CN106220073B - The preparation method of building partition lightweight lath - Google Patents
The preparation method of building partition lightweight lath Download PDFInfo
- Publication number
- CN106220073B CN106220073B CN201610819036.1A CN201610819036A CN106220073B CN 106220073 B CN106220073 B CN 106220073B CN 201610819036 A CN201610819036 A CN 201610819036A CN 106220073 B CN106220073 B CN 106220073B
- Authority
- CN
- China
- Prior art keywords
- lath
- preparation
- centipede space
- centipede
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention provides a kind of preparation method of building partition lightweight lath, this method includes the following steps: that flyash 62-66Kg, cement 310-330Kg, polystyrene foaming particle 2.5-3.15Kg, pottery sand 304.7-439.6Kg are put into feeding device by (one), and the stirring of 150-170Kg water and suitable physical expansion agent is added, it stirs 10-15 minutes;(2) extrusion forming after installation calcium silicate board, obtains semi-finished product;(3) by the offline stacking of above-mentioned light lath, several light laths form centipede space, between adjacent two centipede space there are ventilation cell away from;(4) make above-mentioned centipede space gravity-flow ventilation, obtain lightweight lath finished product.The preparation method does not destroy resource, does not cause secondary pollution, is at low cost, and the building partition produced by the preparation method is light-weight with lightweight lath, intensity is high, heat-insulated, noise reduction, fire-retardant, can also largely utilize flyash and useless benzene plate particle.
Description
Technical field
The present invention relates to a kind of preparation methods of building materials, refer in particular to a kind of preparation method of building partition lightweight lath.
Background technique
With the development of science and technology, people are higher and higher to the performance requirement of building, do not require nothing more than that building materials are light-weight, intensity
It is high, heat-insulated, noise reduction, fire-retardant, it also requires that building material cost is low, does not destroy resource, does not cause secondary pollution;Traditional building partition material
Material is mainly built by solid brick, is taken soil with needing to dig when produce solid brick, is destroyed and plough, not only the feature of environmental protection is poor, heavier-weight,
Noise reduction heat-proof quality is poor, and technique is cumbersome in production process, high production cost.
Summary of the invention
The purpose of the present invention is to provide a kind of building partition preparation method of lightweight lath, which is not destroyed
Resource does not cause secondary pollution, is at low cost, and the building partition produced by the preparation method it is light-weight with lightweight lath,
Intensity is high, heat-insulated, noise reduction, fire-retardant, can also largely utilize flyash and useless benzene plate particle.
In order to achieve the above object, the present invention provides a kind of preparation method of building partition lightweight lath, this method packet
Include following step:
(1) by flyash 62-66Kg, cement 310-330Kg, polystyrene foaming particle 2.5-3.15Kg, pottery sand
304.7-439.6Kg is put into feeding device, and the stirring of 150-170Kg water and suitable physical expansion agent is added, and stirs 10-
15 minutes;
(2) extrusion forming after installation calcium silicate board, obtains the light lath of semi-finished product;
(3) by the offline stacking of above-mentioned light lath, several light laths are sequentially placed to form centipede space from the bottom to top, left
Between right adjacent two centipede space and neighbouring two centipede space there are ventilation cell away from;
(4) make above-mentioned centipede space gravity-flow ventilation, obtain lightweight lath finished product.
The preparation method of building partition of the present invention lightweight lath, wherein in the step (1), using blender into
Row is sufficiently stirred.
The preparation method of building partition of the present invention lightweight lath, wherein in the step (3), ten lightweights
Batten forms a centipede space.
The preparation method of building partition of the present invention lightweight lath, wherein in the step (4), the centipede space is natural
Ventilation 15-20 days.
The preparation method of building partition of the present invention lightweight lath, wherein described neighbouring in the step (3)
Support rod is set between two centipede spaces, formed under the action of the support rod ventilation cell away from.
The preparation method of building partition of the present invention lightweight lath, wherein described neighbouring in the step (3)
Wooden tray is set between two centipede spaces, formed under the action of the Wooden tray ventilation cell away from.
After adopting the above scheme, building partition of the present invention is had an advantage that with the preparation method of lightweight lath due to this
Flyash 62-66Kg, pottery sand 304.7- are used in the preparation method preparation process of invention building partition lightweight lath
439.6Kg, flyash and this edition particle utilization rate of giving up are up to 70% or more, 30,000 tons of waste residue utilization amount of year or more, in preparation process not
Destroyed land resource does not cause secondary pollution, and product makes product have weight by extrusion forming, natural air maintenance
Gently, intensity is high, heat-insulated, noise reduction, the performances such as nonflammable.Inspection for several times through Jilin Province's construction material detection institute, result are remote
It is much better than the indices of national standard, and the lightweight lath produced through the preparation method mitigates building in practical applications
Wall weight 25% saves steel 10%, saves cement 6%, save recruitment 20%, increase usable floor area 5-8%.
Detailed description of the invention
Fig. 1 is the process flow chart of the preparation method of building partition lightweight lath of the present invention.
Specific embodiment
The present invention will be further explained below with reference to the attached drawings and specific examples, so that those skilled in the art can be with
It better understands the present invention and can be practiced, but illustrated embodiment is not as a limitation of the invention.
Embodiment one: a kind of preparation method of building partition lightweight lath, as shown in Figure 1, this method includes following steps
It is rapid:
(1) it by flyash 62Kg, cement 320Kg, polystyrene foaming particle 2.94Kg, pottery sand 304.7Kg, is put into
Expect in device, and the stirring of 160Kg water and suitable physical expansion agent is added, stirs 10-15 minutes;
(2) extrusion forming after installation calcium silicate board, obtains the light lath of semi-finished product, installs anti-flammability after calcium silicate board
It can be more preferable;
(3) by the offline stacking of above-mentioned light lath, ten light laths are sequentially placed from the bottom to top to form a pile
Body, there are ventilation cells away from support rod is arranged between two neighbouring centipede spaces, is propping up between adjacent two centipede spaces in left and right and front and back
Make under the action of strut between two neighbouring centipede spaces there are ventilation cell away from;
(4) make above-mentioned centipede space gravity-flow ventilation 15-20 days, temperature is lower, and ventilation time is more long, obtains lightweight lath finished product;
(5) above-mentioned lightweight lath finished product is examined, qualified lightweight lath is examined to wait dispatching from the factory.
Embodiment two: a kind of preparation method of building partition lightweight lath, as shown in Figure 1, this method includes following steps
It is rapid:
(1) it by flyash 64Kg, cement 310Kg, polystyrene foaming particle 3.15Kg, pottery sand 439.6Kg, is put into
Expect in device, and the stirring of 150Kg water and suitable physical expansion agent is added, stirs 10-15 minutes;
(2) extrusion forming after installation calcium silicate board, obtains the light lath of semi-finished product
(3) by the offline stacking of above-mentioned light lath, ten light laths are sequentially placed from the bottom to top to form a pile
Body, between adjacent two centipede spaces in left and right and front and back there are ventilation cell away from, wood pallets are set between two neighbouring centipede spaces,
Make under the action of wood pallets between two neighbouring centipede spaces formed ventilation cell away from;
(4) make above-mentioned centipede space gravity-flow ventilation 15-20 days, temperature is lower, and ventilation time is more long, obtains lightweight lath finished product;
(5) above-mentioned lightweight lath finished product is examined, qualified lightweight lath is examined to wait dispatching from the factory.
Embodiment three: a kind of preparation method of building partition lightweight lath, as shown in Figure 1, this method includes following steps
It is rapid:
(1) by flyash 66Kg, cement 330Kg, polystyrene foaming particle 2.45Kg, pottery sand 380Kg, it is put into feeding
In device, and the stirring of 170Kg water and suitable physical expansion agent is added, stirs 10-15 minutes;
(2) extrusion forming after installation calcium silicate board, obtains the light lath of semi-finished product;
(3) by the offline stacking of above-mentioned light lath, ten light laths are sequentially placed from the bottom to top to form a pile
Body, between adjacent two centipede spaces in left and right and front and back there are ventilation cell away from, wood pallets are set between two neighbouring centipede spaces,
Make under the action of wood pallets between two neighbouring centipede spaces there are ventilation cell away from;
(4) make above-mentioned centipede space gravity-flow ventilation 15-20 days, temperature is lower, and ventilation time is more long, obtains lightweight lath finished product;
(5) above-mentioned lightweight lath finished product is examined, qualified lightweight lath is examined to wait dispatching from the factory.
Embodiment described above is only to absolutely prove preferred embodiment that is of the invention and being lifted, protection model of the invention
It encloses without being limited thereto.Those skilled in the art's made equivalent substitute or transformation on the basis of the present invention, in the present invention
Protection scope within.Protection scope of the present invention is subject to claims.
Claims (1)
1. a kind of building partition preparation method of lightweight lath, it is characterised in that: this method includes the following steps:
(1) by flyash 62-66Kg, cement 310-330Kg, polystyrene foaming particle 2.5-3.15Kg, pottery sand 304.7-
439.6Kg is put into feeding device, and the stirring of 150-170Kg water and suitable physical expansion agent is added, and is stirred 10-15 minutes;
(2) extrusion forming after installation calcium silicate board, obtains the light lath of semi-finished product;
(3) by the offline stacking of above-mentioned light lath, several light laths are sequentially placed to form centipede space from the bottom to top, and adjacent two
Between centipede space there are ventilation cell away from;
(4) make above-mentioned centipede space gravity-flow ventilation, obtain lightweight lath finished product;
In the step (1), it is sufficiently stirred using blender;
In the step (3), ten light laths form a centipede space, between neighbouring two centipede space
Be arranged support rod, formed under the action of the support rod ventilation cell away from or neighbouring two centipede space between be arranged
Wooden tray, formed under the action of the Wooden tray ventilation cell away from;
In the step (4), described centipede space gravity-flow ventilation 15-20 days.