CN106243810A - A kind of insulating moulding coating and manufacture method thereof - Google Patents
A kind of insulating moulding coating and manufacture method thereof Download PDFInfo
- Publication number
- CN106243810A CN106243810A CN201610764896.XA CN201610764896A CN106243810A CN 106243810 A CN106243810 A CN 106243810A CN 201610764896 A CN201610764896 A CN 201610764896A CN 106243810 A CN106243810 A CN 106243810A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- weight
- insulating moulding
- moulding coating
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to new material and environmental protection and energy saving technical field, particularly relate to a kind of insulating moulding coating and manufacture method thereof.The invention provides a kind of insulating moulding coating, component including following weight portion: water 250 400 weight portion, ethylene group bis-stearamides 10 15 weight portion, oxirane 10 15 weight portion, expoxy propane 10 20 weight portion, styrene 30 35 weight portion, titanium dioxide 50 100 weight portion, silicone acrylic emulsion 80 120 weight portion, elastic emulsion 100 300 weight portion, 2 amino 2 methyl 1 propanol 10 15 weight portions, organosilicon 10 20 weight portion, polyurethane 3 10 weight portion, acrylic resin 30 50 weight portion, fire retardant 15 50 weight portion.The product of the present invention is without harmful substances such as heavy metals, the feature of environmental protection is splendid, weatherability, stain resistance, brushing resistance, thermal insulation, alkali resistance, resistance to water, fire resistance can be excellent, there is construct simple and convenient, storage safety, steady performance, can be directly used for the cooling in summer of building roof and exterior wall, play energy-saving and emission-reduction, environmental protection, the effect of the energy of economizing on water, save.
Description
Technical field
The invention belongs to new material and environmental protection and energy saving technical field, particularly relate to a kind of insulating moulding coating and manufacture method thereof.
Background technology
World industry is the most flourishing, the destruction that population is increasing and the mankind are to the Nature, makes earth surface temperature also
Day by day raising, earth resource is the most exhausted, and life and the existence of the mankind are affected and threat by increasing, therefore, energy-conservation
Consumption reduction work has caused concern and the attention of countries in the world, and each energy-saving material has become the scientific research in the world the most and technology is opened
One of elementary object sent out, energy-saving material also will increasingly be favored by people, especially lives with people closely-related
Building industry,
According to statistics, the building energy consumption of China accounts for more than the 30% of whole nation energy consumption, and this is mainly air-conditioning and heating is consumed,
Wanting effectively to reduce building energy consumption, energy-saving building material plays a leading role, and reduces building surface temperature by energy-saving building material, reduces
Indoor and outdoor heat passes through the mutual convection current of body of wall and transmission.But ageing-resistant, the thermostability of the existing such product of coating and every
Hot property is poor, it is impossible to meet the demand for building low energy consumption and environmental protection in existing society.
Summary of the invention
In view of the problem existing for prior art, the present invention provides a kind of insulating moulding coating, and its ageing-resistant heat resistance is more preferable,
More environmentally-friendly energy-conservation.
The technical scheme is that
The invention provides a kind of insulating moulding coating, including the component of following weight portion: water 250-400 weight portion, ethylene group
Bis-stearamides 10-15 weight portion, oxirane 10-15 weight portion, expoxy propane 10-20 weight portion, styrene 30-35 weight
Part, titanium dioxide 50-100 weight portion, silicone acrylic emulsion 80-120 weight portion, elastic emulsion 100-300 weight portion, 2-amino-2-first
Base-1-propanol 10-15 weight portion, organosilicon 10-20 weight portion, polyurethane 3-10 weight portion, acrylic resin 30-50 weight
Part, fire retardant 15-50 weight portion.
The invention has the beneficial effects as follows: the product of the present invention is without harmful substances such as heavy metals, and the feature of environmental protection is splendid, weather-proof
Property, stain resistance, brushing resistance, thermal insulation, alkali resistance, resistance to water, fire resistance can be excellent, have that construction is simple and convenient, storage
Deposit safety, steady performance.The base materials such as concrete, metal, timber, glass all there are is good adhesive force, once sprays
, convenient construction, can be directly used for the cooling in summer of building roof and exterior wall, play energy-saving and emission-reduction, environmental protection, economize on water, save
The about effect of the energy, improves coating storage period and the physics and chemistry of coating simultaneously, overcomes generation cigarette when fire foaming met by fireproof coating
Mist, health of human body is caused the problems such as high risks.
On the basis of technique scheme, the present invention can also do following improvement.
Further, described insulating moulding coating includes following parts by weight of component: water 300 weight portion, ethylene group bis-stearamides
13 weight portions, oxirane 12 weight portion, expoxy propane 15 weight portion, styrene 33 weight portion, titanium dioxide 50 weight portion, silicon third
Emulsion 90 weight portion, elastic emulsion 200 weight portion, 2-amino-2-methyl-1-propanol 12 weight portion, organosilicon 15 weight portion, poly-
Urethane 8 weight portion, acrylic resin 40 weight portion, fire retardant 30 weight portion.
Further, the average particulate diameter of described titanium dioxide is 0.8-50 micron.
Such scheme is used to provide the benefit that: to improve environment protecting further, simultaneously facilitate mixing.
Further, toughener 10-30 weight portion is also included.
Present invention also offers the preparation method of a kind of insulating moulding coating, comprise the following steps: weigh ethylene group stearic bicine diester
Amine 10-15 weight portion, oxirane 10-15 weight portion, expoxy propane 10-20 weight portion, styrene 30-35 weight portion, titanium white
Powder 50-100 weight portion, silicone acrylic emulsion 80-120 weight portion, elastic emulsion 100-300 weight portion, 2-amino-2-methyl-1-third
Alcohol 10-15 weight portion, organosilicon 10-20 weight portion, polyurethane 3-10 weight portion, acrylic resin 30-50 weight portion, fire retardant
15-50 weight portion, puts in the water of 250-400-weight portion, stirs 30-60 minute under the rotating speed of 1500-3000r/min.
Detailed description of the invention
Principle and feature to the present invention are described below, and example is served only for explaining the present invention, is not intended to limit
Determine the scope of the present invention.
A kind of insulating moulding coating, the invention provides a kind of insulating moulding coating, including the component of following weight portion: water 250-400
Weight portion, ethylene group bis-stearamides 10-15 weight portion, oxirane 10-15 weight portion, expoxy propane 10-20 weight portion, benzene
Ethylene 30-35 weight portion, titanium dioxide 50-100 weight portion, silicone acrylic emulsion 80-120 weight portion, elastic emulsion 100-300 weight
Part, 2-amino-2-methyl-1-propanol 10-15 weight portion, organosilicon 10-20 weight portion, polyurethane 3-10 weight portion, acrylic acid
Resin 30-50 weight portion, fire retardant 15-50 weight portion.
The product of the present invention is without the harmful substance such as heavy metal, and the feature of environmental protection is splendid, weatherability, stain resistance, brushing resistance,
Thermal insulation, alkali resistance, resistance to water, fire resistance can be excellent, have construct simple and convenient, storage safety, steady performance.
The base materials such as concrete, metal, timber, glass all there are is good adhesive force, once sprays, convenient construction, can directly use
In building roof and the cooling in summer of exterior wall, play energy-saving and emission-reduction, environmental protection, the effect of the energy of economizing on water, save, improve simultaneously
Coating storage period and the physics and chemistry of coating, overcome and produce smog when fire foaming met by fireproof coating, health of human body is caused greatly danger
The problems such as evil.It is introduced below by specific embodiment.
Embodiment 1
A kind of insulating moulding coating, including following parts by weight of component: water 250 weight portion, ethylene group bis-stearamides 10 weight portion,
Oxirane 10 weight portion, expoxy propane 10 weight portion, styrene 30 weight portion, titanium dioxide 50 weight portion, silicone acrylic emulsion 80 weight
Amount part, elastic emulsion 100 weight portion, 2-amino-2-methyl-1-propanol 10 weight portion, organosilicon 10 weight portion, polyurethane 3 weight
Amount part, acrylic resin 30-weight portion, fire retardant 15 weight portion and 10 weight portion toughener.
Embodiment 2
A kind of insulating moulding coating, including following parts by weight of component: water 300 weight portion, ethylene group bis-stearamides 13 weight portion,
Oxirane 12 weight portion, expoxy propane 15 weight portion, styrene 33 weight portion, titanium dioxide 50 weight portion, silicone acrylic emulsion 90 weight
Amount part, elastic emulsion 200 weight portion, 2-amino-2-methyl-1-propanol 12 weight portion, organosilicon 15 weight portion, polyurethane 8 weight
Amount part, acrylic resin 40 weight portion, fire retardant 30 weight portion and 20 weight portion toughener.
Embodiment 3
A kind of insulating moulding coating, including the component of following weight portion: water 400 weight portion, ethylene group bis-stearamides 15 weight
Part, oxirane 15 weight portion, expoxy propane 20 weight portion, styrene 35 weight portion, titanium dioxide 100 weight portion, silicone acrylic emulsion
120 weight portions, elastic emulsion 300 weight portion, 2-amino-2-methyl-1-propanol 15 weight portion, organosilicon 20 weight portion, poly-ammonia
Ester 10 weight portion, acrylic resin 50 weight portion, fire retardant 50 weight portion.
Comparative example 1
With implement not use compared with one fire retardant, use wollastonite equivalent to replace titanium dioxide, remaining component and containing simultaneously
Amount is with all identical with embodiment.
Comparative example 2
Do not use fire retardant and 2-amino-2-methyl-1-propanol compared with implementing one, use wollastonite equivalent to replace simultaneously
Change titanium dioxide, remaining component with content with all identical with embodiment.
Comparative example 3
Do not use fire retardant, 2-amino-2-methyl-1-propanol and styrene compared with implementing one, use silicon ash simultaneously
Stone equivalent replace titanium dioxide, remaining component with content with all identical with embodiment.
Measure of merit
Measure the physics in the compositions in insulating moulding coating and comparative example prepared by above-described embodiment and comparative example respectively special
Property.
Test result is as shown in table 1.
Table 1
According to the data in table 1 it can be seen that the insulating moulding coating that technical scheme provides has high ageing-resistant
Property, abrasion resistance, resistance to water, thermostability and fire resistance, and the product of the present invention is without the harmful substances such as heavy metal, the feature of environmental protection
Splendid, weatherability, stain resistance, thermal insulation, alkali resistance, can be excellent, have that construction is simple and convenient, store safety, performance steady
The advantage such as fixed.The base materials such as concrete, metal, timber, glass all there are is good adhesive force, once spray, convenient construction,
Can be directly used for the cooling in summer of building roof and exterior wall, play energy-saving and emission-reduction, environmental protection, the effect of the energy of economizing on water, save, with
Time improve coating storage period and the physics and chemistry of coating, overcome fireproof coating meet fire foaming time produce smog, health of human body is made
Become the problems such as high risks.
Present invention also offers the preparation method of a kind of insulating moulding coating, comprise the following steps: weigh ethylene group stearic bicine diester
Amine 10-15 weight portion, oxirane 10-15 weight portion, expoxy propane 10-20 weight portion, styrene 30-35 weight portion, titanium white
Powder 50-100 weight portion, silicone acrylic emulsion 80-120 weight portion, elastic emulsion 100-300 weight portion, 2-amino-2-methyl-1-third
Alcohol 10-15 weight portion, organosilicon 10-20 weight portion, polyurethane 3-10 weight portion, acrylic resin 30-50 weight portion, fire retardant
15-50 weight portion, puts in the water of 250-400-weight portion, stirs 30-60 minute under the rotating speed of 1500-3000r/min.This
The manufacturing approach craft of invention offer insulating moulding coating is simple, easily manufactured, production efficiency is high, is conducive to producing system on a large scale
Make.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all spirit in the present invention and
Within principle, any modification, equivalent substitution and improvement etc. made, should be included within the scope of the present invention.
Claims (5)
1. an insulating moulding coating, it is characterised in that include the component of following weight portion: water 250-400 weight portion, ethylene group is double hard
Acyl amine 10-15 weight portion, oxirane 10-15 weight portion, expoxy propane 10-20 weight portion, styrene 30-35 weight portion,
Titanium dioxide 50-100 weight portion, silicone acrylic emulsion 80-120 weight portion, elastic emulsion 100-300 weight portion, 2-amino-2-methyl-
1-propanol 10-15 weight portion, organosilicon 10-20 weight portion, polyurethane 3-10 weight portion, acrylic resin 30-50 weight portion, resistance
Combustion agent 15-50 weight portion.
Insulating moulding coating the most according to claim 1, it is characterised in that include following parts by weight of component: water 300 weight portion,
Ethylene group bis-stearamides 13 weight portion, oxirane 12 weight portion, expoxy propane 15 weight portion, styrene 33 weight portion, titanium
White lead 50 weight portion, silicone acrylic emulsion 90 weight portion, elastic emulsion 200 weight portion, 2-amino-2-methyl-1-propanol 12 weight portion,
Organosilicon 15 weight portion, polyurethane 8 weight portion, acrylic resin 40 weight portion, fire retardant 30 weight portion.
Insulating moulding coating the most according to claim 1, it is characterised in that the average particulate diameter of described titanium dioxide is 0.8-50
Micron.
Insulating moulding coating the most according to claim 1, it is characterised in that also include toughener 10-30 weight portion.
5. the preparation method of an insulating moulding coating, it is characterised in that comprise the following steps: weigh ethylene group bis-stearamides 10-15
Weight portion, oxirane 10-15 weight portion, expoxy propane 10-20 weight portion, styrene 30-35 weight portion, titanium dioxide 50-100
Weight portion, silicone acrylic emulsion 80-120 weight portion, elastic emulsion 100-300 weight portion, 2-amino-2-methyl-1-propanol 10-15 weight
Amount part, organosilicon 10-20 weight portion, polyurethane 3-10 weight portion, acrylic resin 30-50 weight portion, fire retardant 15-50 weight
Part, put in the water of 250-400-weight portion, stir 30-60 minute under the rotating speed of 1500-3000r/min.