CN106223002A - A kind of automotive trim is with high-grade sun-resistant wool fabric - Google Patents
A kind of automotive trim is with high-grade sun-resistant wool fabric Download PDFInfo
- Publication number
- CN106223002A CN106223002A CN201610600837.9A CN201610600837A CN106223002A CN 106223002 A CN106223002 A CN 106223002A CN 201610600837 A CN201610600837 A CN 201610600837A CN 106223002 A CN106223002 A CN 106223002A
- Authority
- CN
- China
- Prior art keywords
- fabric
- wool
- wool fiber
- resistant
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of automotive trim manufacture method with high-grade sun-resistant wool fabric, the present invention abundant microbe (acetobacter, bacillus acidophilus, bacillus amyloliquefaciens), the natural environmental-protective materials such as enzyme, the most optimized parameter of production technology by lot of experiment validation, a kind of superior automobile interior trim sun-resistant wool fabric.The present invention uses saccharifying enzyme can be modified wool fiber in Pilus Caprae seu Ovis processes, coordinate microorganism fermentation process below, wool fiber is made to there occurs great excellent modification, Pilus Caprae seu Ovis can be allowed to become sun-resistant, good light stability, it is easy to dyeing, has certain anti pilling effect, and the intensity of wool fiber is not made a difference, is especially suitable for autumn and winter use.
Description
Technical field
The present invention relates to a kind of automotive trim with high-grade sun-resistant wool fabric, belong to field of textiles.
Background technology
Auto industry is the maximum user of fabrics for industrial use.According to statistics, each automobile consumes textile material average out to
42m2(50 square yards), for interior trim (seat, Roof of vehicle, side panel, carpet, luggage compartment etc.), reinforcing material, back boxing, pad
End fabric, tire, belt, air bag, acoustic filter, gas filtering material and heat insulation equipment etc..Over 10 years, the need of textile for automobile
Ask growth the biggest.
It is broadly divided into natural fiber and synthetic fibers for producing the fiber of internal decoration textile of automobile.Natural fiber is mainly
Pilus Caprae seu Ovis, but owing to wool fabric price is higher, it is normally only used for luxury car.It can meet the performance such as fastness to light, wearability
Requirement, good hygroscopicity, there is more preferable hot wet migration and more preferable antistatic effect.But Pilus Caprae seu Ovis fastness to light is little, light is steady
Qualitative difference, life-time service color easily changes, so the use to Pilus Caprae seu Ovis is typically limited to certain color, or passes through blending
Improve its performance.Additionally, other natural fiber such as flaxen fiber, cotton fiber also has a certain degree of application on automotive trim.
Internal decoration textile of automobile, owing to using the particularity of environment, must consider each side when selecting fibrous raw material
Requirement.Interior fabrics in use it is frequently necessary to be chronically exposed under daylight, therefore requires the highest to its fastness to light.
The factor such as intensity, fastness to abrasion is it is also contemplated that as the textile frequently used.
It is desirable to provide a kind of automotive trim is with high-grade sun-resistant wool fabric, the abundant microbe of the present invention,
The natural environmental-protective materials such as enzyme, the most optimized parameter of production technology by lot of experiment validation, a kind of superior automobile interior trim
Use sun-resistant wool fabric.
Summary of the invention
The technical problem existed based on background technology, the present invention provides a kind of automotive trim to knit with high-grade sun-resistant Pilus Caprae seu Ovis
Thing, the abundant microbe of the present invention, the natural environmental-protective material such as enzyme, the optimum of production technology by lot of experiment validation
Change parameter, obtain a kind of sun-resistant wool fabric of superior automobile interior trim, be especially suitable for autumn and winter use.
Technical scheme is as follows:
A kind of automotive trim is with high-grade sun-resistant wool fabric, and its manufacture method is as follows:
(1) wool fiber water-washing pre-treatment:
Selected high-quality wool fiber, carries out three water-washing pre-treatment:
For the first time: 0.5-0.8% citric acid, water temperature is maintained at 45 DEG C;PH controls 7, and the process time is 30min;
For the second time: 0.8-1.2% saccharifying enzyme, water temperature is maintained at 35 DEG C;PH controls 7, and the process time is 10min;
For the third time: pure water rinse, temperature controls at 55 DEG C, oven drying at low temperature;
Various dirt removed by wool fiber after water-washing pre-treatment, and chemical property there occurs change;
(2) fermentable processes:
By acetobacter, bacillus acidophilus, bacillus amyloliquefaciens according to bacterial strain quantity than for 1:0.3-0.5:0.5-0.7
It is configured to 1.1*105Bacteria suspension, described bacteria suspension possibly together with, according to mass percent, the trehalose of 0.3%, the water of 0.2%
Threose;
Then being uniformly sprayed on by bacteria suspension on the wool fiber that step (1) obtains, the weight of sprinkling is wool fiber
0.05 times of weight, is subsequently placed at 30 DEG C standing 5-8 hour, and period keeps constant temperature and ventilation;
(3) inactivation treatment:
Wool fiber after being processed by fermentable rinses 1-1.5 hour with the hot water of 80 DEG C, then dries;
(4) it is woven into automotive fabric:
By the wool fiber after above-mentioned modification, it is woven into wool fabric;
(5) low temperature dyeing processes:
Dye liquor prescription and condition be: pula red 4B dyestuff 2g/L, pH4, temperature 60 C, time 100min, bath raio 1: 30;;
After dyeing, fabric is 30~100 DEG C of washings process 5~20min, bath raioes 1: 30.
Saccharifying enzyme is also known as glucoamylase, and saccharifying enzyme is a kind of customary title, and formal name used at school is α-Isosorbide-5-Nitrae-G/W
Solve enzyme (α-1,4-Glucan glucohydrolace).It is applied to ethanol, starch sugar, monosodium glutamate, antibiotics, citric acid, medicated beer more
Deng industry and Chinese liquor, yellow wine.Saccharifying enzyme is through submerged fermentation refinement by aspergillosis excellent species (Aspergilusniger)
Become.The present inventor finds first, uses saccharifying enzyme can be modified wool fiber, coordinate below micro-in Pilus Caprae seu Ovis processes
Bio-fermentation process so that wool fiber there occurs great excellent modification, can allow Pilus Caprae seu Ovis become sun-resistant, light stability
Good, it is easy to dyeing, there is certain anti pilling effect, and the intensity of wool fiber is not made a difference.
The invention have benefit that:
The abundant microbe of the present invention, the natural environmental-protective material such as enzyme, the production technology by lot of experiment validation
The most optimized parameter, obtain a kind of sun-resistant wool fabric of superior automobile interior trim.
The present invention uses saccharifying enzyme can be modified wool fiber in Pilus Caprae seu Ovis processes, and coordinates microorganism below to send out
Ferment technique so that wool fiber there occurs great excellent modification, can allow Pilus Caprae seu Ovis become sun-resistant, good light stability, it is easy to
Dyeing, has certain anti pilling effect, and does not makes a difference the intensity of wool fiber, is especially suitable for autumn and winter use.
Detailed description of the invention
Embodiment 1:
A kind of automotive trim is with high-grade sun-resistant wool fabric, and its manufacture method is as follows:
(1) wool fiber water-washing pre-treatment:
Selected high-quality wool fiber, carries out three water-washing pre-treatment:
For the first time: 0.5% citric acid, water temperature is maintained at 45 DEG C;PH controls 7, and the process time is 30min;
For the second time: 1.2% saccharifying enzyme, water temperature is maintained at 35 DEG C;PH controls 7, and the process time is 10min;
For the third time: pure water rinse, temperature controls at 55 DEG C, oven drying at low temperature;
Various dirt removed by wool fiber after water-washing pre-treatment, and chemical property there occurs change;
(2) fermentable processes:
By acetobacter, bacillus acidophilus, bacillus amyloliquefaciens is configured to than for 1:0.3:0.7 according to bacterial strain quantity
1.1*105Bacteria suspension, described bacteria suspension possibly together with, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%;
Then being uniformly sprayed on by bacteria suspension on the wool fiber that step (1) obtains, the weight of sprinkling is wool fiber
0.05 times of weight, is subsequently placed at 30 DEG C standing 5 hours, and period keeps constant temperature and ventilation;
(3) inactivation treatment:
Wool fiber after being processed by fermentable rinses 1.5 hours with the hot water of 80 DEG C, then dries;
(4) it is woven into automotive fabric:
By the wool fiber after above-mentioned modification, it is woven into wool fabric;
(5) low temperature dyeing processes:
Dye liquor prescription and condition be: pula red 4B dyestuff 2g/L, pH4, temperature 60 C, time 100min, bath raio 1: 30;
After dyeing, fabric processes 20min, bath raioes 1: 30 30 DEG C of washings.
Embodiment 2:
A kind of automotive trim is with high-grade sun-resistant wool fabric, and its manufacture method is as follows:
(1) wool fiber water-washing pre-treatment:
Selected high-quality wool fiber, carries out three water-washing pre-treatment:
For the first time: 0.8% citric acid, water temperature is maintained at 45 DEG C;PH controls 7, and the process time is 30min;
For the second time: 0.8% saccharifying enzyme, water temperature is maintained at 35 DEG C;PH controls 7, and the process time is 10min;
For the third time: pure water rinse, temperature controls at 55 DEG C, oven drying at low temperature;
Various dirt removed by wool fiber after water-washing pre-treatment, and chemical property there occurs change;
(2) fermentable processes:
By acetobacter, bacillus acidophilus, bacillus amyloliquefaciens is configured to than for 1:0.5:0.5 according to bacterial strain quantity
1.1*105Bacteria suspension, described bacteria suspension possibly together with, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%;
Then being uniformly sprayed on by bacteria suspension on the wool fiber that step (1) obtains, the weight of sprinkling is wool fiber
0.05 times of weight, is subsequently placed at 30 DEG C standing 8 hours, and period keeps constant temperature and ventilation;
(3) inactivation treatment:
Wool fiber after being processed by fermentable rinses 1 hour with the hot water of 80 DEG C, then dries;
(4) it is woven into automotive fabric:
By the wool fiber after above-mentioned modification, it is woven into wool fabric;
(5) low temperature dyeing processes:
Dye liquor prescription and condition be: pula red 4B dyestuff 2g/L, pH4, temperature 60 C, time 100min, bath raio 1: 30;
After dyeing, fabric processes 5min, bath raioes 1: 30 100 DEG C of washings.
Embodiment 3:
A kind of automotive trim is with high-grade sun-resistant wool fabric, and its manufacture method is as follows:
(1) wool fiber water-washing pre-treatment:
Selected high-quality wool fiber, carries out three water-washing pre-treatment:
For the first time: 0.6% citric acid, water temperature is maintained at 45 DEG C;PH controls 7, and the process time is 30min;
For the second time: 1.1% saccharifying enzyme, water temperature is maintained at 35 DEG C;PH controls 7, and the process time is 10min;
For the third time: pure water rinse, temperature controls at 55 DEG C, oven drying at low temperature;
Various dirt removed by wool fiber after water-washing pre-treatment, and chemical property there occurs change;
(2) fermentable processes:
By acetobacter, bacillus acidophilus, bacillus amyloliquefaciens is configured to than for 1:0.4:0.6 according to bacterial strain quantity
1.1*105Bacteria suspension, described bacteria suspension possibly together with, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%;
Then being uniformly sprayed on by bacteria suspension on the wool fiber that step (1) obtains, the weight of sprinkling is wool fiber
0.05 times of weight, is subsequently placed at 30 DEG C standing 6 hours, and period keeps constant temperature and ventilation;
(3) inactivation treatment:
Wool fiber after being processed by fermentable rinses 1.4 hours with the hot water of 80 DEG C, then dries;
(4) it is woven into automotive fabric:
By the wool fiber after above-mentioned modification, it is woven into wool fabric;
(5) low temperature dyeing processes:
Dye liquor prescription and condition be: pula red 4B dyestuff 2g/L, pH4, temperature 60 C, time 100min, bath raio 1: 30;
After dyeing, fabric processes 19min, bath raioes 1: 30 40 DEG C of washings.
Embodiment 4:
A kind of automotive trim is with high-grade sun-resistant wool fabric, and its manufacture method is as follows:
(1) wool fiber water-washing pre-treatment:
Selected high-quality wool fiber, carries out three water-washing pre-treatment:
For the first time: 0.7% citric acid, water temperature is maintained at 45 DEG C;PH controls 7, and the process time is 30min;
For the second time: 0.9% saccharifying enzyme, water temperature is maintained at 35 DEG C;PH controls 7, and the process time is 10min;
For the third time: pure water rinse, temperature controls at 55 DEG C, oven drying at low temperature;
Various dirt removed by wool fiber after water-washing pre-treatment, and chemical property there occurs change;
(2) fermentable processes:
By acetobacter, bacillus acidophilus, bacillus amyloliquefaciens is configured to than for 1:0.5:0.7 according to bacterial strain quantity
1.1*105Bacteria suspension, described bacteria suspension possibly together with, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%;
Then being uniformly sprayed on by bacteria suspension on the wool fiber that step (1) obtains, the weight of sprinkling is wool fiber
0.05 times of weight, is subsequently placed at 30 DEG C standing 7 hours, and period keeps constant temperature and ventilation;
(3) inactivation treatment:
Wool fiber after being processed by fermentable rinses 1.1 hours with the hot water of 80 DEG C, then dries;
(4) it is woven into automotive fabric:
By the wool fiber after above-mentioned modification, it is woven into wool fabric;
(5) low temperature dyeing processes:
Dye liquor prescription and condition be: pula red 4B dyestuff 2g/L, pH4, temperature 60 C, time 100min, bath raio 1: 30;
After dyeing, fabric processes 6min, bath raioes 1: 30 90 DEG C of washings.
Embodiment 5 contrast test:
The each parameter of technique of the present invention is the most extremely important, each step, and parameter serves significant synergy.Contrast test
Be only demonstration, the present embodiment carries out pretreatment without saccharifying enzyme, microorganism also change.
A kind of automotive trim is with high-grade sun-resistant wool fabric, and its manufacture method is as follows:
(1) wool fiber water-washing pre-treatment:
Selected high-quality wool fiber, carries out 2 water-washing pre-treatment:
For the first time: 0.5% citric acid, water temperature is maintained at 45 DEG C;PH controls 7, and the process time is 30min;
For the second time: pure water rinse, temperature controls at 55 DEG C, oven drying at low temperature;
Various dirt removed by wool fiber after water-washing pre-treatment, and chemical property there occurs change;
(2) fermentable processes:
By acetobacter, bacillus acidophilus is configured to 1.1*10 according to bacterial strain quantity than for 1:0.85Bacteria suspension, described
Bacteria suspension possibly together with, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%;
Then being uniformly sprayed on by bacteria suspension on the wool fiber that step (1) obtains, the weight of sprinkling is wool fiber
0.05 times of weight, is subsequently placed at 30 DEG C standing 5 hours, and period keeps constant temperature and ventilation;
(3) inactivation treatment:
Wool fiber after being processed by fermentable rinses 1.3 hours with the hot water of 80 DEG C, then dries;
(4) it is woven into automotive fabric:
By the wool fiber after above-mentioned modification, it is woven into wool fabric;
(5) low temperature dyeing processes:
Dye liquor prescription and condition be: pula red 4B dyestuff 2g/L, pH4, temperature 60 C, time 100min, bath raio 1: 30;
After dyeing, fabric processes 18min, bath raioes 1: 30 50 DEG C of washings.
Embodiment 6: index is tested and assessed
The index of the wool fabric that embodiment 1-5 obtains is tested, as follows:
Pilus Caprae seu Ovis weight-loss ratio measures:
According to fabric regain, calculate the treated front constant dry mass w0 of sample;Fabric after precise process
Constant dry mass w1, is calculated as follows the weight-loss ratio before and after fabric ferment treatment:
Weight-loss ratio=(w0-w1)/w0 × 100%
The pilling resistance detection of tricot de laine uses GB/T 4802.3 2008 balling-up case method.
Evaluate the persistency of antibacterial fabric performance, mainly antibiotic fabric is carried out the wash durability test of anti-microbial property.Anti-
Bacterium fabric washing tests simplification wash conditions and the program of appendix C in reference " FZ/T 73,023 2006 antibiosis knitting product ", right
Fabric washing to be measured 50 times.
Antibiotic fabric performance test methods is with reference to the succusion of Appendix D in " FZ/T 73,023 2006 antibiosis knitting product ".
Succusion be imitate human body wear condition, make antibacterial under oscillating condition with anti-microbial agent in clothing, by calculate antibacterial
Slip, determines a kind of method of anti-microbial property size.Succusion testing procedure is: put into sample to be tested containing finite concentration
Antibacterial (staphylococcus aureus strain) culture fluid in, then sample is placed on reciprocating agitator, in (24 ± 1) DEG C
Under, with the velocity fluctuation 18h of 150r/min, after making sample fabric and bacterium solution be fully contacted by vibration, at (37 ± 1) DEG C biochemistry
Incubator is cultivated 24h, measures the clump count of antibacterial before and after vibrating, carry out quantitative assessment antibacterial effect by method for counting colonies.
The calculating of succusion test anti-microbial property:
Bacteriostasis rate (%)=(A-B)/A × 100%
In formula (1): A is clump count after standard blank sample vibration 18h;B is clump count after sample to be tested vibration 18h.
Table 1 is embodiment 1-5 to be produced the wool fabric obtained detect the result obtained.
Table 1 performance measurement
These detection data are just for above-mentioned detection sample.
Because colour fasteness to sunlight still lacks unified standard, therefore and the good polyester fiber of colour fasteness to sunlight generally acknowledged
Material compares under the conditions of same high Exposure to Sunlight, finds that the wool fabric of embodiment 1-4 has all reached Polyester Fibers
Sun-resistant level, its good light stability, life-time service color does not changes, and is significantly better than common wool fabric, it is adaptable to
Automotive trim material.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto,
Any those familiar with the art in the technical scope that the invention discloses, according to technical scheme and
Inventive concept equivalent or change in addition, all should contain within protection scope of the present invention.
Claims (5)
1. the automotive trim manufacture method of high-grade sun-resistant wool fabric, it is characterised in that its step is as follows:
(1) wool fiber water-washing pre-treatment:
Selected high-quality wool fiber, carries out three water-washing pre-treatment:
For the first time: 0.5-0.8% citric acid, water temperature is maintained at 45 DEG C;PH controls 7, and the process time is 30min;
For the second time: Glucoamylase Solution, water temperature is maintained at 35 DEG C;PH controls 7, and the process time is 10min;
For the third time: pure water rinse, temperature controls at 55 DEG C, oven drying at low temperature;
Various dirt removed by wool fiber after water-washing pre-treatment, and chemical property there occurs change;
(2) fermentable processes:
By acetobacter, bacillus acidophilus, bacillus amyloliquefaciens is configured to 1.1*105Bacteria suspension, described bacteria suspension also contains
Have, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%;
Then being uniformly sprayed on by bacteria suspension on the wool fiber that step (1) obtains, the weight of sprinkling is the weight of wool fiber
0.05 times, be subsequently placed at 30 DEG C standing 5-8 hour, period keeps constant temperature and ventilation;
(3) inactivation treatment:
Wool fiber after being processed by fermentable rinses 1-1.5 hour with the hot water of 80 DEG C, then dries;
(4) it is woven into automotive fabric:
By the wool fiber after above-mentioned modification, it is woven into wool fabric;
(5) low temperature dyeing processes:
Temperature 60 C low temperature is used to dye.
2. the manufacture method of high-grade sun-resistant wool fabric of the automotive trim described in claim 1, it is characterised in that:
Described step (5) low temperature dyeing is processed as:
Dye liquor prescription and condition be: pula red 4B dyestuff 2g/L, pH4, temperature 60 C, time 100min, bath raio 1: 30;
After dyeing, fabric is 30~100 DEG C of washings process 5~20min, bath raioes 1: 30.
3. the manufacture method of high-grade sun-resistant wool fabric of the automotive trim described in claim 1 or 2, it is characterised in that:
Described step (2) is:
By acetobacter, bacillus acidophilus, bacillus amyloliquefaciens is prepared than for 1:0.3-0.5:0.5-0.7 according to bacterial strain quantity
Become 1.1*105Bacteria suspension, described bacteria suspension possibly together with, according to mass percent, the trehalose of 0.3%, the Herba Stachydis Japonicae of 0.2%
Sugar.
4. the manufacture method of high-grade sun-resistant wool fabric of the automotive trim described in claim 1 or 2, it is characterised in that:
Described step (1) second time washing is: mass percent is for use 0.8-1.2% saccharifying enzyme, water temperature to be maintained at 35 DEG C;PH is controlled
System is 7, and the process time is 10min.
5. the automotive trim described in any one of claim 1-4 is made by the manufacture method of high-grade sun-resistant wool fabric
Wool fabric.