CN106221028A - A kind of EPDM rubber waterproof rolling material - Google Patents
A kind of EPDM rubber waterproof rolling material Download PDFInfo
- Publication number
- CN106221028A CN106221028A CN201610658117.8A CN201610658117A CN106221028A CN 106221028 A CN106221028 A CN 106221028A CN 201610658117 A CN201610658117 A CN 201610658117A CN 106221028 A CN106221028 A CN 106221028A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- agent
- dop
- fiber powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of EPDM rubber waterproof rolling material, it relates to field of rubber technology;It is prepared from by the raw material of following weight portion: ethylene propylene diene rubber 20 30 parts, DOP thermal weld agent 25 parts, rubber accelerator DM1 2 parts, reinforcing agent 5 10 parts, carbon fiber powder 5 10 parts, 10 15 parts of age resistor, white carbon black 10 20 parts, 5 10 parts of sulfur;By banburying and mixed glue in ethylene propylene diene rubber, DOP thermal weld agent, rubber accelerator DM, reinforcing agent part, carbon fiber powder, age resistor, white carbon black addition banbury, being subsequently adding sulfur and vulcanize, its curing temperature is 100 150 DEG C;The present invention is easy to improve intensity, and Production Time is short, speed fast, easy to use, increases the service life.
Description
Technical field
The present invention relates to field of rubber technology, be specifically related to a kind of EPDM rubber waterproof rolling material.
Background technology
Ethylene propylene diene rubber is ethylene, propylene and the terpolymer of non-conjugated diene hydrocarbon, and 1963 start commercialization
Produce.Annual global consumption figure is 800,000 tons.The topmost characteristic of EPDM is exactly its superior resistance to oxidation, ozone-resistant and resists
The ability corroded.Owing to ethylene propylene diene rubber belongs to polyene (PA66) hydrocarbon family, it has fabulous vulcanization characteristics.All rubbers
In the middle of glue, EPDM has minimum proportion.It can absorb substantial amounts of filler and oil and influencing characterisitic is little.Therefore can be fabricated to
This cheap rubber compound.
Its formulation cost of existing EPDM rubber waterproof rolling material is high, and its intensity of coiled material is low, operation complexity.
Summary of the invention
Present invention aims to defect and the deficiency of prior art, it is provided that a kind of waterproof volume of ethylene propylene diene rubber
Material.
In order to solve the problem existing for background technology, a kind of EPDM rubber waterproof rolling material of the present invention, by following
The raw material of weight portion is prepared from: ethylene propylene diene rubber 20-30 part, DOP thermal weld agent 2-5 part, rubber accelerator DM1-2 part,
Reinforcing agent 5-10 part, carbon fiber powder 5-10 part, age resistor 10-15 part, white carbon black 10-20 part, sulfur 5-10 part;By EPDM
Rubber, DOP thermal weld agent, rubber accelerator DM, reinforcing agent part, carbon fiber powder, age resistor, white carbon black add banburying in banbury
With mixed glue, being subsequently adding sulfur and vulcanize, its curing temperature is 100-150 DEG C.
Present invention have the beneficial effect that and be easy to improve intensity, and Production Time is short, speed fast, easy to use, extend and use the longevity
Life.
Detailed description of the invention
This detailed description of the invention adopts the following technical scheme that and is prepared from by the raw material of following weight portion: ethylene-propylene-diene monomer
Glue 20-30 part, DOP thermal weld agent 2-5 part, rubber accelerator DM1-2 part, reinforcing agent 5-10 part, carbon fiber powder 5-10 part, anti-
Old agent 10-15 part, white carbon black 10-20 part, sulfur 5-10 part;By ethylene propylene diene rubber, DOP thermal weld agent, rubber accelerator DM, benefit
Strong agent part, carbon fiber powder, age resistor, white carbon black add banburying and mixed glue in banbury, are subsequently adding sulfur and vulcanize, its sulfur
Change temperature and be 100-150 DEG C.
The above, only in order to technical scheme to be described and unrestricted, those of ordinary skill in the art are to this
Other amendment or equivalent that bright technical scheme is made, without departing from the spirit and scope of technical solution of the present invention,
All should contain in the middle of scope of the presently claimed invention.
Claims (1)
1. an EPDM rubber waterproof rolling material, it is characterised in that: it is prepared from by the raw material of following weight portion: EPDM
Rubber 20-30 part, DOP thermal weld agent 2-5 part, rubber accelerator DM1-2 part, reinforcing agent 5-10 part, carbon fiber powder 5-10 part,
Age resistor 10-15 part, white carbon black 10-20 part, sulfur 5-10 part;By ethylene propylene diene rubber, DOP thermal weld agent, rubber accelerator DM,
Reinforcing agent part, carbon fiber powder, age resistor, white carbon black add banburying and mixed glue in banbury, are subsequently adding sulfur and vulcanize, its
Curing temperature is 100-150 DEG C.