CN106149201A - Dry-laying and wet-laying spun lacing complex machining process - Google Patents
Dry-laying and wet-laying spun lacing complex machining process Download PDFInfo
- Publication number
- CN106149201A CN106149201A CN201610764947.9A CN201610764947A CN106149201A CN 106149201 A CN106149201 A CN 106149201A CN 201610764947 A CN201610764947 A CN 201610764947A CN 106149201 A CN106149201 A CN 106149201A
- Authority
- CN
- China
- Prior art keywords
- laying
- spun lacing
- net
- dry
- wet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of dry-laying and wet-laying spun lacing complex machining process, belong to nonwoven cloth material technical field, comprise the following steps: wet-laying raw material is carried out dissolving, thickens by (1) successively, starching, molding, pre-spun lacing, form preforming net one；Meanwhile, dry-laying raw material carries out being mixed into net, pre-spun lacing, form preforming net two；(2), after preforming net one being overlapped as lower floor as upper strata, preforming net two, carry out spun lacing and be combined, dry.The non-woven fabrics produced by dry-laying of the present invention and wet-laying spun lacing complex machining process is applicable to make multiple product, is particularly suited for making curable product and wipe product.
Description
Technical field
The present invention relates to a kind of dry-laying and wet-laying spun lacing complex machining process, belong to nonwoven cloth material technology neck
Territory.
Background technology
In order to expand the application of non-woven fabrics, paper and non-woven fabrics are carried out being combined by part producing enterprise makes Compound Fabric,
It is mainly used as Wiping material, medical material.But this Compound Fabric poor performance, such as: Boardy Feeling, water absorption are poor, the lowest.
Summary of the invention
It is an object of the invention to provide a kind of dry-laying and wet-laying spun lacing complex machining process, raw by this technique
Non-woven fabrics good hygroscopicity that output is come, strength height, thickness thin (in the case of identical grammes per square metre), soft.
For reaching above-mentioned purpose, the technical solution adopted in the present invention is:
A kind of dry-laying and wet-laying spun lacing complex machining process, comprise the following steps:
(1) carry out wet-laying raw material successively dissolving, thicken, starching, molding, pre-spun lacing, form preforming net one；With
Time, dry-laying raw material carries out being mixed into net, pre-spun lacing, forms preforming net two；
(2), after preforming net one being overlapped as lower floor as upper strata, preforming net two, carry out spun lacing and be combined, dry
Dry.
In described step (1), wet-laying raw material is synthetic fibers, and in sizing process, pre-dilution pump discharge is 8000L/
Min, backflow ratio is 30-32%, and vacuum is-20kpa, and the speed of molding procedure is 100m/min, and aspiration vacuum level is
10kpa, forming net tension force is 5N；Dry-laying raw material is wood pulp cellulose and ES fiber, and the speed being mixed into net operation is 100m/
Min, the spun lacing pressure of 4 water jets of pre-spun lacing operation is respectively 50bar, 55bar, 60bar, 60bar.
In described step (2), the lace curtaining speed of spun lacing compound working procedure is 100-101m/min, and aspiration vacuum level is 7kpa,
The spun lacing pressure of its 5 water jets is respectively 30bar, 40bar, 40bar, 50bar, 50bar；Baking operation includes passing sequentially through
Temperature is respectively set to 105 DEG C, 120 DEG C, the baking oven of 130 DEG C, and speed is 100m/min.
By the physical property of the non-woven fabrics that dry-laying of the present invention is produced with wet-laying spun lacing complex machining process
Energy achievement data is as follows:
The non-woven fabrics produced by dry-laying of the present invention and wet-laying spun lacing complex machining process is applicable to system
Make multiple product, be particularly suited for making curable product and wipe product.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further described.Following embodiment is illustrative, is not determinate,
Protection scope of the present invention can not be limited with following embodiment.
Embodiment 1
Dry-laying of the present invention and wet-laying spun lacing complex machining process, comprise the following steps:
(1) carry out wet-laying raw material successively dissolving, thicken, starching, molding, pre-spun lacing, form preforming net one；With
Time, dry-laying raw material carries out being mixed into net, pre-spun lacing, forms preforming net two；
(2), after preforming net one being overlapped as lower floor as upper strata, preforming net two, carry out spun lacing and be combined, dry
Dry.
In above-mentioned steps (1), wet-laying raw material is synthetic fibers, and in sizing process, pre-dilution pump discharge is 8000L/
Min, backflow ratio is 30%, and vacuum is-20kpa, and the speed of molding procedure is 100m/min, and aspiration vacuum level is
10kpa, forming net tension force is 5N；Dry-laying raw material is wood pulp cellulose and ES fiber, and the speed being mixed into net operation is 100m/
Min, the spun lacing pressure of 4 water jets of pre-spun lacing operation is respectively 50bar, 55bar, 60bar, 60bar.
In above-mentioned steps (2), the lace curtaining speed of spun lacing compound working procedure is 100m/min, and aspiration vacuum level is 7kpa, and they are 5 years old
The spun lacing pressure of individual water jet is respectively 30bar, 40bar, 40bar, 50bar, 50bar；Baking operation includes passing sequentially through temperature
Degree is respectively set to 105 DEG C, 120 DEG C, the baking oven of 130 DEG C, and speed is 100m/min.
Embodiment 2
Dry-laying of the present invention and wet-laying spun lacing complex machining process, comprise the following steps:
(1) carry out wet-laying raw material successively dissolving, thicken, starching, molding, pre-spun lacing, form preforming net one；With
Time, dry-laying raw material carries out being mixed into net, pre-spun lacing, forms preforming net two；
(2), after preforming net one being overlapped as lower floor as upper strata, preforming net two, carry out spun lacing and be combined, dry
Dry.
In above-mentioned steps (1), wet-laying raw material is synthetic fibers, and in sizing process, pre-dilution pump discharge is 8000L/
Min, backflow ratio is 32%, and vacuum is-20kpa, and the speed of molding procedure is 100m/min, and aspiration vacuum level is
10kpa, forming net tension force is 5N；Dry-laying raw material is wood pulp cellulose and ES fiber, and the speed being mixed into net operation is 100m/
Min, the spun lacing pressure of 4 water jets of pre-spun lacing operation is respectively 50bar, 55bar, 60bar, 60bar.
In above-mentioned steps (2), the lace curtaining speed of spun lacing compound working procedure is 101m/min, and aspiration vacuum level is 7kpa, and they are 5 years old
The spun lacing pressure of individual water jet is respectively 30bar, 40bar, 40bar, 50bar, 50bar；Baking operation includes passing sequentially through temperature
Degree is respectively set to 105 DEG C, 120 DEG C, the baking oven of 130 DEG C, and speed is 100m/min.
Embodiment 3
Dry-laying of the present invention and wet-laying spun lacing complex machining process, comprise the following steps:
(1) carry out wet-laying raw material successively dissolving, thicken, starching, molding, pre-spun lacing, form preforming net one；With
Time, dry-laying raw material carries out being mixed into net, pre-spun lacing, forms preforming net two；
(2), after preforming net one being overlapped as lower floor as upper strata, preforming net two, carry out spun lacing and be combined, dry
Dry.
In above-mentioned steps (1), wet-laying raw material is synthetic fibers, and in sizing process, pre-dilution pump discharge is 8000L/
Min, backflow ratio is 31%, and vacuum is-20kpa, and the speed of molding procedure is 100m/min, and aspiration vacuum level is
10kpa, forming net tension force is 5N；Dry-laying raw material is wood pulp cellulose and ES fiber, and the speed being mixed into net operation is 100m/
Min, the spun lacing pressure of 4 water jets of pre-spun lacing operation is respectively 50bar, 55bar, 60bar, 60bar.
In above-mentioned steps (2), the lace curtaining speed of spun lacing compound working procedure is 100.5m/min, and aspiration vacuum level is 7kpa, its
The spun lacing pressure of 5 water jets is respectively 30bar, 40bar, 40bar, 50bar, 50bar；Baking operation includes passing sequentially through temperature
Degree is respectively set to 105 DEG C, 120 DEG C, the baking oven of 130 DEG C, and speed is 100m/min.
In all above embodiment, synthetic fibers are both preferably the viscose rayon of 2.0Dtex*10mm.
Above-described embodiment is only used for illustrating the inventive concept of the present invention, rather than the restriction to rights protection of the present invention,
All changes utilizing this design that the present invention carries out unsubstantiality, all should fall into protection scope of the present invention.
Claims (3)
1. a dry-laying and wet-laying spun lacing complex machining process, it is characterised in that comprise the following steps:
(1) carry out wet-laying raw material successively dissolving, thicken, starching, molding, pre-spun lacing, form preforming net one；Meanwhile,
Dry-laying raw material carries out being mixed into net, pre-spun lacing, forms preforming net two；
(2), after preforming net one being overlapped as lower floor as upper strata, preforming net two, carry out spun lacing and be combined, dry.
2. dry-laying as claimed in claim 1 and wet-laying spun lacing complex machining process, it is characterised in that: described step
(1) in, wet-laying raw material is synthetic fibers, and in sizing process, pre-dilution pump discharge is 8000L/min, and backflow ratio is 30-
32%, vacuum is-20kpa, and the speed of molding procedure is 100m/min, and aspiration vacuum level is 10kpa, and forming net tension force is
5N；Dry-laying raw material is wood pulp cellulose and ES fiber, and the speed being mixed into net operation is 100m/min, the 4 of pre-spun lacing operation
The spun lacing pressure of individual water jet is respectively 50bar, 55bar, 60bar, 60bar.
3. dry-laying as claimed in claim 1 and wet-laying spun lacing complex machining process, it is characterised in that: described step
(2) in, the lace curtaining speed of spun lacing compound working procedure is 100-101m/min, and aspiration vacuum level is 7kpa, the water of its 5 water jets
Thorn pressure is respectively 30bar, 40bar, 40bar, 50bar, 50bar；Baking operation includes that passing sequentially through temperature is respectively set to
105 DEG C, 120 DEG C, the baking oven of 130 DEG C, and speed is 100m/min.