CN106243737A - It is a kind of that high transparency is silica gel protected applies mechanically double-component silica gel - Google Patents
It is a kind of that high transparency is silica gel protected applies mechanically double-component silica gel Download PDFInfo
- Publication number
- CN106243737A CN106243737A CN201610705352.6A CN201610705352A CN106243737A CN 106243737 A CN106243737 A CN 106243737A CN 201610705352 A CN201610705352 A CN 201610705352A CN 106243737 A CN106243737 A CN 106243737A
- Authority
- CN
- China
- Prior art keywords
- silica gel
- high transparency
- applies mechanically
- component
- mechanically double
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses that a kind of high transparency is silica gel protected applies mechanically double-component silica gel; the polydimethylsiloxane of the ethenyl blocking including 40 70%, the vinyl polysiloxane of 20 50% and the additive of 1 20% are counted in its constituent by weight, and described additive is platinum catalyst or polysiloxanes and the assembly of inhibitor including at least containing in molecule 3 SI H keys.Silica gel in the present invention, by using transparent reinforced filling to solve the strength problem of transparent silica gel, can reach to meet the requirement of mobile phone protective cover intensity；And protection set can be avoided in use to there is the risk of xanthochromia the same with polyurethane by the design of rational formula.
Description
Technical field
The invention belongs to leather sheath technical field, particularly relate to that a kind of high transparency is silica gel protected applies mechanically double-component silica gel.
Background technology
Along with popularizing of mobile phone, Leather cover for handset is also favored by people.Especially young cluster, following the fashion, individual character
Changing, the style to Leather cover for handset, quality, function etc. requires more and more.The most common Leather cover for handset function has shatter-resistant, anti-
Sliding, antitheft, dormancy, the function such as attractive in appearance.Additionally mobile phone protective cover can effectively prevent hard thing from causing mobile phone screen or fuselage
Cut, it is also possible to avoid mobile phone to fall the problems such as even breakage of colliding with caused.It is currently used in the middle of the material of mobile phone protective cover, bag
Include numerous plastic material such as silica gel and leather sheath.But silica gel sheath is saturating
Gas is poor, and long periods of wear will cause handset accumulated heat, is not particularly suitable for the smart mobile phone that caloric value is higher.And
Silica gel sheath itself has slight viscosity, uses a period of time post-concentration collection a large amount of dusts of absorption on mobile phone, is unfavorable on the contrary
Mobile phone attractive in appearance, runs in the opposite direction with the original intention of protection mobile phone.
Mobile phone protective cover the most on the market has multiple material, has silica gel, polyurethane material.And these protection set materials are such as
Fruit is accomplished fully transparent, and intensity will significantly decline, and can not meet the requirement of strength of mobile phone protective cover, so the most on the market
Silicone Case all with color, it is impossible to accomplish transparent.The most transparent cell-phone cover of main flow is polyurethane material
Material, but it exists the shortcoming of easy xanthochromia, substantially in one month will obvious xanthochromia, have a strong impact on the outward appearance of mobile phone, and
This characteristic is to be determined by the characteristic of polyurethane itself, is difficult to be overcome, and therefore, needs one badly and has intensity and high transparency and not concurrently
Can the Novel electronic product protection set material of xanthochromia, it is i.e. a kind of that high transparency is silica gel protected applies mechanically double-component silica gel.
Summary of the invention
It is an object of the invention to provide that a kind of high transparency is silica gel protected applies mechanically double-component silica gel, the intensity of this silica gel and thoroughly
Lightness is all adapted to the use requirement of existing market, and xanthochromia will not occur, thus efficiently solves in above-mentioned prior art
The problem existed.
For achieving the above object, the present invention adopts the following technical scheme that
A kind of high transparency is silica gel protected applies mechanically double-component silica gel, and its constituent is counted as follows by weight:
The polydimethylsiloxane 40 70% of ethenyl blocking
Vinyl polysiloxane 20 50%
Additive 1 20%.
Preferably, its constituent is counted as follows by weight:
The polydimethylsiloxane 65% of ethenyl blocking
Vinyl polysiloxane 30 35%
Additive 1 5%.
Preferably, described additive is the platinum catalyst of 0.1-100PPM.
Preferably, described additive is the platinum catalyst of 20PPM.
Preferably, described additive includes at least containing 3 SI-H keys in molecule polysiloxanes and 10-10000PPM's
Inhibitor.
Preferably, described inhibitor is ethynylcyclohexanol.
Preferably, described additive includes the hydrogen containing siloxane of 0.75% hydrogen content and the ethynylcyclohexanol of 600PPM.
Preferably, the polydimethylsiloxane of described ethenyl blocking be viscosity be the ethylene of 10000-200000mpa.s
Base terminated polysiloxane.
Preferably, described vinyl polysiloxane be molecular weight between 2000-10000, contents of ethylene is between 0.5-
Silicones between 5.5%.
Preferably, described vinyl polysiloxane be contents of ethylene be the silicones between 3%.
Compared to prior art, the beneficial effects of the present invention is: the silica gel in the present invention is by using transparent reinforcement
Filler solves the strength problem of transparent silica gel, can reach to meet the requirement of mobile phone protective cover intensity；And by reasonably joining
Side's design can avoid protection set in use to there is the risk of xanthochromia the same with polyurethane.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with
Detailed description of the invention, is expanded on further the present invention.
Embodiment 1
A kind of high transparency is silica gel protected applies mechanically double-component silica gel, and the vinyl envelope including 65% is counted in its constituent by weight
End polysiloxanes, the vinyl polysiloxane of 35% and the platinum catalyst of 20PPM.
The viscosity that it should be noted that described vinyl terminated polysiloxane is 10000mpa.s.
In the present embodiment, the molecular weight of described vinyl polysiloxane is 5000, and is the silicon tree of 3% for contents of ethylene
Fat.
Embodiment 2
A kind of high transparency is silica gel protected applies mechanically double-component silica gel, and the vinyl envelope including 70% is counted in its constituent by weight
End polysiloxanes, the vinyl polysiloxane of 30% and the platinum catalyst of 100PPM.
The viscosity that it should be noted that described vinyl terminated polysiloxane is 200000mpa.s.
In the present embodiment, the molecular weight of described vinyl polysiloxane is 2000, and is the silicon of 5.5% for contents of ethylene
Resin.
Embodiment 3
A kind of high transparency is silica gel protected applies mechanically double-component silica gel, and the vinyl envelope including 50% is counted in its constituent by weight
End polysiloxanes, the vinyl polysiloxane of 50% and the platinum catalyst of 0.1PPM.
The viscosity that it should be noted that described vinyl terminated polysiloxane is 100000mpa.s.
In the present embodiment, the molecular weight of described vinyl polysiloxane is 10000, and is the silicon of 0.5% for contents of ethylene
Resin.
Embodiment 4
A kind of high transparency is silica gel protected applies mechanically double-component silica gel, and the vinyl envelope including 65% is counted in its constituent by weight
Polysiloxanes that is that hold polysiloxanes, the vinyl polysiloxane of 30% and 5% and that contain 3 SI-H keys and the acetylene basic ring of 600PPM
Hexanol.
The viscosity that it should be noted that described vinyl terminated polysiloxane is 10000mpa.s.
In the present embodiment, the molecular weight of described vinyl polysiloxane is 5000, and is the silicon tree of 3% for contents of ethylene
Fat.
In the present embodiment, the described hydrogen containing siloxane that polysiloxanes is 0.75% hydrogen content containing 3 SI-H keys.
The reaction mechanism of bi-component polyurethane ester pressure-sensitive of the present invention is: containing the polydimethylsiloxane of vinyl
(can be range of viscosities single viscosity or mixing of several viscosity in the range of 1000-200000mpa.s) and vinyl polysiloxane
Containing extremely in (molecular weight 2000-10000, contents of ethylene 0.5-5.5% can be one can also be several mixing) and molecule
The polysiloxanes of few three si-h bonds occurs additive reaction to prepare under the catalytic action of platinum.
Embodiment 5
A kind of high transparency is silica gel protected applies mechanically double-component silica gel, and the vinyl envelope including 70% is counted in its constituent by weight
Polysiloxanes that is that hold polysiloxanes, the vinyl polysiloxane of 29% and 1% and that contain 4 SI-H keys and the acetylene basic ring of 600PPM
Hexanol.
The viscosity that it should be noted that described vinyl terminated polysiloxane is 10000mpa.s.
In the present embodiment, the molecular weight of described vinyl polysiloxane is 5000, and is the silicon of 5.5% for contents of ethylene
Resin.
In the present embodiment, the described hydrogen containing siloxane that polysiloxanes is 0.75% hydrogen content containing 4 SI-H keys.
Embodiment 6
A kind of high transparency is silica gel protected applies mechanically double-component silica gel, and the vinyl envelope including 40% is counted in its constituent by weight
Polysiloxanes that is that hold polysiloxanes, the vinyl polysiloxane of 40% and 20% and that contain 3 SI-H keys and the acetenyl of 600PPM
Hexalin.
The viscosity that it should be noted that described vinyl terminated polysiloxane is 10000mpa.s.
In the present embodiment, the molecular weight of described vinyl polysiloxane is between 5000, and for contents of ethylene is
The silicones of 0.5%.
In the present embodiment, the described hydrogen containing siloxane that polysiloxanes is 0.75% hydrogen content containing 3 SI-H keys.
Although the present invention is to be described with reference to specific embodiments, but this description is not meant to the present invention is constituted limit
System.With reference to description of the invention, other changes of the disclosed embodiments, for those skilled in the art be all it is anticipated that
, this change should belong in appended claims limited range.
Claims (10)
1. a high transparency is silica gel protected applies mechanically double-component silica gel, it is characterised in that its constituent is counted as follows by weight:
The polydimethylsiloxane 40 70% of ethenyl blocking
Vinyl polysiloxane 20 50%
—20%。
The most according to claim 1 a kind of high transparency is silica gel protected applies mechanically double-component silica gel, it is characterised in that preferably,
Its constituent is counted as follows by weight:
The polydimethylsiloxane 65% of ethenyl blocking
Vinyl polysiloxane 30 35%
Additive 1 5%.
The most according to claim 1 and 2 a kind of high transparency is silica gel protected applies mechanically double-component silica gel, it is characterised in that described
Additive is the platinum catalyst of 0.1-100PPM.
The most according to claim 3 a kind of high transparency is silica gel protected applies mechanically double-component silica gel, it is characterised in that described interpolation
Agent is the platinum catalyst of 20PPM.
The most according to claim 1 and 2 a kind of high transparency is silica gel protected applies mechanically double-component silica gel, it is characterised in that described
Additive includes at least containing the polysiloxanes of 3 SI-H keys and the inhibitor of 10-10000PPM in molecule.
The most according to claim 5 a kind of high transparency is silica gel protected applies mechanically double-component silica gel, it is characterised in that described suppression
Agent is ethynylcyclohexanol.
The most according to claim 6 a kind of high transparency is silica gel protected applies mechanically double-component silica gel, it is characterised in that described interpolation
Agent includes the hydrogen containing siloxane of 0.75% hydrogen content and the ethynylcyclohexanol of 600PPM.
The most according to claim 1 a kind of high transparency is silica gel protected applies mechanically double-component silica gel, it is characterised in that described ethylene
Base end-blocking polydimethylsiloxane be viscosity be the vinyl terminated polysiloxane of 10000-200000mpa.s.
The most according to claim 1 a kind of high transparency is silica gel protected applies mechanically double-component silica gel, it is characterised in that described ethylene
Base silicones be molecular weight between 2000-10000, contents of ethylene silicones between 0.5-5.5%.
The most according to claim 1 a kind of high transparency is silica gel protected applies mechanically double-component silica gel, it is characterised in that described second
Thiazolinyl silicones be contents of ethylene be the silicones between 3%.