CN106273208A - A kind of injection molding alloy material Beautiful Weave Shape panel manufacture method - Google Patents
A kind of injection molding alloy material Beautiful Weave Shape panel manufacture method Download PDFInfo
- Publication number
- CN106273208A CN106273208A CN201610748973.2A CN201610748973A CN106273208A CN 106273208 A CN106273208 A CN 106273208A CN 201610748973 A CN201610748973 A CN 201610748973A CN 106273208 A CN106273208 A CN 106273208A
- Authority
- CN
- China
- Prior art keywords
- alloy material
- shape panel
- manufacture method
- weave shape
- beautiful weave
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of injection molding alloy material Beautiful Weave Shape panel manufacture method, comprises the steps: fusion plastification step: be in molten condition after alloy material is heated to 220 250 degrees Celsius standby;Injection moulding step: molten alloy material is injected in mould in 8 10 seconds with injection system under the conditions of 85 110MPa pressure, flow 85 90%;Cooling and demolding step: the overall demoulding after being cooled down by the mould being filled with alloy material, from obtaining Beautiful Weave Shape panel;Described alloy material is fusing point alloy between 170 220 degrees Celsius.The present invention uses the mode of shot molding i.e. to can get product, is suitable for large-scale batch production.Obtained by hollow out lattice product color lasting, material non-toxic is harmless, safety and environmental protection and easy to clean, life-time service is indeformable, colour-fast, easy for installation.
Description
Technical field
The invention belongs to mechanical field, relate to a kind of Beautiful Weave Shape panel manufacture method, be specifically related to a kind of injection molding
Alloy material Beautiful Weave Shape panel manufacture method.
Background technology
Hollow out is a kind of engraving technology, processes pierced process product.Traditional hollow out lattice mostly is woodwork, and it makes
Process characteristic is: selection sample preparation engraving polishing japanning timeliness;Process characteristic determines its time-consuming, Fei Cai, difficulty
Greatly, cost is high.The demand in market can not be met out and away.
In recent years, along with machinery manufacturing industry, the scientific development of automatic electronic, hollow out goods manufacturing technology and technique,
It it is no longer handicraft workshop formula;The automatic engraving technology of hyundai electronics has been obtained for generally using, plywood, fibre board, particieboard
Occur in and largely instead of traditional pure log board, their appearance and utilize and significantly shorten production system
Make the time, significantly reduce the production cost of hollow out series products;Compared with, log processing technology manual with traditional, use
Common mechanism wooden boards in the market, the modern hollow out production made with the automatic artistic carving of electronics makes and becomes more
For simple, convenient, economical;It is in particular in that such hollow out product market price is greatly reduced, has effectively widened product
Application, has obtained the generally accreditation of consumption market.
Along with progress, the development of science and technology in epoch, modern architecture, the fashionable fine work hollow out lattice of building material industry are able to horizontal stroke
Vacate existing so that traditional technology and the hollow out art application table in a lot of field such as city-building, environmental conservation, at home decoration
Now incisively and vividly;Fretwork technology exists and hollow out artistic effect is seen everywhere.
Traffic route guardrail that modern hollow out lattice product is mainly used in urban construction, footpath, greenbelt, park,
Lawn, Chi Hu, tourist attractions and house, garden, being effectively isolated and protecting of residence district;Various hotels, hotel, club, tea
Building, retail shop, exhibition room, office building, the aesthetic feeling decoration of private Residence and effect are cut off.
Although. modern hollow out lattice series products has fashion, attractive in appearance, simple, convenient, an economic dispatch plurality of advantages, but still
So also exist: waste of material greatly, not environmentally, fugitive color, many defects such as be weak to that burn into weatherability is poor, service life is limited, all
Many unfavorable factors constrain the market application of hollow out artistic product and promote.
As a example by wooden hollow out lattice, major defect have following some:
(1), weatherability is poor, changeableness: the plywood of mechanism, fibre board (being density board on market), particieboard all with wooden carefully
Broken material (or wood fibre) and bonding agent (glue, adhesive) adhesion compacting form, and the weatherability of usual bonding agent is the most poor,
High temperature is meltable, and low temperature is frangible, so, along with the extension (particularly outdoor use) of the time of use, goods there will be local shape;
(2) non-watertight: timber has significant moisture expansion and drying shrinkage.When moisture content is below fibre saturated point, moisture absorption has bright
Aobvious dilatancy phenomenon, has obvious contraction distortion phenomenon during desorbing.The immersion of water can make wooden finely divided material foaming, swollen
Swollen, there are the gross distortions such as layering, degumming, bubbling in fabrication;
(3) apt to rot: timber under conditions of smooth, the humidity of ventilating easily by fungi erosion;Fungus divides mycete, stain fungus and corruption
Rotten bacterium three kinds, it is less on timber impact that the first two plants bacterium, but rot fungi impact is the biggest.Rot fungi colonizes in the cell wall of timber,
It can secret out of a kind of ferment, and cell wall substance is resolved into simple nutrient, for self picked-up existence, thus causes timber to produce
Raw rotten, thoroughly to be destroyed, foxiness can make goods graying brown, light red, maroon, the color such as yellowish occur.Speckle, and
With a kind of unpleasant mycete abnormal smells from the patient.
(4) not corrosion resistant: wood materials not acid and alkali-resistance, most chemical reagent and liquid can make it dehydration carbonization occur
Phenomenon, makes timber product variable color, carbonization and decomposition occur;
(5) not environmentally: paint in the mechanism bonding agent of board making and product japanning, paint thinner all contain formaldehyde,
The harmful substance compositions such as urine aldehyde, toluene, second are stupid, impair one's health;
(6) waste is big: whether hand engraving, or mechanical engraving, and its processing technology feature determines its time-consuming, Fei Cai, and one
As the utilization rate of material below 50%.
Summary of the invention
For the technological deficiency overcoming existing hollow out lattice series products to exist, the invention discloses a kind of injection molding alloy
Material Beautiful Weave Shape panel manufacture method.
Injection molding alloy material Beautiful Weave Shape panel manufacture method of the present invention, comprises the steps:
Fusion plastification step: be in molten condition after alloy material is heated to 220-250 degree Celsius standby;
Injection moulding step: by molten alloy material under the conditions of 85-110MPa pressure, flow 85-90% with injection system at 8-
Inject in mould in 10 seconds;
Cooling and demolding step: the overall demoulding after being cooled down by the mould being filled with alloy material, from obtaining Beautiful Weave Shape panel;
Described alloy material is fusing point alloy between 170-220 degree Celsius.
Preferably, being heated to be in described fusion plastification step uses injection machine partition heating, and each adjacent region temperature difference is the highest
In 40 degrees Celsius.
Preferably, the alloy material in described fusion plastification step is carried out in a rotatable sealer barrel.
Preferably, the components by weight percent of described alloy material is: injection grade polypropylene 70-80%, PA-66 7-15%, calcium carbonate
Powder 5-10%, compatilizer 3-8%.
Preferably, before described fusion plastification step, also including the pre-treatment step to alloy material, described pretreatment walks
Rapid particularly as follows: alloy material is carried out baking the affected part after applying some drugs and does, baking temperature at 60-65 DEG C, 1-2 hour drying time.
Preferably, the type of cooling in described cooling and demolding step is water-cooled.
Use injection molding alloy material Beautiful Weave Shape panel manufacture method of the present invention, possess following superiority:
One. the present invention is no longer necessary to manually be carved by workman or cut welding, and the mode using shot molding is the most available
Product, rapid and convenient, reduce labor strength, personnel's skill set requirements is reduced, be suitable for large-scale batch production.
Two. hollow out lattice shape of product standard stereo obtained by the present invention, color is lasting, material non-toxic is harmless, safety
Environmental protection and easy to clean, life-time service is indeformable, colour-fast, easy for installation, and service life is long.
Three. manufacture process relative ease of the present invention is quick, equipment needed thereby without developing separately, use existing common technology to set
For completing the operation of whole Beautiful Weave Shape panel.
Four. in manufacture process of the present invention, effectively prevent waste of material, significantly reduce production cost.
Accompanying drawing explanation
Fig. 1 is a kind of detailed description of the invention schematic flow sheet of Beautiful Weave Shape panel manufacture method of the present invention;
Fig. 2 is the Beautiful Weave Shape panel one detailed description of the invention schematic diagram that Beautiful Weave Shape panel manufacture method of the present invention prepares.
Detailed description of the invention
Below in conjunction with the accompanying drawings, the detailed description of the invention of the present invention is described in further detail.
One of the present invention injection molding alloy material Beautiful Weave Shape panel manufacture method, comprises the steps:
Fusion plastification step: be in molten condition after alloy material is heated to 220-250 degree Celsius standby;
Injection moulding step: molten alloy material is injected with injection system under the conditions of 85-110MPa pressure, flow 85-90%
In mould;
Cooling and demolding step: the overall demoulding after being cooled down by the mould being filled with alloy material, from obtaining Beautiful Weave Shape panel;
Described alloy material is the fusing point alloy between 200-300 degree Celsius and containing macromolecular polymer.
Fig. 1 provides a kind of detailed description of the invention of the present invention, and the present invention utilizes mould molding technology disposably to generate pane,
Needing to manufacture mould according to pane pattern in advance, mould self can select high temperature resistant indeformable metal material the most stainless
More than the 300 degrees Celsius heat proof materials all without deformation such as steel, mould steel, nickel Lip river alloy.
Raw material, before fusion plastification, can carry out pretreatment, and to remove oligomer in alloy material, residual reaction helps
Agent, moisture and other impurity, these materials percentage ratio in alloy material is typically not greater than 0.05%;Pretreatment baking temperature
At 60-65 DEG C, moisture and oligomer and reaction promoter volatilization, 1-2 hour drying time can be made.
The effect of pretreatment is possible not only to fall the water in alloy and impurity treatment, and can carry out pre-to alloy material
Heat, shortens follow-up melted intensification required time.
Carry out fusion plastification after alloy material pretreatment, be in molten after alloy material is heated to 220-250 degree Celsius
Melt state standby;Owing to the alloy material in the present invention is that multicomponent mixture is modified, for making each component in heating process divide
Cloth is more uniform, it is to avoid the melted effect of uneven impact of being heated, heating process is preferably partition heating, and between adjacent region, the temperature difference is the highest
In 40 degrees Celsius so that it is a mild uniform process that alloy is converted into molten condition from solid.Due to each component fusing point
Differing, the alloy material in fusion plastification step can be carried out, in melting process in a rotatable sealer barrel
Quickly rotate and make the mixing of each component plasticate uniformly, seal to avoid oxidation and inclusion of air, and suppress the gasification of alloy material,
Fusion plastification step can be carried out in existing injection machine.
For avoiding fused materials to cool and solidify in injection moulding step, molten alloy material the most quickly should be pushed away
Going out, pressure limit should be injected in mould with injection system under the conditions of 85-110MPa pressure, flow 85-90%;Make fused materials
Fill up whole mould rapidly and uniformly.Described flow 85-90% is that the oil pump hydraulic oil output of injection machine is general in the prior art
Parameter, i.e. each second pass through oil pump output hydraulic pressure oil flow, are the oil pump output hydraulic pressure oil input injection under high pressure conditions herein
Oil cylinder pushing screw rod fast forwards through, and represents the stream of the fused materials sectional area making fused materials fast injection entrance mold cavity
The speed of amount, unit is m/s, such as 90% flow, represents 90 centimeters squared per second, and in the present invention, product design size is more than
500mm, material cumulative volume about 8000cm3 generally use the large size plastic jetting-moulding device of 1600 tons of clamp forces to carry out injection operation.
With types of cooling such as water-cooleds, the mould entirety containing fused materials is cooled subsequently, obtain final after the demoulding
Beautiful Weave Shape pane product.Water-cooling pattern is conducive to quickly cooling, makes mould utilize the two thermal coefficient of expansion different from material, natural
Come off.After mold releasability, get final product metering packing and put in storage.
In the present invention, containing polypropylene, polyamide, multicomponent high molecular polymer and calcium carbonate inorganic thing in alloy material
Composition, the combination property of alloy material is more preferable than single polypropylene, polyamide, it also avoid getting rusty of hollow out product simultaneously,
Reduce the weight of product, improve the corrosion resistance of product.
In the present invention, disclose the detailed description of the invention of a kind of high-molecular polymer alloy, the weight of described alloy material
Component is: injection grade polypropylene 70-80%, PA-66 7-15%, calcium carbonate powder 5-10%, compatilizer 3-8%.Wherein PA-66 is
The nylon66 fiber being commonly called as, compatilizer, also known as bulking agent, refers to, by means of intermolecular bonding force, promote incompatible two kind polymer
It is combined in one, and then obtains the auxiliary agent of stable blend.Compatilizer is generally selected maleic anhydride grafting, maleic anhydride monomer
Comparing Polarity comparision by force with other monomer, com-patibilising effect is preferable.
Inventor through repeatedly testing, above material blends modification manufacture high-molecular polymer alloy material, fusing point
Stable in 180-220 degree Celsius range, stable chemical nature under molten state, under room temperature, mechanical strength is high, has the most tough
Property, is unlikely to deform or ruptures, and works good with the coloring of various existing coloring earths, is suitable to coloring and beautifies pane.
Specific embodiment 1
Being preheated at 60 c by alloy material 2 hours, injection machine each district temperature respectively 100,140,180,220,260 is taken the photograph
Family name's degree, after being heated to molten condition, injects molten alloy material with injection system under the conditions of 110MPa pressure, flow 85%
In mould;The overall demoulding after being cooled down by the mould being filled with alloy material, from obtaining Beautiful Weave Shape panel.
Specific embodiment 2
Alloy material is preheated 1.5 hours under 65 degrees Celsius, injection machine each district temperature is respectively 100,130,140,160,
200,240 degrees Celsius, after being in molten condition after being heated to 240 degrees Celsius, by molten alloy material at 90MPa pressure, flow
Inject in mould with injection system under the conditions of 90%;The overall demoulding after being cooled down by the mould being filled with alloy material, from obtaining hollow out
Lattice board.
Specific embodiment 3
Being preheated 1.5 hours under 65 degrees Celsius by alloy material, injection machine each district temperature is respectively 100,130,160,200,240
Degree Celsius, after being heated to molten condition, molten alloy material is injected with injection system under the conditions of 90MPa pressure, flow 90%
In mould;The overall demoulding after being cooled down by the mould being filled with alloy material, from obtaining Beautiful Weave Shape panel.
Specific embodiment 4
Being preheated 2 hours under 65 degrees Celsius by alloy material, injection machine each district temperature respectively 100,140,180,230,260 is taken the photograph
Family name's degree, after being heated to molten condition, injects mould with injection system by molten alloy material under the conditions of 90MPa pressure, flow 90%
In tool;The overall demoulding after being cooled down by the mould being filled with alloy material, from obtaining Beautiful Weave Shape panel.
Previously described each preferred embodiment for the present invention, if the preferred implementation in each preferred embodiment
Not being the most contradictory or premised on a certain preferred implementation, each preferred implementation can any stack combinations
Use, the design parameter in described embodiment and embodiment merely to clearly state the invention proof procedure of inventor, and
Being not used to limit the scope of patent protection of the present invention, the scope of patent protection of the present invention is still as the criterion with its claims, all
It is the equivalent structure change using the description of the present invention and accompanying drawing content to be made, in like manner should be included in the protection model of the present invention
In enclosing.
Claims (6)
1. an injection molding alloy material Beautiful Weave Shape panel manufacture method, it is characterised in that comprise the steps:
Fusion plastification step: be in molten condition after alloy material is heated to 220-250 degree Celsius standby;
Injection moulding step: by molten alloy material under the conditions of 85-110MPa pressure, flow 85-90% with injection system at 8-
Inject in mould in 10 seconds;
Cooling and demolding step: the overall demoulding after being cooled down by the mould being filled with alloy material, from obtaining Beautiful Weave Shape panel;
Described alloy material is fusing point alloy between 170-220 degree Celsius.
Injection molding alloy material Beautiful Weave Shape panel manufacture method the most as claimed in claim 1, it is characterised in that described molten
Melting being heated to be in plasticizing process and use injection machine partition heating, each adjacent region temperature difference is not higher than 40 degrees Celsius.
Injection molding alloy material Beautiful Weave Shape panel manufacture method the most as claimed in claim 1, it is characterised in that described molten
The alloy material melted in plasticizing process is carried out in a rotatable sealer barrel.
Injection molding alloy material Beautiful Weave Shape panel manufacture method the most as claimed in claim 1, it is characterised in that described conjunction
The components by weight percent of gold copper-base alloy is: injection grade polypropylene 70-80%, PA-66 7-15%, calcium carbonate powder 5-10%, compatilizer 3-8%.
Injection molding alloy material Beautiful Weave Shape panel manufacture method the most as claimed in claim 1, it is characterised in that described molten
Before melting plasticizing process, also including the pre-treatment step to alloy material, described pre-treatment step is particularly as follows: enter alloy material
Row baking the affected part after applying some drugs do, baking temperature at 60-65 DEG C, 1-2 hour drying time.
Injection molding alloy material Beautiful Weave Shape panel manufacture method the most as claimed in claim 1, it is characterised in that described cold
But the type of cooling in demoulding step is water-cooled.