CN106245327A - The preparation method of flocculus doughnut - Google Patents
The preparation method of flocculus doughnut Download PDFInfo
- Publication number
- CN106245327A CN106245327A CN201610758767.XA CN201610758767A CN106245327A CN 106245327 A CN106245327 A CN 106245327A CN 201610758767 A CN201610758767 A CN 201610758767A CN 106245327 A CN106245327 A CN 106245327A
- Authority
- CN
- China
- Prior art keywords
- parts
- sodium
- treatment fluid
- preparation
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the preparation method of a kind of flocculus doughnut, comprise the steps: 1) preparation treatment fluid;2) on existing spinning equipment, use polyester slice as raw material, the treatment fluid utilizing step 1) to be prepared replaces spinning oil and uses FDY spinning technique to prepare FDY fiber, and spinneret orifice used is annular, and correspondence is prepared fiber and had the tubular cavity that through fiber is axial.Fiber prepared by the present invention has a function of hollow warm-keeping, and has the most antibacterial, mildew-resistant, fire-retardant, anti-wear performance.
Description
Technical field
The present invention relates to the preparation method of flocculus doughnut.
Background technology
Fiber is (beautiful: Fiber;English: Fibre) refer to the material that is made up of continuous or discrete filament.The kind of fiber
A lot of with application, wherein textile fabric is used to the fiber of weaving cloth, is the raw material of field of textiles indispensability.Doughnut is to spin
One in textured fiber, and doughnut is the raw material that flocculus is conventional, it is empty that doughnut has the axial tubulose of through fiber
Chamber.
But the function of existing doughnut is the most single, it is impossible to meet the demand of market diversification.
Summary of the invention
It is an object of the invention to provide the preparation method of a kind of flocculus doughnut, its fiber prepared has hollow
Warming function, and there is the most antibacterial, mildew-resistant, fire-retardant, anti-wear performance.
For achieving the above object, the technical scheme is that the preparation method designing a kind of flocculus doughnut, bag
Include following steps:
1) preparation treatment fluid;
2) on existing spinning equipment, polyester slice is used to replace spinning as raw material, the treatment fluid utilizing step 1) to be prepared
Silk oiling agent also uses FDY spinning technique to prepare FDY fiber, and spinneret orifice used is annular, and correspondence is prepared fiber and had through
The tubular cavity that fiber is axial;
Wherein,
By weight, described treatment fluid is composed of the following components:
20~25 parts of normal polyester spinning oils,
2~4 parts of blocked polyisocyanates,
1.2 parts of malonaldehyde,
1.7 parts of sodium alklyarylsulfonates,
2.2 parts of nonylphenol ethoxylate carboxylates,
1.7 parts of isomeric alcohol polyethenoxy ether,
1.9 parts of α-sodium olefin sulfonates,
2.3 parts of HYDROXY PROPYL METHYLCELLULOSE,
1.4 parts of sodium tripolyphosphates,
1.1 parts of ethyl hydroxybenzoate sodium salts,
2.5 parts of dichloroisocyanuric acid sodiums,
2.6 parts of Pseudolarix acid Bs,
1.7 parts of double (3,5-tri-grades of butyl-4-hydroxy phenyls) thioethers,
2.3 parts of sodium lauryl sulphates,
65 parts of water.
Preferably, by weight, described treatment fluid is composed of the following components:
20 parts of normal polyester spinning oils,
2 parts of blocked polyisocyanates,
1.2 parts of malonaldehyde,
1.7 parts of sodium alklyarylsulfonates,
2.2 parts of nonylphenol ethoxylate carboxylates,
1.7 parts of isomeric alcohol polyethenoxy ether,
1.9 parts of α-sodium olefin sulfonates,
2.3 parts of HYDROXY PROPYL METHYLCELLULOSE,
1.4 parts of sodium tripolyphosphates,
1.1 parts of ethyl hydroxybenzoate sodium salts,
2.5 parts of dichloroisocyanuric acid sodiums,
2.6 parts of Pseudolarix acid Bs,
1.7 parts of double (3,5-tri-grades of butyl-4-hydroxy phenyls) thioethers,
2.3 parts of sodium lauryl sulphates,
65 parts of water.
Preferably, by weight, described treatment fluid is composed of the following components:
25 parts of normal polyester spinning oils,
4 parts of blocked polyisocyanates,
1.2 parts of malonaldehyde,
1.7 parts of sodium alklyarylsulfonates,
2.2 parts of nonylphenol ethoxylate carboxylates,
1.7 parts of isomeric alcohol polyethenoxy ether,
1.9 parts of α-sodium olefin sulfonates,
2.3 parts of HYDROXY PROPYL METHYLCELLULOSE,
1.4 parts of sodium tripolyphosphates,
1.1 parts of ethyl hydroxybenzoate sodium salts,
2.5 parts of dichloroisocyanuric acid sodiums,
2.6 parts of Pseudolarix acid Bs,
1.7 parts of double (3,5-tri-grades of butyl-4-hydroxy phenyls) thioethers,
2.3 parts of sodium lauryl sulphates,
65 parts of water.
Preferably, by weight, described treatment fluid is composed of the following components:
22 parts of normal polyester spinning oils,
2.3 parts of blocked polyisocyanates,
1.2 parts of malonaldehyde,
1.7 parts of sodium alklyarylsulfonates,
2.2 parts of nonylphenol ethoxylate carboxylates,
1.7 parts of isomeric alcohol polyethenoxy ether,
1.9 parts of α-sodium olefin sulfonates,
2.3 parts of HYDROXY PROPYL METHYLCELLULOSE,
1.4 parts of sodium tripolyphosphates,
1.1 parts of ethyl hydroxybenzoate sodium salts,
2.5 parts of dichloroisocyanuric acid sodiums,
2.6 parts of Pseudolarix acid Bs,
1.7 parts of double (3,5-tri-grades of butyl-4-hydroxy phenyls) thioethers,
2.3 parts of sodium lauryl sulphates,
65 parts of water.
Advantages of the present invention and having the beneficial effects that: providing the preparation method of a kind of flocculus doughnut, it is prepared
Fiber has a function of hollow warm-keeping, and has the most antibacterial, mildew-resistant, fire-retardant, anti-wear performance.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
The preparation method of a kind of flocculus doughnut, comprises the steps:
1) preparation treatment fluid;
2) on existing spinning equipment, polyester slice is used to replace spinning as raw material, the treatment fluid utilizing step 1) to be prepared
Silk oiling agent also uses FDY spinning technique to prepare FDY fiber, and spinneret orifice used is annular, and correspondence is prepared fiber and had through
The tubular cavity that fiber is axial;
Wherein,
By weight, described treatment fluid is composed of the following components:
20 parts of normal polyester spinning oils,
2 parts of blocked polyisocyanates,
1.2 parts of malonaldehyde,
1.7 parts of sodium alklyarylsulfonates,
2.2 parts of nonylphenol ethoxylate carboxylates,
1.7 parts of isomeric alcohol polyethenoxy ether,
1.9 parts of α-sodium olefin sulfonates,
2.3 parts of HYDROXY PROPYL METHYLCELLULOSE,
1.4 parts of sodium tripolyphosphates,
1.1 parts of ethyl hydroxybenzoate sodium salts,
2.5 parts of dichloroisocyanuric acid sodiums,
2.6 parts of Pseudolarix acid Bs,
1.7 parts of double (3,5-tri-grades of butyl-4-hydroxy phenyls) thioethers,
2.3 parts of sodium lauryl sulphates,
65 parts of water.
Embodiment 2
The preparation method of a kind of flocculus doughnut, comprises the steps:
1) preparation treatment fluid;
2) on existing spinning equipment, polyester slice is used to replace spinning as raw material, the treatment fluid utilizing step 1) to be prepared
Silk oiling agent also uses FDY spinning technique to prepare FDY fiber, and spinneret orifice used is annular, and correspondence is prepared fiber and had through
The tubular cavity that fiber is axial;
Wherein,
By weight, described treatment fluid is composed of the following components:
25 parts of normal polyester spinning oils,
4 parts of blocked polyisocyanates,
1.2 parts of malonaldehyde,
1.7 parts of sodium alklyarylsulfonates,
2.2 parts of nonylphenol ethoxylate carboxylates,
1.7 parts of isomeric alcohol polyethenoxy ether,
1.9 parts of α-sodium olefin sulfonates,
2.3 parts of HYDROXY PROPYL METHYLCELLULOSE,
1.4 parts of sodium tripolyphosphates,
1.1 parts of ethyl hydroxybenzoate sodium salts,
2.5 parts of dichloroisocyanuric acid sodiums,
2.6 parts of Pseudolarix acid Bs,
1.7 parts of double (3,5-tri-grades of butyl-4-hydroxy phenyls) thioethers,
2.3 parts of sodium lauryl sulphates,
65 parts of water.
Embodiment 3
The preparation method of a kind of flocculus doughnut, comprises the steps:
1) preparation treatment fluid;
2) on existing spinning equipment, polyester slice is used to replace spinning as raw material, the treatment fluid utilizing step 1) to be prepared
Silk oiling agent also uses FDY spinning technique to prepare FDY fiber, and spinneret orifice used is annular, and correspondence is prepared fiber and had through
The tubular cavity that fiber is axial;
Wherein,
By weight, described treatment fluid is composed of the following components:
22 parts of normal polyester spinning oils,
2.3 parts of blocked polyisocyanates,
1.2 parts of malonaldehyde,
1.7 parts of sodium alklyarylsulfonates,
2.2 parts of nonylphenol ethoxylate carboxylates,
1.7 parts of isomeric alcohol polyethenoxy ether,
1.9 parts of α-sodium olefin sulfonates,
2.3 parts of HYDROXY PROPYL METHYLCELLULOSE,
1.4 parts of sodium tripolyphosphates,
1.1 parts of ethyl hydroxybenzoate sodium salts,
2.5 parts of dichloroisocyanuric acid sodiums,
2.6 parts of Pseudolarix acid Bs,
1.7 parts of double (3,5-tri-grades of butyl-4-hydroxy phenyls) thioethers,
2.3 parts of sodium lauryl sulphates,
65 parts of water.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. the preparation method of flocculus doughnut, it is characterised in that comprise the steps:
1) preparation treatment fluid;
2) on existing spinning equipment, polyester slice is used to replace spinning as raw material, the treatment fluid utilizing step 1) to be prepared
Silk oiling agent also uses FDY spinning technique to prepare FDY fiber, and spinneret orifice used is annular, and correspondence is prepared fiber and had through
The tubular cavity that fiber is axial;
Wherein,
By weight, described treatment fluid is composed of the following components:
20~25 parts of normal polyester spinning oils,
2~4 parts of blocked polyisocyanates,
1.2 parts of malonaldehyde,
1.7 parts of sodium alklyarylsulfonates,
2.2 parts of nonylphenol ethoxylate carboxylates,
1.7 parts of isomeric alcohol polyethenoxy ether,
1.9 parts of α-sodium olefin sulfonates,
2.3 parts of HYDROXY PROPYL METHYLCELLULOSE,
1.4 parts of sodium tripolyphosphates,
1.1 parts of ethyl hydroxybenzoate sodium salts,
2.5 parts of dichloroisocyanuric acid sodiums,
2.6 parts of Pseudolarix acid Bs,
1.7 parts of double (3,5-tri-grades of butyl-4-hydroxy phenyls) thioethers,
2.3 parts of sodium lauryl sulphates,
65 parts of water.
The preparation method of flocculus doughnut the most according to claim 1, it is characterised in that by weight, described
Treatment fluid is composed of the following components:
20 parts of normal polyester spinning oils,
2 parts of blocked polyisocyanates,
1.2 parts of malonaldehyde,
1.7 parts of sodium alklyarylsulfonates,
2.2 parts of nonylphenol ethoxylate carboxylates,
1.7 parts of isomeric alcohol polyethenoxy ether,
1.9 parts of α-sodium olefin sulfonates,
2.3 parts of HYDROXY PROPYL METHYLCELLULOSE,
1.4 parts of sodium tripolyphosphates,
1.1 parts of ethyl hydroxybenzoate sodium salts,
2.5 parts of dichloroisocyanuric acid sodiums,
2.6 parts of Pseudolarix acid Bs,
1.7 parts of double (3,5-tri-grades of butyl-4-hydroxy phenyls) thioethers,
2.3 parts of sodium lauryl sulphates,
65 parts of water.
The preparation method of flocculus doughnut the most according to claim 1, it is characterised in that by weight, described
Treatment fluid is composed of the following components:
25 parts of normal polyester spinning oils,
4 parts of blocked polyisocyanates,
1.2 parts of malonaldehyde,
1.7 parts of sodium alklyarylsulfonates,
2.2 parts of nonylphenol ethoxylate carboxylates,
1.7 parts of isomeric alcohol polyethenoxy ether,
1.9 parts of α-sodium olefin sulfonates,
2.3 parts of HYDROXY PROPYL METHYLCELLULOSE,
1.4 parts of sodium tripolyphosphates,
1.1 parts of ethyl hydroxybenzoate sodium salts,
2.5 parts of dichloroisocyanuric acid sodiums,
2.6 parts of Pseudolarix acid Bs,
1.7 parts of double (3,5-tri-grades of butyl-4-hydroxy phenyls) thioethers,
2.3 parts of sodium lauryl sulphates,
65 parts of water.
The preparation method of flocculus doughnut the most according to claim 1, it is characterised in that by weight, described
Treatment fluid is composed of the following components:
22 parts of normal polyester spinning oils,
2.3 parts of blocked polyisocyanates,
1.2 parts of malonaldehyde,
1.7 parts of sodium alklyarylsulfonates,
2.2 parts of nonylphenol ethoxylate carboxylates,
1.7 parts of isomeric alcohol polyethenoxy ether,
1.9 parts of α-sodium olefin sulfonates,
2.3 parts of HYDROXY PROPYL METHYLCELLULOSE,
1.4 parts of sodium tripolyphosphates,
1.1 parts of ethyl hydroxybenzoate sodium salts,
2.5 parts of dichloroisocyanuric acid sodiums,
2.6 parts of Pseudolarix acid Bs,
1.7 parts of double (3,5-tri-grades of butyl-4-hydroxy phenyls) thioethers,
2.3 parts of sodium lauryl sulphates,
65 parts of water.