CN106223565A - A kind of anti-scratching wearproof wall board production technology - Google Patents
A kind of anti-scratching wearproof wall board production technology Download PDFInfo
- Publication number
- CN106223565A CN106223565A CN201610601036.4A CN201610601036A CN106223565A CN 106223565 A CN106223565 A CN 106223565A CN 201610601036 A CN201610601036 A CN 201610601036A CN 106223565 A CN106223565 A CN 106223565A
- Authority
- CN
- China
- Prior art keywords
- resin
- wall board
- lagging
- board production
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-scratching wearproof wall board production technology, comprise the steps: dispensing mixing, extrusion base material, surface lagging, showering resin, UV curing.One anti-scratching wearproof wall board production technology of the present invention, by surface lagging, strengthen the wooden dry and aesthetic property of wood-plastic board, and unsaturated-resin finish paint is applied to uniformly on lagging facing veneer by the way of coater is with showering, after pass through UV curing, finish paint polyvinyl chloride resin and UV mixed with resin obtained is dried, the lagging facing veneer making wallboard generates a floor height hardness anti-scratching wearproof layer, intensity and the anti-scratching wearproof on wood-plastic board surface are all greatly improved, best bright finish and the flatness of plate surface are all effectively improved, solve current plate surface intensity relatively low, easily produce scratch or cut, affect attractive in appearance while also reduce the corrosion resistance of sheet material and the present situation in service life.
Description
[technical field]
The present invention relates to the technical field of wallboard, particularly to a kind of anti-scratching wearproof wall board production technology.
[background technology]
Wood-plastic board, also referred to as wood-plastic composite panel, be a kind of main by material based on timber (lignose, plant cellulose)
Material and thermoplastic macromolecule material (plastics) and processing aid etc., make through die apparatus heating extrusion molding after mix homogeneously again
The high-tech environmental protection new decorative material become, has timber and the performance of plastics and feature concurrently, is to substitute timber and plastics
Advanced composite material (ACM).Owing to wood-plastic board has waterproof and dampproof, stronger plasticity, high-environmental type and preferable processing type, more
Get over and welcome by user.
Current wood-plastic board carrying, install, use during, owing to plate surface intensity is relatively low, easily produce and scrape
Trace or cut, affect attractive in appearance while also reduce corrosion resistance and the service life of sheet material.In order to solve the problems referred to above, improve
The intensity on wood-plastic board surface and anti-scratching wearproof, keep best bright finish and the flatness of plate surface, it is necessary to propose one anti-
Scrape abrasion-resistant wallboard production technology.
[summary of the invention]
It is an object of the invention to overcome above-mentioned the deficiencies in the prior art, it is provided that a kind of anti-scratching wearproof wall board production technology,
It aims to solve the problem that in prior art, plate surface intensity is relatively low, easily produces scratch or cut, affect attractive in appearance while also reduce
The corrosion resistance of sheet material and the technical problem in service life.
For achieving the above object, the present invention proposes a kind of anti-scratching wearproof wall board production technology, comprises the steps:
Step one, dispensing mix: poured into by the Wood plastic wall board production raw material configured in mixer and mix；
Step 2, extrusion base material: being fed in extruder by the raw material after mix homogeneously, in extruder barrel, subregion is carried out
After adding heat fusing, extrude base material by cross-head and die orifice, after cooling and shaping, obtain wallboard blank；
Step 3, surface lagging: lagging facing veneer is affixed on after high-temperature hot press gluing the surface of wallboard blank；
Step 4, showering resin: use unsaturated-resin to make finish paint, by insatiable hunger by the way of coater is with showering
It is applied to uniformly on the lagging facing veneer of the wallboard blank after the lagging of surface with resin finish；
Step 5, UV curing: on the lagging facing veneer of wallboard blank after showering unsaturated-resin finish paint, pass through
UV curing equipment carries out ultraviolet drying, makes the lagging facing veneer of wallboard generate a floor height hardness anti-scratching wearproof layer.
As preferably, the mixing in described step one uses high-speed mixer mixing.
As preferably, in described step 2, extruder uses double screw extruder, is divided into 4 in described extruder barrel
Or 5 thermals treatment zone.
As preferably, in described step 4, unsaturated-resin is prepared from by the raw material of following parts by weight: polyvinyl chloride resin
35～55 parts, UV resin 45～65 parts.
As preferably, described unsaturated-resin is prepared from by the raw material of following parts by weight: polyvinyl chloride resin 50 parts, UV
Resin 50 parts.
As preferably, the described finish paint in step 4 is prepared and is also included defoamer 0.5～1 part, dispersant 0.4 in raw material
～0.9 part, levelling agent 0.1～0.5 part.
As preferably, described defoamer is AC defoamer, and dispersant uses stearmide and higher alcohol use, described
Levelling agent uses esters of acrylic acid levelling agent.
As preferably, the design temperature of described step 5 middle-ultraviolet lamp drying equipment is 50～60 DEG C.
As preferably, the design temperature of described UV curing equipment is 56 DEG C.
Beneficial effects of the present invention: compared with prior art, a kind of anti-scratching wearproof wall board production technology that the present invention provides,
Wood moulds raw material by the wallboard blank that obtains after extrusion, by surface lagging, strengthens the wooden dry and aesthetic property of wood-plastic board, and leads to
Cross coater to be applied to uniformly by unsaturated-resin finish paint on lagging facing veneer in the way of showering, rear dry by ultraviolet
Dry, finish paint polyvinyl chloride resin and UV mixed with resin obtained is dried, and makes the lagging facing veneer of wallboard generate a floor height hardness anti-scratch
Wearing layer, intensity and the anti-scratching wearproof on wood-plastic board surface be all greatly improved, and best bright finish and the flatness of plate surface all have
Effect improves, and solves current plate surface intensity relatively low, easily produces scratch or cut, affect attractive in appearance while also reduce plate
The corrosion resistance of material and the present situation in service life.
Inventive feature and advantage will be described in detail by embodiment.
[detailed description of the invention]
For making the object, technical solutions and advantages of the present invention of greater clarity, below by embodiment, the present invention is entered
Row further describes.However, it should be understood that specific embodiment described herein is only in order to explain the present invention, and need not
In limiting the scope of the present invention.Additionally, in the following description, eliminate the description to known features and technology, so that avoid need not
Idea of the invention is obscured in strategic point.
The embodiment of the present invention provides a kind of anti-scratching wearproof wall board production technology, comprises the steps:
Step one, dispensing mix: poured into by the Wood plastic wall board production raw material configured in mixer and mix.
Wherein, mixing uses high-speed mixer mixing.
Step 2, extrusion base material: being fed in extruder by the raw material after mix homogeneously, in extruder barrel, subregion is carried out
After adding heat fusing, extrude base material by cross-head and die orifice, after cooling and shaping, obtain wallboard blank.
Wherein, extruder uses double screw extruder, is divided into 4 or 5 thermals treatment zone in described extruder barrel.
In embodiments of the present invention, 4 thermals treatment zone it are divided in described extruder barrel.
Step 3, surface lagging: lagging facing veneer is affixed on after high-temperature hot press gluing the surface of wallboard blank.
Step 4, showering resin: use unsaturated-resin to make finish paint, by insatiable hunger by the way of coater is with showering
It is applied to uniformly on the lagging facing veneer of the wallboard blank after the lagging of surface with resin finish.
Wherein, unsaturated-resin is prepared from by the raw material of following parts by weight: polyvinyl chloride resin 35～55 parts, UV resin 45
～65 parts.
Further, defoamer 0.5～1 part, dispersant 0.4～0.9 part, levelling agent are also included during raw material prepared by finish paint
0.1～0.5 part, defoamer is AC defoamer, and dispersant uses stearmide and higher alcohol use, described levelling agent to use third
Olefin(e) acid esters levelling agent.
In embodiments of the present invention, unsaturated-resin is prepared from by the raw material of following parts by weight: polyvinyl chloride resin 50 parts,
UV resin 50 parts, AC defoamer 0.7 part, dispersant 0.6 part, levelling agent 0.3 part.
Step 5, UV curing: on the lagging facing veneer of wallboard blank after showering unsaturated-resin finish paint, pass through
UV curing equipment carries out ultraviolet drying, makes the lagging facing veneer of wallboard generate a floor height hardness anti-scratching wearproof layer.
Wherein, the design temperature of UV curing equipment is 50～60 DEG C.
In embodiments of the present invention, the design temperature of UV curing equipment is 56 DEG C.
A kind of anti-scratching wearproof wall board production technology that the present invention provides, wood moulds raw material by the wallboard base obtained after extrusion
Material, by surface lagging, strengthens the wooden dry and aesthetic property of wood-plastic board, and by unsaturation by the way of coater is with showering
Resin finish is applied on lagging facing veneer uniformly, afterwards by UV curing, polyvinyl chloride resin and UV mixed with resin is obtained
Finish paint is dried, and makes the lagging facing veneer of wallboard generate a floor height hardness anti-scratching wearproof layer, the intensity on wood-plastic board surface and anti-scratch
Wearability is all greatly improved, and best bright finish and the flatness of plate surface are all effectively improved, and solves current plate surface intensity
Relatively low, easily produce scratch or cut, affect attractive in appearance while also reduce the corrosion resistance of sheet material and the present situation in service life.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all essences in the present invention
Any amendment, equivalent or the improvement etc. made within god and principle, should be included within the scope of the present invention.
Claims (9)
1. an anti-scratching wearproof wall board production technology, it is characterised in that: comprise the steps:
Step one, dispensing mix: poured into by the Wood plastic wall board production raw material configured in mixer and mix；
Step 2, extrusion base material: being fed in extruder by the raw material after mix homogeneously, in extruder barrel, subregion heats
After Rong Rong, extrude base material by cross-head and die orifice, after cooling and shaping, obtain wallboard blank；
Step 3, surface lagging: lagging facing veneer is affixed on after high-temperature hot press gluing the surface of wallboard blank；
Step 4, showering resin: use unsaturated-resin to make finish paint, by unsaturation tree by the way of coater is with showering
Fat finish paint is applied on the lagging facing veneer of the wallboard blank after the lagging of surface uniformly；
Step 5, UV curing: on the lagging facing veneer of wallboard blank after showering unsaturated-resin finish paint, pass through ultraviolet
Line drying equipment carries out ultraviolet drying, makes the lagging facing veneer of wallboard generate a floor height hardness anti-scratching wearproof layer.
2. a kind of anti-scratching wearproof wall board production technology as claimed in claim 1, it is characterised in that: mixing in described step one
Close and use high-speed mixer mixing.
3. a kind of anti-scratching wearproof wall board production technology as claimed in claim 1, it is characterised in that: described step 2 is extruded
Machine uses double screw extruder, is divided into 4 or 5 thermals treatment zone in described extruder barrel.
4. a kind of anti-scratching wearproof wall board production technology as claimed in claim 1, it is characterised in that: insatiable hunger in described step 4
It is prepared from by the raw material of following parts by weight with resin: polyvinyl chloride resin 35～55 parts, UV resin 45～65 parts.
5. anti-scratching wearproof wall board production technology as claimed in claim 4 a kind of, it is characterised in that: described unsaturated-resin by
The raw material of following parts by weight is prepared from: polyvinyl chloride resin 50 parts, UV resin 50 parts.
6. a kind of anti-scratching wearproof wall board production technology as claimed in claim 1, it is characterised in that: the described face in step 4
Paint is prepared and is also included defoamer 0.5～1 part, dispersant 0.4～0.9 part, levelling agent 0.1～0.5 part in raw material.
7. a kind of anti-scratching wearproof wall board production technology as claimed in claim 6, it is characterised in that: described defoamer is that AC disappears
Infusion, dispersant uses stearmide and higher alcohol use, described levelling agent to use esters of acrylic acid levelling agent.
8. a kind of anti-scratching wearproof wall board production technology as claimed in claim 1, it is characterised in that: described step 5 medium ultraviolet
The design temperature of line drying equipment is 50～60 DEG C.
9. a kind of anti-scratching wearproof wall board production technology as claimed in claim 8, it is characterised in that: described UV curing sets
Standby design temperature is 56 DEG C.