CN106240097A - A kind of environment-friendly polyvinyl chloride abrasion-proof water-proof floor and manufacture method thereof - Google Patents
A kind of environment-friendly polyvinyl chloride abrasion-proof water-proof floor and manufacture method thereof Download PDFInfo
- Publication number
- CN106240097A CN106240097A CN201610604824.9A CN201610604824A CN106240097A CN 106240097 A CN106240097 A CN 106240097A CN 201610604824 A CN201610604824 A CN 201610604824A CN 106240097 A CN106240097 A CN 106240097A
- Authority
- CN
- China
- Prior art keywords
- environment
- parts
- polyvinyl chloride
- friendly polyvinyl
- floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The open a kind of environment-friendly polyvinyl chloride floor of the present invention and manufacture method thereof, belong to technical field of floor.This environment-friendly polyvinyl chloride floor is prepared from the following components: PVC plastic raw material 40 70 parts, calcium carbonate 30 60 parts, lubricant 0.5 6 parts, chlorinated polyethylene 38 parts, stabilizer 1.5 4 parts, foaming agent 0.3 3 parts, foaming control agent 3 10 parts, plasticizer 0.1 2.5 parts, age resister 0.2 1 parts, bamboo wood powder 3 10 parts.Environment-friendly polyvinyl chloride floor of the present invention is with Corvic and calcium carbonate as primary raw material, through macromolecule modified, and a kind of composite being processed into mixture, high temperature extrusion equipment.The formaldehydeless release of PVC flooring of the present invention, the advantage such as waterproof the most mouldy, aging resistance, acid and alkali-resistance, walking are comfortable.
Description
Technical field
The invention belongs to technical field of floor, specifically a kind of environment-friendly polyvinyl chloride floor and manufacture method thereof.
Background technology
In finishing field, flooring pavement material is generally various wood floors or compoiste wood floor.Wood floors
Sense of touch pleasant, but easily imbibition or drying distortions, the most often occur contraction, dilatancy, warp,
Problems of crack, and need to expend a large amount of timber, the production cycle is longer, relatively costly, and use can destroy forest in a large number,
Unsustainable.A kind of ground that composite floor board is formed mainly by wood flour and binding agent and the blended extruding of other additive
Plate, its surface color and polish enriches, low cost, but there is the problems such as hygroscopic deformation, and the subject matter on this floor is release
Formaldehyde, serious harm health, not environmentally.
PVC flooring is that one mainly has polyvinyl chloride resin powder, calcium carbonate, some processing aids, after mix homogeneously
The high-tech green material made through die apparatus heating extrusion molding again, can substitute solid wooden floor board and compoiste wood floor
Novel environment friendly hitech materials.
Along with people's reinforcement to environmental consciousness, the attention to indoor environmental pollution, Wood-plastic floor will replace containing formaldehyde
Measure high compoiste wood floor and the most wear-resisting, yielding, waste the solid wooden floor board of a large amount of timber resources and become decorative building material at home
The new lover in market.
Summary of the invention
It is an object of the invention to provide a kind of environment-friendly polyvinyl chloride floor and manufacture method thereof.
Technical scheme can be realized by herein below:
A kind of environment-friendly polyvinyl chloride floor, it is characterised in that this environment-friendly polyvinyl chloride floor is prepared from the following components: PVC
Plastic raw materials 40-70 part, calcium carbonate 30-60 part, lubricant 0.5-6 part, chlorinated polyethylene 3-8 part, stabilizer 1.5-4 part, send out
Infusion 0.3-3 part, foaming control agent 3-10 part, plasticizer 0.1-2.5 part, age resister 0.2-1 part, bamboo wood powder 3-10 part.
This environment-friendly polyvinyl chloride floor is prepared from by following component: PVC plastic raw material 40-50 part, calcium carbonate 40-50
Part, lubricant 0.7-5 part, chlorinated polyethylene 4-7 part, stabilizer 2-3 part, foaming agent 0.8-1.5 part, foaming control agent 4-8 part,
Plasticizer 0.5-2 part, age resister 0.4-0.8 part, bamboo wood powder 5-8 part.
This environment-friendly polyvinyl chloride floor is prepared from by following component: PVC plastic raw material 44 parts, calcium carbonate 44 parts, lubrication
Agent 4 parts, chlorinated polyethylene 5 parts, stabilizer 2.5 parts, foaming agent 1 part, foaming control agent 6 parts, plasticizer 1 part, anti-ageing colored agent 0.6
Part, bamboo wood powder 7 parts.
Described stabilizer is heat stabilizer.
Described plasticizer is OPE.
Described lubricant is that Tissuemat E, PE wax, stearic acid, in-lubricant are with the mixing of arbitrary proportion.
The fineness of described light weight calcium is 1000 mesh.
Invention additionally discloses the manufacture method on a kind of environment-friendly polyvinyl chloride floor, the method specifically includes following steps:
(1) premixing: take PVC plastic raw material according to component, plasticizer, heat stabilizer, chlorinated polyethylene carry out premixing, mixing
Temperature is 100-120 DEG C, and the rotating speed of batch mixing is 800 r/min, and incorporation time 10min obtains compound one；
(2) PVC flooring raw material mixing: the compound one that step (1) is obtained and calcium carbonate, lubricant, foaming agent, send out
Bubble regulator, age resister carry out mixed at high speed, and mixing temperature is 100-120 DEG C, and the rotating speed of batch mixing is 800 r/min, mixing
Time 10min, obtains polrvinyl chloride mixed powder；
(3) extrusion molding: polrvinyl chloride mixed powder is through double screw extruder and shaper molding, water-cooled, traction, cutting action
After, make PVC flooring substrate；
(4) board finished product processing: PVC flooring substrate warp bonds through Environment-friendlyglue glue with required PVC cortex, then
Cut according to customer requirement specification, then entered double-end milling machine equipment, after milling out the four sides male and female groove of substrate, be made as polychlorostyrene second
Alkene ground board finished product.
Beneficial effects of the present invention: environment-friendly polyvinyl chloride floor of the present invention is with polyvinyl chloride resin powder and calcium carbonate for the most former
Material,
Through macromolecule modified, a kind of composite being processed into mixture, high temperature extrusion equipment.Polrvinyl chloride of the present invention ground
Plate is the most mouldy, aging resistance, acid and alkali-resistance, insect pest, nontoxic.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in further detail.
Embodiment 1
A kind of environment-friendly polyvinyl chloride floor, this environment-friendly polyvinyl chloride floor is prepared from by following component: PVC plastic raw material 44
Part, calcium carbonate 44 parts, lubricant 4 parts, chlorinated polyethylene 5 parts, stabilizer 2.5 parts, foaming agent 1 part, foaming control agent 6 parts, increasing
Mould agent 1 part, anti-ageing colored agent 0.6 part, bamboo wood powder 7 parts.Wherein the fineness of calcium carbonate is 1000 mesh.
A kind of manufacture method on environment-friendly polyvinyl chloride floor, the method specifically includes following steps:
(1) premixing: take polyvinyl chloride resin powder according to component, plasticizer, heat stabilizer, chlorinated polyethylene carry out premixing,
Mixing temperature is 100-120 DEG C, and the rotating speed of batch mixing is 800 r/min, and incorporation time 10min obtains compound one；
(2) PVC flooring raw material mixing: the compound one that step (1) is obtained and calcium carbonate, lubricant, foaming agent, send out
Bubble regulator, age resister carry out mixed at high speed, and mixing temperature is 100-120 DEG C, and the rotating speed of batch mixing is 800 r/min, mixing
Time 10min, obtains polrvinyl chloride mixed powder；
(3) extrusion molding: polrvinyl chloride mixed powder is through double screw extruder and shaper molding, water-cooled, traction, cutting action
After, make PVC flooring substrate；
(4) board finished product processing: PVC flooring substrate warp bonds through Environment-friendlyglue glue with required PVC cortex, then
Cut according to customer requirement specification, then entered double-end milling machine equipment, after milling out the four sides male and female groove of substrate, be made as polychlorostyrene second
Alkene ground board finished product.
Embodiment 2
A kind of environment-friendly polyvinyl chloride floor, this environment-friendly polyvinyl chloride floor is prepared from by following component: PVC plastic raw material 48
Part, calcium carbonate 48 parts, lubricant 5 parts, chlorinated polyethylene 6 parts, stabilizer 4 parts, foaming agent 2 parts, foaming control agent 6.5 parts, increasing
Mould agent 1.5 parts, anti-ageing colored agent 1 part, bamboo wood powder 7.5 parts.Wherein the fineness of light weight calcium is 1000 mesh.
A kind of manufacture method on environment-friendly polyvinyl chloride floor, the method specifically includes following steps:
(1) premixing: take polyvinyl chloride resin powder according to component, plasticizer, heat stabilizer, chlorinated polyethylene carry out premixing,
Mixing temperature is 100-120 DEG C, and the rotating speed of batch mixing is 800 r/min, and incorporation time 10min obtains compound one；
(2) PVC flooring raw material mixing: the compound one that step (1) is obtained and calcium carbonate, lubricant, foaming agent, send out
Bubble regulator, age resister carry out mixed at high speed, and mixing temperature is 100-120 DEG C, and the rotating speed of batch mixing is 800 r/min, mixing
Time 10min, obtains polrvinyl chloride mixed powder；
(3) extrusion molding: polrvinyl chloride mixed powder is through double screw extruder and shaper molding, water-cooled, traction, cutting action
After, make PVC flooring substrate；
(4) board finished product processing: PVC flooring substrate warp bonds through Environment-friendlyglue glue with required PVC cortex, then
Cut according to customer requirement specification, then entered double-end milling machine equipment, after milling out the four sides male and female groove of substrate, be made as polychlorostyrene second
Alkene ground board finished product.
Embodiment 3
A kind of environment-friendly polyvinyl chloride floor, this environment-friendly polyvinyl chloride floor is prepared from by following component: PVC plastic raw material 44
Part, calcium carbonate 50 parts, lubricant 5.5 parts, chlorinated polyethylene 5.5 parts, stabilizer 2.9 parts, foaming agent 1.5 parts, foaming control agent
6.5 parts, plasticizer 1.5 parts, anti-ageing colored agent 0.8 part, bamboo wood powder 7.5 parts.Wherein the fineness of light weight calcium is 1000 mesh.
A kind of manufacture method on environment-friendly polyvinyl chloride floor, the method specifically includes following steps:
(1) premixing: take polyvinyl chloride resin powder according to component, plasticizer, heat stabilizer, chlorinated polyethylene carry out premixing,
Mixing temperature is 100-120 DEG C, and the rotating speed of batch mixing is 800 r/min, and incorporation time 10min obtains compound one；
(2) PVC flooring raw material mixing: the compound one that step (1) is obtained and calcium carbonate, lubricant, foaming agent, send out
Bubble regulator, age resister carry out mixed at high speed, and mixing temperature is 100-120 DEG C, and the rotating speed of batch mixing is 800 r/min, mixing
Time 10min, obtains polrvinyl chloride mixed powder；
(3) extrusion molding: polrvinyl chloride mixed powder is through double screw extruder and shaper molding, water-cooled, traction, cutting action
After, make PVC flooring substrate；
(4) board finished product processing: PVC flooring substrate warp bonds through Environment-friendlyglue glue with required PVC cortex, then
Cut according to customer requirement specification, then entered double-end milling machine equipment, after milling out the four sides male and female groove of substrate, be made as polychlorostyrene second
Alkene ground board finished product.
The environment-friendly polyvinyl chloride floor of the present invention, has good wearability, resistance to soiling and skid resistance, and passerby is comfortable, can
It is widely used in the places such as hospital, school, office building, market, traffic, industry, household gymnasium.
Claims (9)
1. an environment-friendly polyvinyl chloride floor, it is characterised in that this environment-friendly polyvinyl chloride floor is prepared from by following component:
PVC plastic raw material 40-70 part, calcium carbonate 30-60 part, lubricant 0.5-6 part, chlorinated polyethylene 3-8 part, stabilizer 1.5-4 part,
Foaming agent 0.3-3 part, foaming control agent 3-10 part, plasticizer 0.1-2.5 part, age resister 0.2-1 part, bamboo wood powder 3-10 part.
Environment-friendly polyvinyl chloride floor the most according to claim 1, it is characterised in that this environment-friendly polyvinyl chloride floor is by following
Component is prepared from: PVC plastic raw material 40-50 part, calcium carbonate 40-50 part, lubricant 0.7-5 part, chlorinated polyethylene 4-7 part,
Stabilizer 2-3 part, foaming agent 0.8-1.5 part, foaming control agent 4-8 part, plasticizer 0.5-2 part, age resister 0.4-0.8 part,
Bamboo wood powder 5-8 part.
Environment-friendly polyvinyl chloride floor the most according to claim 1, it is characterised in that this environment-friendly polyvinyl chloride floor is by following
Component is prepared from: PVC plastic raw material 44 parts, calcium carbonate 44 parts, lubricant 4 parts, chlorinated polyethylene 5 parts, stabilizer 2.5 parts,
Foaming agent 1 part, foaming control agent 6 parts, plasticizer 1 part, anti-ageing colored agent 0.6 part, bamboo wood powder 7 parts.
Environment-friendly polyvinyl chloride floor the most according to claim 1, it is characterised in that described stabilizer is heat stabilizer.
Environment-friendly polyvinyl chloride floor the most according to claim 1, it is characterised in that described plasticizer is oxidic polyethylene
Wax.
Environment-friendly polyvinyl chloride floor the most according to claim 1, it is characterised in that described lubricant is Tissuemat E, PE
Wax, stearic acid, in-lubricant are with the mixing of arbitrary proportion.
Environment-friendly polyvinyl chloride floor the most according to claim 1, it is characterised in that described foaming agent be AC yellow hair infusion and
NC poliosis infusion mixes according to foaming requirement.
8. according to the environment-friendly polyvinyl chloride floor described in claim 1 or 2 or 3, it is characterised in that the fineness of described light weight calcium is
1000 mesh.
9. the preparation method on the environment-friendly polyvinyl chloride floor as described in claim 1 or 2 or 3, rises and is characterised by, the method
Specifically include following steps:
Premixing: take PVC plastic raw material according to component, plasticizer, heat stabilizer, chlorinated polyethylene carry out premixing, mixing temperature
Degree is for 100-120 DEG C, and the rotating speed of batch mixing is 800 r/min, incorporation time 10min, obtains compound one；
PVC flooring raw material mixes: the compound one step (1) obtained is adjusted with calcium carbonate, lubricant, foaming agent, foaming
Joint agent, age resister carry out mixed at high speed, and mixing temperature is 100-120 DEG C, and the rotating speed of batch mixing is 800 r/min, incorporation time
10min, obtains polrvinyl chloride mixed powder；
Extrusion molding: polrvinyl chloride mixed powder through double screw extruder and shaper shape molding, water-cooled, draw, cut work
After sequence, make PVC flooring substrate；
Ground board finished product processing: PVC flooring substrate warp bonds through Environment-friendlyglue glue with required PVC cortex, further according to
Customer requirement specification is cut, then enters double-end milling machine equipment, after milling out the four sides male and female groove of substrate, is made as polrvinyl chloride ground
Board finished product.