CN106196747A - A kind of heat absorption plate core structure condenser and processing technology thereof - Google Patents
A kind of heat absorption plate core structure condenser and processing technology thereof Download PDFInfo
- Publication number
- CN106196747A CN106196747A CN201610501151.4A CN201610501151A CN106196747A CN 106196747 A CN106196747 A CN 106196747A CN 201610501151 A CN201610501151 A CN 201610501151A CN 106196747 A CN106196747 A CN 106196747A
- Authority
- CN
- China
- Prior art keywords
- flat tube
- header
- tube block
- coating
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of pipework condensation device, including being provided with the flat tube block of fin, wherein: flat tube block be arranged in parallel and between fin;The outside of flat tube block is provided with plate;Flat tube block two ends connect left header and right header respectively;Left header and described right header are respectively arranged at the two ends with header and block up;Right header connects has catcher, one end to be provided with mounting bracket;Right header is provided with inlet suction port and goes out liquid joint;Thermal diffusivity coating is scribbled inside flat tube block.Processing technology of the present invention is simple, can be effectively improved condenser condensation rate.
Description
Technical field
The present invention relates to a kind of condenser, be specifically related to a kind of heat absorption plate core structure condenser and processing technology thereof.
Technical background
The operation principle of condenser is to be allowed to become liquid by being taken away by the heat of gas or steam.In prior art,
People make coolant and water carry out heat exchange by the way of being set with water pipe on the header of left and right, thus realize the mesh of condensation
's.This mode, current only flow in water pipe, and to change area little with coolant heat to be condensed, and condensation efficiency is low.For solving refrigeration
Problem at the bottom of effect, such as the Chinese invention patent of prior art Authorization Notice No.: CN1287122C, this invention relate to a kind of for
The condenser device of vehicle air conditioner, including a pipe/fin component, is positioned at its both sides the collection connected with tube end
Flow tube, and a catcher being parallel to one of them header, this catcher is by opening and adjacent header fluid
Connecting, and include that a dry/filtration core cylinder is put into from side by a closure elements respectively, described core cylinder is fixed on receipts
In storage and there is a lip ring being arranged between two openings.
Summary of the invention
The present invention solves that above-mentioned technical problem provides a kind of a kind of heat absorption plate core structure condenser improving condensation efficiency and making thereof
Technique.
The present invention solves that the scheme that above-mentioned technical problem is taked is: a kind of pipework condensation device, including being provided with the flat of fin
Plumber block, wherein:
Flat tube block be arranged in parallel and between fin;The outside of flat tube block is provided with plate;Flat tube block two ends connect left header respectively
With right header;Left header and described right header are respectively arranged at the two ends with header and block up;Right header connects catcher,
One end is provided with mounting bracket;Right header is provided with inlet suction port and goes out liquid joint;Thermal diffusivity coating is scribbled inside flat tube block.
Coating material includes following component and composition by weight thereof: organic siliconresin 55-65 part, modified waterproof silicones 10-
20 parts, acetone 50-60 part, firming agent 1-2 part, zinc oxide 3-6 part, silane coupler KH792022-4 part, filler 3-6 part.
Wherein, filler includes following component and components by weight percent: nano carbon microsphere 1-2 part, Afluon (Asta) 1-2 part, carbolic acid 1-2
Part.
As preferably, coating material includes following component and composition by weight thereof: organic siliconresin 60 parts, modified waterproof silicon tree
16 parts of fat, 55 parts of acetone, 1 part of firming agent, nano carbon microsphere 2 parts, zinc oxide 4 parts, Afluon (Asta) 1 part, carbolic acid 2 parts, silane coupled
Agent KH792022 part, coating has high chemical stability, affected by environment little;In the middle of using, cooling anomaly substantially and
Cooling rate is fast, because its mechanism of action is still not clear, still to be tested.
Or, organic siliconresin 55 parts, modified waterproof silicones 13 parts, 56 parts of acetone, 2 parts of firming agent, nano carbon microsphere 1.5
Part, zinc oxide 3.5 parts, Afluon (Asta) 1.5 parts, carbolic acid 1.5 parts, silane coupler KH792021.5 part.
Or, organic siliconresin 53 parts, modified waterproof silicones 12 parts, 50 parts of acetone, 1.5 parts of firming agent, nano carbon microsphere 1
Part, zinc oxide 3 parts, Afluon (Asta) 1 part, carbolic acid 1 part, silane coupler KH792021 part.
Flat tube block (3) a diameter of 18 ~ 22mm, the thickness of flat tube is 1.2mm ~ 1.7mm.
A kind of condenser processing technology, comprises the following steps:
Sintering oil removing: in heating furnace, condenser core is heated, be warmed up to 200 ~ 300 degree of high temperature;
Machinery ball blast method is used to clean: ball blast also uses compressed air dedusting, when Part temperature is down to 20 DEG C, by chiller core body surface
Face impurity is removed, and removes each position burr;
Spraying: the Dacroment Zinc Based Comples Coatings solution prepared is uniformly sprayed in each portion, chiller core surface with spray gun
Position;There is high antiseptical function;
Baking: temperature controlling range is toasted between 200 ~ 300 degree, 10 ~ 15 minutes time;
Secondary sprays;Making the reaction of Dacroment Zinc Based Comples Coatings solution chemistry completely, coating is firm;
Secondary baking: baking temperature in the range of 200 ~ 400,15 ~ 50 minutes time;
Cool drying.
Inside above-mentioned thermal diffusivity coating uniform roller coating and flat tube, make coating layer thickness between 0.1 mm-0.3 mm;
This thickness can strengthen the effect of heat radiation.
Temperature controlling range is toasted between 200 ~ 300 degree, 20 ~ 40 minutes time;
Cool drying.
The diameter range of the shot that ball blast is used is 0.1-0.8mm.
In use, because flat tube block is inside and outside respectively provided with coating, maximize and the result temperature difference with the use of being allowed to area of dissipation
Maximize, be effectively increased condenser efficiency.
Compared with prior art, advantage for present invention is:
1, processing technology of the present invention is simple, can effectively carry condenser height condensation rate.
Accompanying drawing explanation
Fig. 1 condensing tube brief configuration figure
Figure elements identifies: flat tube block 1;Plate 2;Fin 3;Go out liquid joint 4;Inlet suction port 5;Right header 6;Left header 7;
Header blocks up 8;Mounting bracket 9;Catcher 10.
Detailed description of the invention
It is described in further detail below in conjunction with drawings and Examples:
Embodiment 1:
A kind of pipework condensation device, including being provided with the flat tube block 1 of fin 3, wherein: flat tube block 1 be arranged in parallel and between fin 3;Flat tube
The outside of block 1 is provided with plate 2;Flat tube block 1 two ends connect left header 7 and right header 6 respectively;Left header 7 and right afflux
Pipe 6 is respectively arranged at the two ends with header and blocks up 8;Right header 6 connects catcher 10, and one end is provided with mounting bracket 9;Right header 1
It is provided with inlet suction port 5 and goes out liquid joint 4;Flat tube block 3 is internal scribbles thermal diffusivity coating.
Coating material includes following component and composition by weight thereof: organic siliconresin 55-65 part, modified waterproof silicones 10-
20 parts, acetone 50-60 part, firming agent 1-2 part, zinc oxide 3-6 part, silane coupler KH792022-4 part, filler 3-6 part.
Wherein, filler includes following component and components by weight percent: nano carbon microsphere 1-2 part, Afluon (Asta) 1-2 part, carbolic acid 1-2
Part.
Coating material includes following component and composition by weight thereof: organic siliconresin 60 parts, modified waterproof silicones 16 parts, third
Ketone 55 parts, 1 part of firming agent, nano carbon microsphere 2 parts, zinc oxide 4 parts, Afluon (Asta) 1 part, carbolic acid 2 parts, silane coupler KH792022
Part, coating has high chemical stability, affected by environment little;In the middle of using, cooling anomaly is obvious and cooling rate fast,
Because its mechanism of action is still not clear, still to be tested.
A diameter of 18 ~ the 22mm of flat tube block 3, the thickness of flat tube is 1.2mm ~ 1.7mm.
A kind of condenser processing technology, comprises the following steps:
1) sintering oil removing: in heating furnace, condenser core is heated, be warmed up to 200 ~ 300 degree of high temperature;
2) machinery ball blast method is used to clean: ball blast also uses compressed air dedusting, when Part temperature is down to 20 DEG C, by condenser core
Surface impurity is removed, and removes each position burr;
3) spraying: the Dacroment Zinc Based Comples Coatings solution prepared is uniformly sprayed in each portion, chiller core surface with spray gun
Position;There is high antiseptical function;
4) baking: temperature controlling range is toasted between 200 ~ 300 degree, 10 ~ 15 minutes time;
5) secondary spraying;Making the reaction of Dacroment Zinc Based Comples Coatings solution chemistry completely, coating is firm;
6) secondary baking: baking temperature in the range of 200 ~ 400,15 ~ 50 minutes time;
7) cool drying;
8) roller coating: by inside above-mentioned thermal diffusivity coating uniform roller coating and flat tube, make coating layer thickness 0.1 mm-0.3 mm it
Between;This thickness can strengthen the effect of heat radiation;
9) dry: temperature controlling range is toasted between 200 ~ 300 degree, 20 ~ 40 minutes time;
10) cool drying.
The diameter range of the shot that ball blast is used is 0.1-0.8mm.
Embodiment 2:
A kind of pipework condensation device, including being provided with the flat tube block 1 of fin 3, wherein: flat tube block 1 be arranged in parallel and between fin 3;Flat tube
The outside of block 1 is provided with plate 2;Flat tube block 1 two ends connect left header 7 and right header 6 respectively;Left header 7 and right afflux
Pipe 6 is respectively arranged at the two ends with header and blocks up 8;Right header 6 connects catcher 10, and one end is provided with mounting bracket 9;Right header 1
It is provided with inlet suction port 5 and goes out liquid joint 4;Flat tube block 3 is internal scribbles thermal diffusivity coating.
The preparation of coating: weigh organic siliconresin 600g, modified waterproof silicones 160g, acetone 550g, firming agent 10g,
Nano carbon microsphere 20g, zinc oxide 40g, Afluon (Asta) 10g, carbolic acid 20g, silane coupler KH7920220g, uniformly mix, standby
Coating.
The a diameter of 20mm of flat tube block 3, the thickness of flat tube is 1.6mm.
A kind of condenser processing technology, comprises the following steps:
1) sintering oil removing: in heating furnace, condenser core is heated, be warmed up to 250 degree of high temperature;
2) machinery ball blast method is used to clean: to use the shot that diameter range is 0.1-0.8mm of shot to carry out ball blast and with compressing
Air cleaning, when Part temperature is down to 20 DEG C, removes condenser core surface impurity, and removes each position burr;
3) spraying: the Dacroment Zinc Based Comples Coatings solution prepared is uniformly sprayed in each portion, chiller core surface with spray gun
Position;
4) baking: temperature controlling range is toasted between 280 degree, 15 minutes time;
5) secondary spraying;Making the reaction of Dacroment Zinc Based Comples Coatings solution chemistry completely, coating is firm;
6) secondary baking: baking temperature in the range of 360,46 minutes time;
7) cool drying;
8) roller coating: inside above-mentioned standby coating uniform roller coating and flat tube, make coating layer thickness at 0.3 mm;
9) dry: temperature controlling range is toasted between 270 degree, 38 minutes time;
10) cool drying.
It should be noted that the coating procedure using Dacroment is all carried out in indoor, it is to avoid spray solution meets light note
The most aging.
Contrast experiment:
A kind of pipework condensation device, including being provided with the flat tube block of fin, wherein: flat tube block be arranged in parallel and between fin;Flat tube block
Outside is provided with plate;Flat tube block two ends connect left header and right header respectively;Left header and right header two ends respectively set
Header is had to block up;Right header connects has catcher, one end to be provided with mounting bracket;Right header is provided with inlet suction port and goes out liquid
Joint;Thermal diffusivity coating is scribbled inside flat tube block.
The preparation of coating: weigh organic siliconresin 600g, modified waterproof silicones 160g, acetone 550g, firming agent 10g,
Nano carbon microsphere 20g, zinc oxide 40g, Afluon (Asta) 10g, carbolic acid 20g, silane coupler KH7920220g, uniformly mix, standby
Coating (embodiment group);
A kind of pipework condensation device, including being provided with the flat tube block of fin, wherein: flat tube block be arranged in parallel and between fin;Flat tube block
Outside is provided with plate;Flat tube block two ends connect left header and right header respectively;Left header and right header two ends respectively set
Header is had to block up;Right header connects has catcher, one end to be provided with mounting bracket;Right header is provided with inlet suction port and goes out liquid
Joint;Thermal diffusivity coating is scribbled inside flat tube block.The preparation of coating: weigh organic siliconresin 600g, modified waterproof silicones
160g, acetone 550g, firming agent 10g, zinc oxide 40g, silane coupler KH7920220g, uniformly mix, (the comparison of standby coating
Group);
In the case of technique is the same with condition, experimental result such as following table:
Table 1 comparative test result
The temperature difference (DEG C) | Radiating rate | |
Embodiment group | 45 | Hurry up |
Matched group | 30 | Slowly |
Because its mechanism of action is still not clear, or because synergism creates beyond thought effect, as can be seen from the above table, implement
Example group is better than matched group at the temperature difference, radiating rate, and result proves that the condenser refrigerating efficiency of the present embodiment group is better than matched group, can
It is effectively improved condenser refrigerating efficiency.
Although the present invention is open as above with embodiment, but it is not limited to protection scope of the present invention, any ripe
Know those skilled in the art, in the change done without departing from the spirit and scope of the invention and retouching, all should be belonged to this
The protection domain of bright claims.
Claims (7)
1. a pipework condensation device, including the flat tube block (1) being provided with fin (3), it is characterised in that: described flat tube block (1) is parallel
Arrange between fin (3);The outside of described flat tube block (1) is provided with plate (2);Described flat tube block (1) two ends connect respectively
Left header (7) and right header (6);Described left header (7) and described right header (6) are respectively arranged at the two ends with header
Block up (8);Described right header (6) connects catcher (10), and one end is provided with mounting bracket (9);Described right header
(1) it is provided with inlet suction port (5) and goes out liquid joint (4);Described flat tube block (3) is internal scribbles thermal diffusivity coating.
2. according to the air conditioning condenser for vehicle described in claim 1, it is characterised in that: described coating material includes following one-tenth
Divide and composition by weight: organic siliconresin 55-65 part, modified waterproof silicones 10-20 part, acetone 50-60 part, firming agent 1-2
Part, zinc oxide 3-6 part, silane coupler KH792022-4 part, filler 3-6 part.
3. according to the air conditioning condenser for vehicle described in claim 1, it is characterised in that: described filler include following component and
Components by weight percent: nano carbon microsphere 1-2 part, Afluon (Asta) 1-2 part, carbolic acid 1-2 part.
4. according to the air conditioning condenser for vehicle described in claim 1, it is characterised in that: described coating material includes following one-tenth
Divide and composition by weight: organic siliconresin 60 parts, modified waterproof silicones 16 parts, 55 parts of acetone, 1 part of firming agent, nano carbon microsphere 2
Part, zinc oxide 4 parts, Afluon (Asta) 1 part, carbolic acid 2 parts, silane coupler KH792022 part.
5. according to the air conditioning condenser for vehicle described in claim 1, it is characterised in that: described flat tube block (3) is a diameter of 18 ~
22mm, the thickness of flat tube is 1.2mm ~ 1.7mm.
6. a condenser processing technology, it is characterised in that following steps:
1) sintering oil removing: in heating furnace, condenser core is heated, be warmed up to 200 ~ 300 degree of high temperature;
2) machinery ball blast method is used to clean: ball blast also uses compressed air dedusting, when Part temperature is down to 20 DEG C, by condenser core
Surface impurity is removed, and removes each position burr;
3) spraying: the Dacroment Zinc Based Comples Coatings solution prepared is uniformly sprayed in each portion, chiller core surface with spray gun
Position;
4) baking: temperature controlling range is toasted between 200 ~ 300 degree, 10 ~ 15 minutes time;
5) secondary spraying;
6) secondary baking: baking temperature in the range of 200 ~ 400,15 ~ 50 minutes time;
7) cool drying;
8) roller coating: by inside above-mentioned thermal diffusivity coating uniform roller coating and flat tube, make coating layer thickness 0.1 mm-0.3 mm it
Between;
9) dry: temperature controlling range is toasted between 200 ~ 300 degree, 20 ~ 40 minutes time;
10) cool drying.
Preparation method the most according to claim 6, it is characterised in that: the diameter range of the shot that described ball blast is used
For 0.1-0.8mm.