CN106263264A - A kind of thermoplastic shoe pad and processing method thereof and using method - Google Patents
A kind of thermoplastic shoe pad and processing method thereof and using method Download PDFInfo
- Publication number
- CN106263264A CN106263264A CN201610671740.7A CN201610671740A CN106263264A CN 106263264 A CN106263264 A CN 106263264A CN 201610671740 A CN201610671740 A CN 201610671740A CN 106263264 A CN106263264 A CN 106263264A
- Authority
- CN
- China
- Prior art keywords
- eva
- layer
- bed
- shoe pad
- buffer layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of thermoplastic shoe pad, including ductile bed and buffer layer, described ductile bed is made up of EVA layer, terylene layer the most successively, described buffer layer is made up of airport EVA PE composite bed, PP layer, airport EVA PP composite bed the most successively, described ductile bed is positioned at the top of buffer layer, and the lower surface bonds of described buffer layer has magic hook.The invention also discloses processing method and the using method of thermoplastic shoe pad.The thermoplastic shoe pad resilience of the present invention is high, good damping effect, fixes intensity height with shoe body, and thermoplastic is effective, and entirely appropriate individual vola physiological curve shape, force dispersion is uniform, and good damping effect is comfortable and easy to wear, has good market popularization value.
Description
Technical field
The present invention relates to shoe pad field, be specifically related to a kind of thermoplastic shoe pad and processing method thereof and using method.
Background technology
Shoe pad is the very important ingredient of shoe lining, and it is the direct pressure-containing member that foot contacts with shoe body, has point
Dissipate the effect of focus pressure, protect sole safety, largely determine people's comfort level when wearing footwear, for human foot
The shape at the end, profile and curved surface change etc., the produced impact of shoe pad is clearly.At present, shoe pad is with reference to general in producing
The foot-shape of ordinary people is produced in enormous quantities in the factory, and therefore they are not shape and the feature mating individual completely, along with people
Raising that the comfort level write is required, the shoe pad of this large-scale production can not meet everybody needs.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of thermoplastic shoe pad improving wearing comfort and processing side thereof
Method and using method.
For realizing object above, the present invention is achieved by the following technical programs:
A kind of thermoplastic shoe pad, including ductile bed and buffer layer, described ductile bed is the most successively by EVA layer, terylene layer
Composition, described buffer layer is made up of airport EVA-PE composite bed, PP layer, airport EVA-PP composite bed the most successively,
Described ductile bed is positioned at the top of buffer layer, and the lower surface bonds of described buffer layer has magic hook.
Preferably, the specification of described EVA layer is thick 2.5mm, hardness 18-24C；The specification of described terylene is 50g/m2；Institute
The specification stating airport EVA-PE composite bed is thick 2-5mm, hardness 50-55C；Described PP thickness 0.4mm；Described airport EVA-
The specification of PP composite bed is thick 3mm, hardness 50-55C.
The processing method of thermoplastic shoe pad, comprises the following steps:
1) being processed by the upper surface aqueous EVA inorganic agent of EVA layer, after drying, lower surface crosses water-based glue, and washs
Synthetic fibre laminating closes and is bonded together, and forms ductile bed；
2) airport EVA-PE composite bed, PP layer, airport EVA-PP composite bed being crossed water-based glue respectively, magic hook is coated with
Brush water-based glue, laminating bonding is received together successively, forms buffer layer；
3) ductile bed and buffer layer are respectively put into hothouse to toast；
4) lower surface of ductile bed after baking and the upper surface of buffer layer are fit together, secondary baking, it is pressed into
Type, punching, severing i.e. obtains product.
Preferably, described step 3) in the baking condition of ductile bed be 100C, 48-52s；The baking condition of described ductile bed
For 80C, 55-60s.
Preferably, described secondary baking is to be placed down by ductile bed, toasts 23-28s under 150C.
Preferably, described step 4) in pressing condition be 47-52s under 25T pressure.
The using method of thermoplastic shoe pad, is that thermoplastic shoe pad is placed on heating plasticizing in microwave oven, then shoe pad is taken out
Make ductile bed be placed on rear portion upward and have heel shape pit, on the mould that front portion is upturned, moulding by making employment foot step on,
It is exactly to be suitable for the shoe pad that I uses after cooling.
The present invention has the beneficial effect that:
1, after EVA layer being processed with aqueous EVA inorganic agent, its surface roughness is increased, with common shoe insole surface fabric phase
Ratio, comfort level and antiskid property are more preferable, and difficult drop-off；
2, thermoplastic layer uses EVA and terylene to be combined, and effectively prevents contraction distortion in printing process, and thermoplastic is effective；
3, buffer layer uses three-layer composite structure, and resilience is high, good damping effect, and PP layer can keep hard bottom shoe pad
Degree has Gao Dingli transmission, heat deformable simultaneously；
4, use magic hook directly the most bonding with shoe body, fixing intensity height, it is difficult to slip and runs out of, it is to avoid due to shoe pad and footwear
What body separation caused wears discomfort problem, and be conducive to walking and riding stability.
5, thermoplastic shoe pad of the present invention can be according to individual's foot type customization, entirely appropriate individual vola physiological curve shape,
Whole vola comprehensive engagement shoe pad during walking, foot bottom stress is uniformly dispersed, and arch of foot obtains torr to be held up, and wears comfortable, good damping effect,
6, the thermoplastic sock processing method of the present invention is simple, sizing is easy, with low cost, has wide market prospect.
Detailed description of the invention
For making the purpose of the embodiment of the present invention, technical scheme and advantage clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment rather than whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art are not making
The every other embodiment obtained under creative work premise, broadly falls into the scope of protection of the invention.
Embodiment 1:
A kind of thermoplastic shoe pad, including ductile bed and buffer layer, described ductile bed is the most successively by EVA layer, terylene layer
Composition, described buffer layer is made up of airport EVA-PE composite bed, PP layer, airport EVA-PP composite bed the most successively,
Described ductile bed is positioned at the top of buffer layer, and the lower surface bonds of described buffer layer has magic hook.Wherein, the specification of EVA layer is
Thick 2.5mm, hardness 21C；The specification of terylene is 50g/m2；The specification of airport EVA-PE composite bed is thick 4mm, hardness 53C；PP
Thickness 0.4mm；The specification of airport EVA-PP composite bed is thick 3mm, hardness 53C.
The processing method of thermoplastic shoe pad, comprises the following steps:
1) being processed by the upper surface aqueous EVA inorganic agent of EVA layer, after drying, lower surface crosses water-based glue, and washs
Synthetic fibre laminating closes and is bonded together, and forms ductile bed；
2) airport EVA-PE composite bed, PP layer, airport EVA-PP composite bed being crossed water-based glue respectively, magic hook is coated with
Brush water-based glue, laminating bonding is received together successively, forms buffer layer；
3) ductile bed and buffer layer are respectively put into hothouse to toast, wherein the baking condition of ductile bed be 100C,
50s, the baking condition of ductile bed is 80C, 60s；
4) lower surface of ductile bed after baking and the upper surface of buffer layer being fit together, secondary baking, by plasticity
Layer is placed down, toasts 25s under 150C, and pressing 50s molding under 25T pressure, punching, severing i.e. obtains product.
The using method of thermoplastic shoe pad, is that thermoplastic shoe pad is placed on heating plasticizing in microwave oven, then shoe pad is taken out
Make ductile bed be placed on rear portion upward and have heel shape pit, on the mould that front portion is upturned, moulding by making employment foot step on,
It is exactly to be suitable for the shoe pad that I uses after cooling.
Embodiment 2:
A kind of thermoplastic shoe pad, including ductile bed and buffer layer, described ductile bed is the most successively by EVA layer, terylene layer
Composition, described buffer layer is made up of airport EVA-PE composite bed, PP layer, airport EVA-PP composite bed the most successively,
Described ductile bed is positioned at the top of buffer layer, and the lower surface bonds of described buffer layer has magic hook.Wherein, the specification of EVA layer is
Thick 2.5mm, hardness 18C；The specification of terylene is 50g/m2；The specification of airport EVA-PE composite bed is thick 2mm, hardness 50C；PP
Thickness 0.4mm；The specification of airport EVA-PP composite bed is thick 3mm, hardness 50C.
The processing method of thermoplastic shoe pad, comprises the following steps:
1) being processed by the upper surface aqueous EVA inorganic agent of EVA layer, after drying, lower surface crosses water-based glue, and washs
Synthetic fibre laminating closes and is bonded together, and forms ductile bed；
2) airport EVA-PE composite bed, PP layer, airport EVA-PP composite bed being crossed water-based glue respectively, magic hook is coated with
Brush water-based glue, laminating bonding is received together successively, forms buffer layer；
3) ductile bed and buffer layer are respectively put into hothouse to toast, wherein, the baking condition of ductile bed be 100C,
48s；The baking condition of described ductile bed is 80C, 55s；
4) lower surface of ductile bed after baking and the upper surface of buffer layer being fit together, secondary baking, by plasticity
Layer is placed down, toasts 23s under 150C, and pressing 47s molding under 25T pressure, punching, severing i.e. obtains product.
The using method of thermoplastic shoe pad, with embodiment 1.
Embodiment 3:
A kind of thermoplastic shoe pad, including ductile bed and buffer layer, described ductile bed is the most successively by EVA layer, terylene layer
Composition, described buffer layer is made up of airport EVA-PE composite bed, PP layer, airport EVA-PP composite bed the most successively,
Described ductile bed is positioned at the top of buffer layer, and the lower surface bonds of described buffer layer has magic hook.Wherein, the specification of EVA layer is
Thick 2.5mm, hardness 24C；The specification of terylene is 50g/m2；The specification of airport EVA-PE composite bed is thick 5mm, hardness 55C；PP
Thickness 0.4mm；The specification of airport EVA-PP composite bed is thick 3mm, hardness 55C.
The processing method of thermoplastic shoe pad, comprises the following steps:
1) being processed by the upper surface aqueous EVA inorganic agent of EVA layer, after drying, lower surface crosses water-based glue, and washs
Synthetic fibre laminating closes and is bonded together, and forms ductile bed；
2) airport EVA-PE composite bed, PP layer, airport EVA-PP composite bed being crossed water-based glue respectively, magic hook is coated with
Brush water-based glue, laminating bonding is received together successively, forms buffer layer；
3) ductile bed and buffer layer are respectively put into hothouse to toast, wherein, the baking condition of ductile bed be 100C,
52s；The baking condition of described ductile bed is 80C, 60s；
4) lower surface of ductile bed after baking and the upper surface of buffer layer being fit together, secondary baking, by plasticity
Layer is placed down, toasts 28s under 150C, and pressing 52s molding under 25T pressure, punching, severing i.e. obtains product.
The using method of thermoplastic shoe pad, with embodiment 1.
Embodiment 4:
A kind of thermoplastic shoe pad, including ductile bed and buffer layer, described ductile bed is the most successively by EVA layer, terylene layer
Composition, described buffer layer is made up of airport EVA-PE composite bed, PP layer, airport EVA-PP composite bed the most successively,
Described ductile bed is positioned at the top of buffer layer, and the lower surface bonds of described buffer layer has magic hook.Wherein, the specification of EVA layer is
Thick 2.5mm, hardness 20C；The specification of terylene is 50g/m2；The specification of airport EVA-PE composite bed is thick 4mm, hardness 52C；PP
Thickness 0.4mm；The specification of airport EVA-PP composite bed is thick 3mm, hardness 55C.
The processing method of thermoplastic shoe pad, comprises the following steps:
1) being processed by the upper surface aqueous EVA inorganic agent of EVA layer, after drying, lower surface crosses water-based glue, and washs
Synthetic fibre laminating closes and is bonded together, and forms ductile bed；
2) airport EVA-PE composite bed, PP layer, airport EVA-PP composite bed being crossed water-based glue respectively, magic hook is coated with
Brush water-based glue, laminating bonding is received together successively, forms buffer layer；
3) ductile bed and buffer layer are respectively put into hothouse to toast, wherein, the baking condition of ductile bed be 100C,
50s；The baking condition of described ductile bed is 80C, 55s；
4) lower surface of ductile bed after baking and the upper surface of buffer layer being fit together, secondary baking, by plasticity
Layer is placed down, toasts 25s under 150C, and pressing 50s molding under 25T pressure, punching, severing i.e. obtains product.
The using method of thermoplastic shoe pad, with embodiment 1.
Embodiment 5:
A kind of thermoplastic shoe pad, including ductile bed and buffer layer, described ductile bed is the most successively by EVA layer, terylene layer
Composition, described buffer layer is made up of airport EVA-PE composite bed, PP layer, airport EVA-PP composite bed the most successively,
Described ductile bed is positioned at the top of buffer layer, and the lower surface bonds of described buffer layer has magic hook.Wherein, the specification of EVA layer is
Thick 2.5mm, hardness 21C；The specification of terylene is 50g/m2；The specification of airport EVA-PE composite bed is thick 3mm, hardness 55C；PP
Thickness 0.4mm；The specification of airport EVA-PP composite bed is thick 3mm, hardness 53C.
The processing method of thermoplastic shoe pad, comprises the following steps:
1) being processed by the upper surface aqueous EVA inorganic agent of EVA layer, after drying, lower surface crosses water-based glue, and washs
Synthetic fibre laminating closes and is bonded together, and forms ductile bed；
2) airport EVA-PE composite bed, PP layer, airport EVA-PP composite bed being crossed water-based glue respectively, magic hook is coated with
Brush water-based glue, laminating bonding is received together successively, forms buffer layer；
3) ductile bed and buffer layer are respectively put into hothouse to toast, wherein, the baking condition of ductile bed be 100C,
50s；The baking condition of described ductile bed is 80C, 60s；
4) lower surface of ductile bed after baking and the upper surface of buffer layer being fit together, secondary baking, by plasticity
Layer is placed down, toasts 26s under 150C, and pressing 50s molding under 25T pressure, punching, severing i.e. obtains product.
The using method of thermoplastic shoe pad, with embodiment 1.
In sum, the thermoplastic shoe pad resilience of the present invention is high, good damping effect, fixes intensity height, and thermoplastic with shoe body
Effective, entirely appropriate individual vola physiological curve shape, force dispersion is uniform, and good damping effect is comfortable and easy to wear, has well
Market popularization value.
Above example only in order to technical scheme to be described, is not intended to limit；Although with reference to previous embodiment
The present invention is described in detail, it will be understood by those within the art that: it still can be to aforementioned each enforcement
Technical scheme described in example is modified, or wherein portion of techniques feature is carried out equivalent；And these amendment or
Replace, do not make the essence of appropriate technical solution depart from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (7)
1. a thermoplastic shoe pad, it is characterised in that including ductile bed and buffer layer, described ductile bed is the most successively by EVA
Layer, terylene layer composition, described buffer layer is the most successively by airport EVA-PE composite bed, PP layer, airport EVA-PP the most again
Conjunction layer forms, and described ductile bed is positioned at the top of buffer layer, and the lower surface bonds of described buffer layer has magic hook.
2. thermoplastic shoe pad as claimed in claim 1, it is characterised in that the specification of described EVA layer is thick 2.5mm, hardness 18-
24C；The specification of described terylene is 50g/m2；The specification of described airport EVA-PE composite bed is thick 2-5mm, hardness 50-55C；
Described PP thickness 0.4mm；The specification of described airport EVA-PP composite bed is thick 3mm, hardness 50-55C.
3. the processing method of thermoplastic shoe pad as claimed in claim 1 or 2, it is characterised in that comprise the following steps:
1) being processed by the upper surface aqueous EVA inorganic agent of EVA layer, after drying, lower surface crosses water-based glue, with terylene layer
Laminating is bonded together, and forms ductile bed；
2) airport EVA-PE composite bed, PP layer, airport EVA-PP composite bed being crossed water-based glue respectively, magic hook is coated with swabbing
Property glue, successively laminating bonding receive together, formed buffer layer；
3) ductile bed and buffer layer are respectively put into hothouse to toast；
4) lower surface of ductile bed after baking and the upper surface of buffer layer are fit together, secondary baking, pressing and forming, punching
Hole, severing i.e. obtains product.
4. the processing method of thermoplastic shoe pad as claimed in claim 3, it is characterised in that described step 3) in the baking of ductile bed
Condition is 100C, 48-52s；The baking condition of described ductile bed is 80C, 55-60s.
5. the processing method of thermoplastic shoe pad as claimed in claim 3, it is characterised in that described secondary baking is by ductile bed court
Lower placement, toasts 23-28s under 150C.
6. the processing method of thermoplastic shoe pad as claimed in claim 3, it is characterised in that described step 4) in pressing condition be
47-52s under 25T pressure.
7. the using method of thermoplastic shoe pad as claimed in claim 1 or 2, it is characterised in that be that thermoplastic shoe pad is placed on micro-
Heating plasticizing in ripple stove, then making ductile bed be placed on rear portion upward shoe pad taking-up has heel shape pit, and front portion is upturned
Mould on, moulding by making employment foot step on, after cooling be exactly be suitable for I use shoe pad.