CN106167939A - The production method of far infrared yarn wire fabric - Google Patents
The production method of far infrared yarn wire fabric Download PDFInfo
- Publication number
- CN106167939A CN106167939A CN201610641638.2A CN201610641638A CN106167939A CN 106167939 A CN106167939 A CN 106167939A CN 201610641638 A CN201610641638 A CN 201610641638A CN 106167939 A CN106167939 A CN 106167939A
- Authority
- CN
- China
- Prior art keywords
- far infrared
- production method
- yarn
- wire fabric
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the production method of a kind of far infrared yarn wire fabric, use tight SEILE textile technology, 71wt% Mei Yabi acrylic fiber, 29wt% viscose fiber blending are become functional yarn, then prepare fabric with functional yarn for raw material.The production method of far infrared yarn wire fabric of the present invention, it can produce the functional yarn with the health-care effect such as soft and smooth, warming, anti pilling, antistatic, far infrared and fabric.
Description
Technical field
The present invention relates to the production method of far infrared yarn wire fabric.
Background technology
Along with improving constantly of living standard, people have higher pursuit, clothing to class and the requirement of dress ornament
Fabric is not only embodied in appearance, and what is more important presses close to the real daily life of consumer, adapts to consumer demand, various
Change.
Summary of the invention
It is an object of the invention to provide the production method of a kind of far infrared yarn wire fabric, its can produce with soft and smooth,
The functional yarn of the health-care effects such as warming, anti pilling, antistatic, far infrared and fabric.
For achieving the above object, the technical scheme is that the production method designing a kind of far infrared yarn wire fabric, adopt
By tight SEILE textile technology, 71wt% Mei Yabi acrylic fiber, 29wt% viscose fiber blending are become functional yarn, then with function yarn
Line is that fabric prepared by raw material.
Described Mei Yabi acrylic fiber is Mitsubishi Li Yang company " Mei Yabi " fibrous material, its fibre fineness
0.9dtex×38mm。
Preferably, the specification of described Mei Yabi acrylic fiber is 0.9dtex × 38mm.
Preferably, the specification of described viscose rayon is 1.2D × 38mm.
Preferably, the production method of above-mentioned far infrared yarn wire fabric, use hopper mixture.
Preferably, the production method of above-mentioned far infrared yarn wire fabric, including spun yarn step, the steel wire ring in spun yarn step
Number it is culudr7/0, speed 160r/min, workshop humidity 60-65%.
Preferably, the production method of above-mentioned far infrared yarn wire fabric, including air-jet weaving weft yarn step: Toyota of Japan
JAT710 weaves, technological parameter: T:80 °, main jet air pressure 0.18MPa, auxiliary jet pressure 0.32MPa, the time of advent 210 °, opens for 32 °
Before and after the bicker back rest/just 5/-2, through frame height-3, warp tension 260kg.
Advantages of the present invention and having the beneficial effects that: providing the production method of a kind of far infrared yarn wire fabric, it can produce
Go out the functional yarn with the health-care effect such as soft and smooth, warming, anti pilling, antistatic, far infrared and fabric.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
The production method of a kind of far infrared yarn wire fabric, uses tight SEILE textile technology, by 71wt% Mei Yabi acrylic fiber,
29wt% viscose fiber blending becomes functional yarn, then prepares fabric with functional yarn for raw material.
Described Mei Yabi acrylic fiber is Mitsubishi Li Yang company " Mei Yabi " fibrous material, its fibre fineness
0.9dtex×38mm。
The specification of described Mei Yabi acrylic fiber is 0.9dtex × 38mm.
The specification of described viscose rayon is 1.2D × 38mm.
The production method of above-mentioned far infrared yarn wire fabric, uses hopper mixture.
The production method of above-mentioned far infrared yarn wire fabric, including spun yarn step, the wire loop model in spun yarn step is
Culudr7/0, speed 160r/min, workshop humidity 60-65%.
The production method of above-mentioned far infrared yarn wire fabric, including air-jet weaving weft yarn step: Japan's Toyota JAT710 weaving,
Technological parameter: T:80 °, main jet air pressure 0.18MPa, auxiliary jet pressure 0.32MPa, the time of advent 210 °, before 32 ° of angular aperture back rest
Afterwards/just 5/-2, through frame height-3, warp tension 260kg.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (6)
1. the production method of far infrared yarn wire fabric, it is characterised in that use tight SEILE textile technology, by 71wt% Mei Yabi nitrile
Synthetic fibre fiber, 29wt% viscose fiber blending become functional yarn, then prepare fabric with functional yarn for raw material.
The production method of far infrared yarn wire fabric the most according to claim 1, it is characterised in that described Mei Yabi acrylon are fine
The specification of dimension is 0.9dtex × 38mm.
The production method of far infrared yarn wire fabric the most according to claim 2, it is characterised in that the rule of described viscose rayon
Lattice are 1.2D × 38mm.
The production method of far infrared yarn wire fabric the most according to claim 3, it is characterised in that use hopper mixture.
The production method of far infrared yarn wire fabric the most according to claim 4, it is characterised in that include spun yarn step, carefully
Wire loop model in yarn step is culudr7/0, speed 160r/min, workshop humidity 60-65%.
The production method of far infrared yarn wire fabric the most according to claim 5, it is characterised in that include air-jet weaving weft yarn
Step: Japan's Toyota JAT710 weaving, technological parameter: T:80 °, main jet air pressure 0.18MPa, auxiliary jet pressure 0.32MPa, during arrival
Between 210 °, before and after 32 ° of angular aperture back rest/just 5/-2, through frame height-3, warp tension 260kg.