CN106245465A - A kind of method of discarded paper packing material regeneration - Google Patents
A kind of method of discarded paper packing material regeneration Download PDFInfo
- Publication number
- CN106245465A CN106245465A CN201610565332.3A CN201610565332A CN106245465A CN 106245465 A CN106245465 A CN 106245465A CN 201610565332 A CN201610565332 A CN 201610565332A CN 106245465 A CN106245465 A CN 106245465A
- Authority
- CN
- China
- Prior art keywords
- straw
- packing material
- paper
- mixture
- paper packing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of method that the invention discloses discarded paper packing material regeneration, comprise the following steps: the waste paper of recovery is transported to hydrabrusher and carries out size degradation by (1), after hydrabrusher carries out making beating deinking to waste paper, send into deflaker separation impurity, send into after obtaining discongesting mixture after the contamination precipitations such as sand ash are separated by sand cleaning machine and make pure slurry;(2) straw drying being processed into crushing straw, starch and water to mix in 1: 4 ratio, high-temperature stirring becomes gelatinized corn starch, is mixed with weight proportion 1: 1 with gelatinized corn starch by crushing straw, pours composite molding in mould after stirring into.It is big that the present invention can obtain intensity and deflection, anti tear and have certain toughness, elastic paper packing material.And the present invention utilizes waste resource and renewable natural resources, beneficially environmental conservation, the saving energy, and technique is simple, and cost is controlled.
Description
Technical field
The present invention relates to field of packaging material, a kind of method of discarded paper packing material regeneration.
Background technology
Along with economic develops rapidly, the theory such as low-carbon economy, energy saving economy, green economy is gradually rooted in the hearts of the people.Environmental protection
Problem is a large focal spot problem of the world today.Along with countries in the world reinforcement continuous to environmental consciousness and waste paper recycle skill
The fast development of art, overseas enterprise payes attention to waste paper the most more and more and recycles.China paper industry the Tenth Five-Year Plan (2001-2005) proposes,
Require that waste paper utilization proportion brings up to 2010 48% from 41% in 2000, within 2015, reach 55%, the most domestic waste paper profit
Within 2015,43% is reached with proportion.China's waste paper dosage increases to 16,380,000 tons of calendar year 2001 from the 8100000 of nineteen ninety-five tons, 5 years
Turn over some.But compared with the country many with more external waste paper dosage, there is also gap.
The recovery method of existing a kind of waste paper packaging material, comprises the following steps: waste and old packaging material are cut into little by (1)
Sheet, cleans, goes the removal of impurity, dries;(2) material flakes is put in water-soluble alkali solution, stir under 50~100 DEG C of constant temperatures
Mix, make aqueous slkali that the paper packing material of waste and old packaging material is dissolved as paper pulp fiber;Obtain separating mixture;(3) will separate
Mixture sends into deflaker, makes paper pulp fiber dispersion discongest, obtains discongesting mixture;Mixture will be discongested and move into scummer
In, respectively obtain paper pulp fiber after process, be then baked to, obtain the paper pulp of regeneration.The paper pulp that said method obtains is for changing
Learning slurry, its secondary stock quality progressively decays, and causes under the tightness of its recycled writing paper, tensile strength, resistance to broken ability and folding number
Fall.And regenerated paper pulp contains the extract of substantial amounts of lignin, hemicellulose and dissolution, affect paper machine and manufacture paper with pulp and the matter of page
Amount, reduces paper formation, opacity, brightness and intensity, produces aperture and dim spot.
Summary of the invention
It is an object of the invention to utilize the secondary stock repulping of mechanical feedback to solve in existing waste paper recovery method change
The secondary stock quality learning slurry repulping declines problem,.
A kind of method that it is a further object to provide discarded paper packing material regeneration, reduces recycled waste paper
The harmful effect that in slurry, the extract of lignin, hemicellulose and dissolution causes.
To achieve these goals, the technical solution of employing is:
A kind of method of discarded paper packing material regeneration, it is characterised in that comprise the steps of:
1), the pretreatment of discarded paper packing material
Waste paper being transported to hydrabrusher and carries out size degradation, hydrabrusher carries out deinking of pulling an oar to waste paper;
2), the decomposition of discarded paper packing material
Step 1) paper pulp that obtains separates impurity through dither screening, obtains separating mixture, and high temperature constant temperature stirs
After, separating mixture now is sent into deflaker, makes paper pulp fiber dispersion discongest, obtain discongesting mixture;
3), the purification of paper pulp
By step 2) in mixture of discongesting put into sand cleaning machine, through process obtain paper pulp, standby;
4), by starch and cold water 1: 4 mixed dissolution high temperature gelatinizing by weight, after obtaining dextrin, by starch gelatinization
Liquid and straw, by weight 1: 1 mixing and stirring, obtain mixture;
5), by step 3) in the paper pulp that obtains and step 4) in after mixture mix and blend, put into mould composite molding.
Preferably, step 2) in whipping temp be 70~100 DEG C, constant temperature has been regulated by water-bath.
Preferably, step 4) in gelatinization point be 90~100 DEG C.
Preferably, step 4) in straw be Caulis et Folium Oryzae, wheat straw, corn straw or the one of which of Caulis Sacchari sinensis straw or
Multiple.
Preferably, step 4) in straw need dry or dry and be processed into crushing straw.
Preferably, crushing straw is straw and the straw of a length of below 0.5cm of a length of 1-2cm.
The beneficial effect that the present invention can produce:
1, the present invention reclaims and utilizes waste paper packaging material, economizes on resources, and reduces the cutting capacity of trees.
2, the present invention utilizes straw and starch to make up the deficiency of secondary stock performance, and wherein straw and starch are all
Belong to for health environment-friendly, short time reproducible resource, with low cost, recyclable again with.Take full advantage of natural resources.
3 are used in combination with existing paper making equipment, reduce the complexity of technique.
4, the material used is simple and environmentally-friendly, easy to process.The paper packing material intensity obtained and deflection are big, anti tear and
There is certain toughness, elasticity.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in further detail.
Embodiment 1
The method of the discarded paper packing material regeneration of the present embodiment, specifically comprises the following steps that
1), waste paper after unpacking, extracting iron wire, be transported to hydrabrusher and carry out size degradation, hydrabrusher is to waste paper
After carrying out making beating deinking, send into high frequency shale shaker separation impurity, obtain separating mixture;
2), utilize water-bath to regulate temperature to be 100 DEG C, stirred by separating mixture constant temperature at such a temperature, send after stirring
Enter deflaker, make paper pulp fiber dispersion discongest, obtain discongesting mixture;
3), will discongest after the contamination precipitations such as sand ash are separated by mixture feeding sand cleaning machine and make pure slurry;
4), by corn straw dry or dry, corn straw is processed into a length of 1-2cm and a length of below 0.5cm
The crushing straw of two kinds of different lengths, the crushing straw of two kinds of different lengths is mixed to obtain mixed type crushing straw in proportion at 9: 1;
5), starch is mixed by weight 1: 4 with cold water, after stirring, be heated into pasty state in 90 DEG C, prepare pasty state and form sediment
Powder;
6), mixed type crushing straw and pasty state starch by weight 1: 1 are mixed in container and stir, mixed
Thing;
7), by paper pulp and step 6) in mixture by weight 1: 1 mixing, stir, pour vacuum dehydration in mould into
Cooling molding.
Embodiment 2
The method of the discarded paper packing material regeneration of the present embodiment, specifically comprises the following steps that
1), waste paper after unpacking, extracting iron wire, be transported to hydrabrusher and carry out size degradation, hydrabrusher is to waste paper
After carrying out making beating deinking, send into high frequency shale shaker separation impurity, obtain separating mixture;
2), utilize water-bath to regulate temperature to be 70 DEG C, stirred by separating mixture constant temperature at such a temperature, send into after stirring
Deflaker, makes paper pulp fiber dispersion discongest, obtains discongesting mixture;
3), will discongest after the contamination precipitations such as sand ash are separated by mixture feeding sand cleaning machine and make pure slurry;
4), by corn straw and Caulis et Folium Oryzae with weight ratio 7: 3 mix and dry or dry, corn straw and Caulis et Folium Oryzae are processed into
The particle of two kinds of different lengths of a length of 1-2cm and a length of below 0.5cm, by the particle of two kinds of different lengths in proportion 9:
1 mixes to obtain mixed type particle;
5), starch is mixed by weight 1: 4 with cold water, after stirring, at 100 DEG C, be heated into pasty state, prepare pasty state
Starch;
6), mixed type particle and pasty state starch by weight 1: 1 are mixed in container and stir, obtain mixture;
7), by paper pulp and step 6) in mixture by weight 1: 1 mixing, stir, pour vacuum dehydration in mould into
Cooling molding.
Above-described embodiment is only presently preferred embodiments of the present invention, not in order to limit the present invention.For being familiar with this area
For personnel, it is easily achieved other amendment, every according to appointing that above example is made by the technical spirit of the present invention
What trickle amendment, equivalent and improvement, should be included in the protection domain of technical solution of the present invention.
Claims (6)
1. the method for a discarded paper packing material regeneration, it is characterised in that comprise the steps of:
1), the pretreatment of discarded paper packing material
Waste paper being transported to hydrabrusher and carries out size degradation, hydrabrusher carries out deinking of pulling an oar to waste paper;
2), the decomposition of discarded paper packing material
Step 1) paper pulp that obtains separates impurity through dither screening, obtains separating mixture, after high temperature constant temperature stirring, will
Separating mixture now sends into deflaker, makes paper pulp fiber dispersion discongest, obtains discongesting mixture;
3), the purification of paper pulp
By step 2) in mixture of discongesting put into sand cleaning machine, through process obtain paper pulp, standby;
4), by starch and cold water by weight 1: 4 mixed dissolution high temperature gelatinizing, after obtaining dextrin, by starch gelatinization liquid and
Straw, by weight 1: 1 mixing and stirring, obtains mixture;
5), by step 3) in the paper pulp that obtains and step 4) in after mixture mix and blend, put into mould composite molding.
The method of a kind of discarded paper packing material regeneration the most according to claim 1, it is characterised in that step 2) in
Whipping temp be 70~100 DEG C, constant temperature has been regulated by water-bath.
The method of a kind of discarded paper packing material regeneration the most according to claim 1, it is characterised in that step 4) in
Gelatinization point be 90~100 DEG C.
The method of a kind of discarded paper packing material regeneration the most according to claim 1, it is characterised in that step 4) in
Straw be Caulis et Folium Oryzae, wheat straw, corn straw or the one or more of which of Caulis Sacchari sinensis straw.
The method of a kind of discarded paper packing material regeneration the most according to claim 1, it is characterised in that step 4) in
Straw need dry or dry and be processed into crushing straw.
The method of a kind of discarded paper packing material regeneration the most according to claim 5, it is characterised in that crushing straw is
The straw of a length of 1-2cm and the straw of a length of below 0.5cm.