CN106149179A - A kind of two-sided knitting fabric and foaming characteristic test technology thereof - Google Patents

Abstract

The present invention relates to a kind of two-sided knitting fabric and foaming characteristic test technology thereof, it is characterized in that: it is made up of upper strata fabric and lower floor's fabric, upper strata fabric is used the braiding of weft plain weave structure to form by the first yarn, lower floor's fabric is used the braiding of weft plain weave structure to form by the second yarn, upper strata fabric and lower floor's fabric are connected by the striped of knitting braiding structure, and striped is woven in the first yam by the second yarn of lower floor's fabric and constitutes.A kind of two-sided knitting fabric and foaming characteristic test technology thereof are designed by rational structure so that the good permeability of fabric, and comfort level is strong, and warmth retention property is good, elastic strong, are difficult to crumple.

Description

A kind of two-sided knitting fabric and foaming characteristic test technology thereof

Technical field

The present invention relates to a kind of two-sided knitting fabric and foaming characteristic test technology thereof, belong to fabric technical field.

Background technology

Along with the raising of human living standard, the performance requirement of people's fabric to making medicated clothing is more and more higher.But Along with progress and the growth in the living standard of technology, breathability, warmth retention property and the comfortableness of existing knitting fabric can not meet Consumer demand.

Summary of the invention

It is an object of the invention to overcome above-mentioned deficiency, it is provided that good permeability, warmth retention property is good, and one comfortable and easy to wear is two-sided Knitting fabric and foaming characteristic test technology thereof.

The object of the present invention is achieved like this:

A kind of two-sided knitting fabric and foaming characteristic test technology thereof, it is made up of upper strata fabric and lower floor's fabric, upper strata fabric by First yarn uses the braiding of weft plain weave structure to form, and lower floor's fabric is used the braiding of weft plain weave structure to form by the second yarn, Upper strata fabric and lower floor's fabric are connected by the striped of knitting braiding structure, and striped is woven in the by the second yarn of lower floor's fabric One yam is constituted.

Foaming characteristic test technology is:

Step one: lead at 70cm and take two pieces of the sample of 60 cm × 60 cm on paper web sample as test sample；

Step 2: sample is flat on temperature 20 ± 2 DEG C, balances 2 hours under the environmental condition of humidity 65 ± 3%；

Step 3: longitudinal folding for sample sample, the sample after folding is that 30 cm(are horizontal) × 60 cm(longitudinal directions) just face outwardly Being put on pressing machine, spraying steam 10 seconds, steam pressure is 6kg, and fabric is by deforming after damp and hot, bubbling, and surface is risen different big Little or the folding line of different densities or bubble；

Step 4: after having sprayed steam, takes out fabric after being cooled down 5 seconds by fabric with air draught, horizontal one end of sample is clipped in trousers On sub-clothes hanger, sample is made to keep nature vertical；

Step 5: the trousers hanger of sample will be accompanied in temperature 20 ± 2 DEG C, in the environment of humidity 65 ± 3%, will be after balance Sample move on under nature backlight conditions, respectively whole scald after latter 1 hour and whole scald latter 24 hours after the two time period, observe Sample cosmetic variation determines the foaming grade of sample.

Compared with prior art, the invention has the beneficial effects as follows:

A kind of two-sided knitting fabric of the present invention and foaming characteristic test technology thereof are designed by rational structure so that breathing freely of fabric Property good, comfort level is strong, and warmth retention property is good, elastic strong, is difficult to crumple.

Detailed description of the invention

The present invention relates to a kind of two-sided knitting fabric and foaming characteristic test technology thereof, it is by upper strata fabric and lower floor's fabric group Becoming, upper strata fabric is used the braiding of weft plain weave structure to form by the first yarn, and lower floor's fabric is used weft plain weave by the second yarn Structure braiding forms, and upper strata fabric and lower floor's fabric are connected by the striped of knitting braiding structure, and striped is by the of lower floor's fabric Two yarns are woven in the first yam and constitute.

Foaming characteristic test technology is:

Step one: lead at 70cm and take two pieces of the sample of 60 cm × 60 cm on paper web sample as test sample；

Step 2: sample is flat on temperature 20 ± 2 DEG C, balances 2 hours under the environmental condition of humidity 65 ± 3%；

Step 3: longitudinal folding for sample sample, the sample after folding is that 30 cm(are horizontal) × 60 cm(longitudinal directions) just face outwardly Being put on pressing machine, spraying steam 10 seconds, steam pressure is 6kg, and fabric is by deforming after damp and hot, bubbling, and surface is risen different big Little or the folding line of different densities or bubble；

Step 4: after having sprayed steam, takes out fabric after being cooled down 5 seconds by fabric with air draught, horizontal one end of sample is clipped in trousers On sub-clothes hanger, sample is made to keep nature vertical；

Step 5: the trousers hanger of sample will be accompanied in temperature 20 ± 2 DEG C, in the environment of humidity 65 ± 3%, will be after balance Sample move on under nature backlight conditions, respectively whole scald after latter 1 hour and whole scald latter 24 hours after the two time period, observe Sample cosmetic variation determines the foaming grade of sample.

Claims (1)

1. a two-sided knitting fabric and foaming characteristic test technology thereof, it is characterised in that: it is by upper strata fabric and lower floor's fabric group Becoming, upper strata fabric is used the braiding of weft plain weave structure to form by the first yarn, and lower floor's fabric is used weft plain weave by the second yarn Structure braiding forms, and upper strata fabric and lower floor's fabric are connected by the striped of knitting braiding structure, and striped is by the of lower floor's fabric Two yarns are woven in the first yam and constitute；

Foaming characteristic test technology is:

Step one: lead at 70cm and take two pieces of the sample of 60 cm × 60 cm on paper web sample as test sample；

Step 2: sample is flat on temperature 20 ± 2 DEG C, balances 2 hours under the environmental condition of humidity 65 ± 3%；

Step 3: longitudinal folding for sample sample, the sample after folding is that 30 cm(are horizontal) × 60 cm(longitudinal directions) just face outwardly Being put on pressing machine, spraying steam 10 seconds, steam pressure is 6kg, and fabric is by deforming after damp and hot, bubbling, and surface is risen different big Little or the folding line of different densities or bubble；

Step 4: after having sprayed steam, takes out fabric after being cooled down 5 seconds by fabric with air draught, horizontal one end of sample is clipped in trousers On sub-clothes hanger, sample is made to keep nature vertical；

Step 5: the trousers hanger of sample will be accompanied in temperature 20 ± 2 DEG C, in the environment of humidity 65 ± 3%, will be after balance Sample move on under nature backlight conditions, respectively whole scald after latter 1 hour and whole scald latter 24 hours after the two time period, observe Sample cosmetic variation determines the foaming grade of sample.