CN106242414A - Non-burning brick composition of raw materials - Google Patents

Non-burning brick composition of raw materials Download PDF

Info

Publication number
CN106242414A
CN106242414A CN201610892256.7A CN201610892256A CN106242414A CN 106242414 A CN106242414 A CN 106242414A CN 201610892256 A CN201610892256 A CN 201610892256A CN 106242414 A CN106242414 A CN 106242414A
Authority
CN
China
Prior art keywords
parts
burning brick
raw materials
brick composition
composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610892256.7A
Other languages
Chinese (zh)
Inventor
陈超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui University of Science and Technology
Original Assignee
Anhui University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui University of Science and Technology filed Critical Anhui University of Science and Technology
Priority to CN201610892256.7A priority Critical patent/CN106242414A/en
Publication of CN106242414A publication Critical patent/CN106242414A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of non-burning brick composition of raw materials, relate to field of civil engineering, this non-burning brick composition of raw materials includes coal ash, Iron Ore Powder, cement, quick lime, and add triethanolamine as early strength agent, add bauxite and sodium silicate as accelerator, this non-burning brick intensity can be effectively improved, increase its service life.

Description

Non-burning brick composition of raw materials
Technical field
The present invention relates to field of civil engineering, it is more particularly related to a kind of non-burning brick composition of raw materials.
Background technology
Non-burning brick is to utilize flyash, cinder, gangue, mine tailings, residue of chemical industry or natural sand, tidal land mud etc. as main Want raw material, a kind of materials for wall manufactured without high-temperature calcination.The raw material of existing non-burning brick employing is more traditional, it is impossible to protect The hardness of barrier brick, not only makes brick be easily broken in the course of processing, and reduces the life-span of brick.
Summary of the invention
Problem to be solved by this invention is to provide the composition of raw materials that a kind of high rigidity is non-burning brick.
To achieve these goals, the technical scheme that the present invention takes is: a kind of non-burning brick composition of raw materials, and its feature exists The raw material of following parts by weight is included: coal ash 45～60 parts, Iron Ore Powder 35～45 parts, cement 45 in, this non-burning brick composition of raw materials ～60 parts, quick lime 25～35 parts, triethanolamine 1～4 parts, bauxite 1～3 parts, sodium silicate 1～3 parts.
Beneficial effect: this non-burning brick composition of raw materials includes coal ash, Iron Ore Powder, cement, quick lime, and adds three ethanol Amine as accelerator, can be effectively improved this non-burning brick intensity as early strength agent, addition bauxite and sodium silicate, increases it and uses Life-span.
Detailed description of the invention
Embodiment 1:
This non-burning brick composition of raw materials includes the raw material of following parts by weight: coal ash 45 parts, Iron Ore Powder 45 parts, cement 45 parts, Quick lime 35 parts, triethanolamine 2 parts, bauxite 2 parts, sodium silicate 2 parts.
Embodiment 2:
This non-burning brick composition of raw materials includes the raw material of following parts by weight: coal ash 50 parts, Iron Ore Powder 40 parts, cement 50 parts, Quick lime 30 parts, triethanolamine 1 part, bauxite 1 part, sodium silicate 1 part.
Embodiment 3:
This non-burning brick composition of raw materials includes the raw material of following parts by weight: coal ash 60 parts, Iron Ore Powder 35 parts, cement 60 parts, Quick lime 25 parts, triethanolamine 3 parts, bauxite 3 parts, sodium silicate 3 parts.
The foregoing is only embodiments of the invention, not thereby limit the scope of the claims of the present invention, every utilize this Equivalent structure or equivalence flow process that bright description and embodiment content are made convert, or it is relevant to be directly or indirectly used in other Technical field, be the most in like manner included in the scope of patent protection of the present invention.

Claims (1)

1. a non-burning brick composition of raw materials, it is characterised in that this non-burning brick composition of raw materials includes the raw material of following parts by weight: coal Ash 45～60 parts, Iron Ore Powder 35～45 parts, cement 45～60 parts, quick lime 25～35 parts, triethanolamine 1～4 parts, bauxite 1 ～3 parts, sodium silicate 1～3 parts.
CN201610892256.7A 2016-10-12 2016-10-12 Non-burning brick composition of raw materials Pending CN106242414A (en)