CN106270938A - Wear-resisting DTA flywheel shaft pulley - Google Patents
Wear-resisting DTA flywheel shaft pulley Download PDFInfo
- Publication number
- CN106270938A CN106270938A CN201610899374.0A CN201610899374A CN106270938A CN 106270938 A CN106270938 A CN 106270938A CN 201610899374 A CN201610899374 A CN 201610899374A CN 106270938 A CN106270938 A CN 106270938A
- Authority
- CN
- China
- Prior art keywords
- flux
- cored wire
- sandwich layer
- dta
- hard alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of wear-resisting DTA flywheel shaft pulley, belong to technical field of mechanical equipment.Being made up of the hollow cylindrical sandwich layer of both ends open and the hard alloy abrasion-resistant layer being positioned at sandwich layer periphery, described hard alloy abrasion-resistant layer surface is U-type groove shape.Described hard alloy abrasion-resistant layer includes the composition of following mass percent: Mo:28 40%, Cr:3.2 6%, C:0.3 2.3%, Mn:1 5%, Cu:0.5 3%, Si:0.3 5%, N:0.2 2.4%, and remainder is ferrum.The present invention solve shell-rinding wheel after the phenomenon of abrasion that the most easily occurs of swage pulley, thus the working cycle of swage wheel after extending shell-rinding wheel, solve the defect of its frequent failure, decrease the consumption of swage pulley after shell-rinding wheel, saved cost.
Description
Technical field
The present invention relates to a kind of wear-resisting DTA flywheel shaft pulley, belong to technical field of mechanical equipment.
Background technology
DTA flywheel shaft pulley is one of important composition parts, and its performance quality directly affects strander production capacity
Performance, the consumption of power, stable working and the service life of other related components.GT3/G2 crosses sth. made by twisting pulley in work
In, owing to running up, at its working surface, abrasion easily occurs thus cause seminess.
Summary of the invention
The technical problem to be solved is to provide a kind of wear-resisting DTA flywheel shaft pulley.
Wear-resisting DTA flywheel shaft pulley, is closed by the hollow cylindrical sandwich layer of both ends open and the hard being positioned at sandwich layer periphery
Gold wearing layer composition, described hard alloy abrasion-resistant layer surface is U-type groove shape.
As priority option, described hard alloy abrasion-resistant layer includes the composition of following mass percent: Mo:28-40%,
Cr:3.2-6%, C:0.3-2.3%, Mn:1-5%, Cu:0.5-3%, Si:0.3-5%, N:0.2-2.4%, remainder is ferrum.
As preference, described hard alloy abrasion-resistant layer is to be deposited over above sandwich layer by deposition techniques.
The preparation method of described wear-resisting DTA flywheel shaft pulley, comprises the steps:
One), flux-cored wire is prepared: described flux-cored wire skin material is carbon steel or rustless steel, and remaining powder is by mixed powder machine
Mixing and within 2-3 hour, be fabricated to flux-cored wire, the composition of whole flux-cored wire is Mo:28-40%, Cr:3.2-6%, C:0.3-2.3%,
Mn:1-5%, Cu:0.5-3, Si:0.3-5%, N:0.2-2.4%, remainder is ferrum;The a diameter of 2.4mm of described flux-cored wire;
Two), cylindric sandwich layer being heated up to 220-250 DEG C, the flux-cored wire then step one prepared is by regulation electric current heap
It is welded in sandwich layer periphery, then will be welded with the sandwich layer outer wrap insulation material of flux-cored wire, after being incubated ten hours and get final product.
As preference, in described step 2, electric current is between 180-185 ampere.
As preferably, the material of described substrate core is steel.
The Advantageous Effects of the present invention: base steel core and novel hard alloy are combined in one by the way of deposition
Rising, novel hard alloy composition includes Mo, Cr, C, Mn, Cu, Si, N, Fe, simultaneously containing a large amount of Mo elements in composition, in friction
Time become the product of oxide of Mo, the presence of which can have certain lubrication, solve alignment after shell-rinding wheel contact surface
The phenomenon of the abrasion that device pulley the most easily occurs, thus the working cycle of swage wheel after extending shell-rinding wheel, solve
The defect of its frequent failure, decreases the consumption of swage pulley after shell-rinding wheel, has saved cost.
Accompanying drawing explanation
Fig. 1, wear-resisting DTA flywheel shaft pulley structure schematic diagram, 1, cylindric sandwich layer, 2-wearing layer, 3-U shape groove.
Detailed description of the invention
The present invention is described in further detail with detailed description of the invention below in conjunction with the accompanying drawings:
In Fig. 1, wear-resisting DTA flywheel shaft pulley, by the hollow cylindrical sandwich layer of both ends open and be positioned at the hard of sandwich layer periphery
Matter alloy wear-resisting layer forms, and described hard alloy abrasion-resistant layer surface is U-type groove shape.
Hard alloy abrasion-resistant layer of the present invention includes the composition of following mass percent: MO:28-40, Cr:3.2-6%,
C:0.3-2.3%, Mn:1-5%, Cu:0.5-3%, Si:0.3-5%, N:0.2-2.4%, remainder is ferrum.
Embodiment 1,
One), preparing flux-cored wire: described flux-cored wire skin material is carbon steel, remaining powder was by mixed powder machine mixing 2-3 hour
Being fabricated to flux-cored wire, the composition of whole flux-cored wire is Mo:28%, Cr:3.2%, C:0.3%, Mn:1%, Cu:0.5%, Si:
0.3%, N:0.2%, remainder is ferrum;The a diameter of 2.4mm of described flux-cored wire;
Two), by cylindric sandwich layer being heated up to 220 DEG C, the flux-cored wire then step one prepared is welded in by regulation electric current heap
Sandwich layer periphery, then will be welded with the sandwich layer outer wrap insulation material of flux-cored wire, after being incubated ten hours and get final product.
Embodiment 2
One), preparing flux-cored wire: described flux-cored wire skin material is rustless steel, remaining powder is little by mixed powder machine mixing 2-3
Time be fabricated to flux-cored wire, the composition of whole flux-cored wire is Mo:40%, Cr:6%, C:2.3%, Mn:5%, Cu:3%, Si:5%,
N:2.4%, remainder is ferrum;The a diameter of 2.4mm of described flux-cored wire;
Two), by cylindric sandwich layer being heated up to 250 DEG C, the flux-cored wire then step one prepared is welded in by regulation electric current heap
Sandwich layer periphery, then will be welded with the sandwich layer outer wrap insulation material of flux-cored wire, after being incubated ten hours and get final product.
Product of the present invention uses in Wuhan one factory, its life-span upgrading 5 times.The Advantageous Effects of the present invention: by steel
Base core and novel hard alloy combine by the way of deposition, novel hard alloy composition include Mo, Cr, C, Mn,
Cu, Si, N, Fe, simultaneously containing a large amount of Mo elements in composition, become the product of the oxide of Mo when friction, and the presence of which can be right
Contact surface has certain lubrication, the phenomenon of the abrasion that swage pulley the most easily occurs after solving shell-rinding wheel,
Thus the working cycle of swage wheel after extending shell-rinding wheel, solve the defect of its frequent failure, decrease school after shell-rinding wheel
The consumption of straight device pulley, has saved cost.
Claims (6)
1. a wear-resisting DTA flywheel shaft pulley, it is characterised in that by the hollow cylindrical sandwich layer of both ends open and be positioned at sandwich layer
The hard alloy abrasion-resistant layer composition of periphery, described hard alloy abrasion-resistant layer surface is U-type groove shape.
DTA flywheel shaft pulley the most according to claim 1, it is characterised in that under described hard alloy abrasion-resistant layer includes
State the composition of mass percent: Mo:28-40%, Cr:3.2-6%, C:0.3-2.3%, Mn:1-5%, Cu:0.5-3%, Si:0.3-
5%, N:0.2-2.4%, remainder is ferrum.
DTA flywheel shaft pulley the most according to claim 1, it is characterised in that described hard alloy abrasion-resistant layer is to pass through
Deposition techniques is deposited over above sandwich layer.
4. the preparation method of DTA flywheel shaft pulley wear-resisting described in claim 1, it is characterised in that comprise the steps:
One), flux-cored wire is prepared: described flux-cored wire skin material is carbon steel or rustless steel, and remaining powder is by mixed powder machine
Mixing and within 2-3 hour, be fabricated to flux-cored wire, the composition of whole flux-cored wire is Mo:28-40%, Cr:3.2-6%, C:0.3-2.3%,
Mn:1-5%, Cu:0.5-3, Si:0.3-5%, N:0.2-2.4%, remainder is ferrum;The a diameter of 2.4mm of described flux-cored wire;
Two), cylindric sandwich layer being heated up to 220-250 DEG C, the flux-cored wire then step one prepared is by regulation electric current heap
It is welded in sandwich layer periphery, then will be welded with the sandwich layer outer wrap insulation material of flux-cored wire, after being incubated ten hours and get final product.
Method the most according to claim 4, it is characterised in that in described step 2, electric current is between 180-185 ampere.
Method the most according to claim 4, it is characterised in that the material of described substrate core is steel.