CN106147654A - A kind of permanent tack type rubber cement for presulfurization method tyre rebuilding and preparation method thereof - Google Patents
A kind of permanent tack type rubber cement for presulfurization method tyre rebuilding and preparation method thereof Download PDFInfo
- Publication number
- CN106147654A CN106147654A CN201510160228.1A CN201510160228A CN106147654A CN 106147654 A CN106147654 A CN 106147654A CN 201510160228 A CN201510160228 A CN 201510160228A CN 106147654 A CN106147654 A CN 106147654A
- Authority
- CN
- China
- Prior art keywords
- floating weight
- mixing
- parts
- seconds
- rubber cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of permanent tack type rubber cement for presulfurization method tyre rebuilding and preparation method thereof, it is characterized in that, feed components is as follows according to weight portion composition: natural rubber is 100 parts, white carbon black 15~35 parts, environmental protection peptizer 0.1~0.4 part, stearic acid 0.5~2 parts, zinc oxide 3~7 parts, carbon black disperser 0~2 parts, anti-aging agent RD 0.5~2 parts, antioxidant 4020 1~3 parts, tackifying resin 6-9 part, insoluble sulfur 6033 1-3 part, accelerator NS 0.5-1.5 part, altax 0.3-1 part, diphenylguanidine PG 0.3-1 part, anti-scorching agent CTP 0.1~0.4 part.The present invention, by optimizing rubber cement glue recipe ingredient and preparation technology, strengthens durable adhesion performance, is applied to tyre rebuilding carcass and the coating of precured tread buffed surface, improves its performance, reduces the generation of defective products, improves retreads service life;By the optimization of mixer mixing process quick to Large Copacity, solve roll banding and a difficult problem for dust dispersion quality difference, make production efficiency improve.
Description
Technical field
The present invention relates to retreads precured tread produce and tyre rebuilding field, be specifically related to a kind of for
Permanent tack type rubber cement of presulfurization method tyre rebuilding and preparation method thereof.
Background technology
Presulfurization method tyre rebuilding: precured tread is pasted onto on the carcass polished, then through second time
The cover tire renovation method of sulfuration.Its technical process is through polishing by precured tread, sticks to after being coated with rubber cement
On carcass after polishing, painting rubber cement, upper middle pad glue, it is then charged into envelope, vulcanizes at low-temp low-pressure
Kettle cure becomes the process of retreads.Precured tread: the i.e. adhesive tape that recaps of prevulcanization
Or glue ring.Rubber cement: refer mainly to dissolve by the sizing material appropriate solvent that rubber cement glue formula and compounding process produce add
The liquid/paste that work becomes, for precured tread and the brushing of carcass buffed surface, plays adhesive effect.
In precured tread production process, be polished in the tyre surface back side, then brushing rubber cement, packaging,
Stand-by.The main purpose of brushing rubber cement, one is tyre surface buffed surface to carry out cladding avoid oxidation;Two are to maintain
Good viscosity, can fit tightly with the middle pad glue being attached on carcass buffed surface when tyre rebuilding;Three are
Between rubber cement and the rubber components of other joints, under low temperature, low pressure and special time conditions of vulcanization, make
Can effectively combine between rubber macromolecule, form firm network structure, make each position of retreads become one
Individual firm entirety, it can be seen that, the quality of retreads is played the most crucial effect by rubber cement glue.Due to
Product standby time is different in size, and is affected by transport, weather and condition of storage, the brushing tyre surface back side
Rubber cement occur that viscosity declines, the problem not reaching retreads manufacturing requirements, if being continuing with meeting
Cause not bonding between tread rubber pulp layer and middle pad glue, partial delamination, severe patient occur after retreaded tyre vulcanization
Tire blow-out can be caused.
At present precured tread produce rubber cement used be typically with in pad glue solubilizer and replace, because of in pad glue main
Being the cushioning effect of retreads, its compound physical mechanical performance lays particular emphasis on the coupling of intensity, to reduce wheel
Stress during tire travels is grouped as main purpose, reduces the consumption of reinforcing agent, then can reduce in recipe ingredient
Intensity, and reinforcing agent too much can reduce viscosity, particularly permanent tack is poor, is only suitable for making in a short time
With;Although special adhesive glue formula can overcome the problems referred to above in design, but there is also, rubber and
Tackifying resin content is high, the difficult problems such as viscosity is big, Mooney viscosity is low, causes elastomeric compound roll banding, processing difficulties,
Original way is to use low capacity banbury or mill to carry out mixing, but it is low to there is production efficiency, mixed
The problem of material glue dust dispersion quality difference.
In existing rubber cement glue formula, rubber hydrocarbon content is low, and black-reinforced agent accounting amount is big, sizing material stretching strength
Height, causes the autohension of rubber itself to bring into play;For reducing Mooney viscosity, part formulation also increases
7 parts of aromatic naphtha are added, although add the mobile performance of sizing material, but can separate out in depositing, to viscosity
Long-term keep unfavorable.In existing rubber cement glue formula, tackifying resin selects C5 Petropols and tert-butyl phenol
Formaldehyde resin use, total number is at about 9 parts, and common tackifying resin initial viscosity is preferable, but generally exists
The problem of permanent tack difference, and when large usage quantity, rubber compounding roll banding is serious, and preparation technology is very
Difficulty.
In production technology, in order to make up the problem that viscosity keeps difference, it will usually big at precured tread buffed surface
Amount brushing rubber cement, when do so is easily caused packaging, rubber cement is not done and is adhered on shield, makes shield give a discount,
Easily tear during tyre rebuilding and stick to storeroom, and cause retreads delamination.It addition, current rubber cement glue
In formula, vulcanizing system accelerator be chosen as thiazole accelerator DM and diphenylguanidine diphenylguanidine PG also
With, curingprocess rate is fast, the easy incipient scorch of the course of processing.
In prior art, because precured tread rubber cement viscosity is the most up to standard, the return of goods that are that cause account for about 20%, occur
Tyre surface delamination accounts for about 2%, its exist poor specificity, sensitivity is low, cost is high, productivity is low, qualification rate is low,
Response speed is slow, side effect, weak effect in-convenience in use etc. problems.Therefore, how designing one " should
Permanent tack type rubber cement for presulfurization method tyre rebuilding and preparation method thereof " be the present invention will faced by ask
Topic.
Summary of the invention
For problems of the prior art, it is an object of the invention to provide a kind of for the presulfurization wheel of the law
Permanent tack type rubber cement of tire renovation and preparation method thereof.
The technical scheme that the present invention takes is:
A kind of permanent tack type rubber cement for presulfurization method tyre rebuilding, it is characterised in that feed components
As follows according to weight portion composition:
Natural rubber be 100 parts, white carbon black 15~35 parts, environmental protection peptizer 0.1~0.4 part, stearic acid 0.5~2 parts,
Zinc oxide 3~7 parts, carbon black disperser 0~2 parts, anti-aging agent RD 0.5~2 parts, antioxidant 4020 1~3 parts,
Tackifying resin 6-9 part, insoluble sulfur 60331-3 part, accelerator NS 0.5-1.5 part, altax 0.3-
1 part, diphenylguanidine PG 0.3-1 part, anti-scorching agent CTP 0.1~0.4 part.
Further, feed components is as follows according to weight portion composition:
Natural rubber is 100 parts, white carbon black 15-35 part, environmental protection peptizer 0.1~0.4 part, stearic acid 1~2 parts, oxygen
Change zinc 4~6 parts, carbon black disperser 1~2 parts, anti-aging agent RD 1~1.5 parts, antioxidant 4020 1.5~2.5 parts,
Tackifying resin 6-9 part, insoluble sulfur 6,033 1.8~2.5 parts, accelerator NS consumption are 0.6~1.2 part,
Altax 0.4-0.8 part, diphenylguanidine PG 0.4-0.8 part, anti-scorching agent CTP 0.1~0.4 part.
Further, described white carbon black is selected from N330 white carbon black or N326 white carbon black, and its content is preferably 20~30
Part.
Further, described tackifying resin is acetylene type tert-butyl group phenolic aldehyde super tackifying resin KORESIN, moral
State's BASF product.
Further, described environmental protection peptizer is RENACIT-11, produces product for Lanxess Corporation of Germany.
Further, described carbon black disperser is GE3082, Rhein chemical (Qingdao) company limited product.
Further, other raw material is that rubber industry commonly uses raw material.
Further, the gum content of described rubber cement is 65%-75%.
A kind of preparation method of the permanent tack type rubber cement for presulfurization method tyre rebuilding, it is characterised in that
Specifically include following steps:
(1) one section of elastomeric compound: F370 banbury rotating speed is adjusted to 50 revs/min, by natural rubber, Environment-friendlyplastic plastic solution
Agent, zinc oxide, stearic acid, carbon black disperser, with the tackifying resin KORESIN of weight ratio 1/2 consumption
Add, mixing 20 seconds of pressure floating weight, rise floating weight, add N330 or N326 white carbon black, press floating weight,
Mixing 30 seconds, rise floating weight and clean, mixing 25 seconds of pressure floating weight, rise floating weight and clean, pressure floating weight mixes
Refine 25 seconds, bin gate binder removal of starting discharging, control dump temperature 140 DEG C-150 DEG C;Extruder extrusion bottom sheet, cooling
Build buttress;
(2) two-stage mixing glue: F270 banbury rotating speed is adjusted to 35 revs/min, by one section of masterbatch, age resistor
Add, mixing 30 seconds of pressure floating weight, rise floating weight and clean 5 seconds, mixing 35 seconds of pressure floating weight, go up top
Bolt cleans 5 seconds, mixing 20 seconds of pressure floating weight, bin gate binder removal of starting discharging, control dump temperature 120~130 DEG C;
Extruder bottom sheet, buttress is built in cooling;
(3) three sections of masterbatch: F270 banbury rotating speed is adjusted to 35 revs/min, add two-stage nitration masterbatch, pressure
Mixing 30 seconds of floating weight, rises floating weight and cleans 5 seconds, and mixing 25 seconds of pressure floating weight rises floating weight and cleans 5
Second, mixing 25 seconds of pressure floating weight, bin gate binder removal of starting discharging, control dump temperature 115-125 DEG C;Under extruder
Sheet, buttress is built in cooling;
(4) finished composition: F270 banbury rotating speed is adjusted to 25 revs/min, by three sections of masterbatch, insoluble sulfur
6033, accelerator NS, altax, diphenylguanidine PG, antiscorching agent adds, and presses floating weight mixing 30
Second, rise floating weight and clean 5 seconds, mixing 30 seconds of pressure floating weight, rise floating weight, press floating weight mixing 30
Second, rise floating weight, mixing 30 seconds of pressure floating weight, rise floating weight, bin gate binder removal of starting discharging, control dump temperature
85~95 DEG C;Mill bottom sheet, buttress is built in cooling;
(5) mixed sheet is prepared: elastomeric compound uses tri-roll press machine be prepared as thick 2mm, the glue of wide 300mm
Sheet, uses shield to be cut into the length square piece less than 100mm after batching, stand-by;
(6) prepared by rubber cement: by 120# petrolic solvent, residue 1/2 tackifying resin calculated in proportion, cut out
Mixed sheet, put in rubber cement preparing tank the most successively, solvent load is 3.5-4.0 times of rubber material using quantity,
Soak 2h, continuous stirring >=12h, be completely dissolved to film, pick out preservation, note sealing and place at shady and cool.
Further, in described step (1), the tackifying resin KORESIN of one section of mixing 1/2 consumption will be
The mixing initial stage adds, and by controlling rotating speed and mixing time, it is ensured that melting temperature reaches KORESIN
Ring and ball softening point be 130-145 DEG C.
Further, described step (2) and step (3) use low temperature close in two-stage nitration, three-stage mixing glue
Refining machine is mixing.
The invention have the benefit that
The tackifying resin that the present invention uses is acetylene type tert-butyl group phenolic aldehyde super tackifying resin KORESIN, viscosity
Good endurance, its in natural rubber and rubber polymer high temperature, low temperature, high damp and hot etc. under the conditions of can
The viscosity that long-term holding is good, and there is the heat generation that more common tert-butyl group phenolic tackifying resins is lower.
The rubber cement formula of the present invention takes three kinds of accelerator combinations, is protected by the synergism between accelerator
Card cryogenic vulcanization efficiency, extends time of scorch simultaneously, improves process safety.
The present invention, by optimizing rubber cement glue recipe ingredient and preparation technology, strengthens durable adhesion performance, reduces not
The generation of non-defective unit, improves retreads service life.
The present invention, by the optimization of mixer mixing process quick to Large Copacity, solves roll banding and dust dispersion quality
A difficult problem for difference, makes production efficiency improve.
The present invention improves the permanent tack of rubber cement, is applied to tyre rebuilding carcass and precured tread polishing
The coating in face, improves its performance, after the precured tread long period deposits, tyre surface still can be kept to polish
The adhesive strength of face rubber cement, the bonding between retreads tyre surface and middle pad glue is excellent;Owing to permanent tack carries
Height, decreases the thickness of brushing rubber cement, eliminates and sticks to plastics shield because rubber cement brushing amount crosses very much not dry
On, cause shield foldover, the mass defect easily torn during use, thus improve retreads service life.
The present invention is to rubber cement optimum preparation condition, and the tackifying resin KORESIN of one section of mixing 1/2 consumption wants
Add at the mixing initial stage, and by controlling rotating speed and mixing time, it is ensured that melting temperature reaches KORESIN
Ring and ball softening point be 130-145 DEG C, this make soften KORESIN tackifying resin be uniformly dispersed,
Otherwise, filler during KORESIN is only equivalent to sizing material and its stickiness cannot be showed;Two-stage nitration, three-stage mixing glue
Middle employing low temperature mixer mixing, fully reduces the Mooney viscosity of sizing material, ensures mixing not roll banding simultaneously.
Replace original little banbury with the quick banbury of Large Copacity or mill carries out mixing method, by soon
Speed banbury low temperature is the most mixing, it is achieved that rubber compounding is uniform, improves production efficiency simultaneously;Improve sulfur
Change system, extends time of scorch while applicable cryogenic vulcanization characteristic further, improves product at specific ring
Safety is stored under border;Mixing process controls well dump temperature, to ensure giving full play to of resin viscosity,
And it is prevented effectively from sizing material and glues closed-smelting machine rotor, Dump gate, extruder roller, feed belt etc., reach raw
Product efficiency maximizes.
Detailed description of the invention
The embodiment of the present invention and the recipe list of comparative example
A kind of preparation method of the permanent tack type rubber cement for presulfurization method tyre rebuilding, it is characterised in that
Specifically include following steps:
(1) one section of elastomeric compound: F370 banbury rotating speed is adjusted to 50 revs/min, by natural rubber, Environment-friendlyplastic plastic solution
Agent, zinc oxide, stearic acid, carbon black disperser, with the tackifying resin KORESIN of weight ratio 1/2 consumption
Add, mixing 20 seconds of pressure floating weight, rise floating weight, add N330 or N326 white carbon black, press floating weight,
Mixing 30 seconds, rise floating weight and clean, mixing 25 seconds of pressure floating weight, rise floating weight and clean, pressure floating weight mixes
Refine 25 seconds, bin gate binder removal of starting discharging, control dump temperature 140 DEG C-150 DEG C;Extruder extrusion bottom sheet, cooling
Build buttress;
(2) two-stage mixing glue: F270 banbury rotating speed is adjusted to 35 revs/min, by one section of masterbatch, age resistor
Add, mixing 30 seconds of pressure floating weight, rise floating weight and clean 5 seconds, mixing 35 seconds of pressure floating weight, go up top
Bolt cleans 5 seconds, mixing 20 seconds of pressure floating weight, bin gate binder removal of starting discharging, control dump temperature 120~130 DEG C;
Extruder bottom sheet, buttress is built in cooling;
(3) three sections of masterbatch: F270 banbury rotating speed is adjusted to 35 revs/min, add two-stage nitration masterbatch, pressure
Mixing 30 seconds of floating weight, rises floating weight and cleans 5 seconds, and mixing 25 seconds of pressure floating weight rises floating weight and cleans 5
Second, mixing 25 seconds of pressure floating weight, bin gate binder removal of starting discharging, control dump temperature 115-125 DEG C;Under extruder
Sheet, buttress is built in cooling;
(4) finished composition: F270 banbury rotating speed is adjusted to 25 revs/min, by three sections of masterbatch, insoluble sulfur
6033, accelerator NS, altax, diphenylguanidine PG, antiscorching agent adds, and presses floating weight mixing 30
Second, rise floating weight and clean 5 seconds, mixing 30 seconds of pressure floating weight, rise floating weight, press floating weight mixing 30
Second, rise floating weight, mixing 30 seconds of pressure floating weight, rise floating weight, bin gate binder removal of starting discharging, control dump temperature
85~95 DEG C;Mill bottom sheet, buttress is built in cooling;
(5) mixed sheet is prepared: elastomeric compound uses tri-roll press machine be prepared as thick 2mm, the glue of wide 300mm
Sheet, uses shield to be cut into the length square piece less than 100mm after batching, stand-by;
(6) prepared by rubber cement: by 120# petrolic solvent, residue 1/2 tackifying resin calculated in proportion, cut out
Mixed sheet, put in rubber cement preparing tank the most successively, solvent load is 3.5-4.0 times of rubber material using quantity,
Soak 2h, continuous stirring >=12h, be completely dissolved to film, pick out preservation, note sealing and place at shady and cool.
Embodiment of the present invention properties of rubber
Embodiment of the present invention rubber cement viscosity is tested
Testing equipment: RZE-II type rubber autohension analyzer, Beijing all things on earth one side technology & development Co. produces;
Experimental condition: pressing speed, 20cm/min;Avulse speed, 20cm/min;Pressing time, 5s;
Exposure air carries out after precured tread brushing rubber cement viscosity test:
PE shield, routine test surface viscosity it is coated with after precured tread brushing rubber cement
The above is not limitation of the present invention, it should be pointed out that: for the ordinary skill of the art
For personnel, on the premise of without departing from essential scope of the present invention, it is also possible to make some changes, remodeling,
Adding or replace, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (10)
1. the permanent tack type rubber cement for presulfurization method tyre rebuilding, it is characterised in that feed components is pressed
As follows according to weight portion composition:
Natural rubber be 100 parts, white carbon black 15~35 parts, environmental protection peptizer 0.1~0.4 part, stearic acid 0.5~2 parts,
Zinc oxide 3~7 parts, carbon black disperser 0~2 parts, anti-aging agent RD 0.5~2 parts, antioxidant 4020 1~3 parts,
Tackifying resin 6-9 part, insoluble sulfur 60331-3 part, accelerator NS 0.5-1.5 part, altax 0.3-
1 part, diphenylguanidine PG 0.3-1 part, anti-scorching agent CTP 0.1~0.4 part.
A kind of permanent tack type rubber cement for presulfurization method tyre rebuilding, its feature
Being, feed components is as follows according to weight portion composition:
Natural rubber is 100 parts, white carbon black 15-35 part, environmental protection peptizer 0.1~0.4 part, stearic acid 1~2 parts, oxygen
Change zinc 4~6 parts, carbon black disperser 1~2 parts, anti-aging agent RD 1~1.5 parts, antioxidant 4020 1.5~2.5 parts,
Tackifying resin 6-9 part, insoluble sulfur 60331.8~2.5 parts, accelerator NS consumption are 0.6~1.2 part,
Altax 0.4-0.8 part, diphenylguanidine PG 0.4-0.8 part, anti-scorching agent CTP 0.1~0.4 part.
A kind of permanent tack type rubber cement for presulfurization method tyre rebuilding the most according to claim 1 or claim 2, its
Being characterised by, described white carbon black is selected from N330 white carbon black or N326 white carbon black, and its content is preferably 20~30 parts.
A kind of permanent tack type rubber cement for presulfurization method tyre rebuilding the most according to claim 1 or claim 2, its
Being characterised by, described tackifying resin is acetylene type tert-butyl group phenolic aldehyde super tackifying resin KORESIN.
A kind of permanent tack type rubber cement for presulfurization method tyre rebuilding the most according to claim 1 or claim 2, its
Being characterised by, described environmental protection peptizer is RENACIT-11.
A kind of permanent tack type rubber cement for presulfurization method tyre rebuilding the most according to claim 1 or claim 2, its
Being characterised by, described carbon black disperser is GE3082.
A kind of permanent tack type rubber cement for presulfurization method tyre rebuilding, its feature
Being, the gum content of described rubber cement is 65%-75%.
8. the preparation method for the permanent tack type rubber cement of presulfurization method tyre rebuilding, it is characterised in that tool
Body comprises the steps:
(1) one section of elastomeric compound: F370 banbury rotating speed is adjusted to 50 revs/min, by natural rubber, Environment-friendlyplastic plastic solution
Agent, zinc oxide, stearic acid, carbon black disperser, with the tackifying resin KORESIN of weight ratio 1/2 consumption
Add, mixing 20 seconds of pressure floating weight, rise floating weight, add N330 or N326 white carbon black, press floating weight,
Mixing 30 seconds, rise floating weight and clean, mixing 25 seconds of pressure floating weight, rise floating weight and clean, pressure floating weight mixes
Refine 25 seconds, bin gate binder removal of starting discharging, control dump temperature 140 DEG C-150 DEG C;Extruder extrusion bottom sheet, cooling
Build buttress;
(2) two-stage mixing glue: F270 banbury rotating speed is adjusted to 35 revs/min, by one section of masterbatch, age resistor
Add, mixing 30 seconds of pressure floating weight, rise floating weight and clean 5 seconds, mixing 35 seconds of pressure floating weight, go up top
Bolt cleans 5 seconds, mixing 20 seconds of pressure floating weight, bin gate binder removal of starting discharging, control dump temperature 120~130 DEG C;
Extruder bottom sheet, buttress is built in cooling;
(3) three sections of masterbatch: F270 banbury rotating speed is adjusted to 35 revs/min, add two-stage nitration masterbatch, pressure
Mixing 30 seconds of floating weight, rises floating weight and cleans 5 seconds, and mixing 25 seconds of pressure floating weight rises floating weight and cleans 5
Second, mixing 25 seconds of pressure floating weight, bin gate binder removal of starting discharging, control dump temperature 115-125 DEG C;Under extruder
Sheet, buttress is built in cooling;
(4) finished composition: F270 banbury rotating speed is adjusted to 25 revs/min, by three sections of masterbatch, insoluble sulfur
6033, accelerator NS, altax, diphenylguanidine PG, antiscorching agent adds, and presses floating weight mixing 30
Second, rise floating weight and clean 5 seconds, mixing 30 seconds of pressure floating weight, rise floating weight, press floating weight mixing 30
Second, rise floating weight, mixing 30 seconds of pressure floating weight, rise floating weight, bin gate binder removal of starting discharging, control dump temperature
85~95 DEG C;Mill bottom sheet, buttress is built in cooling;
(5) mixed sheet is prepared: elastomeric compound uses tri-roll press machine be prepared as thick 2mm, the glue of wide 300mm
Sheet, uses shield to be cut into the length square piece less than 100mm after batching, stand-by;
(6) prepared by rubber cement: by 120# petrolic solvent, residue 1/2 tackifying resin calculated in proportion, cut out
Mixed sheet, put in rubber cement preparing tank the most successively, solvent load is 3.5-4.0 times of rubber material using quantity,
Soak 2h, continuous stirring >=12h, be completely dissolved to film, pick out preservation, note sealing and place at shady and cool.
A kind of preparation side of the permanent tack type rubber cement for presulfurization method tyre rebuilding
Method, it is characterised in that in described step (1), the tackifying resin KORESIN of one section of mixing 1/2 consumption wants
Add at the mixing initial stage, and by controlling rotating speed and mixing time, it is ensured that melting temperature reaches KORESIN
Ring and ball softening point be 130-145 DEG C.
A kind of preparation of the permanent tack type rubber cement for presulfurization method tyre rebuilding
Method, it is characterised in that use low in described step (2) and step (3) in two-stage nitration, three-stage mixing glue
Temperature mixer mixing.