CN106189956A - A kind of clean taste soybean-based sheet material adhesive and preparation method thereof - Google Patents
A kind of clean taste soybean-based sheet material adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN106189956A CN106189956A CN201610656702.4A CN201610656702A CN106189956A CN 106189956 A CN106189956 A CN 106189956A CN 201610656702 A CN201610656702 A CN 201610656702A CN 106189956 A CN106189956 A CN 106189956A
- Authority
- CN
- China
- Prior art keywords
- mentioned
- soybean
- add
- minute
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of clean taste soybean-based sheet material adhesive, it is made up of the raw material of following weight parts: double octyl methyl tertiary amines 12, tert-butyl hydroquinone 0.5 1, polyvinyl alcohol 24, defatted soybean flour 170 200, iron chloride 0.3 0.4, ferrous chloride 0.1 0.2, epoxychloropropane 0.8 1, N n-methylolacrylamide 23, styrene 16 20, potassium peroxydisulfate 0.1 0.2, hemicellulase 34, poly-methyl diphenylene diisocyanate 10 19, the hydrochloric acid solution 60 70 of 20 30%, chlorine dimethyl phthalate 0.1 0.3, Tetramethylammonium hydroxide 0.6 1, aluminum isopropylate. 23, PTMG 35, n N-phenylsalicylamide 12 etc..The present invention is difficult to cause equipment corrosion, working life to deposit the features such as phase longer, formaldehydeless, residual monomer content is low, the feature of environmental protection, water-tolerant.
Description
Technical field
The present invention relates to adhesive technical field, particularly relate to a kind of clean taste soybean-based sheet material adhesive and preparation side thereof
Method.
Background technology
Aldehyde system adhesive consumption in timber industry adhesive is maximum, but it exists shortcomings: primary raw material multi-source
In the non-renewable resources such as oil, coal;Produce and use process constantly distributes carcinogen (such as formaldehyde), can be good for by harmful to human
Health;Product non-degradable, easily pollutes environment.Therefore, biomass-based adhesive is researched and developed to substitute aldehyde system adhesive by the whole world
Pay much attention to.In various biological materials, Semen sojae atricolor (including genetically engineered soybean) has that yield is big, low cost, vegetable protein contain
Measure high feature, be good adhesive raw material;Research soybean-based adhesive so that it is all or part of petroleum replacing base gluing
Agent, to reduce depletion of non-renewable resources, ensure food safety the most significant, be outside Present Domestic research focus;
Adhesive the most nontoxic, free of contamination is applied to become trend, plant along with using the exploitation of reproducible biomass from producing to
The research of albumen adhesive causes the extensive concern of people.Wherein, utilizing soybean protein to prepare soybean-based adhesive is study hotspot,
Improving its resistance to water is then primary study content, and it is the most resistance to that oneself there are some researches show that adhesive prepared by soybean protein isolate has
Aqueous;But, SPI is isolatable from Semen sojae atricolor defatted soy flour, and the price of its costliness necessarily limits its application in terms of adhesive.Cause
This, the DSF of cost and low percentages of protein becomes the preferred raw materials preparing water-resistant soybean base adhesive;
SPI and DSF, SPI that after preparation soybean-based adhesive mainly uses soybean extract oil at present, defat bean cypress produces derive from
DSF, its soybean protein content is typically larger than 90%, it is easy to modified, the adhesive of preparation has good resistance to water.But SPI costliness
Its application in terms of adhesive of price limit.Therefore, the DSF of cost and low percentages of protein become preparation resistance to water big
The preferred material of bean base adhesive.A large amount of research methoies based on SPI adhesive are also used for modified DSF and prepare adhesive, and
Achieve certain effect, it is thus achieved that low resistance to water (cold water or humid air), medium resistance to water (63 DEG C of water) and enhanced water resistance
The modified soybean base adhesive formula of (boiling water);Wherein, enhanced water resistance soybean-based adhesive is mainly by excellent with boiling water resistance energy
Obtain after different synthetic resin mixing.But, DSF is complicated mixture, by the soybean protein of nearly 50%, the carbon hydrate of 40%
Thing and other micro constitutent form;
Current research method all lays particular emphasis on modified soybean protein therein, and is not directed to the carbohydrate of 40%, causes this
Resistance to water after adhesive is solidified by component is inoperative, even plays negative interaction, wastes raw material.Additionally, have resistance to boiling
Aqueous can be adhesive for making the precondition of outdoor cementing thing, if when with DSF glue so that it is in carbon hydrate
Thing converts the component that raising adhesive resistance to water rises positive interaction, in conjunction with Soybean Protein Modification method, prepares the bean of resistance to boiling water base
Adhesive, not only takes full advantage of raw material, can be also that a new way is opened up in the soybean-based adhesive research being applied to open air.
The research solving problem that aldehyde system adhesive exists and the based Wood Adhesives that instructs other similar biomass to be raw material is all anticipated by this
Justice is great;
Epoxy radicals is the polar group that a kind of work is dialled, and can form chemistry and be bonded with the radical reaction containing active oxygen, utilize containing epoxy
The compound on organism matter adhesive of group is modified improving research existing many reports of its performance, if therefore used
Containing epoxy compounds, it is modified, or access ring epoxide in the component containing these functional groups, necessarily can carry further
High Semen sojae atricolor base adhesive resistance to water.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of clean taste soybean-based sheet material adhesive and
Preparation method.
The present invention is achieved by the following technical solutions:
A kind of clean taste soybean-based sheet material adhesive, it is made up of the raw material of following weight parts:
Double octyl methyl tertiary amine 1-2, tert-butyl hydroquinone 0.5-1, polyvinyl alcohol 2-4, defatted soybean flour 170-200, chlorine
Change ferrum 0.3-0.4, ferrous chloride 0.1-0.2, epoxychloropropane 0.8-1, N hydroxymethyl acrylamide 2-3, styrene 16-20,
Potassium peroxydisulfate 0.1-0.2, hemicellulase 3-4, the hydrochloric acid solution 60-of poly-methyl diphenylene diisocyanate 10-19,20-30%
70, chlorine dimethyl phthalate 0.1-0.3, Tetramethylammonium hydroxide 0.6-1, aluminum isopropylate. 2-3, PTMG 3-5, three
Normal-butyl myristyl phosphonium chloride 1-2, calcium oxide 1-2, n-N-phenylsalicylamide 1-2.
The preparation method of a kind of described clean taste soybean-based sheet material adhesive, comprises the following steps:
(1) by above-mentioned iron chloride, ferrous chloride mixing, join in the hydrochloric acid solution of 20-30%, stir, obtain iron salt molten
Liquid;
(2) above-mentioned Tetramethylammonium hydroxide is joined in the deionized water of its weight 20-30 times, stir, add n-water
Poplar anilide, rises high-temperature and is 57-60 DEG C, and insulated and stirred 10-17 minute adds above-mentioned calcium oxide, and stirring, to room temperature, obtains aniline
Dispersion liquid;
(3) above-mentioned aluminum isopropylate. is joined in the deionized water of its weight 40-50 times, rise high-temperature and be 60-70 DEG C, with above-mentioned
Aniline dispersion liquid mixes, insulated and stirred 30-40 minute, the hydrochloric acid solution of dropping 3-5mol/l, and regulation pH is 2-3, and stirring is to often
Temperature, obtains modified aluminium colloidal sol;
(4) above-mentioned defatted soybean flour is joined in the distilled water of its weight 20-27 times, stirs, add hemicellulase,
Enzymolysis 18-20 minute at 50-55 DEG C, reduces temperature and is 26-30 DEG C, add above-mentioned iron salt solutions, be incubated 30-35 minute, add
Entering the sodium hydroxide of 3-5mol/l, regulation pH is 5-6, adds above-mentioned epoxychloropropane, rises high-temperature and is 70-75 DEG C, and insulation is stirred
Mixing 30-35 minute, add the sodium hydroxide of 3-5mol/l, regulation pH is 10-11, adds above-mentioned modified aluminium colloidal sol, stirring reaction
30-40 minute, obtain epoxide modified Semen sojae atricolor latex;
(5) take above-mentioned epoxide modified Semen sojae atricolor latex, be passed through nitrogen, rise high-temperature and be 70-75 DEG C, add above-mentioned N-methylol propylene
Amide, drips acetic acid, and regulation pH is 5-6, and insulated and stirred 60-60 minute obtains acid amide-grafted epoxy soybean latex;
(6) above-mentioned tert-butyl hydroquinone is joined in the dehydrated alcohol of its weight 6-10 times, rises high-temperature and be 60-70 DEG C,
Add above-mentioned three normal-butyl myristyl phosphonium chlorides, insulated and stirred 10-17 minute, add above-mentioned PTMG, stir
Mix to room temperature, obtain compound alcohol liquid;
(7) take above-mentioned acid amide-grafted epoxy soybean latex, add above-mentioned polyvinyl alcohol, rise high-temperature and be 76-80 DEG C, add above-mentioned
Compound alcohol liquid, insulated and stirred 20-30 minute, add the 20-25% of above-mentioned styrene weight, the 18-of above-mentioned potassium peroxydisulfate weight
20%, stirring mixing 10-20 minute, drip remaining styrene, potassium peroxydisulfate, reduce temperature and be 40-45 DEG C, insulation reaction 60-
70 minutes, cooling, obtain Polystyrene grafting rubber made from soybean cake;
(8) above-mentioned Polystyrene grafting rubber made from soybean cake is mixed with remaining each raw material, stir, to obtain final product.
The invention have the advantage that using method:
During use, adhesive of the present invention 2-poly-with the firming agent of its weight 8-10% phenylmethane cyanate (PMDI) is mixed, stir
Mixing uniformly, be coated on plate surface, plate surface coating amount is 280 g/m2, and after gluing, room temperature Guan Bi ageing 10 min, are re-fed into
Press, sheeting process is: room temperature, 4.0 MPa, 40 min,.
First defatted soybean flour is used hemicellulose ferment treatment by the present invention, then by acid, alkali, salt Combined Treatment, can be by big
Soybean protein partial hydrolysis, destroys oxygen key, unfolds the chondritic of soybean protein so that it is active center is exposed, and improves in adhesive
The content of active function groups and reactivity, can form preferably crosslinking, thus improve its water resistance after causing its solidification,
And the Semen sojae atricolor latex after hemicellulose ferment treatment contains substantial amounts of active group, such as-NH2 ,-C00H ,-OH etc., can be with epoxy chlorine
Epoxy radicals generation chemical reaction in propane, is conducive to eliminating the hydrophilic radical in soybean-based adhesive, is cross-linked into said three-dimensional body
Type structure, improves the resistance to water after its solidification, then utilizes methylol and the epoxy soybean base gluing of N hydroxymethyl acrylamide
Agent contains the component reaction of these functional groups, forms grafting, and the vinyl in N hydroxymethyl acrylamide can be with styrene
Monomer forms stable copolymer, and after styrene copolymerized, vinyl residual quantity declines, the phenyl in polystyrene structure, alkane
Hydrocarbon methyl composition increases, and improves the stability of modified soybean base adhesive, and only containing phenyl, parent in styrene molecules structure
Aqueous is little;Meanwhile, the more preferable phenyl ring of a large amount of stability is introduced into modification by copolymerization soybean-based adhesive, causes its resistance to water to improve.
The styrene copolymerized modified soybean base adhesive of the present invention is difficult to cause equipment corrosion, working life to deposit, and the phase is longer, do not contain
The features such as formaldehyde, residual monomer content are low, the feature of environmental protection, water-tolerant
The adhesive of the present invention is without poisonous and harmful substances volatilizations such as formaldehyde, and Safety and Environmental Protection is good, and also the adhesion strength of base material is high, tough
Property is good, and combination property is superior.
Detailed description of the invention
A kind of clean taste soybean-based sheet material adhesive, it is made up of the raw material of following weight parts:
Double octyl methyl tertiary amines 1, tert-butyl hydroquinone 0.5, polyvinyl alcohol 2, defatted soybean flour 170, iron chloride 0.3, chlorine
Change ferrous iron 0.1, epoxychloropropane 0.8, N n-methylolacrylamide 2, styrene 16, potassium peroxydisulfate 0.1, hemicellulase 3, gather
The hydrochloric acid solution 60 of methyl diphenylene diisocyanate 10,20%, chlorine dimethyl phthalate 0.1, Tetramethylammonium hydroxide 0.6, isopropyl
Aluminium alcoholates 2, PTMG 3, three normal-butyl myristyl phosphonium chloride 1, calcium oxide 1, n N-phenylsalicylamide 1.
The preparation method of a kind of described clean taste soybean-based sheet material adhesive, comprises the following steps:
(1) by above-mentioned iron chloride, ferrous chloride mixing, join in the hydrochloric acid solution of 20%, stir, obtain iron salt solutions;
(2) above-mentioned Tetramethylammonium hydroxide is joined in the deionized water of its weight 20 times, stir, add n salicyloyl
Aniline, rising high-temperature is 57 DEG C, insulated and stirred 10 minutes, adds above-mentioned calcium oxide, and stirring, to room temperature, obtains aniline dispersion liquid;
(3) being joined by above-mentioned aluminum isopropylate. in the deionized water of its weight 40 times, rising high-temperature is 60 DEG C, divides with above-mentioned aniline
Dissipating liquid mixing, insulated and stirred 30 minutes, the hydrochloric acid solution of dropping 3mol/l, regulation pH is 2, and stirring, to room temperature, obtains modified aluminium molten
Glue;
(4) above-mentioned defatted soybean flour is joined in the distilled water of its weight 20 times, stir, add hemicellulase,
Enzymolysis 18 minutes at 50 DEG C, reducing temperature is 26 DEG C, adds above-mentioned iron salt solutions, is incubated 30 minutes, adds the hydrogen-oxygen of 3mol/l
Changing sodium, regulation pH is 5, adds above-mentioned epoxychloropropane, and rising high-temperature is 70 DEG C, and insulated and stirred 30 minutes adds 3mol/l's
Sodium hydroxide, regulation pH is 10, adds above-mentioned modified aluminium colloidal sol, stirring reaction 30 minutes, obtains epoxide modified Semen sojae atricolor latex;
(5) taking above-mentioned epoxide modified Semen sojae atricolor latex, be passed through nitrogen, rising high-temperature is 70 DEG C, adds above-mentioned N methylol acryloyl
Amine, drips acetic acid, and regulation pH is 5, and insulated and stirred 60 minutes obtains acid amide-grafted epoxy soybean latex;
(6) being joined by above-mentioned tert-butyl hydroquinone in the dehydrated alcohol of its weight 6 times, rising high-temperature is 60 DEG C, in addition
State three normal-butyl myristyl phosphonium chlorides, insulated and stirred 10 minutes, add above-mentioned PTMG, stir to room temperature,
Alcohol liquid must be combined;
(7) taking above-mentioned acid amide-grafted epoxy soybean latex, add above-mentioned polyvinyl alcohol, rising high-temperature is 76 DEG C, adds above-mentioned multiple
Close alcohol liquid, insulated and stirred 20 minutes, add the 20% of above-mentioned styrene weight, the 18% of above-mentioned potassium peroxydisulfate weight, stirring mixing
10 minutes, dripping remaining styrene, potassium peroxydisulfate, reducing temperature is 40 DEG C, insulation reaction 60 minutes, and cooling obtains polyphenyl second
Alkene modification grafting rubber made from soybean cake;
(8) above-mentioned Polystyrene grafting rubber made from soybean cake is mixed with remaining each raw material, stir, to obtain final product.
Performance test:
Viscosity 4.9Pa.s;
Bonding strength: 1.3Mpa.
Claims (2)
1. a clean taste soybean-based sheet material adhesive, it is characterised in that it is made up of the raw material of following weight parts:
Double octyl methyl tertiary amine 1-2, tert-butyl hydroquinone 0.5-1, polyvinyl alcohol 2-4, defatted soybean flour 170-200, chlorine
Change ferrum 0.3-0.4, ferrous chloride 0.1-0.2, epoxychloropropane 0.8-1, N hydroxymethyl acrylamide 2-3, styrene 16-20,
Potassium peroxydisulfate 0.1-0.2, hemicellulase 3-4, the hydrochloric acid solution 60-of poly-methyl diphenylene diisocyanate 10-19,20-30%
70, chlorine dimethyl phthalate 0.1-0.3, Tetramethylammonium hydroxide 0.6-1, aluminum isopropylate. 2-3, PTMG 3-5, three
Normal-butyl myristyl phosphonium chloride 1-2, calcium oxide 1-2, n-N-phenylsalicylamide 1-2.
2. the preparation method of a clean taste soybean-based sheet material adhesive as claimed in claim 1, it is characterised in that include following
Step:
(1) by above-mentioned iron chloride, ferrous chloride mixing, join in the hydrochloric acid solution of 20-30%, stir, obtain iron salt molten
Liquid;
(2) above-mentioned Tetramethylammonium hydroxide is joined in the deionized water of its weight 20-30 times, stir, add n-water
Poplar anilide, rises high-temperature and is 57-60 DEG C, and insulated and stirred 10-17 minute adds above-mentioned calcium oxide, and stirring, to room temperature, obtains aniline
Dispersion liquid;
(3) above-mentioned aluminum isopropylate. is joined in the deionized water of its weight 40-50 times, rise high-temperature and be 60-70 DEG C, with above-mentioned
Aniline dispersion liquid mixes, insulated and stirred 30-40 minute, the hydrochloric acid solution of dropping 3-5mol/l, and regulation pH is 2-3, and stirring is to often
Temperature, obtains modified aluminium colloidal sol;
(4) above-mentioned defatted soybean flour is joined in the distilled water of its weight 20-27 times, stirs, add hemicellulase,
Enzymolysis 18-20 minute at 50-55 DEG C, reduces temperature and is 26-30 DEG C, add above-mentioned iron salt solutions, be incubated 30-35 minute, add
Entering the sodium hydroxide of 3-5mol/l, regulation pH is 5-6, adds above-mentioned epoxychloropropane, rises high-temperature and is 70-75 DEG C, and insulation is stirred
Mixing 30-35 minute, add the sodium hydroxide of 3-5mol/l, regulation pH is 10-11, adds above-mentioned modified aluminium colloidal sol, stirring reaction
30-40 minute, obtain epoxide modified Semen sojae atricolor latex;
(5) take above-mentioned epoxide modified Semen sojae atricolor latex, be passed through nitrogen, rise high-temperature and be 70-75 DEG C, add above-mentioned N-methylol propylene
Amide, drips acetic acid, and regulation pH is 5-6, and insulated and stirred 60-60 minute obtains acid amide-grafted epoxy soybean latex;
(6) above-mentioned tert-butyl hydroquinone is joined in the dehydrated alcohol of its weight 6-10 times, rises high-temperature and be 60-70 DEG C,
Add above-mentioned three normal-butyl myristyl phosphonium chlorides, insulated and stirred 10-17 minute, add above-mentioned PTMG, stir
Mix to room temperature, obtain compound alcohol liquid;
(7) take above-mentioned acid amide-grafted epoxy soybean latex, add above-mentioned polyvinyl alcohol, rise high-temperature and be 76-80 DEG C, add above-mentioned
Compound alcohol liquid, insulated and stirred 20-30 minute, add the 20-25% of above-mentioned styrene weight, the 18-of above-mentioned potassium peroxydisulfate weight
20%, stirring mixing 10-20 minute, drip remaining styrene, potassium peroxydisulfate, reduce temperature and be 40-45 DEG C, insulation reaction 60-
70 minutes, cooling, obtain Polystyrene grafting rubber made from soybean cake;
(8) above-mentioned Polystyrene grafting rubber made from soybean cake is mixed with remaining each raw material, stir, to obtain final product.