A kind of long-life uniform elastic trampoline
Technical field
The invention belongs to trampoline and for the elastic trampoline cloth field of trampoline.
Background technique
It 2009 " Bedjump ", runs away rapidly on website, Chinese is translated into " trampoline " or " trampoline ".It is gathered around in all parts of the world
There are numerous fans for growing tender of this movement.Fan would generally select the bed that elasticity is good, jump up, and make in the sky various dynamic
Make.Trampoline is mainly equipped with a fabric tightened by most springs in the frame for the foot prop support that lands, and stands on for user
Constantly spring carries out interest movement on spring face.Trampoline in the prior art has the following deficiencies: the frame body of 1. trampolines
Product is larger, thus after manufacturer produces bouncer products, each assembled trampoline has sizable volume,
Finished product is not only stored up in factory can occupy the confined space in factory, and when export trade also will increase transportation cost, furthermore, no matter exhibition sale
Shop or personal use person, trampoline be intended to occupy sizable interior space without using under state.2. current trampoline is adopted
It uses spring as its elastic force source, for the sake of security, needs to be laid with neonychium above spring, avoid unexpected generation.So
This neonychium needs to increase the cost of trampoline;Built-up time is increased, simultaneously as spring can generate flexible deformation, it is former
Neonychium is tightly to cover, but after the flexible deformation of spring, neonychium can deviate, and cause to cover when this is not used
Lid is uneven and exposes spring, so as to will increase the incidence of safety accident.3. again due to being using spring as elasticity
Part is covered using neonychium and is laid with, greatly reduces effective usable floor area of trampoline, the reality of trampoline has been limited in the presence of spring
It jumps space.The problems such as elastical cloth of trampoline in the prior art, service life is short, cloth cover uniform elastic is poor.
Summary of the invention
To solve the above-mentioned problems, technical scheme is as follows:
A kind of long-life uniform elastic trampoline, it is characterised in that: including frame, elastic trampoline cloth and protective net, the frame
Frame includes bottom frame and the foot lever that is installed below bottom frame.
Elastic trampoline cloth is double-layer structure, and one layer is resilient material made of nylon fiber, and another layer is cellulose fiber
Manufactured material strips are tieed up, are combined between two layers by high polymer elastic layer;Every layer all from through elastic to elastic webbing and broadwise
Band composition, it is described through being diamond shape to the gap between elastic webbing and broadwise elastic webbing;The gap is 10 to 25 squares of millis
Rice;It is described through being 2-5 millimeters to the spacing between elastic webbing;Spacing between the broadwise elastic webbing is 3-6 millimeters;Institute
The high polymer elastic layer stated includes at least thermoplastic elastomer (TPE) or thermo-setting elastomer using high polymer elastic material;Its
Middle thermoplastic elastomer (TPE) includes thermoplastic, Polyurethane, polyvinyl chloride;Thermo-setting elastomer then includes silica gel.The Buddhist nun
Imperial resilient material have passed through anti-aging processing, processing step are as follows:
1) preparation of age resister
Under nitrogen protection, by 3,4- chloro-2-methyl aniline or 2- naphthylamines or 4- amino -3,2- dimethyl azobenzene or 2-
Amino -4- nitrotoleune, is added in the water of the sodium hydroxide of 1.5 ~ 4 mol/L and the mixed solution of ethyl alcohol, stirs simultaneously by several times
Reducing agent thiourea dioxide is added, is cooled to room temperature after reacting 0.5 ~ 3h at 75 ~ 80 DEG C, sulfuric acid is added and adjusts pH value 5
Between~6, filtering, dry in the shade, re-dry after recrystallization obtains functional modifier crude product, then by functional modifier crude product,
Hydrofluoric acid and concentrated nitric acid are added in reaction vessel, and after being heated to 45 ~ 50 DEG C of 1.5~2.0h of reaction, Off-white product is obtained by filtration,
It is filtered through cooling, dries in the shade, recrystallize and dry, obtain age resister;
2) preparation of anti-ageing microcapsules and age resister finishing fluid
Using deionized water as solvent, in a solvent age resister dispersion, whipping temp is room temperature, is controlled in whipping process
Rate is 500~1000r/min, and being dispersed with stirring the time is 50~65min, and age resister molecule is enable to be formed in aqueous solution
Then suspension system adds hydroxyethyl cellulose and is dissolved, then carries out high-speed stirred dispersion, whipping temp is 35~40
DEG C, stirring rate is 3400~3600r/min, and mixing time is 10~15min, and it is poly- then to add butane tetracarboxylic acid progress shell
Sugar crosslinking, then curing 10min is carried out under the conditions of 85~90 DEG C, thick modified capsule is obtained by filtration, then dry in 60 DEG C of progress vacuum
It is dry for 24 hours after, obtain the modification capsule containing age resister;Its sandwich layer is age resister, and cystoblast is hydroxyethylcellulose materials,
In, the thickness ratio of cystoblast and sandwich layer is 1: 18;By manufactured age resister microcapsules 3-6%(owf), penetrating agent JFC 1-2g/l,
PH value is 7-7.5, is made into age resister finishing fluid;
The volume ratio of water and ethyl alcohol in the mixed solution of the water and ethyl alcohol is 1: 2;The thiourea dioxide with
3, the molar ratio of 4- chloro-2-methyl aniline or 2- naphthylamines or 4- amino -3,2- dimethyl azobenzene or 2- amino -4- nitrotoleune
It is 2: 1.5;The molar ratio 2: 2.2: 1.1 of the functional modifier crude product, hydrofluoric acid and concentrated nitric acid.
The age resister additive amount is 3.5-16% relative to the mass fraction of water;
The hydroxyethyl cellulose additive amount is 2.0-8% relative to the mass fraction of water;
The weight average molecular weight of the hydroxyethyl cellulose is 20000~25000, and molar substitution is 1.8~1.9.
The butane tetracarboxylic acid is 0.3% relative to the mass fraction of chitosan.
The diameter of modified capsule is 2~5 μm, is conducive to capsule and passes through spinneret orifice, and guarantees capsule and fiber
Be firmly combined, the mechanical performance of fiber can't be influenced.
The capsule of modified capsule/core guarantees that microcapsules have certain mechanical strength and heat-resisting than being generally higher than equal to 1: 10
Property.
The effect of modified capsule is, plays the role of the anti-aging functional particles of slow release, is conducive to its anti-aging function
Effect is able to permanent holding.
3) anti-aging arrangement is carried out to nylon elastic material strips with the finishing fluid prepared.
Nylon elastic material strips are put into age resister finishing fluid and are impregnated, bath raio 1:20-50 soaks at 40 ~ 50 DEG C
Stain 30-80 minutes, washing drying;Then the band arranged by age resister is immersed with fixed liquid by the bath raio of 1:20-30 solid
In liquid, after permeating completely under room temperature, two leachings two are rolled, and pick-up 70-90% is dried in 80 DEG C, and 100-140 DEG C bake 2-3 points
Clock is washed, is soaped, is dried;The composition of the fixation liquid includes glyoxal, magnesium chloride, tartaric acid and water, and concentration is 40% second
Dialdehyde content in every liter of water is 20-50g, and magnesium chloride content in every liter of water is 2-5g, and tartaric acid content in every liter of water is
1-3g, the mixed liquor stirred evenly at room temperature.
Trampoline in the present invention, compared with the prior art, have it is following the utility model has the advantages that
(1) Double-layer elastic material is used, the combined type constituted between elastic woven material is set to by high polymer elastic layer
Structural form, and by the cooperation of nylon elastic layer and cellulose material bilayer, for making present invention control prior art, energy
Enough while there is different degrees of elastic telescopic power to enhance elasticity and durability and gas permeability;
(2) the synthesized age resister of invention has the anti-aging property of excellent absorption living radical, preparation process
Simply, yield is high, and is easily isolated, and raw material employed in preparation process and solvent are environmentally protective;Using with reactive end
The age resister of hydroxy functional group is coated by the method for microcapsules with hydroxyethyl cellulose, and age resister is both improved
Dispersibility and stability, while also achieving the dispersibility of organic aging agent in the material, realize age resister uniformly point
It dissipates and the high performance purpose of few additive;Simultaneously in age resister molecule due to benzotriazole functional group have it is excellent anti-ageing
Change performance, being particularly due to radiation makes material generate living radical, loses living radical under the action of age resister
It is living, to improve the ageing-resistant performance of material;Hydroxyethyl cellulose wall material and the compatibility of basis material are preferable, and it is micro- to be conducive to modification
Disperse in capsule material nylon material, spinning and fibrous mechanical property are influenced less, on the basis of guaranteeing fibre property, to mention
The high anti-aging property of material.
Specific embodiment
Embodiment 1
Nylon elastic material strips first be have passed through into anti-aging processing, processing step are as follows:
1) preparation of age resister
Under nitrogen protection, by 3,4- chloro-2-methyl aniline, the water and ethyl alcohol of the sodium hydroxide of 4 mol/L are added to
In mixed solution, stirs and reducing agent thiourea dioxide is added by several times, be cooled to room temperature after reacting 3h at 80 DEG C, sulfuric acid is added
PH value is adjusted between 6, filters, dries in the shade, re-dry after recrystallization obtains functional modifier crude product, then changes function
Property agent crude product, hydrofluoric acid and concentrated nitric acid are added in reaction vessel, after being heated to 50 DEG C of reaction 1.5h, canescence are obtained by filtration and produces
Object filters through cooling, dries in the shade, recrystallize and dry, obtain age resister;
2) preparation of anti-ageing microcapsules and age resister finishing fluid
Using deionized water as solvent, in a solvent age resister dispersion, whipping temp is room temperature, is controlled in whipping process
Rate is 1000r/min, and being dispersed with stirring the time is 65min, and age resister molecule is enable to form suspension system in aqueous solution,
Then it adds hydroxyethyl cellulose to be dissolved, then carries out high-speed stirred dispersion, whipping temp is 40 DEG C, and stirring rate is
3600r/min, mixing time 15min, then add butane tetracarboxylic acid carry out it is chitosan crosslinked, then under the conditions of 85 DEG C into
Row curing 10min is obtained by filtration thick modified capsule, then after 60 DEG C are dried in vacuo for 24 hours, obtains changing containing age resister
Property capsule;Its sandwich layer is age resister, and cystoblast is hydroxyethylcellulose materials, wherein the thickness of cystoblast and sandwich layer ratio is 1: 18;
By manufactured age resister microcapsules 3.6%(owf), penetrating agent JFC 1.2g/l, pH value 7 is made into age resister finishing fluid;
The volume ratio of water and ethyl alcohol in the mixed solution of the water and ethyl alcohol is 1: 2;The thiourea dioxide with
3, the molar ratio of 4- chloro-2-methyl aniline is 2: 1.5;The functional modifier crude product, mole of hydrofluoric acid and concentrated nitric acid
Than 2: 2.2: 1.1.
The age resister additive amount is 8% relative to the mass fraction of water;
The hydroxyethyl cellulose additive amount is 2. 8% relative to the mass fraction of water;
The weight average molecular weight of the hydroxyethyl cellulose is 28000, molar substitution 1.8.
The butane tetracarboxylic acid is 0.3% relative to the mass fraction of chitosan.
The diameter of modified capsule is 4 μm, is conducive to capsule and passes through spinneret orifice, and guarantees capsule and fiber
It is firmly combined, the mechanical performance of fiber can't be influenced.
The capsule of modified capsule/core guarantees that microcapsules have certain mechanical strength and heat-resisting than being generally higher than equal to 1: 10
Property.
3) anti-aging arrangement is carried out to nylon elastic material strips with the finishing fluid prepared.
Nylon elastic material strips are put into age resister finishing fluid and be impregnated, bath raio 1:25,46 points of dipping at 44 DEG C
Clock, washing drying;Then the band arranged by age resister is immersed in fixed liquid with fixed liquid by the bath raio of 1:25, under room temperature
Completely after infiltration, two leachings two are rolled, and pick-up 89% is dried in 80 DEG C, and 130 DEG C bake 3 minutes, are washed, soaped, dried;It is described
The composition of fixed liquid includes glyoxal, magnesium chloride, tartaric acid and water, and concentration is that 40% glyoxal content in every liter of water is 26g,
Magnesium chloride content in every liter of water is 2.5g, and tartaric acid content in every liter of water is 1.3g, the mixing stirred evenly at room temperature
Liquid.
It is material strips made of cellulose fibre by another layer of resilient material made of nylon fiber, passes through between two layers
High polymer elastic layer is combined;Every layer all from through being formed to elastic webbing and broadwise elastic webbing, it is described through to elastic webbing and latitude
It is diamond shape to the gap between elastic webbing;The gap is 18 square millimeters;It is described through being to the spacing between elastic webbing
2.5 millimeter;Spacing between the broadwise elastic webbing is 3.6 millimeters;The high polymer elastic layer is using macromolecule
Elastic material, including polyvinyl chloride.
Elastic trampoline cloth is used for trampoline.
Embodiment 2
Nylon elastic material strips first be have passed through into anti-aging processing, processing step are as follows:
1) preparation of age resister
Under nitrogen protection, by 2- naphthylamines, the water of the sodium hydroxide of 1.5mol/L and the mixed solution of ethyl alcohol are added to
In, it stirs and reducing agent thiourea dioxide is added by several times, be cooled to room temperature after reacting 3h at 80 DEG C, sulfuric acid is added by pH value tune
Section is filtered, is dried in the shade, re-dry after recrystallization obtains functional modifier crude product, then slightly produces functional modifier between 6
Object, hydrofluoric acid and concentrated nitric acid are added in reaction vessel, after being heated to 50 DEG C of reaction 2.0h, Off-white product are obtained by filtration, through cold
But it filters, dries in the shade, recrystallize and dry, obtain age resister;
2) preparation of anti-ageing microcapsules and age resister finishing fluid
Using deionized water as solvent, in a solvent age resister dispersion, whipping temp is room temperature, is controlled in whipping process
Rate is 1000r/min, and being dispersed with stirring the time is 50min, and age resister molecule is enable to form suspension system in aqueous solution,
Then it adds hydroxyethyl cellulose to be dissolved, then carries out high-speed stirred dispersion, whipping temp is 40 DEG C, and stirring rate is
3600r/min, mixing time 15min, then add butane tetracarboxylic acid carry out it is chitosan crosslinked, then under the conditions of 90 DEG C into
Row curing 10min is obtained by filtration thick modified capsule, then after 60 DEG C are dried in vacuo for 24 hours, obtains changing containing age resister
Property capsule;Its sandwich layer is age resister, and cystoblast is hydroxyethylcellulose materials, wherein the thickness of cystoblast and sandwich layer ratio is 1: 18;
By manufactured age resister microcapsules 3%(owf), penetrating agent JFC 2g/l, pH value 7 is made into age resister finishing fluid;
The volume ratio of water and ethyl alcohol in the mixed solution of the water and ethyl alcohol is 1: 2;The thiourea dioxide with
The molar ratio of 2- naphthylamines is 2: 1.5;The molar ratio 2: 2.2 of the functional modifier crude product, hydrofluoric acid and concentrated nitric acid:
1.1。
The age resister additive amount is 3.5% relative to the mass fraction of water;
The hydroxyethyl cellulose additive amount is 2.0% relative to the mass fraction of water;
The weight average molecular weight of the hydroxyethyl cellulose is 20000, molar substitution 1.8.
The butane tetracarboxylic acid is 0.3% relative to the mass fraction of chitosan.
The diameter of modified capsule is 2 μm, is conducive to capsule and passes through spinneret orifice, and guarantees capsule and fiber
It is firmly combined, the mechanical performance of fiber can't be influenced.
The capsule of modified capsule/core guarantees that microcapsules have certain mechanical strength and heat-resisting than being generally higher than equal to 1: 10
Property.
3) anti-aging arrangement is carried out to nylon elastic material strips with the finishing fluid prepared.
Nylon elastic material strips are put into age resister finishing fluid and be impregnated, bath raio 1:20,30 points of dipping at 50 DEG C
Clock, washing drying;Then the band arranged by age resister is immersed in fixed liquid with fixed liquid by the bath raio of 1:20, under room temperature
Completely after infiltration, two leachings two are rolled, and pick-up 90% is dried in 80 DEG C, and 140 DEG C bake 2 minutes, are washed, soaped, dried;Institute
The composition for stating fixed liquid includes glyoxal, magnesium chloride, tartaric acid and water, and concentration is that 40% glyoxal content in every liter of water is
50g, magnesium chloride content in every liter of water are 5g, and tartaric acid content in every liter of water is 3g, the mixing stirred evenly at room temperature
Liquid.
It is material strips made of cellulose fibre by another layer of resilient material made of nylon fiber, passes through between two layers
High polymer elastic layer is combined;Every layer all from through being formed to elastic webbing and broadwise elastic webbing, it is described through to elastic webbing and latitude
It is diamond shape to the gap between elastic webbing;The gap is 15 square millimeters;It is described through being 5 to the spacing between elastic webbing
Millimeter;Spacing between the broadwise elastic webbing is 4 millimeters;The high polymer elastic layer is using high polymer elastic material
Matter, including silica gel.
Elastic trampoline cloth is used for trampoline.
Comparative example 1
Capsule will be modified and polypropylene particles carry out melt spinning, modified polypropene silk is obtained, then again by modification poly- third
Alkene silk is woven into yarn, is made into elastic trampoline cloth by yarn;
The mass fraction of modification capsule in the modified polypropene silk is 2%.
The preparation method of modified capsule, the specific steps are that:
(a) to the preparation of dihydroxy Pyrogentisinic Acid's base phosphine
Using Phenylphosphine and paraformaldehyde as raw material, using water and isopropyl alcohol mixture as solvent, send out under the action of catalyst
Raw affine addition reaction, control reaction temperature are 35~50 DEG C, and the reaction time is 3~4h;Dihydroxymethyl phenyl is prepared
Phosphine, then at 85~95 DEG C, the mixed solution that hydrogen peroxide and the concentrated sulfuric acid is added is strong oxidizer, 45~60min of oxidation,
Dihydroxymethyl phenyl phosphine oxide is prepared, by the hydroquinol base phosphine of synthesis, bromine water and iron powder are added in reaction vessel,
Kermesinus product is obtained by filtration after being heated to 65~75 DEG C of 0.5~1.75h of reaction, it is added to 0.2mol/L at normal temperature
Potassium hydroxide and ethyl alcohol potassium solution in, in 80~95 DEG C of 1~3h of reaction after being completely dissolved, then by product in steam bath weigh
Crystallization, in triplicate, obtain white to dihydroxy Pyrogentisinic Acid's base phosphine;
The molar ratio of the Phenylphosphine and paraformaldehyde is 1: 2.1;
Catalyst is vanadic anhydride, and the Phenylphosphine and catalyst molar ratio value are 1: 0.03;
The volume ratio of the water and isopropanol is 1: 0.75;
The mass fraction of the paraformaldehyde is 10%;
The mass values of the strong oxidizer and Phenylphosphine are 1: 2.5;
The mass fraction of the hydrogen peroxide is 20%;
Hydrogen peroxide and concentrated sulfuric acid volume ratio are 1: 1 in the hydrogen peroxide and concentrated sulfuric acid solution;
The hydroquinol base phosphine, the molar ratio 1: 1.2: 0.01 of bromine water and iron powder;
The molar ratio of the potassium hydroxide and potassium ethoxide is 1: 2.5;
(b) preparation of ortho-nitraniline diazonium salt
Ortho-nitraniline is stirred strongly in the concentrated nitric acid of 12mol/L and is quickly cooled to 0 DEG C, is added after 1.5h
4mol/L potassium nitrite aqueous solution filters after reacting 0.5~1.0h at 0~5 DEG C, obtains ortho-nitraniline diazonium salt;
(c) preparation of azo-compound
By step (a) preparation dihydroxy Pyrogentisinic Acid's base phosphine is added into the mixed solution of isopropanol and distilled water, protect
It holds 5~10 DEG C of solution temperature, instills the ortho-nitraniline diazonium salt of step (b) preparation by several times, filter, washing, dry azo
Compound is rediance crystal;
The volume ratio of isopropanol and distilled water in the mixed solution of the isopropanol and distilled water is 1: 0.75;
Described is 4% in the mass fraction of isopropanol and the mixed solution of distilled water to dihydroxy Pyrogentisinic Acid's base phosphine;
The molar ratio to dihydroxy Pyrogentisinic Acid's base phosphine and ortho-nitraniline diazonium salt is 1: 1;
(d) preparation of age resister
Under nitrogen protection, by step (c) prepare azo-compound be added to 3.0mol/L sodium hydroxide water with
In the mixed solution of ethyl alcohol, stirs and reducing agent thiourea dioxide is added by several times, be cooled to room after reacting 2h at 60~65 DEG C
Temperature is added nitric acid pH and adjusts between 5~6, filters, dry in the shade, re-dry after recrystallization obtains functional modifier crude product, so
Afterwards by functional modifier crude product, hydrofluoric acid and concentrated nitric acid are added in reaction vessel, be heated to 65~75 DEG C of reactions 0.5~
After 1.0h, Off-white product is obtained by filtration, is filtered through cooling, dries in the shade, recrystallize and dry, obtain age resister;
The volume ratio of water and ethyl alcohol in the mixed solution of the water and ethyl alcohol is 1: 1;
The molar ratio of the thiourea dioxide and azo-compound is 1: 0.5;
The molar ratio 1: 1.2: 0.01 of the functional modifier crude product, hydrofluoric acid and concentrated nitric acid;
(e) preparation of modified capsule
Using deionized water as solvent, in a solvent age resister dispersion, whipping temp is room temperature, controls whipping process
Medium-rate is 800~1200r/min, and being dispersed with stirring the time is 30~45min, enables age resister molecule shape in aqueous solution
At suspension system, then add hydroxyethyl cellulose and dissolved, then carry out high-speed stirred dispersion, whipping temp be 45~
55 DEG C, stirring rate is 2000~3300r/min, and mixing time is 20~30min, then adds butane tetracarboxylic acid progress
It is chitosan crosslinked, then curing 30min is carried out under the conditions of 65~80 DEG C, thick modified capsule is obtained by filtration, then carry out very at 60 DEG C
After sky drying for 24 hours, the modification capsule containing age resister is obtained;Its sandwich layer is age resister, and cystoblast is hydroxy ethyl fiber material
Material, wherein the thickness of cystoblast and sandwich layer ratio is 1: 15.
The age resister additive amount is 3.5% relative to the mass fraction of water;
The hydroxyethyl cellulose additive amount is 2.0% relative to the mass fraction of water;
The weight average molecular weight of the hydroxyethyl cellulose is 20000~25000, and molar substitution is 1.8~1.9.
The butane tetracarboxylic acid is 0.3% relative to the mass fraction of chitosan.
The diameter of modified capsule is 2~5 μm, is conducive to capsule and passes through spinneret orifice, and guarantees capsule and fiber
Be firmly combined, the mechanical performance of fiber can't be influenced.
The capsule of modified capsule/core guarantees that microcapsules have certain mechanical strength and heat-resisting than being generally higher than equal to 1: 10
Property.
Elastic trampoline cloth is used for trampoline.
Comparative example 2
Only with the nylon elastic band that age resister is handled, cellulose fibre belt is not contained, i.e., does not use composite construction
Layer.Remaining step is the same as embodiment 2.
After trampoline spring 100,1000,10000 times, measuring center point recess situation, it can be found that the embodiment of the present application
The obvious resilient material deformation of 1-2 wants small, and durability is good.
Table 1
|
100 times (mm) |
1000 times (mm) |
10000 times (mm) |
Embodiment 1 |
0 |
0 |
2 |
Embodiment 2 |
0 |
0 |
3 |
Comparative example 1 |
0 |
2 |
57 |
Comparative example 2 |
0 |
4 |
78 |
It is measured with same people in central point and trampoline surrounding jumping height, discovery jumping height difference average value is implemented
Example 1-2 is smaller, illustrates that the application elastic webbing elasticity is balanced.
Table 2
|
Difference in height average value (%) |
Embodiment 1 |
1 |
Embodiment 2 |
2.5 |
Comparative example 1 |
6.7 |
Comparative example 2 |
9.9 |