CN106243417A - Tire low rolling resistance and the manufacture method of shearing Hardening type rubber composite - Google Patents
Tire low rolling resistance and the manufacture method of shearing Hardening type rubber composite Download PDFInfo
- Publication number
- CN106243417A CN106243417A CN201610691216.6A CN201610691216A CN106243417A CN 106243417 A CN106243417 A CN 106243417A CN 201610691216 A CN201610691216 A CN 201610691216A CN 106243417 A CN106243417 A CN 106243417A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- rubber
- parts
- tire
- shear thickening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the low rolling resistance of a kind of tire and the manufacture method shearing Hardening type rubber composite, it specifically comprises the following steps that and 1. utilizes existing mill technology that rubber composition is joined rubber mixing mill, 2. in the mixture that 1. step obtains, add rubber pange agent, 3. to step 2. in mixture in add shear thickening materials, 4. 3. step is obtained mixture, by screw extruder extrusion molding, i.e. can get the present invention, tire slowly runs when, shear thickening materials in rubber/shear thickening composite can be with flow deformation, cause the deformation that rubber/shear thickening composite is bigger, cause rubber/shear thickening composite deliquescing, increase the earth-grasping force of tire；Otherwise, tire quickly rotates the resistance to rolling that just can reduce tire, adds appropriate filler in formula, makes the hardness of material of the present invention be highly improved, and reduces the rolling resistance of tire.
Description
Technical field
The present invention relates to elastomeric material manufacturing technology field, specifically a kind of tire is with low rolling resistance and shears Hardening type
The manufacture method of rubber composite.
Background technology
The contact area on tire and ground is mainly adjusted by the air pressure of inside tires at present, and tire internal gas pressure is high, wheel
The contact area on tire and ground is little, and tire internal gas pressure reduces, and the contact area on tire and ground increases.In vehicle travel process,
Tire and contact area of ground are big, be conducive to grabbing and braking, but be detrimental to reduce the resistance of tire；Whereas if tire
Little with contact area of ground, although to advantageously reduce the resistance of tire, but be detrimental to grab and braking.As can be seen here, existing
Tire can not dynamically change the contact area on tire and ground.The characteristic of current this tire comes from the characteristic of rubber, rubber
Glue is as a kind of elastomer, and its internal stress deformation is proportional to applied stress, and its internal deformation can not be along with rolling speed
The change of degree and change, the deformation of tread-rubber is mainly the most relevant with tire pressure-bearing, and therefore, the most this deformation can not dynamically change
Become.
It is thus desirable to a kind of new type rubber, the hardness of rubber can be changed according to the rotating speed of tire, and change tire and ground
The contact area in face.
Summary of the invention
The technical problem to be solved in the present invention is the defect overcoming prior art, it is provided that a kind of tire is with low rolling resistance and shears
The manufacture method of Hardening type rubber composite.
For solving above-mentioned technical problem, the present invention provides techniques below scheme: a kind of tire is with low rolling resistance and shears Hardening
The manufacture method of type rubber composite, it specifically comprises the following steps that
Step is 1.: utilizing existing mill technology that rubber composition joins rubber mixing mill, the formula of rubber composition is:
Ethylene propylene diene rubber weight portion is 15 to 26 parts, and cis-butadiene cement weight portion is 15 to 24 parts, and natural gum weight portion is 10 to 20 parts, helps
Agent weight portion is 20 to 25 parts, and filler weight part is 25 to 35 parts, and the parameter of rubber mixing mill is 400 to the 500 seconds glue time of refining,
Temperature 140 to 150 degrees Celsius, pressure 0.5 to 0.7MPa；
Step is 2.: adding rubber pange agent in the mixture that 1. step obtains, the weight portion of foaming agent is 10 to 15 parts, gained
Mixture is then added to rubber mixing mill, and the parameter of rubber mixing mill is 600 to the 800 seconds glue time of refining, and temperature 100 to 110 is taken the photograph
Family name's degree, pressure 0.3 to 0.4MPa；
Step is 3.: to step 2. in mixture in add shear thickening materials, the weight portion of shear thickening materials is 50 parts, institute
Obtain mixture and be then added to rubber mixing mill, the first stage: the parameter of rubber mixing mill is 1000 to the 1200 seconds glue time of refining, temperature
Spend 110 to 130 degrees Celsius, pressure 0.4 to 0.5MPa, second stage: the parameter of rubber mixing mill is the refining glue time 100 to 200
Second, temperature 150 to 180 degrees Celsius, pressure 0.2 to 0.3MPa；
Step is 4.: 3. step obtains mixture, by screw extruder extrusion molding, i.e. can get the present invention.
Preferably, rubber pange agent is azo-compound or sulfonephthalein takes off compounds.
Preferably, auxiliary agent weight portion is 20 to 25 parts, and the formula of auxiliary agent is: the weight portion of silicon dioxide is 10 to 15 parts,
The weight portion of zinc oxide is 1 to 5 parts, and stearic weight portion is 0.1 to 3 parts, and the weight portion of other auxiliary agent is 3 to 6 parts, sulfur
Weight portion be 1 to 6 parts, the weight portion of vulcanization accelerator is 1.5 to 3 parts.
Preferably, the formula of shear thickening materials is, high viscosity Polyethylene Glycol 15 ~ 30 weight portion, fiber floccule 1 ~ 2 weight
Amount part, nano-calcium carbonate 7 ~ 12 weight portion, Nano carbon white 5 ~ 8 weight portion, natural gum 2 ~ 10 weight portion.
Preferably, the formula of high viscosity Polyethylene Glycol is, polyethylene glycol 200 is 1 ~ 3 weight portion, PEG400 is 2 ~
10 weight portions, cetomacrogol 1000 is 12 ~ 22 weight portions.
Preferably, the formula of filler is: the weight portion of white carbon black is 5 to 10 parts, and the weight portion of nano barium sulfate is 10 to 15
Part, the weight portion of nano-calcium carbonate is 10 to 25 parts.
The principle that realizes of the present invention is, by elastomeric material and the mixing of rubber pange agent, is mutually mixed in mill
And make rubber pange agent produce foaming effect to produce substantial amounts of foaming structure in elastomeric material, then remix
Shear thickening materials, shear thickening materials enters the cavity in foaming structure, produces and fills, and then forms rubber/shear thickening
The composite construction of composite, shear thickening materials, namely non-Newtonian fluid material, have under high speed shear motion effect
Keep the characteristic of original form, can deform under low velocity shear motion effect meanwhile, enter rubber by compound for shear thickening materials
Glue material also forms the composite construction of rubber/shear thickening composite, plays the effect of support, so, at tire low speed rotation
The when of dynamic, the shear thickening materials in rubber/shear thickening composite can cause rubber/shear thickening with flow deformation
The deformation that composite is bigger, causes rubber/shear thickening composite deliquescing；When tire is atwirl time, rubber/cut
Cut shear thickening materials in thickening composite because of shear thickening hardening, it is not possible to flowing, cause rubber/shear thickening to be combined
The deformation that material is less, causes rubber/shear thickening composite hardening；Polyethylene Glycol is joining of conventional shear thickening materials
Square bar material, low-molecular-weight polyethylene glycol good fluidity, solid-liquid dispersing are good, but shear thickening intensity is poor, polyphosphazene polymer second two
Alcohol poor fluidity, solid-liquid dispersing are poor, but shear thickening intensity is high, the Polyethylene Glycol mixing of various molecular weight, are conducive to solid
Liquid disperses, and shear thickening intensity simultaneously is high；Shear thickening materials adds a small amount of natural gum, is conducive to increasing shear thickening strong
Being combined of degree, the most beneficially shear thickening materials and elastomeric material.The present invention compared with prior art has the advantage that
It is: tire slowly runs when that the shear thickening materials in rubber/shear thickening composite can cause with flow deformation
Make the deformation that rubber/shear thickening composite is bigger, cause rubber/shear thickening composite deliquescing, tire sinking degree
Increase, cause tire and contact area of ground to increase, increase the earth-grasping force of tire；When tire is atwirl time, rubber/cut
Cut shear thickening materials in thickening composite because of shear thickening hardening, it is not possible to flowing, cause rubber/shear thickening to be combined
The deformation that material is less, causes rubber/shear thickening composite hardening, and tire sinking degree reduces, and causes tire and ground
Contact area reduces, and reduces the earth-grasping force of tire, reduces the resistance to rolling of tire.Formula adds appropriate filler, makes this
The hardness of bright material is highly improved, and reduces the rolling resistance of tire.
Detailed description of the invention
In order to make the purpose of the present invention, technical scheme and advantage clearer, below in conjunction with embodiment, to the present invention
It is further elaborated.Should be appreciated that specific embodiment described herein, only in order to explain the present invention, is not used to
Limit the present invention.
Embodiment 1
A kind of tire low rolling resistance and the manufacture method of shearing Hardening type rubber composite, it specifically comprises the following steps that
Step is 1.: utilizing existing mill technology that rubber composition joins rubber mixing mill, the formula of rubber composition is:
Ethylene propylene diene rubber weight portion is 16 parts, and cis-butadiene cement weight portion is 18 parts, and natural gum weight portion is 12 parts, and auxiliary agent weight portion is 23
Part, filler weight part is 35 parts, and the parameter of rubber mixing mill is 500 seconds glue time of refining, temperature 145 degrees Celsius, pressure 0.6
MPa；
Step is 2.: adding rubber pange agent in the mixture that 1. step obtains, the weight portion of foaming agent is 12 parts, and gained mixes
Thing is then added to rubber mixing mill, and the parameter of rubber mixing mill is 700 seconds glue time of refining, temperature 110 degrees Celsius, pressure 0.3
MPa；
Step is 3.: to step 2. in mixture in add shear thickening materials, the weight portion of shear thickening materials is 50 parts, institute
Obtain mixture and be then added to rubber mixing mill, the first stage: the parameter of rubber mixing mill is 1000 seconds glue time of refining, temperature 110
Degree Celsius, pressure 0.4 MPa, second stage: the parameter of rubber mixing mill is the 100 seconds glue time of refining, temperature 170 degrees Celsius, pressure
Power 0.2 MPa；
Step is 4.: 3. step obtains mixture, by screw extruder extrusion molding, i.e. can get the present embodiment.
Rubber pange agent in the present embodiment is azo-compound.
Auxiliary agent weight portion in the present embodiment is 23 parts, and the formula of auxiliary agent is: the weight portion of silicon dioxide is 12 parts, oxidation
The weight portion of zinc is 2 parts, and stearic weight portion is 0.8 part, and the weight portion of other auxiliary agent is 4.2 parts, and the weight portion of sulfur is 2
Part, the weight portion of vulcanization accelerator is 2 parts.
The formula of the shear thickening materials in the present embodiment is, high viscosity Polyethylene Glycol 30 weight portion, fiber floccule 1 weight
Amount part, nano-calcium carbonate 7 weight portion, Nano carbon white 8 weight portion, natural gum 4 weight portion.
The formula of the high viscosity Polyethylene Glycol in the present embodiment is, polyethylene glycol 200 is 3 weight portions, and PEG400 is
10 weight portions, cetomacrogol 1000 is 17 weight portions.
The formula of the filler in the present embodiment is: the weight portion of white carbon black is 10 parts, and the weight portion of nano barium sulfate is 15 parts,
The weight portion of nano-calcium carbonate is 10 parts.
Embodiment 2
A kind of tire low rolling resistance and the manufacture method of shearing Hardening type rubber composite, it specifically comprises the following steps that
Step is 1.: utilizing existing mill technology that rubber composition joins rubber mixing mill, the formula of rubber composition is:
Ethylene propylene diene rubber weight portion is 22 parts, and cis-butadiene cement weight portion is 22 parts, and natural gum weight portion is 10 parts, and auxiliary agent weight portion is 25
Part, filler weight part is 35 parts, and the parameter of rubber mixing mill is 500 seconds glue time of refining, temperature 150 degrees Celsius, pressure 0.7MPa；
Step is 2.: adding rubber pange agent in the mixture that 1. step obtains, the weight portion of foaming agent is 15 parts, and gained mixes
Thing is then added to rubber mixing mill, and the parameter of rubber mixing mill is 600 seconds glue time of refining, temperature 110 degrees Celsius, pressure
0.4MPa；
Step is 3.: to step 2. in mixture in add shear thickening materials, the weight portion of shear thickening materials is 50 parts, institute
Obtain mixture and be then added to rubber mixing mill, the first stage: the parameter of rubber mixing mill is 1000 seconds glue time of refining, temperature 120
Degree Celsius, pressure 0.4 MPa, second stage: the parameter of rubber mixing mill is the 100 seconds glue time of refining, temperature 180 degrees Celsius, pressure
Power 0.3MPa；
Step is 4.: 3. step obtains mixture, by screw extruder extrusion molding, i.e. can get the present embodiment.
Rubber pange agent in the present embodiment is azo-compound.
Auxiliary agent weight portion in the present embodiment is 25 parts, and the formula of auxiliary agent is: the weight portion of silicon dioxide is 10 parts, oxidation
The weight portion of zinc is 5 parts, and stearic weight portion is 1 part, and the weight portion of other auxiliary agent is 5 parts, and the weight portion of sulfur is 2 parts,
The weight portion of vulcanization accelerator is 2 parts.
The formula of the shear thickening materials in the present embodiment is, high viscosity Polyethylene Glycol 25 weight portion, fiber floccule 2 weight
Amount part, nano-calcium carbonate 12 weight portion, Nano carbon white 8 weight portion, natural gum 3 weight portion.
The formula of the high viscosity Polyethylene Glycol in the present embodiment is, polyethylene glycol 200 is 3 weight portions, and PEG400 is
10 weight portions, cetomacrogol 1000 is 12 weight portions.
The formula of the filler in the present embodiment is: the weight portion of white carbon black is 10 parts, and the weight portion of nano barium sulfate is 15 parts,
The weight portion of nano-calcium carbonate is 10 parts.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all essences in the present invention
Any amendment, equivalent and the improvement etc. made within god and principle, should be included within the scope of the present invention.
Claims (6)
1. tire low rolling resistance and the manufacture method of shearing Hardening type rubber composite, it specifically comprises the following steps that
Step is 1.: by existing mill technology, rubber composition joins rubber mixing mill, joining of described rubber composition
Fang Wei: ethylene propylene diene rubber weight portion is 15 to 26 parts, cis-butadiene cement weight portion is 15 to 24 parts, and natural gum weight portion is 10 to 20
Part, auxiliary agent weight portion is 20 to 25 parts, and filler weight part is 25 to 35 parts, and the parameter of rubber mixing mill arrived for the refining glue time 400
500 seconds, temperature 140 to 150 degrees Celsius, pressure 0.5 to 0.7MPa；
Step is 2.: adding rubber pange agent in the mixture that 1. step obtains, the weight portion of described foaming agent is 10 to 15 parts,
Gained mixture is then added to rubber mixing mill, and the parameter of rubber mixing mill is 600 to the 800 seconds glue time of refining, and temperature 100 arrives
110 degrees Celsius, pressure 0.3 to 0.4MPa；
Step is 3.: step 2. in mixture in add shear thickening materials, the weight portion of described shear thickening materials is 50
Part, gained mixture is then added to rubber mixing mill, the first stage: the parameter of rubber mixing mill is the refining glue time 1000 to 1200
Second, temperature 110 to 130 degrees Celsius, pressure 0.4 to 0.5MPa, second stage: the parameter of rubber mixing mill is the refining glue time 100
By 200 seconds, temperature 150 to 180 degrees Celsius, pressure 0.2 to 0.3MPa；
Step is 4.: 3. step obtains mixture, by screw extruder extrusion molding, i.e. can get the present invention.
Tire the most according to claim 1 low rolling resistance and the manufacture method of shearing Hardening type rubber composite, it is special
Levy and be: described rubber pange agent is azo-compound or sulfonephthalein takes off compounds.
Tire the most according to claim 1 low rolling resistance and the manufacture method of shearing Hardening type rubber composite, it is special
Levying and be: described auxiliary agent weight portion is 20 to 25 parts, the formula of auxiliary agent is: the weight portion of silicon dioxide is 10 to 15 parts, oxygen
The weight portion changing zinc is 1 to 5 parts, and stearic weight portion is 0.1 to 3 parts, and the weight portion of other auxiliary agent is 3 to 6 parts, sulfur
Weight portion is 1 to 6 parts, and the weight portion of vulcanization accelerator is 1.5 to 3 parts.
Tire the most according to claim 1 low rolling resistance and the manufacture method of shearing Hardening type rubber composite, it is special
Levy and be: the formula of described shear thickening materials is, high viscosity Polyethylene Glycol 15 ~ 30 weight portion, fiber floccule 1 ~ 2 weight
Part, nano-calcium carbonate 7 ~ 12 weight portion, Nano carbon white 5 ~ 8 weight portion, natural gum 2 ~ 10 weight portion.
Tire the most according to claim 4 low rolling resistance and the manufacture method of shearing Hardening type rubber composite, it is special
Levy and be: the formula of described high viscosity Polyethylene Glycol is, polyethylene glycol 200 is 1 ~ 3 weight portion, and PEG400 is 2 ~ 10
Weight portion, cetomacrogol 1000 is 12 ~ 22 weight portions.
Tire the most according to claim 1 low rolling resistance and the manufacture method of shearing Hardening type rubber composite, it is special
Levy and be: the formula of described filler is: the weight portion of white carbon black is 5 to 10 parts, and the weight portion of nano barium sulfate is 10 to 15 parts,
The weight portion of nano-calcium carbonate is 10 to 25 parts.