent 0.3 part；Each constituent mass ratio of described polymeric base layer is: polyether-polyurethane resin 100 parts, N-Methyl pyrrolidone 30
Part, butanone 20 parts, dimethyl acetylamide 100 parts, microsphere foaming agent 5 parts, Masterbatch 2 parts, the ultra-fine fine particle calcium carbonate of nanometer 1 part, aqueous increases
Thick dose 1 part；Described polymer base coat each constituent mass ratio is: polyurethane resin 60 parts, dimethylformamide 100 parts, solidification
Agent 4 parts, accelerator 2 parts, silicon system waterproofing agent 0.4 part.
5. a kind of double-face leather fabric as claimed in claim 2, it is characterised in that: each constituent mass of described polymeric surface layer
Ratio is: polyether-polyurethane resin 80 parts, polyurethane resin 25 parts, dimethylformamide 180 parts, and Masterbatch 6 parts, silicon system is waterproof
Agent 0.5 part；Each constituent mass ratio of described polymeric base layer is: polyether-polyurethane resin 100 parts, N-Methyl pyrrolidone 25
Part, butanone 25 parts, dimethyl acetylamide 90 parts, microsphere foaming agent 6 parts, Masterbatch 3 parts, the ultra-fine fine particle calcium carbonate of nanometer 1 part, aqueous thickening
Agent 1 part；Described polymer base coat each constituent mass ratio is: polyurethane resin 70 parts, dimethylformamide 90 parts, firming agent 3
Part, accelerator 2 parts, silicon system waterproofing agent 0.6 part.
6. a kind of double-face leather fabric as claimed in claim 2, it is characterised in that: each constituent mass of described polymeric surface layer
Ratio is: polyether-polyurethane resin 60 parts, polyurethane resin 45 parts, dimethylformamide 220 parts, and Masterbatch 4 parts, silicon system is waterproof
Agent 0.1 part；Each constituent mass ratio of described polymeric base layer is: polyether-polyurethane resin 107 parts, N-Methyl pyrrolidone 43
Part, butanone 18 parts, dimethyl acetylamide 109 parts, microsphere foaming agent 4 parts, Masterbatch 1.8 parts, the ultra-fine fine particle calcium carbonate of nanometer 1.2 parts, water
Property thickening agent 0.8 part；Described polymer base coat each constituent mass ratio is: polyurethane resin 53 parts, dimethylformamide 108
Part, 4.6 parts of firming agent, accelerator 1.5 parts, silicon system waterproofing agent 0.2 part.
7. a kind of double-face leather fabric as described in any one in claim 2 to 6, it is characterised in that: described polymer table
Silicon system waterproofing agent in Ceng uses Dow corning company Z-6689 waterproofing agent；Described microsphere foaming agent uses Beijing Hu Jin science and technology
The microsphere foaming agent of company limited；Water-based thickener uses the logical technology of Wuhuization to apply the V-2100 high efficiency water of company limited to increase
Thick dose；Firming agent uses the NJ-1 epoxy curing agent of Wuxi light chemical company；Accelerator uses Tai Chang Resins Corporation
Unsaturated polyester resin accelerator cobalt iso-octoate；Silicon system waterproofing agent in polymer base coat is also adopted by Dow corning company Z-
6689 waterproofing agents.