CN106242630A - A kind of low density foam concrete segment - Google Patents
A kind of low density foam concrete segment Download PDFInfo
- Publication number
- CN106242630A CN106242630A CN201610564112.9A CN201610564112A CN106242630A CN 106242630 A CN106242630 A CN 106242630A CN 201610564112 A CN201610564112 A CN 201610564112A CN 106242630 A CN106242630 A CN 106242630A
- Authority
- CN
- China
- Prior art keywords
- foam concrete
- low density
- concrete segment
- density foam
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The open a kind of low density foam concrete segment of the present invention; this low density foam concrete segment by weight, by including that following raw material is made: cement 50~60 parts, glass bead 15~25 parts, foaming agent 25 parts, foam stabilizer 0.1 0.5 parts, water reducer 0.5 1 parts.Compared with existing foam concrete block, the foam concrete block apparent density of the present invention is 300~400 kg/m3, heat conductivity≤0.03 W/ (m K), and there is good soundproof effect.
Description
Technical field
The invention belongs to building material field, be specifically related to a kind of low density foam concrete segment.
Background technology
Saving the strategic emphasis that the energy is China's economic development, specifically at building materials field, within 1986, Minstry of Housing and Urban-Rural Development of People Republic of China (MOHURD) promulgates
" Civil Building Energy Conservation design standard ", on October 1st, 2001, Minstry of Housing and Urban-Rural Development of People Republic of China (MOHURD) has issued that " hot-summer and cold-winter area is lived and built
Saving energy design in a building standard ".From 2000, the reducing energy consumption work of the existing building big to heating zone thermal environment difference or energy consumption
Having begun to, within 2005, country starts reducing energy consumption in key cities.Development of Novel construction material is to reduce building
The energy of building enclosure runs off, and is one of major measure improving building energy utilization ratio.
Summary of the invention
It is an object of the invention to provide a kind of low density foam concrete segment.
In order to solve above-mentioned technical problem, the invention provides following technical scheme:
A kind of low density foam concrete segment, by weight, by including that following raw material is made: cement 50~60 parts, vitreous are micro-
Pearl 15~25 parts, foaming agent 2-5 part, foam stabilizer 0.1-0.5 part, water reducer 0.5-1 part.
Described foaming agent is sodium lauryl sulphate or dodecylbenzene sodium sulfonate.
Described foam stabilizer is polyacrylamide, polyvinyl alcohol, gelatin or starch.
Described water reducer is sodium lignin sulfonate or naphthalene series high-efficiency water-reducing agent.
The particle diameter of described glass bead is 30-50 mesh.
The preparation process of above-mentioned low density foam concrete segment is as follows:
(1) cement mixes with water, makes slurry;
(2) in the slurry of step (1), add glass bead, after mixing thoroughly, add foaming agent, foam stabilizer and water reducer, stirring
0.5-2 hour;
(3) the slurry injection molding that step (2) is obtained, first maintenance 20-24 hour at 50-60 DEG C, then maintenance at 80-100 DEG C
After 2-3 hour, the demoulding, i.e. obtain described low density foam concrete segment.
Detailed description of the invention
Hereinafter the preferred embodiments of the present invention are illustrated, it will be appreciated that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
Embodiment 1
A kind of low density foam concrete segment, proportioning raw materials is as follows: cement 50 weight portion, glass bead 15 weight portion, 12
Alkyl sodium sulfate 2 weight portion, gelatin 0.1 weight portion, sodium lignin sulfonate 0.5 weight portion.
The particle diameter of described glass bead is 30-50 mesh.
Preparation process is as follows:
(1) cement is with water by weight mixing for 2:1, makes slurry;
(2) in the slurry of step (1), add glass bead, after mixing thoroughly, add sodium lauryl sulphate, gelatin and lignin
Sodium sulfonate, stirs half an hour;
(3) the slurry injection molding that step (2) is obtained, first maintenance 20-24 hour at 50-60 DEG C, then maintenance at 80-100 DEG C
After 2-3 hour, the moisture control after maintenance, in 7-8wt%, the demoulding, i.e. obtains described low density foam concrete segment.
Embodiment 2
A kind of low density foam concrete segment, proportioning raw materials is as follows: cement 60 weight portion, glass bead 25 weight portion, 12
Sodium alkyl benzene sulfonate 5 weight portion, polyacrylamide 0.5 weight portion, commercially available naphthalene series high-efficiency water-reducing agent 1 weight portion.
The particle diameter of described glass bead is 30-50 mesh.
Preparation process is as follows:
(1) cement is with water by weight mixing for 2:1.5, makes slurry;
(2) in the slurry of step (1), add glass bead, after mixing thoroughly, add dodecylbenzene sodium sulfonate, polyacrylamide
Amine and naphthalene series high-efficiency water-reducing agent, stir 2 hours;
(3) the slurry injection molding that step (2) is obtained, first maintenance 20-24 hour at 50-60 DEG C, then maintenance at 80-100 DEG C
After 2-3 hour, the moisture control after maintenance, in 7-8wt%, the demoulding, i.e. obtains described low density foam concrete segment.
The foam concrete block apparent density of the present invention is 300~400 kg/m3, heat conductivity≤0.03 W/ (m
And there is good soundproof effect K),.
Finally it is noted that the foregoing is only the preferred embodiments of the present invention, it is not limited to the present invention,
Although being described in detail the present invention with reference to previous embodiment, for a person skilled in the art, it still may be used
So that the technical scheme described in foregoing embodiments to be modified, or wherein portion of techniques feature is carried out equivalent.
All within the spirit and principles in the present invention, any modification, equivalent substitution and improvement etc. made, should be included in the present invention's
Within protection domain.
Claims (5)
1. a low density foam concrete segment, by weight, by including that following raw material is made: cement 50~60 parts, vitreous
Microballon 15~25 parts, foaming agent 2-5 part, foam stabilizer 0.1-0.5 part, water reducer 0.5-1 part.
Low density foam concrete segment the most according to claim 1, it is characterised in that described foaming agent is dodecyl
Sodium sulfate or dodecylbenzene sodium sulfonate.
Low density foam concrete segment the most according to claim 1, it is characterised in that described foam stabilizer is polyacrylamide
Amine, polyvinyl alcohol, gelatin or starch.
Low density foam concrete segment the most according to claim 1, it is characterised in that described water reducer is sulfomethylated lignin
Acid sodium or naphthalene series high-efficiency water-reducing agent.
Low density foam concrete segment the most according to claim 1, it is characterised in that the particle diameter of described glass bead is
30-50 mesh.