CN106181787A - A kind of preparation method of the composite fibre matrix emery wheel of energy synchronous consumption - Google Patents
A kind of preparation method of the composite fibre matrix emery wheel of energy synchronous consumption Download PDFInfo
- Publication number
- CN106181787A CN106181787A CN201610582701.XA CN201610582701A CN106181787A CN 106181787 A CN106181787 A CN 106181787A CN 201610582701 A CN201610582701 A CN 201610582701A CN 106181787 A CN106181787 A CN 106181787A
- Authority
- CN
- China
- Prior art keywords
- emery wheel
- matrix
- preparation
- abrasive material
- natural fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of can the preparation method of composite fibre matrix emery wheel of synchronous consumption, comprise the following steps: step one, respectively by glass fabric, natural fiber cloth by cement dipping machine coated with resins；Step 2, by having coated resin fiberglass cloth, natural fiber cloth be laminated into the composite sheet of some layers；Step 3, composite sheet cutting, shape, solidify to form matrix, be connected by binding agent and emery wheel abrasive material again and become emery wheel, or, composite sheet directly, after sizing cutting become matrix, by press, the abrasive material mixing resin being pressed into one again, final curing molding becomes emery wheel.Present invention glass fabric and natural fiber cloth is hybrid laminated makes matrix, can there is enough intensity that emery wheel abrasive material is made well support, meet use requirement, matrix can grinding consumption Tong Bu with emery wheel abrasive material, abrasive material, good damping effect can be taken turns by propping sand constantly, effectively stop butterfly-shaped shortbread phenomenon, the utilization rate of emery wheel is higher, and utilization rate is up to more than 80%.
Description
Technical field
The present invention relates to a kind of resin wheel, the preparation side of the composite fibre matrix emery wheel of a kind of energy synchronous consumption
Method.
Background technology
In prior art, resin wheel is the emery wheel being made with emery wheel abrasive material as bonding agent with resin.
Conventional resin wheel becomes emery wheel with some groups of glass fabrics, emery wheel abrasive material compacting sintering.It grinds in reality
When cutting use, when especially marginal position grinding obtains relatively thin, being very easy to edge butterfly-shaped shortbread, (lacking block), even generation emery wheel are quick-fried
The phenomenon split, it is impossible to continue safe handling, cause utilization rate the lowest.
If the matrix that the resin wheel also having is made by using dried layer glass fabric, re-compacted, bonded abrasive wheel abrasive material
Layer thus make emery wheel.Because of glass fibre as support substrate, its intensity, durability have promoted, but glass fibers
Wiki body is difficult to and emery wheel synchronous consumption, and matrix easily produces alice phenomenon, so it is existing to be effectively improved very much above-mentioned butterfly-shaped shortbread
As, grinding efficiency is the lowest.
Accordingly, it would be desirable to improve further.
Summary of the invention
It is an object of the invention to provide a kind of mechanical strength high, easy grinding, matrix can be with emery wheel synchronous consumption, matrixes
Edge to emery wheel good supporting force, utilization rate high can the preparation method of composite fibre matrix emery wheel of synchronous consumption, existing to overcome
There is the weak point in technology.
The object of the present invention is achieved like this:
The preparation method of the composite fibre matrix emery wheel of a kind of energy synchronous consumption, it is characterised in that comprise the following steps:
Step one, respectively by glass fabric, natural fiber cloth by cement dipping machine coated with resins；
Step 2, by having coated resin fiberglass cloth, natural fiber cloth be laminated into the composite sheet of some layers；
Step 3, composite sheet cutting, shape, solidify to form matrix, then be connected with emery wheel abrasive material by binding agent and become sand
Wheel, or, composite sheet directly, after sizing cutting become matrix, then the emery wheel abrasive material of resin will be mixed by press and be laminated
Being formed integrally, final curing molding becomes emery wheel.
When described glass fabric, natural fiber cloth are by cement dipping machine coated with resins, coloring agent can be added.
Described emery wheel abrasive material can add coloring agent.
Described resin is alcohol-soluble resin or water-soluble resin.
The solidification temperature of described resin is 70-200 degree.
If if described composite sheet is made up of dried layer glass fabric and dried layer natural fiber cloth.
The number of plies of described composite sheet is 1-10 layer.
Beneficial effects of the present invention is as follows:
With glass fabric with natural fiber cloth is hybrid laminated makes matrix, it is possible to there is enough intensity that emery wheel abrasive material is made
Well supporting, meet use requirement, matrix can grinding consumption Tong Bu with emery wheel abrasive material, it is possible to propping sand disc sharpener constantly
The bed of material, good damping effect, effectively stop butterfly-shaped shortbread phenomenon, the utilization rate of emery wheel is higher, and utilization rate is up to more than 80%.
It addition, use the grinding wheel base body of the present invention, can be made into the emery wheel of various model, such as T27 type, T28 type and T29 type
Emery wheel, meets more use occasion.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
The preparation method of the composite fibre matrix emery wheel of energy synchronous consumption, it is characterised in that comprise the following steps:
Step one, respectively by glass fabric, natural fiber cloth by cement dipping machine coated with resins；
Step 2, by having coated resin fiberglass cloth, natural fiber cloth be laminated into the composite sheet of some layers；
Step 3, composite sheet cutting, shape, solidify to form matrix, then be connected with emery wheel abrasive material by binding agent and become sand
Wheel, or, composite sheet directly, after sizing cutting become matrix, then the emery wheel abrasive material of resin will be mixed by press and be laminated
Being formed integrally, final curing molding becomes emery wheel.
During they solidifications, mould one curing molding can be used, in hgher efficiency.Matrix can realize same with emery wheel abrasive material
Step consumes, and can reduce vibrations, plasticity higher, it is possible to making the emery wheel of Multiple Type, emery wheel abrasive material surface is also during work
Various decorative pattern can be extruded.
By using this technical scheme, the matrix of gained by relative glass fabric and natural fiber cloth hybrid laminated and
Becoming, it is compared with the matrix that pure glass fabric is made, and is more prone to grinding and ensure that its mechanical strength simultaneously, keeps
It meets use requirement to the support degree of emery wheel abrasive material, and can damping further, matrix can be with attached thereto
Emery wheel abrasive material synchronous consumption make the utilization rate of emery wheel higher, utilization rate is up to more than 80%.
Preferably, when glass fabric, natural fiber cloth are by cement dipping machine coated with resins, also can add coloring agent, help
Matrix is dyed different colours, and emery wheel abrasive material can also add coloring agent, emery wheel is dyed different colours.
Preferably, resin is alcohol-soluble resin or water-soluble resin, such as phenolic resin, epoxy resin, Lauxite etc..
Preferably, the solidification temperature of resin is 70-200 degree, and relatively low solidification temperature makes processing cost lower, and matrix is more
Add reliable and stable.
Preferably, if if composite sheet is made up of dried layer glass fabric and dried layer natural fiber cloth.State composite sheet
The number of plies is 1-10 layer.Composite sheet has multiple stacked combination mode.Such as, the top layer of composite sheet and bottom are by glass fibers
Dimension sheet material is constituted, and this technical scheme makes the support degree of matrix more preferably, and the intermediate layer of composite sheet is at least by natural fiber sheet material
Constituting, be very easy to grinding, for another example, intermediate layer is preferably 2 layers or 3 layers of natural fiber sheet materials composition, it also may be preferable for be 2 layers of sky
So fibre sheet material and 1 layer of glass fibre sheet are constituted, and now, set for interval between natural fiber sheet material and glass fibre sheet
Putting, also can there be more combining form in certain intermediate layer, and those skilled in the art is all appreciated that.
The above-mentioned preferred version for the present invention, has been shown and described the ultimate principle of the present invention, principal character and the present invention
Advantage.Those skilled in the art it should be recognized that the present invention is not restricted to the described embodiments, above-described embodiment and description
Described in the principle that the present invention is simply described, the present invention also has various without departing from the spirit and scope of the present invention
Changes and improvements, these changes and improvements both fall within scope of the claimed invention.Claimed scope is by institute
Attached claims and equivalent thereof define.
Claims (7)
1. the preparation method of the composite fibre matrix emery wheel of an energy synchronous consumption, it is characterised in that comprise the following steps:
Step one, respectively by glass fabric, natural fiber cloth by cement dipping machine coated with resins；
Step 2, by having coated resin fiberglass cloth, natural fiber cloth be laminated into the composite sheet of some layers；
Step 3, composite sheet cutting, shape, solidify to form matrix, then be connected with emery wheel abrasive material by binding agent and become sand
Wheel, or, composite sheet directly, after sizing cutting become matrix, then the emery wheel abrasive material of resin will be mixed by press and be laminated
Being formed integrally, final curing molding becomes emery wheel.
The most according to claim 1 can the preparation method of composite fibre matrix emery wheel of synchronous consumption, it is characterised in that: described
When glass fabric, natural fiber cloth are by cement dipping machine coated with resins, coloring agent can be added.
The most according to claim 1 can the preparation method of composite fibre matrix emery wheel of synchronous consumption, it is characterised in that: described
Emery wheel abrasive material can add coloring agent.
The most according to claim 1 can the preparation method of composite fibre matrix emery wheel of synchronous consumption, it is characterised in that: described
Resin is alcohol-soluble resin or water-soluble resin.
The most according to claim 1 can the preparation method of composite fibre matrix emery wheel of synchronous consumption, it is characterised in that: described
The solidification temperature of resin is 70-200 degree.
6. according to the preparation method of the composite fibre matrix emery wheel of energy synchronous consumption, its feature described in any one of claim 1-5
It is: if if described composite sheet is made up of dried layer glass fabric and dried layer natural fiber cloth.
The most according to claim 6 can the preparation method of composite fibre matrix emery wheel of synchronous consumption, it is characterised in that: described
The number of plies of composite sheet is 1-10 layer.