CN106244198A - A kind of straight-run naphtha hydrofining technology - Google Patents
A kind of straight-run naphtha hydrofining technology Download PDFInfo
- Publication number
- CN106244198A CN106244198A CN201610694590.1A CN201610694590A CN106244198A CN 106244198 A CN106244198 A CN 106244198A CN 201610694590 A CN201610694590 A CN 201610694590A CN 106244198 A CN106244198 A CN 106244198A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- fixed bed
- kit
- bed reactors
- hydrofining technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of straight-run naphtha hydrofining technology, described technique uses fixed bed reactors, is filled with hydrogenation desulfurization and denitrogenation catalyst in fixed bed reactors, and described catalyst includes carrier and active component;Described carrier is incorporation hetero atom Cu in synthetic bone shelf structure2+KIT 1;Described active component is nitridation two molybdenum MO2N, tungsten nitride W2N, molybdenum carbide Mo2C and the mixture of tungsten carbide wc;Described catalyst is possibly together with catalyst aid, and described catalyst aid is Cr2O3、ZrO2、CeO2、V2O5And NbOPO4Mixture;The reaction condition of described fixed bed reactors is: reaction temperature is 250 300 DEG C, and hydrogen dividing potential drop is 1.5 2.0MPa, hydrogen to oil volume ratio 80 150, volume space velocity 9 14h‑1.Straight-run naphtha total sulfur content can be controlled less than 0.5ppm by this technique.
Description
Technical field
The present invention relates to straight-run naphtha hydrodesulfurization process for refining, be specifically related to a kind of use special catalyst to carry out
Straight-run naphtha hydrofining technology.
Background technology
Petroleum (chemical industry light oil) is all a kind of main raw material in oil refining and petroleum chemical industry.Petroleum is a kind of
Do the refinery less than 200-250 DEG C once or the petroleum distillate of secondary operations gained, be typically derived from refinery's atmospheric and vacuum distillation
Straight-run naphtha and refinery catalytic cracking, be hydrocracked, coking plant secondary operations Petroleum, some condensates are also a kind of
Naphtha cut.Here it should be stressed that because Chinese Crude Oils is generally laid particular stress on, its straight-run naphtha ends content is the lowest, so
Making good use of secondary operations Petroleum as petrochemical material is a critically important problem, the most also pays much attention to the degree of depth of crude oil
Processing, gained secondary Petroleum is used as petroleum products blending component, replaces the raw material for petrochemical industry industry by many refineries.Therefore,
First oil refining, petrochemical industry resource over all Integration are the integrated of Petroleum (including secondary operations Petroleum).
The purposes of Petroleum is many, is the primary raw material manufacturing clean gasoline, at oil in terms of petroleum refining
Chemical industry aspect is to manufacture ethylene, aromatic hydrocarbons/polyester, synthesis ammonia/chemical fertilizer and the raw material of hydrogen manufacturing.In terms of quantitative relation, Petroleum makes
Maximum for the quantity of oil product, secondly, aromatic hydrocarbons is less for feed ethylene.Oil product, feed ethylene, aromatic hydrocarbons material three substantially quantity ratio in the world
Example is: 6.82:1:0.36.
And in an important use of straight-run naphtha, such as time as reforming raw oil, due to reforming catalyst pair
Sulfur poisoning, it is therefore necessary to the sulfur content in raw material is reduced to below 0.5ppm.
Along with heaviness, the in poor quality of world's crude oil are deepened day by day, crude oil sulfur content is more and more higher, and the lightweight of high-quality is former
Oil is constantly reducing.The crude oil of refinery's processing in recent years mostly is imported crude oil, and relative density increases year by year, in several years of the beginning of this century
The average density of whole world refinery processing crude oil rises to about 0.8633.The problem that sulfur content is high is the most extremely serious, the current world
The yield of upper sour crude oil and sour crude accounts for more than the 75% of world's crude oil total output.20th century the mid-90 whole world refinery
The crude oil average sulfur content of processing is 0.9%, and the beginning of this century has increased to 1.6%.
But existing straight-run naphtha hydrofining technology for be all low sulfur product, treat with Venezuelan crude (oil)
The straight-run naphtha produced for the sour crude represented, sulfur content is too high, causes desulphurizing ability limited, and catalysqt deactivation is fast.
The most how straight-run naphtha process for refining is provided, can effectively the sulfur content in high-sulfur straight-run naphtha be controlled at 0.5ppm
Hereinafter, to meet burning and exhausting standard, it it is a difficult problem facing of this area.
Summary of the invention
It is an object of the invention to propose a kind of straight-run naphtha hydrodesulfurization process for refining, this technique can be by straight run stone
Total sulfur content in cerebrol is reduced to below 0.5ppm, to meet following process requirement and to meet burning and exhausting standard.
For reaching this purpose, the present invention by the following technical solutions:
A kind of straight-run naphtha hydrofining technology, described technique uses fixed bed reactors, fills in fixed bed reactors
Being filled with hydrogenation catalyst, described catalyst includes carrier and active component.
Described carrier is incorporation hetero atom Cu in synthetic bone shelf structure2+KIT-1.
Described active component is nitridation two molybdenum MO2N, tungsten nitride W2N, molybdenum carbide Mo2C and the mixture of tungsten carbide wc.
Described catalyst is possibly together with catalyst aid, and described catalyst aid is Cr2O3、ZrO2、CeO2、V2O5And NbOPO4's
Mixture.
The reaction condition of described fixed bed reactors is: reaction temperature is 250-300 DEG C, and hydrogen dividing potential drop is 1.5-2.0MPa,
Hydrogen to oil volume ratio 80-150, volume space velocity 9-14h-1。
High-sulfur straight-run naphtha of the present invention refers to the straight-run naphtha that sulfur content is more than 1000ppm, such as breathes out
The smooth straight-run naphtha of saxophone, its sulfur content is up to 2400ppm.
KIT-1 molecular sieve has one-dimensional channels and crosses each other to form three-dimensional disordered structure, and this structure is conducive to catalysis, absorption
During material transmission.Pure silicon mesopore molecular sieve KIT-1 has heat stability more more preferable than MCM-241, HMS and hydrothermally stable
Property.The present invention through in numerous mesoporous materials, such as KIT-1, KIT-6, MCM-22, MCM-36, MCM-48, MCM-49,
MCM56 etc., carry out contrast test selection, find that only KIT-1 can reach the goal of the invention of the present invention, and other mesoporous materials are all
Having such-and-such defect, there is the technical difficulty being difficult to overcome when being applied in the present invention, therefore the present invention selects to use
KIT-1 is as carrier basis.
Although pure silicon KIT-1 mesopore molecular sieve hydro-thermal performance is outstanding, but inventor's research is later discovered that, it adds
Hetero atom or surface are after chemical modification, and its hydrothermal stability obtains bigger raising.Therefore, it is modified by the present invention, with
Increase its catalysis activity.The approach that KIT-1 mesopore molecular sieve is modified is by the present invention: to the total silicon KIT-1 mesoporous molecular of finished product
Sieve inner surfaces of pores introduces Cu2+, this approach can be exchanged Cu by ion2+It is supported on the inner surface of KIT-1, thus
Improve catalysis activity, absorption and the Thermodynamically stable performance etc. of KIT-1 mesopore molecular sieve on the whole.
Although the method being modified KIT-1 mesopore molecular sieve or approach are a lot, inventor finds, the catalysis of the present invention
Agent can only use doping Cu2+KIT-1 as carrier could realize sulfur content control effect, inventor has attempted in KIT-1
Doping: Al3+、Fe3+、Zn2+、Ga3+In the ion at generation anionic surface center, find all to realize described effect.Although institute
State mechanism current and unclear, but this have no effect on the enforcement of the present invention, inventor according to well-known theory with it is experimentally confirmed that its with
Cooperative effect is there is between the active component of the present invention.
Described Cu2+Doping in KIT-1 must control within specific content range, and its doping is with weight
Meter, for the 0.56%-0.75% of KIT-1 weight, such as 0.57%, 0.58%, 0.59%, 0.6%, 0.61%, 0.62%,
0.63%, 0.64%, 0.65%, 0.66%, 0.67%, 0.68%, 0.69%, 0.7%, 0.71%, 0.72%, 0.73%,
0.74 etc..
Inventor finds, outside this range, can cause drastically reducing of straight-run naphtha desulfurized effect.More pleasurable
, work as Cu2+When doping in KIT-1 controls in the range of 0.63%-0.72%, its desulphurizing ability is the strongest, works as drafting
With Cu2+Doping is transverse axis, and during curve chart with target desulfurized effect as the longitudinal axis, in this content range, sulfur content can control in pole
Within the scope of low, its desulfurized effect produced, far beyond expection, belongs to unforeseeable technique effect.
The total content of described active component is the 1%-15% of carrier KIT-1 weight, preferably 3-12%, further preferred 5-
10%.Such as, described content can be 2%, 2.5%, 3%, 3.5%, 4%, 4.5%, 5%, 5.5%, 6%, 6.5%,
7%, 7.5%, 8%, 8.5%, 9%, 9.5%, 10%, 10.5%, 11%, 11.5%, 12%, 12.5%, 13%,
13.5%, 14%, 14.5% etc..
In the present invention, it is particularly limited to active component for nitridation two molybdenum MO2N, tungsten nitride W2N, molybdenum carbide Mo2C and tungsten carbide wc
Mixed proportion, inventor find, the effect that different mixed proportions reaches is entirely different.Inventor finds, nitrogenizes two molybdenums
MO2N, tungsten nitride W2N, molybdenum carbide Mo2The mixed proportion (mol ratio) of C and tungsten carbide wc is 1:(0.4-0.6): (0.28-
0.45): (0.8-1.2), nitridation two molybdenum MO are only controlled2N, tungsten nitride W2N, molybdenum carbide Mo2The mol ratio of C and tungsten carbide wc exists
In the range of Gai, sulfur content in straight-run naphtha can be realized and control at below 10ppm and denitrification ability notable.It is to say,
Four kinds of active components of the present invention are only 1:(0.4-0.6 in mol ratio): (0.28-0.45): time (0.8-1.2), just possess
Cooperative effect.Outside this molar ratio range, or omit or replace any one component, all can not realize collaborative effect
Should.
Preferably, two molybdenum MO are nitrogenized2N, tungsten nitride W2N, molybdenum carbide Mo2The mol ratio of C and tungsten carbide wc is 1:(0.45-
0.5): (0.35-0.45): (0.8-1.0), more preferably 1:(0.45-0.48): (0.4-0.45): (0.9-1.0),
Preferably 1:0.48:0.42:0.95.
An object of the present invention also resides in the promoter providing described catalyst.Catalyst of the present invention also contains
Having catalyst aid, described catalyst aid is Cr2O3、ZrO2、CeO2、V2O5And NbOPO4The mixture of (niobium phosphate).
Although in hydrofinishing particularly hydrodesulfurization field, had maturation catalyst aid, such as P, F and B etc., its
For regulating the character of carrier, weaken interaction strong between metal and carrier, improve the surface texture of catalyst, improve metal
Reducibility, promote active component to be reduced to lower valency, to improve the catalytic performance of catalyst.But above-mentioned P, F and B catalysis helps
Agent application with the carrier of the present invention with active component time, for high-sulfur component, it promotes the effect of catalytic desulfurization/refined
?.
The present invention passes through in numerous conventional cocatalyst component, and carries out in amount of activated component selecting, compounding,
Find eventually to use Cr2O3、ZrO2、CeO2、V2O5And NbOPO4The mixture of (niobium phosphate) the catalyst facilitation to the present invention
Substantially, its hydrothermal stability can be significantly improved, and improve its anti-coking deactivation, thus improve its service life.
Described Cr2O3、ZrO2、CeO2、V2O5And NbOPO4Between there is no fixing ratio, say, that Cr2O3、ZrO2、
CeO2、V2O5And NbOPO4Each respective content reaches effective dose.Preferably, the Cr that the present invention uses2O3、ZrO2、
CeO2、V2O5And NbOPO4Respective content is the 1-7% of (respectively) carrier quality, preferably 2-4%.
Although there is no specific proportion requirement between catalyst aid of the present invention, but each auxiliary agent allowing for reaching
To the requirement of effective dose, the 1-7% of the content of catalyst aid effect, such as carrier quality i.e. can be played.The present invention is selecting
During find, omit or replace one or more in described auxiliary agent, all do not reach the present invention technique effect (improve water
Heat stability, reduces coking and improves service life), say, that exist between the catalyst aid of the present invention and specifically coordinate pass
System.
It is true that the present invention once attempted the niobium phosphate NbOPO in catalyst aid4Replace with five oxidation two girl Nb2O5,
Have found that while in auxiliary agent and have also been introduced Nb, but its technique effect is significantly lower than niobium phosphate NbOPO4, not only hydrothermal stability is slightly for it
Difference, its beds coking is relatively rapid, thus causes catalyst duct to block, and beds pressure drop rise is relatively
Hurry up.The present invention the most once attempted introducing other phosphate, although but this trial introduces phosphate anion, but equally exist hydro-thermal
Stability is the most slightly worse, and its beds coking is relatively rapid, thus causes catalyst duct to block, beds pressure drop
Rise relatively fast.
Although present invention introduces catalyst aid have so many advantage, but the present invention should be noted that, introduce catalysis
Auxiliary agent is only one of preferred version, even if not introducing this catalyst aid, nor affects on the enforcement of main inventive purpose of the present invention.
Not introducing the catalyst aid particularly niobium phosphate of the present invention, it is compared to the scheme of introducing catalyst aid, and its defect is only phase
To.This defect i.e. is that it is relative to other prior aries outside the present invention relative to the defect introduced after catalyst aid,
Mentioned by the present invention had superiority or new features yet suffer from.This catalyst aid is not to solve technical problem underlying of the present invention
Indispensable technological means, its simply further optimization to technical solution of the present invention, solve new technical problem.
The preparation method of described catalyst can take infusion process and other alternative methods, the people in the art of routine
The prior art unrestricted choice that member can grasp according to it, the present invention repeats no more.The typical but non-limiting example of the present invention
As follows:
Sodium silicate, cetyl trimethylammonium bromide (CTAB), sodium ethylene diamine tetracetate (EDTA) and distilled water are massaged
You mix the ratio than 1:0.25:1:60, load with in teflon-lined autoclave pressure, after stirring under 373K
Constant temperature 24h, the pH of re-adjustments mixture are 10.5, after constant temperature 4 times, take out product, with distilled water cyclic washing to filtrate
PH=7, then under 373K, constant temperature overnight, obtains the KIT-1 with surfactant.KIT-1 with surfactant is existed
Roasting 1.5h under 523K, then roasting 6h in air atmosphere under 813K, obtains KIT-1 powder body.By this powder body 0.1mol/L
Salpeter solution carry out pickling (control solid-to-liquid ratio is 1:10), under room temperature stir 0.5h, filter, be washed with distilled water to filtrate
Dry under pH=7,373K and obtain matrix KIT-1 molecular sieve.
Preferably, the reaction condition of described fixed bed reactors is: reaction temperature is 260-280 DEG C, and hydrogen dividing potential drop is 1.8-
2.0MPa, hydrogen to oil volume ratio 100-150, volume space velocity 9-12h-1。
Preferably, described technological process includes, raw material, after filter, surge tank, is pumped into heat exchanger by feed pump and become
Product heat exchange, is mixed to form hydrogen oil mixture, again enters heating furnace with after product heat exchange with recycle hydrogen and new hydrogen after heat exchange,
Being heated to reaction temperature and enter hydrofining reactor (fixed bed reactors), hydrogen oil mixture is made at catalyst in the reactor
Under with, carrying out the reaction such as hydrodesulfurization, denitrogenation, product is through heat exchange more water cooled to predetermined temperature, enters high pressure and separates
Device, high-pressure separator top gas phase returns recycle hydrogen surge tank as recycle hydrogen, and oil phase enters low pressure separator, low pressure separator
The generation oil that bottom is drawn enters stripper after product heat exchange, and tower top oil gas enters separatory tank after air cooling, water-cooled and obtains
To lighter hydrocarbons, stripping tower bottom obtains straight-run naphtha.
Preferably, described fixed bed reactors include 1-5 beds, further preferred 2-3 beds.
The hydrofining technology of the present invention is by choosing specific catalyst, and described catalyst is by mixing hetero atom Cu2+
KIT-1 as carrier, and choose the nitridation two molybdenum MO of special ratios2N, tungsten nitride W2N, molybdenum carbide Mo2C and tungsten carbide wc
As active component, described catalyst is possibly together with catalyst aid, and described catalyst aid is Cr2O3、ZrO2、CeO2、V2O5With
NbOPO4Mixture so that this catalyst produce cooperative effect, the hydrodesulfurization to straight-run naphtha can control to contain at total sulfur
Total nitrogen content in straight-run naphtha, less than 0.5ppm, is controlled within 10ppm by amount simultaneously.
Detailed description of the invention
The hydrofining technology of the present invention is illustrated by the present invention by following embodiment.
Embodiment 1
Preparing catalyst by infusion process, carrier is doping Cu2+KIT-1, Cu2+Doping control in KIT-1
System is at the 0.65% of carrier quality.Described active component nitrogenizes two molybdenum MO2N, tungsten nitride W2N, molybdenum carbide Mo2C and tungsten carbide wc
Total content is the 10% of carrier quality, and its mol ratio is 1:0.4:0.3:0.8.
Described Catalyst packing enters fixed bed reactors, and the reaction tube of described reactor is by the stainless steel of internal diameter 50mm
Become, beds is set to 3 layers, reaction bed temperature with UGU808 type temp controlled meter measure, raw material straight-run naphtha by
The double plunger micro pump that Beijing Satellite Manufacturing Factory manufactures carries continuously, and hydrogen is supplied by gas cylinder and uses Beijing Sevenstar-HC
D07-11A/ZM mass-flow gas meter coutroi velocity, loaded catalyst is 2kg.Reacted product cools down through water-bath room temperature
Laggard row gas-liquid separation.
Raw materials used for Kazakhstan's straight-run naphtha, its sulfur content is up to 2400ppm.
Controlling reaction condition is: temperature 270 DEG C, hydrogen dividing potential drop 2.0MPa, hydrogen to oil volume ratio 150, volume space velocity 10h-1。
Testing final product, total sulfur content is reduced to 0.4ppm.
Embodiment 2
Preparing catalyst by infusion process, carrier is doping Cu2+KIT-1, Cu2+Doping control in KIT-1
System is at the 0.7% of carrier quality.Described active component nitrogenizes two molybdenum MO2N, tungsten nitride W2N, molybdenum carbide Mo2C and tungsten carbide wc
Total content is the 10% of carrier quality, and its mol ratio is 1:0.6:0.45): 1.2.
Remaining condition is same as in Example 1.
Testing final product, total sulfur content is reduced to 0.3ppm.
Comparative example 1
The carrier of embodiment 1 is replaced with γ-Al2O3, remaining condition is constant.
Testing final product, total sulfur content is reduced to 21ppm.
Comparative example 2
The carrier of embodiment 1 is replaced with unadulterated KIT-1, and remaining condition is constant.
Testing final product, total sulfur content is reduced to 26ppm.
Comparative example 3
Cu by embodiment 12+Replace with Zn2+, remaining condition is constant.
Testing final product, total sulfur content is reduced to 19ppm.
Comparative example 4
By the Cu in embodiment 12+Doping in KIT-1 controls at the 0.5% of carrier quality, and remaining condition is constant.
Testing final product, total sulfur content is reduced to 14ppm.
Comparative example 5
By the Cu in embodiment 12+Doping in KIT-1 controls at the 0.8% of carrier quality, and remaining condition is constant.
Testing final product, total sulfur content is reduced to 18ppm.
Embodiment 1 shows with comparative example 1-5, certain content scope that the application uses and certain loads metal ion
KIT-1 carrier, when replacing with other known carriers of this area, or carrier is identical but Cu2+During doping difference, all reach not
To the technique effect of the present invention, the therefore Cu of the certain content scope of the present invention2+Doping KIT-1 carrier and other components of catalyst
Between possess cooperative effect, described hydrofining technology creates unforeseeable technique effect.
Comparative example 6
Omit the MO in embodiment 12N, remaining condition is constant.
Testing final product, total sulfur content is reduced to 21ppm.
Comparative example 7
Omitting the WC in embodiment 1, remaining condition is constant.
Testing final product, total sulfur content is reduced to 22ppm.
Above-described embodiment and comparative example 6-7 explanation, several active component of catalyst of the hydrofining technology of the present invention it
Between there is specific contact, be omitted or substituted one of which or several, all can not reach the certain effects of the application, it was demonstrated that it produces
Give birth to cooperative effect.
Embodiment 3
Containing catalyst aid Cr in catalyst2O3、ZrO2、CeO2、V2O5And NbOPO4, its content is respectively 1%, 1.5%,
2%, 1% and 3%, remaining is same as in Example 1.
Testing final product, after it uses 3 months, beds pressure drop is not any change, and uses compared to same
The beds pressure drop of time embodiment 1 reduces 16.4%.
Comparative example 8
Compared to embodiment 3, by NbOPO therein4Omitting, remaining condition is identical.
Testing final product, after it uses 3 months, beds pressure drop raises, and uses the time real compared to same
The beds pressure drop executing example 1 only reduces 5.2%.
Comparative example 9
Compared to embodiment 3, by CeO therein2Omitting, remaining condition is identical.
Testing final product, after it uses 3 months, beds pressure drop raises, and uses the time real compared to same
The beds pressure drop executing example 1 only reduces 4.5%.
Embodiment 3 shows with comparative example 8-9, there is conspiracy relation between the catalyst aid of the present invention, when being omitted or substituted
When one of them or several component, all can not reach the minimizing coking when present invention adds catalyst aid thus stop catalyst bed
The technique effect that lamination falling-rising is high.That is, its catalyst aid demonstrating the present invention can improve the service life of described catalyst,
And other catalyst aid effects are not as this specific catalyst aid.
Applicant states, the present invention illustrates the technique of the present invention by above-described embodiment, but the invention is not limited in
Above-mentioned technique, does not i.e. mean that the present invention has to rely on above-mentioned detailed catalysts and could implement.Those of skill in the art
Member is it will be clearly understood that any improvement in the present invention, and the equivalence of raw material each to product of the present invention is replaced and the interpolation of auxiliary element, tool
Body way choice etc., within the scope of all falling within protection scope of the present invention and disclosure.
Claims (7)
1. a high-sulfur straight-run naphtha hydrofining technology, described technique uses fixed bed reactors, in fixed bed reactors
Being filled with hydrogenation catalyst, described catalyst includes carrier and active component, it is characterised in that
Described carrier is incorporation hetero atom Cu in synthetic bone shelf structure2+KIT-1, described active component for nitridation two molybdenum MO2N、
Tungsten nitride W2N, molybdenum carbide Mo2C and the mixture of tungsten carbide wc, described catalyst possibly together with catalyst aid, described catalyst aid
For Cr2O3、ZrO2、CeO2、V2O5And NbOPO4Mixture;
The reaction condition of described fixed bed reactors is: reaction temperature is 250-300 DEG C, and hydrogen dividing potential drop is 1.5-2.0MPa, hydrogen oil
Volume ratio 80-150, volume space velocity 9-14h-1。
2. hydrofining technology as claimed in claim 1, it is characterised in that hetero atom Cu2+Doping be KIT-1 weight
0.63%-0.72%.
3. hydrofining technology as claimed in claim 1, it is characterised in that the total content of described active component is carrier KIT-
The 3-12% of 1 weight, preferably 5-10%.
4. hydrofining technology as claimed in claim 1, it is characterised in that nitrogenize two molybdenum MO2N, tungsten nitride W2N, molybdenum carbide
Mo2The mol ratio of C and tungsten carbide wc is 1:(0.45-0.5): (0.35-0.45): (0.8-1.0), more preferably 1:
(0.45-0.48): (0.4-0.45): (0.9-1.0), most preferably 1:0.48:0.42:0.95.
5. hydrofining technology as claimed in claim 1, it is characterised in that the reaction condition of described fixed bed reactors is:
Reaction temperature is 260-280 DEG C, and hydrogen dividing potential drop is 1.8-2.0MPa, hydrogen to oil volume ratio 100-150, volume space velocity 9-12h-1。
6. hydrofining technology as claimed in claim 1, it is characterised in that described fixed bed reactors include 1-5 catalysis
Agent bed, preferably includes 2-3 beds.
7. hydrofining technology as claimed in claim 1, it is characterised in that Cr2O3、ZrO2、CeO2、V2O5And NbOPO4Each
Content be respectively the 1-7%, preferably 2-4% of carrier quality.