CN106145108A - A kind of preparation method of medicinal carbon - Google Patents
A kind of preparation method of medicinal carbon Download PDFInfo
- Publication number
- CN106145108A CN106145108A CN201610483361.5A CN201610483361A CN106145108A CN 106145108 A CN106145108 A CN 106145108A CN 201610483361 A CN201610483361 A CN 201610483361A CN 106145108 A CN106145108 A CN 106145108A
- Authority
- CN
- China
- Prior art keywords
- preparation
- retort
- carbonization
- dried
- activation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the preparation method of a kind of medicinal carbon, it is with corncob as material, by carbonization, grind into powder, activate and drying steps make, utilize the minute aperture that activated carbon granule is covered with above, the thing cholesterol molecule of the nuisance in human body and surplus can be absorbed, become a kind of natural " filter ", the nuisance of human body and superfluous cholesterol can have been absorbed in vivo, thus play the effect of building body, eliminating toxin and beautifying the skin, blood fat reducing.
Description
Technical field
The present invention relates to the preparation method of a kind of medicine, the preparation method of a kind of medicinal carbon
Preparation method.
Background technology
By timber, the heated carbonization of xylocarp shell, then grinding as smalls, the activated carbon made is for treating hyperlipemia.Existing
Generation research is thought, the minute aperture that activated carbon is covered with above, cholesterol molecule superfluous in food and in human body can be absorbed, and live
Property charcoal be one " passerby " hurriedly, with the effect of digestive function of human body, excrete together with stool, can be in human body
Nuisance and surplus thing cholesterol molecule absorb, become a kind of natural " filter ", having of human body can have been absorbed in vivo
Pest and superfluous cholesterol, thus play the effect of building body, eliminating toxin and beautifying the skin, blood fat reducing.Its mechanism of action is, each broken
Activated carbon granule surface, end has all been covered with microscopic pinholes, just because of have thousands of pores on charcoal granule, and one
Natural " filter ", can filter gas and liquid so that it is becomes pure, and has no side effect.
Summary of the invention
Disclosed by the invention is a kind of medicinal carbon manufacture method, is with corncob as carbonated material, by following step
Rapid preparation:
1) carbonization:
A. by the corncob after threshing, put into retort completely cuts off in air or anaerobic environment and heat, temperature control
System, at 200~300 DEG C, after heating 3~4 hours, turns off thermal source, after natural cooling, obtains primary carbonization body A;
B. the primary carbonization body A obtained in step a is placed in retort and is warmed up to 600~700 DEG C and retort
Fire door to be opened, and after primary carbonization body A naked light burns 30~60 minutes, retort completely cuts off air or is quickly closed by fire door
Close, with cold water, naked light in retort is put out by water simultaneously, natural cooling 2~after 3 hours, obtain carbonization block B;
2) grind into powder: the carbonization block B pulverization that will obtain, sieve, obtain powdered carbon powder C;
3) activation: powdered carbon powder C is carried out activation processing, obtains activating charcoal end D;
4) it is dried: activation charcoal end D is put into and is dried process, obtain clinical active carbon powder E;
Wherein, step 1) a in, preferable temperature is 250 DEG C, and the time of heating is 4h, the primary carbonization body so obtained
Just ratio is more thoroughly.
Wherein, further step 1) b in, the temperature being rapidly heated is 660 DEG C, and the time of naked light burning is 50 points
Clock, till the degree then put out by water by naked light in retort with cold water is for can not see Mars.
Wherein further, step 2) in the sieve selected that sieves be 120 mesh sieve.
Wherein further, step 3) in the method for activation processing be: powdered carbon powder C is placed in steam kettle, at one
Standard atmosphere is depressed, and the temperature controlled in steam kettle is 100 DEG C, distills 40~50 minutes, and that plays powdered carbon powder C is thorough
Activation.
Wherein further, step 4) in the drying equipment of dried be drying baker, the temperature control of dried
System is at 120~130 DEG C, and the water content of dried activated carbon end D is less than 5%.
The invention discloses the preparation method of a kind of medicinal carbon, be with corncob as material, by carbonization, grind into powder,
Activation and drying steps make, and utilize the minute aperture that activated carbon granule is covered with above, can be the nuisance in human body and surplus
Thing cholesterol molecule absorbs, and has become a kind of natural " filter ", and nuisance and the superfluous gallbladder that can absorb human body in vivo are solid
Alcohol, thus play the effect of building body, eliminating toxin and beautifying the skin, blood fat reducing.
Detailed description of the invention
Elaborating embodiments of the invention below, the present embodiment is carried out under premised on technical solution of the present invention
Implement, give detailed embodiment and concrete operating process, but protection scope of the present invention is not limited to following enforcement
Example.
Embodiment 1
The material selected is the corncob after threshing, including following preparation process:
1) carbonization:
A. by the corncob after threshing, putting into isolation air in retort and heat, temperature controls at 200 DEG C, heats 3
After hour, turn off thermal source, after natural cooling, obtain primary carbonization body A;
B. the primary carbonization body A obtained in step a is placed in retort and is warmed up to 600 DEG C, primary carbonization body A naked light
After burning 30 minutes, retort being completely cut off air, put out by water by naked light in retort with cold water simultaneously, the degree put out by water is for can not see
Till Mars, then natural cooling is after 2 hours, obtains carbonization block B;
2) grind into powder: the carbonization block B mortar pulverization that will obtain, sieve and use 120 mesh sieve, obtain powdered carbon powder C;
3) activation: powdered carbon powder C is carried out activation processing, and the method for activation processing is: powdered carbon powder C is placed in steam kettle
In, to depress at a standard atmosphere, the temperature controlled in steam kettle is 100 DEG C, distills and within 40 minutes, obtains activating charcoal end D;
4) it is dried: being put into by activation charcoal end D and be dried process, the equipment of dried is drying baker, dried
Temperature control at 120 DEG C, the water content of dried activated carbon end D be less than 5%, obtain clinical active carbon powder E;
Embodiment 2
The material selected is the corncob after threshing, including following preparation process:
1) carbonization:
A. by the corncob after threshing, putting into isolation air in retort and heat, temperature controls at 300 DEG C, heats 4
After hour, turn off thermal source, after natural cooling, obtain primary carbonization body A;
B. the primary carbonization body A obtained in step a is placed in retort and is warmed up to 700 DEG C, described primary carbonization body A
After naked light burns 60 minutes, by retort fire door quick closedown, with cold water, naked light in retort is put out by water, with cold water by charcoal simultaneously
Till the degree that in change stove, naked light is put out by water is for can not see Mars, then natural cooling is after 3 hours, obtains carbonization block B;
2) grinding into powder: the carbonization block B pulverization that will obtain, sieve, the sieve of selection is 120 mesh sieve, obtains powdered carbon powder
End C;
3) activation: powdered carbon powder C is carried out activation processing, and the method for activation processing is: powdered carbon powder C is placed in steam kettle
In, to depress at a standard atmosphere, the temperature controlled in steam kettle is 100 DEG C, distills 50 minutes, obtains activating charcoal end D;
4) it is dried: being put into by activation charcoal end D and be dried process, the equipment of dried is drying baker, dried
Temperature control at 130 DEG C, the water content of dried activated carbon end D be less than 5%, obtain clinical active carbon powder E;
Embodiment 3
The material selected is the corncob after threshing, including following preparation process:
1) carbonization:
A. by the corncob after threshing, putting into isolation air in retort and heat, temperature controls at 250 DEG C, heats 4
After hour, turn off thermal source, after natural cooling, obtain primary carbonization body A;
B. the primary carbonization body A obtained in step a is placed in retort and is warmed up to 660 DEG C, described primary carbonization body A
After naked light burns 50 minutes, retort is completely cut off air, with cold water, naked light in retort is put out by water, with cold water by retort simultaneously
Till the degree that interior naked light is put out by water is for can not see Mars, then natural cooling is after 3 hours, obtains carbonization block B;
2) grinding into powder: the carbonization block B pulverization that will obtain, sieve, the sieve sieved is 120 mesh sieve, obtains powdered carbon
Powder C;
3) activation: powdered carbon powder C is carried out activation processing, and the method for activation processing is: powdered carbon powder C is placed in steam kettle
In, to depress at a standard atmosphere, the temperature controlled in steam kettle is 100 DEG C, distills 40~50 minutes, obtains activating charcoal end D;
4) it is dried: being put into by activation charcoal end D and be dried process, dried is drying baker, the temperature of dried
Degree controls at 120 DEG C, and the water content of dried activated carbon end D is less than 5%, obtains clinical active carbon powder E.
Claims (6)
1. the preparation method of a medicinal carbon, it is characterised in that with corncob as carbonated material, by following steps system
Standby:
1) carbonization:
A. by the corncob after threshing, putting into isolation air in retort and heat, temperature controls at 200~300 DEG C, heating
After 3~4 hours, turn off thermal source, after natural cooling, obtain primary carbonization body A;
B. the primary carbonization body A obtained in step a is placed in retort and is warmed up to 600~700 DEG C, described primary carbonization body
After A naked light burns 30~60 minutes, described retort is completely cut off air, with cold water, naked light in retort is put out by water simultaneously, natural
After cooling down 2~3 hours, obtain carbonization block B;
2) grind into powder: the carbonization block B pulverization that will obtain, sieve, obtain powdered carbon powder C;
3) activation: powdered carbon powder C is carried out activation processing, obtains activating charcoal end D;
4) it is dried: activation charcoal end D is put into and is dried process, obtain clinical active carbon powder E.
The preparation method of a kind of medicinal carbon the most as claimed in claim 1, it is characterised in that step 1) a in, described temperature
Degree is 250 DEG C, and the time of described heating is 4h.
The preparation method of a kind of medicinal carbon the most as claimed in claim 1, it is characterised in that described step 1) b in, institute
Stating temperature is 660 DEG C, and the time of described naked light burning is 50 minutes, and the degree that naked light in retort is put out by water by described cold water is
Till can not see Mars.
The preparation method of a kind of medicinal carbon the most as claimed in claim 1, it is characterised in that step 2) in described in sieve
Sieve be 120 mesh sieve.
The preparation method of a kind of medicinal carbon the most as claimed in claim 1, it is characterised in that described step 3) at activation
The method of reason is: be placed in steam kettle by powdered carbon powder C, depresses at a standard atmosphere, and the temperature controlled in steam kettle is 100
DEG C, distill 40~50 minutes.
The preparation method of a kind of medicinal carbon the most as claimed in claim 1, it is characterised in that step 4) in described be dried
Process is drying baker, and the temperature of described dried controls at 120~130 DEG C, the water content of dried activated carbon end D
Less than 5%.