CN106187104A - Low-loss temperature-stabilized dielectric constant microwave dielectric ceramic Li2caMgGeO5 - Google Patents
Low-loss temperature-stabilized dielectric constant microwave dielectric ceramic Li2caMgGeO5 Download PDFInfo
- Publication number
- CN106187104A CN106187104A CN201610571750.3A CN201610571750A CN106187104A CN 106187104 A CN106187104 A CN 106187104A CN 201610571750 A CN201610571750 A CN 201610571750A CN 106187104 A CN106187104 A CN 106187104A
- Authority
- CN
- China
- Prior art keywords
- hours
- camggeo
- dielectric ceramic
- low
- dielectric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of low-loss temperature-stabilized dielectric constant microwave dielectric ceramic Li2CaMgGeO5And preparation method thereof.(1) by Li that purity is more than 99.9% (percentage by weight)2CO3、CaCO3, MgO and GeO2Starting powder press Li2CaMgGeO5Composition weigh dispensing;(2) by step (1) raw material wet ball-milling mix 12 hours, ball-milling medium is distilled water, after drying in 1100 DEG C of air atmosphere pre-burning 6 hours;(3) after adding binding agent pelletize in the powder that step (2) prepares, re-compacted molding, finally sinter 4 hours in 1150~1200 DEG C of air atmosphere;Described binding agent uses mass concentration to be the poly-vinyl alcohol solution of 5%, and the addition of polyvinyl alcohol accounts for the 3% of powder gross mass.Pottery prepared by the present invention sinters well below 1200 DEG C, and dielectric constant reaches 20.0~20.7, and its quality factor q f value is up to 86000 108000GHz, and temperature coefficient of resonance frequency is little, industrially has great using value.
Description
Technical field
The present invention relates to dielectric ceramic material, particularly relate to for manufacturing ceramic resonator and the filter that microwave frequency uses
Dielectric ceramic materials of microwave device such as ripple device and preparation method thereof.
Background technology
Microwave dielectric ceramic refers to be applied in microwave frequency band (mainly UHF and SHF frequency range) circuit as dielectric material
And complete the pottery of one or more functions, modern communication is widely used as resonator, wave filter, dielectric substrate and medium
The components and parts such as wave circuit, are the key foundation materials of modern communication technology, in portable mobile phone, automobile telephone, nothing
The aspect such as rope phone, television satellite accepter and military radar has highly important application, small-sized at modern communication instrument
Change, integrated during just playing increasing effect.
It is applied to the dielectric ceramic of microwave frequency band, should meet the requirement of following dielectric property: (1) seriation DIELECTRIC CONSTANT εr
To adapt to different frequency and the requirement of different application occasion;(2) high quality factor q value or low dielectric loss tan δ are to reduce
Noise, typically requires Qf >=3000GHz;(3) the temperature coefficient τ of resonant frequencyfThe least to ensure the heat that device has had
Stability ,-10ppm/ DEG C≤τ of general requirementf≤+10ppm/℃.Just have tried to electricity from late 1930s in the world
Dielectric material is applied to microwave technology, and prepares TiO2Microwave dielectric filter, but its temperature coefficient of resonance frequency τfToo big and
Cannot be practical.Since the seventies in last century, start the large-scale development to medium ceramic material, according to being relatively situated between
Electric constant εrSize different from use frequency range, generally can will have been developed that and the microwave-medium ceramics developed be divided into 4
Class.
(1) ultralow dielectric microwave dielectric ceramic, main representative is Al2O3-TiO2、Y2BaCuO5、MgAl2O4With
Mg2SiO4Deng, its εr≤ 20, quality factor q × f >=50000GHz, τf≤10ppm/℃.It is mainly used in microwave base plate and height
End microwave device.
(2) low εrWith the microwave dielectric ceramic of high q-factor, mainly BaO-MgO-Ta2O5,BaO-ZnO-Ta2O5Or BaO-
MgO-Nb2O5,BaO-ZnO-Nb2O5System or the hybrid system MWDC material between them.Its εr=20~35, Q=(1~2)
×104(under f >=10GHz), τf≈0.In the microwave communication equipments such as the direct broadcasting satellite being mainly used in f >=8GHz humorous as medium
Shake device.
(3) medium εrWith the microwave dielectric ceramic of Q-value, it is mainly with BaTi4O9、Ba2Ti9O20(Zr, Sn) TiO4Etc. for
The MWDC material of base, its εr=35~45, Q=(6~9) × 103(under f=3~-4GHz), τf≤5ppm/℃.Main use
As dielectric resonance device in microwave military radar in 4~8GHz frequency ranges and communication system.
(4) high εrAnd the microwave dielectric ceramic that Q-value is relatively low, in being mainly used in 0.8~4GHz frequency range, civilian movement is led to
News system, this is also the emphasis of microwave dielectric ceramic research.Since the eighties, Kolar, Kato et al. in succession find and have studied
Perovskite-like tungsten bronze type BaO Ln2O3—TiO2Series (Ln=La, Sm, Nd or Pr etc. are called for short BLT system), composite perofskite
Structure C aO Li2O—Ln2O3—TiO2Series, lead base series material, Ca1-xLn2x/3TiO3It is contour εrMicrowave dielectric ceramic,
The wherein BaO Nd of BLT system2O3—TiO2Material dielectric constant reaches 90, lead base series (Pb, Ca) ZrO3Dielectric constant reaches
To 105.
The sintering temperature of the above material system is generally greater than 1300 DEG C, it is impossible to directly and the low-melting-point metal such as Ag and Cu
Burn altogether and form multilayer ceramic capacitor.In recent years, along with LTCC Technology (Low Temperature Co-fired
Ceramics, LTCC) development and microwave multilayer device development requirement, research worker both domestic and external is to some low grade fever's system materials
Material has carried out exploring widely and studying, and mainly uses devitrified glass or glassceramic composites system, because of low melting point glass
Glass has of a relatively high dielectric loss mutually, and the existence of glass phase substantially increases the dielectric loss of material.Therefore develop without glass
The low fired microwave dielectric ceramic material of glass phase is the emphasis of current research.
Explore novel with exploitation can be during low fired microwave dielectric ceramic materials, the Li base that intrinsic sintering temperature is low
The material systems such as compound, Bi based compound, tungstates architecture compound and tellurate architecture compound get the attention with
Research, but due to three performance indications (ε of microwave dielectric ceramicrWith Q f and τfIt is that the relation of mutually restriction is (see literary composition between)
Offer: the restricting relation between microwave dielectric ceramic materials dielectric properties, Zhu Jianhua, Liang Fei, Wang little Hong, Lv Wenzhong, electronic component with
Material, phase March the 3rd in 2005), meet three performance requirements and the single-phase microwave-medium ceramics of low temperature sintering is considerably less, main
Cannot application request if their temperature coefficient of resonance frequency is the most excessive or quality factor are on the low side.At present to micro-
The research major part of ripple media ceramic is the summary of experience drawn by great many of experiments, does not but have complete theory micro-to illustrate
See the relation of structure and dielectric properties, therefore, the most also cannot predict its resonance frequency from the composition of compound with structure
The microwave dielectric properties such as rate temperature coefficient and quality factor, which greatly limits low temperature co-fired technology and microwave multilamellar
The development of device.Explore and low-temperature sintering can have near-zero resonance frequency temperature coefficient (-10ppm/ DEG C≤τ with exploitation simultaneouslyf≤
+ 10ppm/ DEG C) it is that those skilled in the art thirst for solving always but are difficult to all the time with the microwave dielectric ceramic of higher figure of merit
The difficult problem succeeded.We are to consisting of Li2CaMgGeO5And Li2CaZnGeO5Pottery carried out sintering and micro-wave dielectric
Performance study, finds that their sintering temperature is less than 1200 DEG C, wherein Li2CaMgGeO5There is near-zero resonance frequency temperature coefficient
With high quality factor, Li2CaZnGeO5Pottery is quasiconductor, and it is big and do not have resonance peak at microwave frequency band dielectric loss, therefore without
Method as can be practical microwave-medium ceramics.
Summary of the invention
It is an object of the invention to provide and a kind of there is good heat stability and low-loss dielectric constant microwave dielectric
Ceramic material and preparation method thereof.
The chemical composition of the microwave dielectric ceramic material of the present invention is Li2CaMgGeO5。
The preparation method step of this microwave dielectric ceramic material is:
(1) by Li that purity is more than 99.9% (percentage by weight)2CO3、CaCO3, MgO and GeO2Starting powder press
Li2CaMgGeO5Composition weigh dispensing.
(2) being mixed 12 hours by step (1) raw material wet ball-milling, ball-milling medium is distilled water, big at 1100 DEG C after drying
Pre-burning 6 hours in gas atmosphere.
(3) after adding binding agent pelletize in the powder that step (2) prepares, re-compacted molding, finally 1150~
1200 DEG C of air atmosphere sinter 4 hours;Described binding agent uses mass concentration to be the poly-vinyl alcohol solution of 5%, polyethylene
Alcohol addition accounts for the 3% of powder gross mass.
Advantages of the present invention: Li2CaMgGeO5Ceramic sintering temperature is relatively low, and cost of material is low;Its quality factor q f value is up to
86000-108000GHz, dielectric constant reaches 20.0~20.7, the temperature coefficient τ of its resonant frequencyfLittle, temperature stability is good;
Can be widely used for the manufacture of the microwave devices such as various dielectric resonator and wave filter, low temperature co-fired technology and microwave multilamellar can be met
The technology of device needs.
Detailed description of the invention
Embodiment:
Table 1 shows 3 specific embodiments and the microwave dielectric property thereof of the different sintering temperatures constituting the present invention.Its system
Preparation Method as it has been described above, carry out the evaluation of microwave dielectric property by cylindrical dielectric resonator method.
This pottery can be widely used for the manufacture of the microwave devices such as various dielectric resonator and wave filter, can meet mobile communication
Need with the technology of the system such as satellite communication.
Table 1:
Claims (1)
1. a high quality factor temperature-stable dielectric constant microwave dielectric ceramic, it is characterised in that described micro-wave dielectric is made pottery
The chemical composition of porcelain is: Li2CaMgGeO5;
The preparation method of described microwave dielectric ceramic concretely comprises the following steps:
(1) by Li that purity is more than 99.9% (percentage by weight)2CO3、CaCO3, MgO and GeO2Starting powder press
Li2CaMgGeO5Composition weigh dispensing;
(2) being mixed 12 hours by step (1) raw material wet ball-milling, ball-milling medium is distilled water, at 1100 DEG C of air gas after drying
Pre-burning 6 hours in atmosphere;
(3), after adding binding agent pelletize in the powder that step (2) prepares, re-compacted molding, finally at 1150~1200 DEG C
Air atmosphere sinters 4 hours;Described binding agent uses mass concentration to be the poly-vinyl alcohol solution of 5%, and polyvinyl alcohol adds
Amount accounts for the 3% of powder gross mass.