CN106243918A - A kind of high-efficient diffusion barrier powdery paints for sewage disposal - Google Patents
A kind of high-efficient diffusion barrier powdery paints for sewage disposal Download PDFInfo
- Publication number
- CN106243918A CN106243918A CN201610628414.8A CN201610628414A CN106243918A CN 106243918 A CN106243918 A CN 106243918A CN 201610628414 A CN201610628414 A CN 201610628414A CN 106243918 A CN106243918 A CN 106243918A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy resin
- sewage disposal
- diffusion barrier
- powdery paints
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of high-efficient diffusion barrier powdery paints for sewage disposal, successively by epoxy resin, novolac epoxy resin, white carbon black, titanium dioxide, Benzoinum, mica powder, Firebrake ZB, antimony oxide, TDE, brium carbonate, compacted ink carbon, polyglycerol polyricinoleate, wintergreen oil, 3 hydroxy benzoic acids, sulfated lauryl alcohol, plant saponin, Rhizoma Zingiberis Recens liquid, terpineol, sulfur proportionally add high-speed mixer and are sufficiently mixed uniformly；Being melt extruded through extruder by mixture, the tablet after extrusion carries out pulverizing in flour mill, and then screening is packaged into product.Coating of the present invention has the corrosion-and high-temp-resistant performance of excellence, has the antikathode fissility of excellence under the high temperature conditions.
Description
Technical field
The invention belongs to technical field of coatings, a kind of high-efficient diffusion barrier powdery paints for sewage disposal.
Background technology
At sewage treatment area, membrane bioreactor is excellent owing to having effluent quality, and operation runs simple, and mud produces
The advantages such as rate is low, and floor space is little, it constantly expands in range of application and the scale of sewage disposal and increases.Separating film is that film is raw
Most important building block in thing reactor, the quality of its performance is extremely important to the performance of sewage disposal.Traditional membrance separation
Material typically has polyvinyl alcohol, polysulfones, polysulfonamides, polyacrylonitrile, polrvinyl chloride, chitosan and various modified cellulose,
The most all there is more serious fouling membrane situation in these separation membranes, it is difficult to popularization and application on a large scale.
Before more than 200 years, the mankind just disclose membrance separation phenomenon, and membrane separation technique enters engineering in the sixties in 20th century
Field, the seventies, along with the industrialized production of membrane separation device, membrane separation technique is able at each industrial circle and scientific research field
Extensively application.In the development of membrane separation technique, novel separation membrane and the research of film-forming method are one all the time
Important problem.
Summary of the invention
It is an object of the invention to overcome prior art defect, it is provided that a kind of high-efficient diffusion barrier powder for sewage disposal
Coating.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of high-efficient diffusion barrier powdery paints for sewage disposal, includes following component by weight: epoxy resin 40-
65 parts, novolac epoxy resin 35-45 part, white carbon black 5-8 part, titanium dioxide 3.5-4.5 part, Benzoinum 2-3 part, mica powder 4-6 part, boron
Acid zinc 2.0-2.5 part, antimony oxide 5.5-7.5 part, TDE 5-7 part, brium carbonate 8-10 part, compacted ink carbon 6-8 part,
Polyglycerol polyricinoleate 6-8 part, wintergreen oil 0.1-0.2 part, 3-hydroxy benzoic acid 4-6 part, sulfated lauryl alcohol 1-2 part, plant
Saponin 4-6 part, Rhizoma Zingiberis Recens liquid 0.1-0.3 part, terpineol 0.1-0.2 part, sulfur 1-3 part.
Described a kind of high-efficient diffusion barrier powdery paints for sewage disposal, includes following component by weight: asphalt mixtures modified by epoxy resin
55 parts of fat, novolac epoxy resin 40 parts, white carbon black 6 parts, titanium dioxide 4 parts, Benzoinum 2 parts, mica powder 5 parts, Firebrake ZB 2 parts, three oxygen
Change 6 parts of two antimony, TDE 6 parts, brium carbonate 9 parts, compacted 7 parts of carbon of ink, polyglycerol polyricinoleate 7 parts, wintergreen oil 0.2 part,
3-hydroxy benzoic acid 4 parts, sulfated lauryl alcohol 1 part, plant saponin 6 parts, Rhizoma Zingiberis Recens liquid 0.3 part, terpineol 0.1 part, 1 part of sulfur.
Described a kind of high-efficient diffusion barrier powdery paints for sewage disposal, its preparation method comprises the following steps:
(1) successively by epoxy resin, novolac epoxy resin, white carbon black, titanium dioxide, Benzoinum, mica powder, Firebrake ZB, three oxygen
Change two antimony, TDE part, brium carbonate, compacted ink carbon, polyglycerol polyricinoleate, wintergreen oil, 3-hydroxy benzoic acid, lauryl alcohol
Sulfate, plant saponin, Rhizoma Zingiberis Recens liquid, terpineol part, sulfur add high-speed mixer and are sufficiently mixed uniformly；
(2) being melt extruded through extruder by step (1) mixture, the tablet after extrusion grinds in flour mill
Powder, then screening is packaged into product.
Described mica powder granularity is 100-260 mesh.
Beneficial effects of the present invention: coating of the present invention has the corrosion-and high-temp-resistant performance of excellence, has under the high temperature conditions
There is the antikathode fissility of excellence.
Detailed description of the invention
For the ease of it will be appreciated by those skilled in the art that the present invention is further illustrated below in conjunction with specific embodiment.
Embodiment 1
A kind of high-efficient diffusion barrier powdery paints for sewage disposal, includes following component by weight: epoxy resin 40,
Novolac epoxy resin 35, white carbon black 5, titanium dioxide 3.5, Benzoinum 2, mica powder 4, Firebrake ZB 2, antimony oxide
5.5, TDE 5, brium carbonate 8, compacted ink carbon 6, polyglycerol polyricinoleate 6, wintergreen oil 0.1,3-hydroxyl
Yl benzoic acid 4, sulfated lauryl alcohol 1, plant saponin 4, Rhizoma Zingiberis Recens liquid 0.1, terpineol 0.1, sulfur 1.
Its preparation method comprises the following steps:
(1) successively by epoxy resin 40, novolac epoxy resin 35, white carbon black 5, titanium dioxide 3.5, Benzoinum 2,
Mica powder 4, Firebrake ZB 2, antimony oxide 5.5, TDE 5, brium carbonate 8, compacted ink carbon 6, poly-sweet
Oil polyricinoleate 6, wintergreen oil 0.1,3-hydroxy benzoic acid 4, sulfated lauryl alcohol 1, plant saponin 4, Rhizoma Zingiberis Recens liquid
0.1, terpineol 0.1, sulfur 1 add high-speed mixer and are sufficiently mixed uniformly；
(2) being melt extruded through extruder by step (1) mixture, the tablet after extrusion grinds in flour mill
Powder, then screening is packaged into product.
Embodiment 2
A kind of high-efficient diffusion barrier powdery paints for sewage disposal, includes following component by weight: epoxy resin 65,
Novolac epoxy resin 45, white carbon black 8, titanium dioxide 4.5, Benzoinum 3, mica powder 6, Firebrake ZB 2.5, three oxidation two
Antimony 7.5, TDE 7, brium carbonate 10, compacted ink carbon 8, polyglycerol polyricinoleate 8, wintergreen oil 0.2,3-
Hydroxy benzoic acid 6, sulfated lauryl alcohol 2, plant saponin 6, Rhizoma Zingiberis Recens liquid 0.3, terpineol 0.2, sulfur 3.
Its preparation method comprises the following steps:
(1) successively by epoxy resin 65, novolac epoxy resin 45, white carbon black 8, titanium dioxide 4.5, Benzoinum 3,
Mica powder 6, Firebrake ZB 2.5, antimony oxide 7.5, TDE 7, brium carbonate 10, compacted ink carbon 8, poly-
Glycerol polyricinoleate 8, wintergreen oil 0.2,3-hydroxy benzoic acid 6, sulfated lauryl alcohol 2, plant saponin 6, Rhizoma Zingiberis Recens
Liquid 0.3, terpineol 0.2, sulfur 3 add high-speed mixer and are sufficiently mixed uniformly；
(2) being melt extruded through extruder by step (1) mixture, the tablet after extrusion grinds in flour mill
Powder, then screening is packaged into product.
Embodiment 3
A kind of high-efficient diffusion barrier powdery paints for sewage disposal, includes following component by weight: epoxy resin 50,
Novolac epoxy resin 40, white carbon black 6, titanium dioxide 4, Benzoinum 3, mica powder 5, Firebrake ZB 2, antimony oxide 6
, TDE 6, brium carbonate 9, compacted ink carbon 6, polyglycerol polyricinoleate 6, wintergreen oil 0.1,3-hydroxy benzenes
Formic acid 6, sulfated lauryl alcohol 1, plant saponin 6, Rhizoma Zingiberis Recens liquid 0.1, terpineol 0.2, sulfur 1.
Its preparation method comprises the following steps:
(1) successively by epoxy resin 50, novolac epoxy resin 40, white carbon black 6, titanium dioxide 4, Benzoinum 3, cloud
Female powder 5, Firebrake ZB 2, antimony oxide 6, TDE 6, brium carbonate 9, compacted ink carbon 6, polyglycereol castor
Fiber crops alcohol ester 6, wintergreen oil 0.1,3-hydroxy benzoic acid 6, sulfated lauryl alcohol 1, plant saponin 6, Rhizoma Zingiberis Recens liquid 0.1
, terpineol 0.2, sulfur 1 adds high-speed mixer and is sufficiently mixed uniformly；
(2) being melt extruded through extruder by step (1) mixture, the tablet after extrusion grinds in flour mill
Powder, then screening is packaged into product.
Embodiment 4
A kind of high-efficient diffusion barrier powdery paints for sewage disposal, includes following component by weight: epoxy resin 60,
Novolac epoxy resin 40, white carbon black 8, titanium dioxide 4.5, Benzoinum 2, mica powder 4, Firebrake ZB 2, antimony oxide
7.5, TDE 6, brium carbonate 9, compacted ink carbon 7, polyglycerol polyricinoleate 7, wintergreen oil 0.2,3-hydroxyl
Yl benzoic acid 5, sulfated lauryl alcohol 1, plant saponin 5, Rhizoma Zingiberis Recens liquid 0.2, terpineol 0.2, sulfur 2.
Its preparation method comprises the following steps:
(1) successively by epoxy resin 60, novolac epoxy resin 40, white carbon black 8, titanium dioxide 4.5, Benzoinum 2,
Mica powder 4, Firebrake ZB 2, antimony oxide 7.5, TDE 6, brium carbonate 9, compacted ink carbon 7, poly-sweet
Oil polyricinoleate 7, wintergreen oil 0.2,3-hydroxy benzoic acid 5, sulfated lauryl alcohol 1, plant saponin 5, Rhizoma Zingiberis Recens liquid
0.2, terpineol 0.2, sulfur 2 add high-speed mixer and are sufficiently mixed uniformly；
(2) being melt extruded through extruder by step (1) mixture, the tablet after extrusion grinds in flour mill
Powder, then screening is packaged into product.
Embodiment 5
A kind of high-efficient diffusion barrier powdery paints for sewage disposal, includes following component by weight: epoxy resin 60,
Novolac epoxy resin 40, white carbon black 6, titanium dioxide 4, Benzoinum 2, mica powder 5, Firebrake ZB 2, antimony oxide 7
, TDE 6, brium carbonate 8, compacted ink carbon 8, polyglycerol polyricinoleate 6, wintergreen oil 0.2,3-hydroxy benzenes
Formic acid 4, sulfated lauryl alcohol 1, plant saponin 6, Rhizoma Zingiberis Recens liquid 0.1, terpineol 0.2, sulfur 2.
Its preparation method comprises the following steps:
(1) successively by epoxy resin 60, novolac epoxy resin 40, white carbon black 6, titanium dioxide 4, Benzoinum 2, cloud
Female powder 5, Firebrake ZB 2, antimony oxide 7, TDE 6, brium carbonate 8, compacted ink carbon 8, polyglycereol castor
Fiber crops alcohol ester 6, wintergreen oil 0.2,3-hydroxy benzoic acid 4, sulfated lauryl alcohol 1, plant saponin 6, Rhizoma Zingiberis Recens liquid 0.1
, terpineol 0.2, sulfur 2 adds high-speed mixer and is sufficiently mixed uniformly；
(2) being melt extruded through extruder by step (1) mixture, the tablet after extrusion grinds in flour mill
Powder, then screening is packaged into product.
Above content is only citing made for the present invention and explanation, and affiliated those skilled in the art are to being retouched
The specific embodiment stated makes various amendment or supplements or use similar mode to substitute, without departing from inventing or super
More scope defined in the claims, all should belong to protection scope of the present invention.
Claims (4)
1. the high-efficient diffusion barrier powdery paints for sewage disposal, it is characterised in that include following component by weight: ring
Epoxy resins 40-65 part, novolac epoxy resin 35-45 part, white carbon black 5-8 part, titanium dioxide 3.5-4.5 part, Benzoinum 2-3 part, Muscovitum
Powder 4-6 part, Firebrake ZB 2.0-2.5 part, antimony oxide 5.5-7.5 part, TDE 5-7 part, brium carbonate 8-10 part is compacted
Ink carbon 6-8 part, polyglycerol polyricinoleate 6-8 part, wintergreen oil 0.1-0.2 part, 3-hydroxy benzoic acid 4-6 part, sulfated lauryl alcohol
1-2 part, plant saponin 4-6 part, Rhizoma Zingiberis Recens liquid 0.1-0.3 part, terpineol 0.1-0.2 part, sulfur 1-3 part.
A kind of high-efficient diffusion barrier powdery paints for sewage disposal, it is characterised in that by weight
Including following component: epoxy resin 55 parts, novolac epoxy resin 40 parts, white carbon black 6 parts, titanium dioxide 4 parts, Benzoinum 2 parts, mica powder
5 parts, Firebrake ZB 2 parts, antimony oxide 6 parts, TDE 6 parts, brium carbonate 9 parts, compacted ink 7 parts of carbon, polyglycereol Semen Ricini alcohol
Ester 7 parts, wintergreen oil 0.2 part, 3-hydroxy benzoic acid 4 parts, sulfated lauryl alcohol 1 part, plant saponin 6 parts, Rhizoma Zingiberis Recens liquid 0.3 part, pine
Oleyl alcohol 0.1 part, 1 part of sulfur.
A kind of high-efficient diffusion barrier powdery paints for sewage disposal, it is characterised in that its preparation side
Method comprises the following steps:
(1) successively by epoxy resin, novolac epoxy resin, white carbon black, titanium dioxide, Benzoinum, mica powder, Firebrake ZB, three oxidations two
Antimony, TDE, brium carbonate, compacted ink carbon, polyglycerol polyricinoleate, wintergreen oil, 3-hydroxy benzoic acid, lauryl alcohol sulphuric acid
Salt, plant saponin, Rhizoma Zingiberis Recens liquid, terpineol, sulfur add high-speed mixer and are sufficiently mixed uniformly；
(2) being melt extruded through extruder by step (1) mixture, the tablet after extrusion carries out pulverizing in flour mill, so
Rear screening is packaged into product.
A kind of high-efficient diffusion barrier powdery paints for sewage disposal the most according to claim 1, it is characterised in that described
Mica powder granularity is 100-260 mesh.