CN106189464A - Putty for interior wall powder - Google Patents
Putty for interior wall powder Download PDFInfo
- Publication number
- CN106189464A CN106189464A CN201610784545.5A CN201610784545A CN106189464A CN 106189464 A CN106189464 A CN 106189464A CN 201610784545 A CN201610784545 A CN 201610784545A CN 106189464 A CN106189464 A CN 106189464A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- putty
- interior wall
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of putty for interior wall powder, the most composed of the following components: 1~2 part of alkylolamides polyethylene oxide ether, 0.8 part of sodium polyacrylate, 1.5 parts of alkyl sulfate sodium, 1.3 parts of normal-butyl sodium naphthalene sulfonates, 1.5 parts of isomerous tridecanol polyoxyethylene ethers, 0.6 part of cerous carbonate, 3.8 parts of wood fibres, 18 parts of sepiolite powders, 28 parts of cold polyvinyl alcohol rubber powders that melt, 42 parts of silicate foam cement powder.Putty for interior wall powder of the present invention, its good leveling property, adhesive force is strong, water-tolerant, intensity is high, resistance to polishing, the change of acid-alkali-corrosive-resisting, high-low temperature resistant, resistance to go mouldy, without hollowing, peeling, be full of cracks, obscission after being made moist by water, also without turning to be yellow, mouldy, a black speck phenomenon.
Description
Technical field
The present invention relates to putty for interior wall powder.
Background technology
Existing putty for interior wall powder, its levelability, adhesive force, resistance to water, intensity, rub resistance energy, acid-alkali-corrosive-resisting
Can, high-low temperature resistant change performance, resistance to performance of going mouldy all have much room for improvement, easily occur after being made moist by water hollowing, peeling, chap, de-
Fall phenomenon, and jaundice, mouldy, a black speck phenomenon easily occurs.
Summary of the invention
It is an object of the invention to provide a kind of putty for interior wall powder, its good leveling property, adhesive force is strong, water-tolerant, by force
Degree height, resistance to polishing, the change of acid-alkali-corrosive-resisting, high-low temperature resistant, resistance to go mouldy, after being made moist by water without hollowing, peeling, chap, coming off shows
As, also without jaundice, mouldy, a black speck phenomenon.
For achieving the above object, the technical scheme is that a kind of putty for interior wall powder of design, by weight by with
Lower component forms:
1~2 part of alkylolamides polyethylene oxide ether,
0.8 part of sodium polyacrylate,
1.5 parts of alkyl sulfate sodium,
1.3 parts of normal-butyl sodium naphthalene sulfonates,
1.5 parts of isomerous tridecanol polyoxyethylene ethers,
0.6 part of cerous carbonate,
3.8 parts of wood fibres,
18 parts of sepiolite powders,
28 parts cold melts polyvinyl alcohol rubber powder,
42 parts of silicate foam cement powder.
Preferably, putty for interior wall powder, the most composed of the following components:
1 part of alkylolamides polyethylene oxide ether,
0.8 part of sodium polyacrylate,
1.5 parts of alkyl sulfate sodium,
1.3 parts of normal-butyl sodium naphthalene sulfonates,
1.5 parts of isomerous tridecanol polyoxyethylene ethers,
0.6 part of cerous carbonate,
3.8 parts of wood fibres,
18 parts of sepiolite powders,
28 parts cold melts polyvinyl alcohol rubber powder,
42 parts of silicate foam cement powder.
Preferably, putty for interior wall powder, the most composed of the following components:
2 parts of alkylolamides polyethylene oxide ethers,
0.8 part of sodium polyacrylate,
1.5 parts of alkyl sulfate sodium,
1.3 parts of normal-butyl sodium naphthalene sulfonates,
1.5 parts of isomerous tridecanol polyoxyethylene ethers,
0.6 part of cerous carbonate,
3.8 parts of wood fibres,
18 parts of sepiolite powders,
28 parts cold melts polyvinyl alcohol rubber powder,
42 parts of silicate foam cement powder.
Preferably, putty for interior wall powder, the most composed of the following components:
1.2 parts of alkylolamides polyethylene oxide ethers,
0.8 part of sodium polyacrylate,
1.5 parts of alkyl sulfate sodium,
1.3 parts of normal-butyl sodium naphthalene sulfonates,
1.5 parts of isomerous tridecanol polyoxyethylene ethers,
0.6 part of cerous carbonate,
3.8 parts of wood fibres,
18 parts of sepiolite powders,
28 parts cold melts polyvinyl alcohol rubber powder,
42 parts of silicate foam cement powder.
Advantages of the present invention and having the beneficial effects that: providing a kind of putty for interior wall powder, its good leveling property, adhesive force is strong,
Water-tolerant, intensity is high, resistance to polishing, the change of acid-alkali-corrosive-resisting, high-low temperature resistant, resistance to goes mouldy, after being made moist by water without hollowing, peeling,
Be full of cracks, obscission, also without jaundice, mouldy, a black speck phenomenon.
Performance and the purposes of " powder of lacquer putty for use on " are determined by its component and proportioning, and the different component meeting in " powder of lacquer putty for use on "
Influencing each other, component and proportioning thereof can determine the final performance of " powder of lacquer putty for use on ", as the most mutually coordinated in fruit component and proportioning thereof, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, and the when of serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " putty
Powder " optimal component and proportioning so that multiple components combine, mutually coordinated and produce forward comprehensive effect.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Putty for interior wall powder, the most composed of the following components:
1~2 part of alkylolamides polyethylene oxide ether,
0.8 part of sodium polyacrylate,
1.5 parts of alkyl sulfate sodium,
1.3 parts of normal-butyl sodium naphthalene sulfonates,
1.5 parts of isomerous tridecanol polyoxyethylene ethers,
0.6 part of cerous carbonate,
3.8 parts of wood fibres,
18 parts of sepiolite powders,
28 parts cold melts polyvinyl alcohol rubber powder,
42 parts of silicate foam cement powder.
Embodiment 2
Putty for interior wall powder, the most composed of the following components:
1 part of alkylolamides polyethylene oxide ether,
0.8 part of sodium polyacrylate,
1.5 parts of alkyl sulfate sodium,
1.3 parts of normal-butyl sodium naphthalene sulfonates,
1.5 parts of isomerous tridecanol polyoxyethylene ethers,
0.6 part of cerous carbonate,
3.8 parts of wood fibres,
18 parts of sepiolite powders,
28 parts cold melts polyvinyl alcohol rubber powder,
42 parts of silicate foam cement powder.
Embodiment 3
Putty for interior wall powder, the most composed of the following components:
2 parts of alkylolamides polyethylene oxide ethers,
0.8 part of sodium polyacrylate,
1.5 parts of alkyl sulfate sodium,
1.3 parts of normal-butyl sodium naphthalene sulfonates,
1.5 parts of isomerous tridecanol polyoxyethylene ethers,
0.6 part of cerous carbonate,
3.8 parts of wood fibres,
18 parts of sepiolite powders,
28 parts cold melts polyvinyl alcohol rubber powder,
42 parts of silicate foam cement powder.
Embodiment 4
Putty for interior wall powder, the most composed of the following components:
1.2 parts of alkylolamides polyethylene oxide ethers,
0.8 part of sodium polyacrylate,
1.5 parts of alkyl sulfate sodium,
1.3 parts of normal-butyl sodium naphthalene sulfonates,
1.5 parts of isomerous tridecanol polyoxyethylene ethers,
0.6 part of cerous carbonate,
3.8 parts of wood fibres,
18 parts of sepiolite powders,
28 parts cold melts polyvinyl alcohol rubber powder,
42 parts of silicate foam cement powder.
Powder of lacquer putty for use in the various embodiments described above, good leveling property, adhesive force is strong, water-tolerant, and intensity is high, and resistance to polishing is resistance to
The change of acid and alkali corrosion, high-low temperature resistant, resistance to go mouldy, without hollowing, peeling, be full of cracks, obscission after being made moist by water, also without turning to be yellow,
Mould, a black speck phenomenon.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. putty for interior wall powder, it is characterised in that the most composed of the following components:
1~2 part of alkylolamides polyethylene oxide ether,
0.8 part of sodium polyacrylate,
1.5 parts of alkyl sulfate sodium,
1.3 parts of normal-butyl sodium naphthalene sulfonates,
1.5 parts of isomerous tridecanol polyoxyethylene ethers,
0.6 part of cerous carbonate,
3.8 parts of wood fibres,
18 parts of sepiolite powders,
28 parts cold melts polyvinyl alcohol rubber powder,
42 parts of silicate foam cement powder.
Putty for interior wall powder the most according to claim 1, it is characterised in that the most composed of the following components:
1 part of alkylolamides polyethylene oxide ether,
0.8 part of sodium polyacrylate,
1.5 parts of alkyl sulfate sodium,
1.3 parts of normal-butyl sodium naphthalene sulfonates,
1.5 parts of isomerous tridecanol polyoxyethylene ethers,
0.6 part of cerous carbonate,
3.8 parts of wood fibres,
18 parts of sepiolite powders,
28 parts cold melts polyvinyl alcohol rubber powder,
42 parts of silicate foam cement powder.
Putty for interior wall powder the most according to claim 1, it is characterised in that the most composed of the following components:
2 parts of alkylolamides polyethylene oxide ethers,
0.8 part of sodium polyacrylate,
1.5 parts of alkyl sulfate sodium,
1.3 parts of normal-butyl sodium naphthalene sulfonates,
1.5 parts of isomerous tridecanol polyoxyethylene ethers,
0.6 part of cerous carbonate,
3.8 parts of wood fibres,
18 parts of sepiolite powders,
28 parts cold melts polyvinyl alcohol rubber powder,
42 parts of silicate foam cement powder.
Putty for interior wall powder the most according to claim 1, it is characterised in that the most composed of the following components:
1.2 parts of alkylolamides polyethylene oxide ethers,
0.8 part of sodium polyacrylate,
1.5 parts of alkyl sulfate sodium,
1.3 parts of normal-butyl sodium naphthalene sulfonates,
1.5 parts of isomerous tridecanol polyoxyethylene ethers,
0.6 part of cerous carbonate,
3.8 parts of wood fibres,
18 parts of sepiolite powders,
28 parts cold melts polyvinyl alcohol rubber powder,
42 parts of silicate foam cement powder.