CN106145725A - The flying dust utilizing desulfurization to generate electricity is manufactured into the composition of building materials - Google Patents
The flying dust utilizing desulfurization to generate electricity is manufactured into the composition of building materials Download PDFInfo
- Publication number
- CN106145725A CN106145725A CN201610638796.2A CN201610638796A CN106145725A CN 106145725 A CN106145725 A CN 106145725A CN 201610638796 A CN201610638796 A CN 201610638796A CN 106145725 A CN106145725 A CN 106145725A
- Authority
- CN
- China
- Prior art keywords
- flying dust
- building materials
- manufactured
- generate electricity
- reactant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of flying dust utilizing desulfurization to generate electricity and be manufactured into the composition of building materials, with produced flying dust anhydrous gypsum (the β CaSO of circulation of fluid bed steam generating4Anhydrite) 90% add that cohering reactant 10% makes building materials, it is used in non-structural cement mortar, pavement brick, artistic wall face brick, indoor compartment fire wall or plasterboard, the reactant that coheres therein has half-H 2 O calcium sulphate 70%, sodium sulfate 10%, calcium oxide 10%, sodium hydroxide 5%, cement 0 5%, starch 0 5%, and the aquiform stool being formed plus gross weight ten to four 13 percent can form hydration reaction.The flying dust utilizing desulfurization to generate electricity of the present invention is manufactured into building materials and is mixed into flying dust anhydrous gypsum regeneration with the applicable reactant that coheres, and only needs suitable quantity of water can produce the building materials of the strength of cement that matches in excellence or beauty, can effectively utilize flying dust.
Description
Technical field
The present invention relates to discarded flying dust recycling field, particularly relate to a kind of flying dust utilizing desulfurization to generate electricity and be manufactured into building materials
Composition.
Background technology
Platform moulds the six CFB Boiler (circulation of fluid bed steam power-generating system) gently using U.S. ALSTOM, with oil
Burnt: limestone=2:1 mixing is sent into CFB and carried out high-temperature oxydation burning promotion gas-turbine generating and supply steam, and it produces every day
The side-product flying dust (including powdery mixed gypsum, granular by-product lime and aquation Gypsum Fibrosum) of hundreds of tonnes, cannot effectively locate so far
Reason, owing to this mixing by-product lime is 850 DEG C more than-900 DEG C side-products produced, β anhydrous gypsum (β CaSO4anhydrite)
Formation condensation cannot be reacted by fast hydration at normal temperatures and pressures with water, therefore have influence on the usability of flying dust.
Summary of the invention
It is an object of the invention to provide a kind of flying dust utilizing desulfurization to generate electricity and be manufactured into the composition of building materials, cohere with applicable
Reactant is mixed into flying dust (CFB ash) anhydrous gypsum regeneration, only needs suitable quantity of water can produce the building materials of the strength of cement that matches in excellence or beauty, can
Effectively utilize flying dust.
For achieving the above object, the present invention provides a kind of flying dust utilizing desulfurization to generate electricity to be manufactured into the composition of building materials, to follow
The produced flying dust anhydrous gypsum 90% of ring fluidized bed steam generating makes building materials plus cohering reactant 10%, therein glutinous
Knot reactant has half-H 2 O calcium sulphate 70%, sodium sulfate 10%, calcium oxide 10%, sodium hydroxide 5%, cement 0-5%, starch 0-
5%, the aquiform stool being formed plus gross weight ten to four 13 percent can form hydration reaction.
As a further improvement on the present invention, wherein powdery mixed gypsum 100% can also add the granular Calx of flying dust 130%
Or aquation Gypsum Fibrosum 75% is to make various building materials.
Compared with prior art, the flying dust utilizing desulfurization to generate electricity of the present invention is manufactured into the composition of building materials and coheres with applicable
Reactant is mixed into flying dust anhydrous gypsum regeneration, only needs suitable quantity of water can produce the building materials of the strength of cement that matches in excellence or beauty, can be effective
Utilize flying dust.
Detailed description of the invention
The described flying dust utilizing desulfurization to generate electricity is manufactured into the composition of building materials, is produced with the generating of circulation of fluid bed steam
Flying dust anhydrous gypsum (β CaSO4) 90% make building materials plus cohering reactant 10%, it is mainly used for non-structural cement bonded sand
Slurry, pavement brick, artistic wall face brick, indoor compartment fire wall and plasterboard etc., the reactant that coheres therein has half water
Calcium sulfate (CaSO4.1/2H2O) 70%, sodium sulfate (Na2SO4) 10%, calcium oxide (CaO quick lime) 10%, sodium hydroxide
(NaOH burns salty) 5%, cement 0-5%, starch 0-5%, therefore formed the water of ten to four 13 percent plus gross weight
Just hydration reaction can be formed.
Its chemical reaction is as follows:
It is as follows that it makes product:
The goods of the present invention can meet the building materials demand of normality, only need to add the 10% of above-mentioned total amount, and the present invention's is anti-
Adhesive agent is answered i.e. to may conform to the building materials strength demand of normality.Wherein powdery mixed gypsum 100% can also add the granular Calx of flying dust
130% or aquation Gypsum Fibrosum 75% to make various building materials.
In compositions in sum, the present invention use specifically cohere reactant add produce reaction facilitate anhydrous gypsum
Reaction produce and cohere, so being provided that good usability, be one completely from known different compositing formula.
Above in association with most preferred embodiment, invention has been described, but the invention is not limited in enforcement disclosed above
Example, and amendment, the equivalent combinations that the various essence according to the present invention is carried out should be contained.
Claims (2)
1. the flying dust utilizing desulfurization to generate electricity is manufactured into the composition of building materials, it is characterised in that: send out with circulation of fluid bed steam
The produced flying dust anhydrous gypsum of electricity 90% adds that cohering reactant 10% makes building materials, is used in non-structural cement mortar, people
Row Footpath brick, artistic wall face brick, indoor compartment fire wall or plasterboard, the reactant that coheres therein has half-H 2 O calcium sulphate
70%, sodium sulfate 10%, calcium oxide 10%, sodium hydroxide 5%, cement 0-5%, starch 0-5%, is formed plus gross weight
Ten to four 13 percent aquiform stool can form hydration reaction.
The flying dust utilizing desulfurization to generate electricity the most as claimed in claim 1 is manufactured into the composition of building materials, it is characterised in that: wherein powdery
Mixed gypsum 100% can also add the granular Calx of flying dust 130% or aquation Gypsum Fibrosum 75% to make various building materials.