CN106166417A - The manufacture method of screen plate used by high-efficiency environment friendly air purifier - Google Patents
The manufacture method of screen plate used by high-efficiency environment friendly air purifier Download PDFInfo
- Publication number
- CN106166417A CN106166417A CN201610572073.7A CN201610572073A CN106166417A CN 106166417 A CN106166417 A CN 106166417A CN 201610572073 A CN201610572073 A CN 201610572073A CN 106166417 A CN106166417 A CN 106166417A
- Authority
- CN
- China
- Prior art keywords
- plank
- screen plate
- air purifier
- acid
- dipped
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Used by high-efficiency environment friendly air purifier, the manufacture method of screen plate belongs to field of Environment Protection, especially air filter machine field.The present invention proposes: the manufacture method of screen plate used by high-efficiency environment friendly air purifier, it is characterized in that: the manufacturing step of described screen plate is: the first step, timber is processed as plank, second step, plank is dipped in calcium hydroxide saturated solution, the 3rd step, plank is dried, 4th step, is dipped into plank in the mixed solution of oxalic acid and sulphuric acid.The screen plate efficiency that the present invention obtains is high, effective.
Description
Technical field
The invention belongs to field of Environment Protection, especially air purifier field.
Background technology
The air purifier overwhelming majority on market uses screen plate to come the little granule in air filtering, existing screen plate system
Make complex process, during manufacturing screen plate, bring the most difficult or pollutant of difficult degradation to environment.
Summary of the invention
In order to overcome the deficiencies in the prior art, the present invention proposes:
The manufacture method of screen plate used by a kind of high-efficiency environment friendly air purifier, is characterized in that:
The manufacturing step of described screen plate is:
The first step, is processed as, timber, the plank that thickness is 1-2mm,
Second step, is dipped into the plank of first step gained in calcium hydroxide saturated solution, and during immersion, a length of 12-24 is little
Time,
3rd step, is placed on the plank after second step processes in normal temperature environment and is dried, and a length of 6-8 when placing
My god,
4th step, is dipped into the plank after three step process in the mixed solution of oxalic acid and sulphuric acid, soaks duration
For 3-4 hour,
5th step, is soaked in water the plank after the 4th step processes and/or rinse, to wash away soluble substance,
6th step, through the 5th step process after plank be placed into normal temperature drying, then strike off board surface duricrust until
Spill wooden part and i.e. obtain screen plate used by air purifier for environment protection.
The method for designing of a kind of air purifier, is characterized in that: screen plate is arranged at inlet channel and outlet passageway it
Between, and the manufacturing step of screen plate is:
The first step, is processed as, timber, the plank that thickness is 1-2mm,
Second step, is dipped into the plank of first step gained in calcium hydroxide saturated solution, and during immersion, a length of 12-24 is little
Time,
3rd step, is placed on the plank after second step processes in normal temperature environment and is dried, and a length of 6-8 when placing
My god,
4th step, is dipped into the plank after three step process in the mixed solution of oxalic acid and sulphuric acid, soaks duration
For 3-4 hour,
5th step, is soaked in water the plank after the 4th step processes and/or rinse, to wash away soluble substance,
6th step, through the 5th step process after plank be placed into normal temperature drying, then strike off board surface duricrust until
Spill wooden part and i.e. obtain screen plate used by air purifier for environment protection.
The screen plate efficiency that the present invention obtains is high, removes the effective of air small particles, and the raw material used
Though nontoxic or have certain toxicity, it is easily handled, and environmental pollution is little.
Accompanying drawing explanation
Fig. 1 is the test data figure of embodiment one.
Fig. 2 is the test data figure of embodiment two.
Detailed description of the invention
In the present invention, described room temperature is 20-35 degree Celsius.
This specification defines: grass aqueous acid is also referred to as: oxalic acid solution, oxalic acid aqueous solution.Sulfur aqueous acid
Also referred to as: sulfuric acid solution, aqueous sulfuric acid.
Air purifier is also air filter.
Embodiment one
The manufacturing step of described screen plate is:
The first step, is processed as, timber, the plank that thickness is 1mm.
Described timber is Pinus massoniana Lamb (Classification system: Pinus massoniana Lamb.), and described timber is dry wood
Material, density 0.69 gram every cubic centimetre.
Second step, is dipped into the plank of first step gained in calcium hydroxide saturated solution, during immersion a length of 12 hours.
Described calcium hydroxide saturated solution is the aqueous solution of calcium hydroxide.Described calcium hydroxide is to be reacted by calcium oxide and water
Obtain.
3rd step, through second step process after plank be placed in normal temperature environment be dried, and place time a length of 6 days.
4th step, is dipped into the plank after three step process in the mixed solution of oxalic acid and sulphuric acid, soaks duration
It it is 3 hours.
The collocation method of described " oxalic acid and the mixed solution of sulphuric acid ": the first step, configuration quality percent concentration is 6.7%
Careless aqueous acid, second step, configuration quality percent concentration is the sulfur aqueous acid of 4%, the 3rd step, mix the first step
The oxalic acid solution of configuration and the sulfuric acid solution of second step configuration.
Those skilled in the art are it is to be understood that the careless aqueous acid that concentration is 6.7% refers to: 6.7 mass parts oxalic acid, molten
Liquid mass parts is 100.Aqueous sulfuric acid the most so understands.
5th step, is soaked in water and/or rinses, the plank after the 4th step processes to wash away soluble substance.
During immersion a length of 1 hour, then rinse 1 hour with the water of flowing.Or rinse 1.5 hours with the water of flowing.Or
Person was with substantial amounts of water soaking 2 hours.Described refers in a large number: be enough to wash away the water of the amount of soluble substance.
6th step, through the 5th step process after plank be placed into normal temperature drying, then strike off board surface duricrust until
Spill wooden part and i.e. obtain screen plate used by air purifier for environment protection.
Embodiment two
The manufacturing step of described screen plate is:
The first step, is processed as, timber, the plank that thickness is 2mm.
Described timber is Pinus massoniana Lamb (Classification system: Pinus massoniana Lamb.), and described timber is dry wood
Material, density 0.69 gram every cubic centimetre.
Second step, is dipped into the plank of first step gained in calcium hydroxide saturated solution, during immersion a length of 24 hours.
Described calcium hydroxide saturated solution is the aqueous solution of calcium hydroxide.Described calcium hydroxide is to be reacted by calcium oxide and water
Obtain.
3rd step, through second step process after plank be placed in normal temperature environment be dried, and place time a length of 8 days.
4th step, is dipped into the plank after three step process in the mixed solution of oxalic acid and sulphuric acid, soaks duration
It it is 4 hours.
The collocation method of described " oxalic acid and the mixed solution of sulphuric acid ": the first step, configuration quality percent concentration is 6.7%
Careless aqueous acid, second step, configuration quality percent concentration is the sulfur aqueous acid of 4%, the 3rd step, mix the first step
The oxalic acid solution of configuration and the sulfuric acid solution of second step configuration.
Those skilled in the art are it is to be understood that the careless aqueous acid that concentration is 6.7% refers to: 6.7 mass parts oxalic acid, molten
Liquid quality is 100 parts.Aqueous sulfuric acid the most so understands.
5th step, is soaked in water and/or rinses, the plank after the 4th step processes to wash away soluble substance.
During immersion a length of 1 hour, then rinse 1 hour with the water of flowing.Or rinse 1.5 hours with the water of flowing.Or
Person was with substantial amounts of water soaking 2 hours.Described refers in a large number: be enough to wash away the water of the amount of soluble substance.
6th step, through the 5th step process after plank be placed into normal temperature drying, then strike off board surface duricrust until
Spill wooden part and i.e. obtain screen plate used by air purifier for environment protection.
Embodiment three
Above-mentioned screen plate is placed in air purifier, substitutes original filtering material in air purifier, it is to note that 1,
The conscientious air inlet of clean air depurator, outlet passageway.2, screen plate will with original filtering material shape, in the same size, and
And notice that the edge of screen plate to seal, in order to avoid air filtered just row is to outlet passageway.
The method for designing of a kind of air purifier, is characterized in that: screen plate is arranged at inlet channel and outlet passageway it
Between, and the manufacturing step of screen plate is:
The first step, is processed as, timber, the plank that thickness is 1-2mm,
Second step, is dipped into the plank of first step gained in calcium hydroxide saturated solution, and during immersion, a length of 12-24 is little
Time,
3rd step, is placed on the plank after second step processes in normal temperature environment and is dried, and a length of 6-8 when placing
My god,
4th step, is dipped into the plank after three step process in the mixed solution of oxalic acid and sulphuric acid, soaks duration
For 3-4 hour,
5th step, is soaked in water the plank after the 4th step processes and/or rinse, to wash away soluble substance,
6th step, through the 5th step process after plank be placed into normal temperature drying, then strike off board surface duricrust until
Spill wooden part and i.e. obtain screen plate used by air purifier for environment protection.
Test data:
Test method: in the big room closed, room area 300 square metres, different air purifiers is set, different
The difference of air purifier be: screen plate used is different.The filtering material that air purifier is used is institute of the present invention
The material prepared, without other materials, such as: Linesless charcoal.
Detecting instrument is: trade name: Bramc air quality detector, model: BR-HOL-1210.
Before air purifier work, the mean concentration of detection room air pm2.5 is 172 microgram every cubic metre.
Air purifier works latter 30 seconds, at air vent detection air after filtering.
Same steps prepare screen plate, manufacture 3 pieces, then, make 3 air purifiers.Each filter test 3
Secondary, take 9 times after filtering the meansigma methods of measured value as the filter effect value of this screen plate (or filter).
This specification relates to these words: the collocation method of described " oxalic acid and the mixed solution of sulphuric acid ": the first step, join
Putting the careless aqueous acid that mass percent concentration is 6.7%, second step, configuration quality percent concentration is the sulphuric acid of 4%
Aqueous solution, the 3rd step, the oxalic acid solution of mixing first step configuration and the sulfuric acid solution of second step configuration.
Inventor finds, in the 3rd step described in the preceding paragraph, oxalic acid solution, the quality proportioning of sulfuric acid solution, be to affect
The key factor of filter effect.
Order: concentration be the careless aqueous acid mass parts of 6.7% be 200；The sulphuric acid that packet adds different quality part is water-soluble
Liquid, the mass parts of addition is respectively as follows: 0,5,10,15,20,25,30,35,40,45,50,55,60,65,70,75,80,85,90,
95、100。
The test data of embodiment one, two is as shown in Figure 1 and Figure 2.
In figure:
The meaning of transverse axis is: the mass fraction of sulfuric acid solution.
The meaning of the longitudinal axis is: the pm2.5 concentration of filtered air, unit: microgram every cubic metre.
Showing in figure: in special value interval, the addition of sulfuric acid solution significantly have impact on final filtration effect
Really.Concentration be the careless aqueous acid mass parts of 6.7% be 200, mass percent concentration is the matter of the sulfur aqueous acid of 4%
When amount part is 50,55,60, filter effect is preferable, and the air pm2.5 concentration after filtration is less than 25 microgram every cubic metre, especially
Mass percent concentration is the mass parts of the sulfur aqueous acid of 4% when being 55, and filter effect is optimal.
Test is also found that embodiment one, two to be affected little on the gas flow of air purifier.Gas flow is 196-
209 cubic metres per hour.
The present invention first penetrates into calcium hydroxide in timber, then, the slow effect of the carbon dioxide in air, become
For the hardest limestone, then, carry out attacking limestone with acid, and discharge carbon dioxide, through the erosion of alkali liquor, then
Plus the spilling of carbon dioxide, plank becomes the material of porous, and becomes the material that may filter that gas.Select oxalic acid and sulfur
The solid matter that acid obtains has the advantage that soft or hard is suitable, pore is little and intensive.
In terms of the selection of acid: test also finds, do not reach such effect with hydrochloric acid, use hydrochloric acid, not only cross air filtration
The efficiency of body is low (flow 140-152 cubic meter is per hour), and, the air after filtration, the concentration value of its pm2.5 is the biggest: 46-
82 micrograms every cubic metre.Test also find, only with sulphuric acid also cannot, only with sulphuric acid as select processed with acid must filter
Plate, after one month, filter effect is the worst: filter the efficiency low (flow 103-121 cubic meter is per hour) of gas, and,
Air after filtration, the concentration value of its pm2.5 is the biggest: 84-105 microgram every cubic metre.Only with oxalic acid, in freshly prepared mistake
In filter, filter effect still can, but, after one month, capacity greatly reduces: flow 94-118 cubic meter is per hour.
Test finds, the acid solution used, preferable by the mixed acid effect of oxalic acid and sulphuric acid, and inventor have found suitable
The proportioning closed.
Under normal circumstances, it is believed that the sulfuric acid amount of addition is the most, acidity is the strongest, then, and the plate after calcium carbonate reaction
Material effect should be dull change or simple transformation relation.But, it is a discovery of the invention that special value when,
The filter effect of sheet material there occurs the mixed acid selection acid as the present invention of sudden change, oxalic acid and sulphuric acid, its screen plate prepared
Capacity is big, good filtration effect, and such good effect duration was up to three months.
Claims (1)
1. the manufacture method of screen plate used by high-efficiency environment friendly air purifier, is characterized in that:
The manufacturing step of described screen plate is:
The first step, is processed as, timber, the plank that thickness is 1mm,
Second step, is dipped into the plank of first step gained in calcium hydroxide saturated solution, during immersion a length of 12 hours,
3rd step, through second step process after plank be placed in normal temperature environment be dried, and place time a length of 6 days,
4th step, is dipped into the plank after three step process in the mixed solution of oxalic acid and sulphuric acid, a length of 3 little during immersion
Time,
5th step, is soaked in water the plank after the 4th step processes and/or rinse, to remove soluble substance,
6th step, is placed into normal temperature drying the plank after the 5th step processes and i.e. obtains screen plate used by air purifier for environment protection.