CN106189341A - A kind of high-elasticity rubber - Google Patents
A kind of high-elasticity rubber Download PDFInfo
- Publication number
- CN106189341A CN106189341A CN201610563790.3A CN201610563790A CN106189341A CN 106189341 A CN106189341 A CN 106189341A CN 201610563790 A CN201610563790 A CN 201610563790A CN 106189341 A CN106189341 A CN 106189341A
- Authority
- CN
- China
- Prior art keywords
- parts
- elasticity rubber
- elasticity
- firebrake
- toughener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-elasticity rubber, weight proportion is as follows: latex 10 parts;Firebrake ZB 10 15 parts;Nanometer grade silica 2 parts;50 parts of water;Toughener 5 10 parts, according to the above ratio, stirs and i.e. obtains a kind of high-elasticity rubber;The present invention can improve the elasticity of elastic gum.
Description
Technical field
The present invention relates to field of compound material, be specifically related to a kind of high-elasticity rubber.
Background technology
The elastic gum intensity of traditional chemical crosslinking is the highest, shows as glue the most crisp, and intensity is the lowest, it is difficult to meet in some application
Stress and the requirement of deformation, existing elastic gum elasticity is poor, by bigger pressure time, easily make object fracture or damage
Bad, can not meet use requirement, limit elastic gum application in many aspects.
Summary of the invention
It is an object of the invention to provide a kind of high-elasticity rubber, the elasticity of elastic gum can be improved.
A kind of high-elasticity rubber, weight proportion is as follows:
Latex 10 parts;
Firebrake ZB 10-15 part;
Nanometer grade silica 2 parts;
50 parts of water;
Toughener 5-10 part
According to the above ratio, stir and i.e. obtain a kind of high-elasticity rubber.
The present invention is by adding invention by adding Firebrake ZB, toughener so that this glue has good high resiliency advantage,
Add nanometer grade silica, improve the activity of material surface, reach the material cohesive force to basic unit, reinforcing material simultaneously
Inter-layer bonding force, meet use requirement, be with a wide range of applications.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment one: a kind of high-elasticity rubber, weight proportion is as follows: latex 10 parts;Firebrake ZB 10 parts;Nanoscale titanium dioxide
Silicon 2 parts;50 parts of water;Toughener 5 parts.According to the above ratio, stir and i.e. obtain a kind of high-elasticity rubber.
Embodiment two: a kind of high-elasticity rubber, weight proportion is as follows: latex 10 parts;Firebrake ZB 10 parts;Nanoscale titanium dioxide
Silicon 2 parts;50 parts of water;Toughener 10 parts.According to the above ratio, stir and i.e. obtain a kind of high-elasticity rubber.
Embodiment three: a kind of high-elasticity rubber, weight proportion is as follows: latex 10 parts;Firebrake ZB 13 parts;Nanoscale titanium dioxide
Silicon 2 parts;50 parts of water;Toughener 8 parts.According to the above ratio, stir and i.e. obtain a kind of high-elasticity rubber.
Embodiment four: a kind of high-elasticity rubber, weight proportion is as follows: latex 10 parts;Firebrake ZB 15 parts;Nanoscale titanium dioxide
Silicon 2 parts;50 parts of water;Toughener 5 parts.According to the above ratio, stir and i.e. obtain a kind of high-elasticity rubber.
Embodiment five: a kind of high-elasticity rubber, weight proportion is as follows: latex 10 parts;Firebrake ZB 15 parts;Nanoscale titanium dioxide
Silicon 2 parts;50 parts of water;Toughener 5 parts.According to the above ratio, stir and i.e. obtain a kind of high-elasticity rubber.
In addition to the implementation, the present invention can also have other embodiments, all employing equivalents or equivalent transformation shape
The technical scheme become, all falls within the protection domain of application claims.
Claims (1)
1. a high-elasticity rubber, it is characterised in that: weight proportion is as follows:
Latex 10 parts;
Firebrake ZB 10-15 part;
Nanometer grade silica 2 parts;
50 parts of water;
Toughener 5-10 part
According to the above ratio, stir and i.e. obtain a kind of high-elasticity rubber.