CN106147015A - Tourist souvenir material and preparation method thereof moulded by a kind of PP wood - Google Patents
Tourist souvenir material and preparation method thereof moulded by a kind of PP wood Download PDFInfo
- Publication number
- CN106147015A CN106147015A CN201610502192.5A CN201610502192A CN106147015A CN 106147015 A CN106147015 A CN 106147015A CN 201610502192 A CN201610502192 A CN 201610502192A CN 106147015 A CN106147015 A CN 106147015A
- Authority
- CN
- China
- Prior art keywords
- parts
- tourist souvenir
- mah
- wood
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of PP wood and mould tourist souvenir material and preparation method thereof, mainly include that following raw material is made: PP resin-oatmeal 100 parts, sisal fiber 50 80 parts, coupling agent 7 12 parts, magnesium stearate 23 parts, Firebrake ZB 35 parts, primary antioxidant 0.2 0.5 parts, auxiliary anti-oxidant 0.5 1.5 parts, maleic anhydride (MAH) 0.5 1 parts, coloring agent 0.2 0.5, ethylene bis stearic acid amide 2 parts, present invention also offers this PP wood and mould the preparation method of tourist souvenir material, above-mentioned formula combines preparation method and provides a kind of energy-conserving and environment-protective, with low cost, processing characteristics is excellent, it is easy to the tourist souvenir material of various coloring and material emulation, meet the needs of economic life.
Description
Technical field
The present invention relates to a kind of tourist souvenir material, particularly relate to a kind of PP wood and mould tourist souvenir material and system thereof
Preparation Method.
Background technology
Tourist souvenir, as the term suggests be i.e. that the exquisiteness that visitor buys in tourism process is portable, be rich in region feature and
The artware gift of national characters, and allow the souvenir that people bears in mind.Someone likens the name that tourist souvenir is a city
Sheet, this name cards elegance is magnificent, has high collection and value of appreciation.China is vast in territory, populous, and mobility is big, especially
The popularization of its golden week for tourism in recent years, has more expedited the emergence of the exploitation of all kinds of souvenir.Yet with its regional feature, economic development
Imbalance, culture, the difference of environmental protection concept, the quality of materials that all kinds of souvenirs use, useful all kinds of rare wood are planted, useful
The former waste material of industry, useful animal osseous remains, it is provided that a kind of energy-conserving and environment-protective, with low cost, processing characteristics is excellent, be easy to various coloring with
The tourist souvenir material of material emulation, it has also become a kind of needs of economic life.
Summary of the invention
It is an object of the invention to provide a kind of PP wood and mould tourist souvenir material and preparation method thereof, it is provided that be a kind of energy-conservation
Environmental protection, the tourist souvenir material that with low cost, processing characteristics is excellent, is easy to various coloring emulates with material, meet economy
A kind of needs of life.
In the present invention, " consumption ", " part " are all quality criterias, and the amount of each component is all on the basis of 100 parts of PP resins.
For solving the problems referred to above, the present invention uses following scheme:
Tourist souvenir material moulded by a kind of PP wood, mainly includes that following raw material is made: PP resin-oatmeal 100 parts, sisal fiber
50-80 part, coupling agent 7-12 part, magnesium stearate 2-3 part, Firebrake ZB 3-5 part, primary antioxidant 0.2-0.5 part, auxiliary anti-oxidant 0.5-
1.5 parts, maleic anhydride (MAH) 0.5-1 part, coloring agent 0.2-0.5, ethylene bis stearic acid amide 2 parts.
As preferably, described primary antioxidant uses antioxidant 1010, and auxiliary anti-oxidant uses dilauryl thiodipropionate；
As preferably, described coupling agent uses MAH-g-PP；
As preferably, described coloring agent is selected according to required color: (1) red mainly phthalocyanine is red；(2) yellow mainly has chromium
Yellow；(3) black is mainly carbon black.
The preparation method of tourist souvenir material moulded by this PP wood, comprises the following steps:
(1) after sisal fiber being soaked 2 hours in water, using single screw extrusion machine, extrusion stripping obtains in an extruder
Plant fiber, places in fiber disintegrating machine broken, the Plant fiber after broken is crossed 80 mesh sieves, dries, water content ＜ 2wt%；
(2) according to proportioning raw materials, PP resin-oatmeal, step (1) are obtained sisal fiber, MAH-g-PP, magnesium stearate addition stirring
Mixing in machine, rotating speed is 600 revs/min, and the time is 10-15 minute, and temperature is 90 DEG C, obtains mixture standby；
(3) batch mixing that step (2) is obtained, add Firebrake ZB, primary antioxidant, auxiliary anti-oxidant, maleic anhydride (MAH), coloring agent,
Ethylene bis stearic acid amide continues stirring, and rotating speed is 1100 revs/min, and the time is 8-10 minute, and temperature is 100 DEG C, is mixed
Compound is standby；
(4) pelletize is carried out at a temperature of the mixture that step (3) obtains being joined comminutor 120 DEG C, the granulate cooling that will obtain
After, obtain a kind of tourist souvenir material, further according to different ornameutal handiwork requirements, carve after die casting or casting,
Coloring etc..
The invention have benefit that: the present invention uses technique scheme to provide a kind of PP wood to mould tourist souvenir material
Material and preparation method thereof, it is provided that a kind of energy-conserving and environment-protective, with low cost, processing characteristics is excellent, be easy to various coloring and material is imitated
Genuine tourist souvenir material, meets a kind of needs of economic life.
Detailed description of the invention
The present invention is described in detail, in illustrative examples and the explanation of this present invention below in conjunction with specific embodiment
It is used for explaining the present invention, but not as a limitation of the invention.
Embodiment 1
Tourist souvenir material moulded by a kind of PP wood, mainly includes that following raw material is made: PP resin-oatmeal 100 parts, sisal fiber
50 parts, MAH-g-PP 7 parts, magnesium stearate 2 parts, Firebrake ZB 3 parts, primary antioxidant 0.3 part, auxiliary anti-oxidant 1 part, maleic anhydride
(MAH) 0.5 part, phthalocyanine is red 0.3, ethylene bis stearic acid amide 2 parts；Described primary antioxidant uses antioxidant 1010, auxiliary anti-oxidant
Use dilauryl thiodipropionate.
The preparation method of tourist souvenir material moulded by this PP wood, comprises the following steps:
(1) after sisal fiber being soaked 2 hours in water, using single screw extrusion machine, extrusion stripping obtains in an extruder
Plant fiber, places in fiber disintegrating machine broken, the Plant fiber after broken is crossed 80 mesh sieves, dries, water content ＜ 2wt%；
(2) according to proportioning raw materials, PP resin-oatmeal, step (1) are obtained sisal fiber, MAH-g-PP, magnesium stearate addition stirring
Mixing in machine, rotating speed is 600 revs/min, and the time is 10 minutes, and temperature is 90 DEG C, obtains mixture standby；
(3) batch mixing that step (2) is obtained, add Firebrake ZB, primary antioxidant, auxiliary anti-oxidant, maleic anhydride (MAH), phthalocyanine red,
Ethylene bis stearic acid amide continues stirring, and rotating speed is 1100 revs/min, and the time is 8-10 minute, and temperature is 100 DEG C, is mixed
Compound is standby；
(4) pelletize is carried out at a temperature of the mixture that step (3) obtains being joined comminutor 120 DEG C, the granulate cooling that will obtain
After, obtain a kind of tourist souvenir material, further according to different ornameutal handiwork requirements, carve after die casting or casting,
Coloring etc..
Embodiment 2
Tourist souvenir material moulded by a kind of PP wood, mainly includes that following raw material is made: PP resin-oatmeal 100 parts, sisal fiber
60 parts, MAH-g-PP 10 parts, magnesium stearate 2 parts, Firebrake ZB 3 parts, primary antioxidant 0.4 part, auxiliary anti-oxidant 1 part, maleic anhydride
(MAH) 0.5 part, chrome yellow 0.4, ethylene bis stearic acid amide 2 parts；Described primary antioxidant uses antioxidant 1010, and auxiliary anti-oxidant is adopted
Use dilauryl thiodipropionate.
The preparation method of tourist souvenir material moulded by this PP wood, comprises the following steps:
(1) after sisal fiber being soaked 2 hours in water, using single screw extrusion machine, extrusion stripping obtains in an extruder
Plant fiber, places in fiber disintegrating machine broken, the Plant fiber after broken is crossed 80 mesh sieves, dries, water content ＜ 2wt%；
(2) according to proportioning raw materials, PP resin-oatmeal, step (1) are obtained sisal fiber, MAH-g-PP, magnesium stearate addition stirring
Mixing in machine, rotating speed is 600 revs/min, and the time is 12 minutes, and temperature is 90 DEG C, obtains mixture standby；
(3) batch mixing step (2) obtained, adds Firebrake ZB, primary antioxidant, auxiliary anti-oxidant, maleic anhydride (MAH), chrome yellow, second
The double stearic amide of support continues stirring, and rotating speed is 1100 revs/min, and the time is 8-10 minute, and temperature is 100 DEG C, is mixed
Thing is standby；
(4) pelletize is carried out at a temperature of the mixture that step (3) obtains being joined comminutor 120 DEG C, the granulate cooling that will obtain
After, obtain a kind of tourist souvenir material, further according to different ornameutal handiwork requirements, carve after die casting or casting,
Coloring etc..
Embodiment 3
Tourist souvenir material moulded by a kind of PP wood, mainly includes that following raw material is made: PP resin-oatmeal 100 parts, sisal fiber
80 parts, MAH-g-PP 12 parts, magnesium stearate 3 parts, Firebrake ZB 5 parts, primary antioxidant 0.5 part, auxiliary anti-oxidant 1.5 parts, maleic anhydride
(MAH) 1 part, carbon black 0.5, ethylene bis stearic acid amide 2 parts；Described primary antioxidant uses antioxidant 1010, and auxiliary anti-oxidant uses
Dilauryl thiodipropionate.
The preparation method of tourist souvenir material moulded by this PP wood, comprises the following steps:
(1) after sisal fiber being soaked 2 hours in water, using single screw extrusion machine, extrusion stripping obtains in an extruder
Plant fiber, places in fiber disintegrating machine broken, the Plant fiber after broken is crossed 80 mesh sieves, dries, water content ＜ 2wt%；
(2) according to proportioning raw materials, PP resin-oatmeal, step (1) are obtained sisal fiber, MAH-g-PP, magnesium stearate addition stirring
Mixing in machine, rotating speed is 600 revs/min, and the time is 15 minutes, and temperature is 90 DEG C, obtains mixture standby；
(3) batch mixing step (2) obtained, adds Firebrake ZB, primary antioxidant, auxiliary anti-oxidant, maleic anhydride (MAH), carbon black, second
The double stearic amide of support continues stirring, and rotating speed is 1100 revs/min, and the time is 10 minutes, and temperature is 100 DEG C, obtains mixture
Standby；
(4) pelletize is carried out at a temperature of the mixture that step (3) obtains being joined comminutor 120 DEG C, the granulate cooling that will obtain
After, obtain a kind of tourist souvenir material, further according to different ornameutal handiwork requirements, carve after die casting or casting,
Coloring etc..
The principle of above-described embodiment only illustrative present invention and effect thereof, not for limiting the present invention.Any ripe
Above-described embodiment all can be modified under the spirit and the scope of the present invention or change by the personage knowing this technology.Cause
This, have usually intellectual such as complete with institute under technological thought without departing from disclosed spirit in art
All equivalences become are modified or change, and must be contained by the claim of the present invention.
Claims (2)
1. tourist souvenir material and preparation method thereof moulded by a PP wood, it is characterised in that mainly include following raw material make and
Become: PP resin-oatmeal 100 parts, sisal fiber 50-80 part, coupling agent 7-12 part, magnesium stearate 2-3 part, Firebrake ZB 3-5 part, master resist
Oxygen agent 0.2-0.5 part, auxiliary anti-oxidant 0.5-1.5 part, maleic anhydride (MAH) 0.5-1 part, coloring agent 0.2-0.5, the double tristearin of ethylene
Acid amide 2 parts；Described primary antioxidant uses antioxidant 1010, and auxiliary anti-oxidant uses dilauryl thiodipropionate；Described coupling
Agent uses MAH-g-PP；Described coloring agent is selected according to required color: (1) red mainly phthalocyanine is red；(2) yellow mainly has chromium
Yellow；(3) black is mainly carbon black.
The preparation method of tourist souvenir material moulded by PP wood the most according to claim 1, it is characterised in that include following step
Rapid:
(1) after sisal fiber being soaked 2 hours in water, using single screw extrusion machine, extrusion stripping obtains in an extruder
Plant fiber, places in fiber disintegrating machine broken, the Plant fiber after broken is crossed 80 mesh sieves, dries, water content ＜ 2wt%；
(2) according to proportioning raw materials, PP resin-oatmeal, step (1) are obtained sisal fiber, MAH-g-PP, magnesium stearate addition stirring
Mixing in machine, rotating speed is 600 revs/min, and the time is 10-15 minute, and temperature is 90 DEG C, obtains mixture standby；
(3) batch mixing that step (2) is obtained, add Firebrake ZB, primary antioxidant, auxiliary anti-oxidant, maleic anhydride (MAH), coloring agent,
Ethylene bis stearic acid amide continues stirring, and rotating speed is 1100 revs/min, and the time is 8-10 minute, and temperature is 100 DEG C, is mixed
Compound is standby；
(4) pelletize is carried out at a temperature of the mixture that step (3) obtains being joined comminutor 120 DEG C, the granulate cooling that will obtain
After, obtain a kind of tourist souvenir material, further according to different ornameutal handiwork requirements, carve after die casting or casting,
Coloring etc..