CN106189849A - Antiseptic and rustproof wax of solvent-free automobile chassis and preparation method thereof - Google Patents
Antiseptic and rustproof wax of solvent-free automobile chassis and preparation method thereof Download PDFInfo
- Publication number
- CN106189849A CN106189849A CN201610605128.XA CN201610605128A CN106189849A CN 106189849 A CN106189849 A CN 106189849A CN 201610605128 A CN201610605128 A CN 201610605128A CN 106189849 A CN106189849 A CN 106189849A
- Authority
- CN
- China
- Prior art keywords
- solvent
- antiseptic
- automobile chassis
- wax
- emulsifying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides antiseptic and rustproof wax of solvent-free automobile chassis and preparation method thereof, the present invention is made up of component Cera Flava, microwax, organic siliconresin polyacrylate dispersion, coconut oil fat acyl diethanolamine, Tween80, Span80, water.Its preparation method is: 1) Cera Flava, microwax, organic siliconresin polyacrylate dispersion is joined by proportioning and is slowly heated to 110~130 DEG C of hybrid reactions 15 in rustless steel container~makes oil phase material in 50 minutes;2) Tween80, Span80 are joined distilled water is heated to 80~90 DEG C for aqueous phase;3) mixing and emulsifying in aqueous phase will be joined under oil phase material high-speed stirred, it is stirred for after mixing and emulsifying stablizing 10~25 minutes, adds coconut oil fat acyl diethanolamine, continuation emulsifying 10~20 minutes, homogenizing cooling, is the antiseptic and rustproof wax product of solvent-free automobile chassis again.Product of the present invention, it is possible to automobile chassis effectively carrying out antiseptic and rustproof protection, reduces automobile chassis retrial probability, this product is non-solvent product, uses process environmental protection, can effectively reduce the harm to environment.
Description
Technical field
The present invention relates to the rust-proofing wax for automobile, the antiseptic and rustproof wax of the most solvent-free automobile chassis and preparation thereof
Method.
Background technology
Rust-proofing wax is used for preventing automobile appearance corrosion, pitting, function rust etc., and prime coats connects position, vehicle body in car body panel
In closed section, at muddy water accumulation, vehicle chassis etc..Each position should determine difference according to varying environment condition and purpose when selecting
Rust-proofing wax.
Around vehicle chassis, the mount point of wheel portion part many, if to the marginal portion of wheel portion and welding portion
Carrying out antirust treatment Deng respectively, cost will significantly rise.It addition, the corrosion that when installing part, damage surface causes also has been difficult to
Entirely avoid, therefore, after vehicle is completed, rust-proofing wax is applied on vehicle chassis, the increase of controllable costs, and
Chassis of vehicle body plate is carried out antirust.Specific performance requires have rust-preventing characteristic, spalling resistance, the detergency of resistance to steam, thermostability, tolerance to cold
Etc..
Automobile rust-proofing wax mainly has two types at present: one is oil-soluble antirust wax;One is water-soluble anti-rust wax.Oil
Dissolubility rust-proofing wax is to form with the allotment of various additives with fat hydrocarbon solvent, and performance is good and production technology is simple.But in product
Containing a large amount of organic solvents, there are easy breaking out of fire, pollution environment, affect the shortcomings such as health.Along with economic development, send out
Reaching National Environment Policy Act rule increasingly stringent, some department or the producer that have some countries at present have formulated relevant regulation, limit
The system antirusting paint containing solvent.
Water emulsification rust-proofing wax has the advantages such as storage stable, abnormal smells from the patient is little, easy construction, high-efficiency anticorrosive, and it is actually
The emulsion that wax is dispersed in water with nominal particle size, i.e. emulsifing wax.Due to water compositing dispersion medium, it is clear that do not have oil soluble wax above-mentioned scarce
Point, transports and applies all very convenient, and storage is stable, and abnormal smells from the patient is little.Because water is immiscible with wax, the emulsifying of good stability to be prepared
Wax, production technology and formula are necessarily complicated than oil soluble wax.In sum, two kinds of wax is the most all using, due to water and milk
Changing wax and have more obvious feature of environmental protection advantage, it will expanding day at automobile and other antirust industrial applications.
Summary of the invention
It is desirable to provide a kind of antiseptic and rustproof wax of solvent-free automobile chassis and preparation method thereof, the present invention does not uses molten
Agent, uses process environmental protection, can effectively reduce the harm to environment.
For realizing above-mentioned technical purpose, the technical scheme that the present invention takes is:
The antiseptic and rustproof wax of solvent-free automobile chassis, according to mass percent, is made up of following component:
The antiseptic and rustproof wax of solvent-free automobile chassis, according to mass percent, is preferably constituted by following component:
The preparation method of the antiseptic and rustproof wax of solvent-free automobile chassis, its preparation method is:
1) Cera Flava, microwax, organic siliconresin polyacrylate dispersion are joined in rustless steel container slow by proportioning
It is heated to 110~130 DEG C of hybrid reactions 15~makes oil phase material in 50 minutes;
2) Tween80, Span80 are joined distilled water is heated to 80~90 DEG C for aqueous phase;
3) mixing and emulsifying in aqueous phase will be joined under oil phase material high-speed stirred, be stirred for after mixing and emulsifying stablizing 10~25
Minute, add coconut oil fat acyl diethanolamine, continuation emulsifying 10~20 minutes, then homogenizing cooling, be solvent-free automobile bottom
The antiseptic and rustproof wax product of dish.
Product of the present invention, it is possible to effectively automobile chassis is carried out antiseptic and rustproof protection, reduces automobile chassis retrial several
Rate, this product is non-solvent product, uses process environmental protection, can effectively reduce the harm to environment.
Detailed description of the invention
Embodiment 1
The antiseptic and rustproof wax of solvent-free automobile chassis, according to mass percent, is made up of following component:
The preparation method of the antiseptic and rustproof wax of solvent-free automobile chassis, its preparation method is:
1) Cera Flava, microwax, organic siliconresin polyacrylate dispersion are joined in rustless steel container slow by proportioning
It is heated to 110~130 DEG C of hybrid reactions 15~makes oil phase material in 50 minutes;
2) Tween80, Span80 are joined distilled water is heated to 80~90 DEG C for aqueous phase;
3) mixing and emulsifying in aqueous phase will be joined under oil phase material high-speed stirred, be stirred for after mixing and emulsifying stablizing 10~25
Minute, add coconut oil fat acyl diethanolamine, continuation emulsifying 10~20 minutes, then homogenizing cooling, be solvent-free automobile bottom
The antiseptic and rustproof wax product of dish.
Embodiment 2
The antiseptic and rustproof wax of solvent-free automobile chassis, according to mass percent, is made up of following component:
The preparation method of the antiseptic and rustproof wax of solvent-free automobile chassis, its preparation method is:
1) Cera Flava, microwax, organic siliconresin polyacrylate dispersion are joined in rustless steel container slow by proportioning
It is heated to 110~130 DEG C of hybrid reactions 15~makes oil phase material in 50 minutes;
2) Tween80, Span80 are joined distilled water is heated to 80~90 DEG C for aqueous phase;
3) mixing and emulsifying in aqueous phase will be joined under oil phase material high-speed stirred, be stirred for after mixing and emulsifying stablizing 10~25
Minute, add coconut oil fat acyl diethanolamine, continuation emulsifying 10~20 minutes, then homogenizing cooling, be solvent-free automobile bottom
The antiseptic and rustproof wax product of dish.
Embodiment 3
The antiseptic and rustproof wax of solvent-free automobile chassis, according to mass percent, is made up of following component:
The preparation method of the antiseptic and rustproof wax of solvent-free automobile chassis, its preparation method is:
1) Cera Flava, microwax, organic siliconresin polyacrylate dispersion are joined in rustless steel container slow by proportioning
It is heated to 110~130 DEG C of hybrid reactions 15~makes oil phase material in 50 minutes;
2) Tween80, Span80 are joined distilled water is heated to 80~90 DEG C for aqueous phase;
3) mixing and emulsifying in aqueous phase will be joined under oil phase material high-speed stirred, be stirred for after mixing and emulsifying stablizing 10~25
Minute, add coconut oil fat acyl diethanolamine, continuation emulsifying 10~20 minutes, then homogenizing cooling, be solvent-free automobile bottom
The antiseptic and rustproof wax product of dish.
Claims (3)
- The antiseptic and rustproof wax of the most solvent-free automobile chassis, it is characterised in that according to mass percent, be made up of following component:
- The antiseptic and rustproof wax of solvent-free automobile chassis the most according to claim 1, it is characterised in that according to mass percent Meter, is made up of following component:
- The preparation method of the antiseptic and rustproof wax of the most solvent-free automobile chassis, it is characterised in that its preparation method is:1) Cera Flava, microwax, organic siliconresin polyacrylate dispersion are joined in rustless steel container by proportioning it is slowly heated To 110~130 DEG C of hybrid reactions 15~make oil phase material in 50 minutes;2) Tween80, Span80 are joined distilled water is heated to 80~90 DEG C for aqueous phase;3) mixing and emulsifying in aqueous phase will be joined under oil phase material high-speed stirred, be stirred for after mixing and emulsifying stablizing 10~25 points Clock, adds coconut oil fat acyl diethanolamine, continuation emulsifying 10~20 minutes, then homogenizing cooling, is solvent-free automobile chassis Antiseptic and rustproof wax product.