CN106192399A - A kind of fiber is made to have good spinnability fibre finishing - Google Patents
A kind of fiber is made to have good spinnability fibre finishing Download PDFInfo
- Publication number
- CN106192399A CN106192399A CN201610636201.XA CN201610636201A CN106192399A CN 106192399 A CN106192399 A CN 106192399A CN 201610636201 A CN201610636201 A CN 201610636201A CN 106192399 A CN106192399 A CN 106192399A
- Authority
- CN
- China
- Prior art keywords
- polyoxyethylene ether
- ether
- imidazoline
- smooth
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses and a kind of make fiber have good every kilogram of oil preparation of spinnability fibre finishing containing following component: fatty alcohol-polyoxyethylene ether 50.0 120.0g, benzalkonium bromide 100.0 180.0g, alkyl phenol oxygen second dilute ether 50.0 160.0g, dilaurate polyoxyethylene ether 40.0 70.0g, Adeps Bovis seu Bubali base diethanolamine 50.0 70.0g, butyl cellosolve 20.0 40.0g, smooth 10.0 25.0g of fatty acid Pyrusussuriensis, imidazoline 5.0 10.0g, remaining is paraffin oil.
Description
Technical field
The invention belongs to weaving face fabric processing technique field, be specifically related to that a kind of to make fiber have good spinnability fine
Dimension oil preparation.
Background technology
Preparation medium be chemical fibre in fabrication processes, in order to eliminate produce because of friction electrostatic, reduce coefficient of friction, make
Fiber has preferable convergence, flatness and fiber separation, thus makes it have good spinnability and post-treatment, and necessary
A kind of oil preparation added.
, owing to it constitutes the difference of component, in field of textiles application process, easily there is hair in existing synthetic fiber oiling agent
The phenomenons such as silk, broken end, cause coiling and molding poor, and quality product rate is low, and corrosion phenomenon is serious, it is difficult to use the use of high speed PET weaving
Requirement.
Summary of the invention
Goal of the invention: the problem and shortage existed for above-mentioned prior art, it is an object of the invention to provide one and makes fibre
Dimension has good spinnability fibre finishing.
Technical scheme: the invention discloses and a kind of make fiber have good spinnability fibre finishing, every kilogram of oil preparation
Containing following component: fatty alcohol-polyoxyethylene ether 50.0-120.0g, benzalkonium bromide 100.0-180.0g, the dilute ether of alkyl phenol oxygen second
50.0-160.0g, dilaurate polyoxyethylene ether 40.0-70.0g, Adeps Bovis seu Bubali base diethanolamine 50.0-70.0g, butyl cellosolve
20.0-40.0g, the smooth 10.0-25.0g of fatty acid Pyrusussuriensis, imidazoline 5.0-10.0g, remaining is paraffin oil.
As the further optimization of the present invention, every kilogram of oil preparation of the present invention is containing following component: fatty alcohol-polyoxyethylene ether
60.0-100.0g, benzalkonium bromide 120.0-160.0g, alkyl phenol oxygen second dilute ether 80.0-120.0g, dilaurate polyoxyethylene
Ether 55.0-65.0g, Adeps Bovis seu Bubali base diethanolamine 55.0-68.0g, butyl cellosolve 25.0-35.0g, the smooth 15.0-of fatty acid Pyrusussuriensis
20.0g, imidazoline 8.0-10.0g, remaining is paraffin oil.
As the further optimization of the present invention, every kilogram of oil preparation of the present invention is containing following component: fatty alcohol-polyoxyethylene ether
50.0g, benzalkonium bromide 100.0g, alkyl phenol oxygen second dilute ether 50.0g, dilaurate polyoxyethylene ether 40.0g, Adeps Bovis seu Bubali base diethyl
Hydramine 50.0g, butyl cellosolve 20.0g, the smooth 10.0g of fatty acid Pyrusussuriensis, imidazoline 5.0g, remaining is paraffin oil.
As the further optimization of the present invention, every kilogram of oil preparation of the present invention is containing following component: fatty alcohol-polyoxyethylene ether
120.0g, benzalkonium bromide 180.0g, alkyl phenol oxygen second dilute ether 160.0g, dilaurate polyoxyethylene ether 70.0g, Adeps Bovis seu Bubali base two
Ethanolamine 70.0g, butyl cellosolve 40.0g, the smooth 25.0g of fatty acid Pyrusussuriensis, imidazoline 10.0g, remaining is paraffin oil.
As the further optimization of the present invention, every kilogram of oil preparation of the present invention is containing following component: fatty alcohol-polyoxyethylene ether
60.0g, benzalkonium bromide 120.0g, alkyl phenol oxygen second dilute ether 80.0g, dilaurate polyoxyethylene ether 55.0g, Adeps Bovis seu Bubali base diethyl
Hydramine 55.0g, butyl cellosolve 25.0g, the smooth 15.0g of fatty acid Pyrusussuriensis, imidazoline 8.0g, remaining is paraffin oil.
As the further optimization of the present invention, every kilogram of oil preparation of the present invention is containing following component: diethyl alcohol sulfonic acid amber
Amber sodium 100.0g, benzalkonium bromide 160.0g, alkyl phenol oxygen second dilute ether 120.0g, dilaurate polyoxyethylene ether 65.0g, Adeps Bovis seu Bubali
Base diethanolamine 68.0g, butyl cellosolve 35.0g, the smooth 20.0g of fatty acid Pyrusussuriensis, imidazoline 10.0g, remaining is paraffin oil.
Beneficial effect: the present invention compared with prior art, has the advantage that coefficient of friction is relatively stable, improves lousiness, breaks
First-class phenomenon, more conducively industrialized production.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in detail, but protection scope of the present invention is described also simultaneously
Being not limited to the concrete scope of the present embodiment, based on the embodiment in the present invention, those of ordinary skill in the art are not making
The every other embodiment obtained under creative work premise, broadly falls into the scope of protection of the invention.
Embodiment 1
Every kilogram of oil preparation of the present embodiment is containing following component: fatty alcohol-polyoxyethylene ether 50.0g, benzalkonium bromide 100.0g, alkyl
Phenol oxygen second dilute ether 50.0g, dilaurate polyoxyethylene ether 40.0g, Adeps Bovis seu Bubali base diethanolamine 50.0g, butyl cellosolve
20.0g, the smooth 10.0g of fatty acid Pyrusussuriensis, imidazoline 5.0g, remaining is paraffin oil.
Embodiment 2
Every kilogram of oil preparation of the present embodiment is containing following component: fatty alcohol-polyoxyethylene ether 120.0g, benzalkonium bromide 180.0g, alkyl
Phenol oxygen second dilute ether 160.0g, dilaurate polyoxyethylene ether 70.0g, Adeps Bovis seu Bubali base diethanolamine 70.0g, butyl cellosolve
40.0g, the smooth 25.0g of fatty acid Pyrusussuriensis, imidazoline 10.0g, remaining is paraffin oil.
Embodiment 3
Every kilogram of oil preparation of the present embodiment is containing following component: fatty alcohol-polyoxyethylene ether 60.0g, benzalkonium bromide 120.0g, alkyl
Phenol oxygen second dilute ether 80.0g, dilaurate polyoxyethylene ether 55.0g, Adeps Bovis seu Bubali base diethanolamine 55.0g, butyl cellosolve
25.0g, the smooth 15.0g of fatty acid Pyrusussuriensis, imidazoline 8.0g, remaining is paraffin oil.
Embodiment 4
Every kilogram of oil preparation of the present embodiment is containing following component: diethyl alcohol sulfonic acid succinum sodium 100.0g, benzalkonium bromide 160.0g,
Alkyl phenol oxygen second dilute ether 120.0g, dilaurate polyoxyethylene ether 65.0g, Adeps Bovis seu Bubali base diethanolamine 68.0g, butyl cellosolve
35.0g, the smooth 20.0g of fatty acid Pyrusussuriensis, imidazoline 10.0g, remaining is paraffin oil.
Claims (6)
1. one kind makes fiber have good spinnability fibre finishing, it is characterised in that: every kilogram of oil preparation is containing following component: fat
Fat polyoxyethylenated alcohol 50.0-120.0g, benzalkonium bromide 100.0-180.0g, alkyl phenol oxygen second dilute ether 50.0-160.0g, double
Lauric acid polyoxyethylene ether 40.0-70.0g, Adeps Bovis seu Bubali base diethanolamine 50.0-70.0g, butyl cellosolve 20.0-40.0g, fat
The smooth 10.0-25.0g of fat acid Pyrusussuriensis, imidazoline 5.0-10.0g, remaining is paraffin oil.
The most according to claim 1 a kind of fiber is made to have good spinnability fibre finishing, it is characterised in that: every thousand
Gram oil preparation is containing following component: fatty alcohol-polyoxyethylene ether 60.0-100.0g, benzalkonium bromide 120.0-160.0g, alkyl phenol oxygen second
Dilute ether 80.0-120.0g, dilaurate polyoxyethylene ether 55.0-65.0g, Adeps Bovis seu Bubali base diethanolamine 55.0-68.0g, butyl
Cellosolve 25.0-35.0g, the smooth 15.0-20.0g of fatty acid Pyrusussuriensis, imidazoline 8.0-10.0g, remaining is paraffin oil.
The most according to claim 1 a kind of fiber is made to have good spinnability fibre finishing, it is characterised in that: every thousand
Gram oil preparation is containing following component: fatty alcohol-polyoxyethylene ether 50.0g, benzalkonium bromide 100.0g, and alkyl phenol oxygen second dilute ether 50.0g is double
Lauric acid polyoxyethylene ether 40.0g, Adeps Bovis seu Bubali base diethanolamine 50.0g, butyl cellosolve 20.0g, the smooth 10.0g of fatty acid Pyrusussuriensis,
Imidazoline 5.0g, remaining is paraffin oil.
The most according to claim 1 a kind of fiber is made to have good spinnability fibre finishing, it is characterised in that: every thousand
Gram oil preparation is containing following component: fatty alcohol-polyoxyethylene ether 120.0g, benzalkonium bromide 180.0g, alkyl phenol oxygen second dilute ether 160.0g,
Dilaurate polyoxyethylene ether 70.0g, Adeps Bovis seu Bubali base diethanolamine 70.0g, butyl cellosolve 40.0g, fatty acid Pyrusussuriensis is smooth
25.0g, imidazoline 10.0g, remaining is paraffin oil.
The most according to claim 2 a kind of fiber is made to have good spinnability fibre finishing, it is characterised in that: every thousand
Gram oil preparation is containing following component: fatty alcohol-polyoxyethylene ether 60.0g, benzalkonium bromide 120.0g, and alkyl phenol oxygen second dilute ether 80.0g is double
Lauric acid polyoxyethylene ether 55.0g, Adeps Bovis seu Bubali base diethanolamine 55.0g, butyl cellosolve 25.0g, the smooth 15.0g of fatty acid Pyrusussuriensis,
Imidazoline 8.0g, remaining is paraffin oil.
The most according to claim 2 a kind of fiber is made to have good spinnability fibre finishing, it is characterised in that: every thousand
Gram oil preparation is containing following component: diethyl alcohol sulfonic acid succinum sodium 100.0g, benzalkonium bromide 160.0g, the dilute ether of alkyl phenol oxygen second
120.0g, dilaurate polyoxyethylene ether 65.0g, Adeps Bovis seu Bubali base diethanolamine 68.0g, butyl cellosolve 35.0g, fatty acid Pyrusussuriensis
Smooth 20.0g, imidazoline 10.0g, remaining is paraffin oil.