CN106178054A - A kind of production method of concave-convex rod deodorant agent for refrigerator - Google Patents
A kind of production method of concave-convex rod deodorant agent for refrigerator Download PDFInfo
- Publication number
- CN106178054A CN106178054A CN201510217697.2A CN201510217697A CN106178054A CN 106178054 A CN106178054 A CN 106178054A CN 201510217697 A CN201510217697 A CN 201510217697A CN 106178054 A CN106178054 A CN 106178054A
- Authority
- CN
- China
- Prior art keywords
- refrigerator
- concave
- convex rod
- attapulgite clay
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the production method of a kind of concave-convex rod deodorant agent for refrigerator, its technical scheme is characterized by, concave-convex rod deodorant agent for refrigerator is made up of attapulgite clay, bentonite, anhydrite, calcium chloride, calcium oxide, wood flour, rice hulls or Plant fiber, acidified process, pulverizing, pelletize roasting, be packaged as finished product.Its feature: surface light and do not slide, the most coarse hard, specific surface area is big, and porosity is high, deodorant effect is obvious, indeformable during use, do not lump, not heat release, will not become liquid, and also will not produce powder etc. pollutes, and cost is the cheapest.It is mainly used in houshold refrigerator, restaurant refrigerator-freezer, various freezer and needs the place of deodorization and peculiar smell suction.The spraying of all kinds of liquid flavor, spice or deodorant can also be accepted, for processing the place with special odor as a kind of carrier.
Description
Technical field
The present invention relates to deodorant, be specifically related to the production method of a kind of concave-convex rod deodorant agent for refrigerator.
Background technology
The deodorant for refregerator odor absorber kind developed is more, mainly has calcium chloride, silica gel, calcium oxide, activated carbon, Linesless charcoal and bamboo charcoal etc..These deodorant for refregerator odor absorbers have their own characteristics each, through repeatedly putting into practice, conventional deodorant for refregerator odor absorber is analyzed: the moisture absorption odor-absorbing of calcium chloride and calcium oxide can be preferably, but owing to refrigerator humidity is relatively large, liquid is i.e. become after the calcium chloride moisture absorption, easily pollute food in refrigerator, after the calcium oxide moisture absorption, i.e. become powder, food in same easily pollution refrigerator；Activated carbon and bamboo charcoal using effect are also good, but are once easy for caking after the moisture absorption, thus affects adsorption effect, it is impossible to continue deodorization, and have the dust of black, formation secondary pollution.Calcium chloride, activated carbon and bamboo charcoal price are higher, and the price of calcium oxide is relatively low.
Summary of the invention
It is an object of the invention to overcome weak point in prior art, it is provided that the production method of a kind of concave-convex rod deodorant agent for refrigerator.
The concave-convex rod deodorant agent for refrigerator of the present invention is made up of attapulgite clay, bentonite, anhydrite, calcium chloride, calcium oxide, wood flour, rice hulls or Plant fiber, after attapulgite clay and bentonite acidifying are dried, pulverizing common with anhydrite, calcium chloride, calcium oxide, wood flour, rice hulls or Plant fiber, through pelletize roasting, it is packaged as finished product.
Attapulgite clay is a kind of aqueous magnesium alumino metasilicate salt mine, and it has the performances such as good deodorization and absorption, and due to attapulgite clay internal porous road, specific surface area is big, up to 500m2/ more than g, most cation, hydrone and a certain size organic molecule all can directly be adsorbed in inlet hole road, and be difficult to be flocculated by electrolyte；Bentonite and anhydrite plasticity are good, intensity is high, the ability of deodorant can be increased, the moisture pick-up properties of calcium chloride and calcium oxide is preferable, wood flour, rice hulls or Plant fiber, carry out imperfect combustion, the characteristic of the most active charcoal in granule, and be conducive to being formed hole in granule, to strengthen the effect of the deodorant of granule.
The technical scheme is that:
1, selecting materials: attapulgite clay and bentonite dry after weathering 20～60 days, moisture answers≤13%.
2, dispensing (1) (percentage by weight): attapulgite clay 30～50%, bentonite 10～25%, water 33～50%, sulphuric acid (concentration is 98%) 0.5～2%, each component summation=100% (weight).
3, acidifying: sulphuric acid is sprayed on attapulgite clay and bentonite after dilution, after piling up 24～48 hours, stir with blender, in input twin rollers, it is squeezed into attapulgite clay and the bentonite flaky mixture of thickness≤2.5mm, and it being transported to dry in the sun on cement floor, the moisture after drying answers≤13%.
4, dispensing (2) (percentage by weight): attapulgite clay and bentonitic flaky mixture 70～85%, anhydrite 2～8%, calcium chloride 2～10%, calcium oxide 2～10%, wood flour (rice hulls or Plant fiber) 2～15%.
5, the common pulverizing of mixture of dispensing (2), fineness≤0.074mm, carry out pelletize with granulating disc or sugar coating machine; Task-size Controlling is 0.5～3mm, and sintering temperature controls at 350～400 DEG C, the granule after roasting; moisture answers≤1%, and sieves rapidly, is packaged as finished product.
The feature of the concave-convex rod deodorant agent for refrigerator of the present invention: particle surface light and do not slide, the most coarse hard, specific surface area is big, porosity is high, deodorant effect obvious, indeformable during use, do not lump, not heat release, will not become liquid, also will not produce powder etc. and pollute, granule drying after using, can repeatedly Reusability, cost is the cheapest, and its cost only has the 8～15% of activated carbon.
Concave-convex rod deodorant agent for refrigerator, is mainly used in houshold refrigerator, restaurant refrigerator-freezer, various freezer and needs the place of deodorization and peculiar smell suction.The spraying of all kinds of liquid flavor, spice or deodorant can also be accepted, for processing the place with special odor as a kind of carrier.Lose the granule of deodorant effect, can be used for planting flowers and plants, or as general waste treatment.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described:
1, selecting materials: choose the preferable attapulgite clay of absorption property and bentonite, dry after weathering 20～60 days, moisture answers≤13%.
2, dispensing (1) (percentage by weight): attapulgite clay 45%, bentonite 10%, water 43%, sulphuric acid (concentration is 98%) 2%.
3, acidifying: attapulgite clay and bentonitic pH value all >=7.5, in order to improve attapulgite clay and bentonitic activity, adjusting its pH value, need to carry out acidification, sulphuric acid is sprayed on attapulgite clay and bentonite after dilution, after piling up 24～48 hours, stir with blender, in input twin rollers, be squeezed into attapulgite clay and the bentonite flaky mixture of thickness≤2.5mm, and it being transported to dry in the sun on cement floor, the moisture after drying answers≤13%.
4, dispensing (2) (percentage by weight): attapulgite clay and bentonitic flaky mixture 80%, anhydrite 3%, calcium chloride 6%, calcium oxide 5%, wood flour (rice hulls or Plant fiber) 6%.
5, the common pulverizing of mixture of dispensing (2), fineness≤0.074mm, carry out pelletize with granulating disc or sugar coating machine; Task-size Controlling is 0.5～3mm, and sintering temperature controls at 350～400 DEG C, the granule after roasting; moisture answers≤1%, and sieves rapidly, is packaged as finished product.
Claims (6)
1. the production method of a concave-convex rod deodorant agent for refrigerator, it is characterised in that concave-convex rod deodorant agent for refrigerator be by attapulgite clay, bentonite, anhydrite, calcium chloride, calcium oxide, wood flour,
After rice hulls or Plant fiber's composition, attapulgite clay and bentonite acidifying are dried, pulverizing common with anhydrite, calcium chloride, calcium oxide, wood flour, rice hulls or Plant fiber, through pelletize roasting, it is packaged as finished product.
The production method of a kind of concave-convex rod deodorant agent for refrigerator the most according to claim 1, it is characterised in that attapulgite clay and bentonite dry after weathering 20～60 days, moisture answers≤13%.
The production method of a kind of concave-convex rod deodorant agent for refrigerator the most according to claim 1, it is characterized in that, dispensing (1) (percentage by weight): attapulgite clay 30～50%, bentonite 10～25%, water 33～50%, sulphuric acid (concentration is 98%) 0.5～2%, each component summation=100% (weight).
The production method of a kind of concave-convex rod deodorant agent for refrigerator the most according to claim 1, it is characterized in that, sulphuric acid is sprayed on attapulgite clay and bentonite after dilution, after piling up 24～48 hours, stir with blender, in input twin rollers, be squeezed into attapulgite clay and the bentonite flaky mixture of thickness≤2.5mm, and it being transported to dry in the sun on cement floor, the moisture after drying answers≤13%.
The production method of a kind of concave-convex rod deodorant agent for refrigerator the most according to claim 1, it is characterized in that, dispensing (2) (percentage by weight): attapulgite clay and bentonitic flaky mixture 70～85 %, anhydrite 2～8%, calcium chloride 2～10%, calcium oxide 2～10%, wood flour (rice hulls or Plant fiber) 2～15%.
The production method of a kind of concave-convex rod deodorant agent for refrigerator the most according to claim 1; it is characterized in that; the common pulverizing of mixture of dispensing (2); fineness≤0.074mm; pelletize is carried out with granulating disc or sugar coating machine; Task-size Controlling is 0.5～3mm, and sintering temperature controls at 350～400 DEG C, after roasting
Granule, moisture is answered≤1%, and is sieved rapidly, is packaged as finished product.