CN106136779A - A kind of processing method of Dual-color cup - Google Patents
A kind of processing method of Dual-color cup Download PDFInfo
- Publication number
- CN106136779A CN106136779A CN201610694139.XA CN201610694139A CN106136779A CN 106136779 A CN106136779 A CN 106136779A CN 201610694139 A CN201610694139 A CN 201610694139A CN 106136779 A CN106136779 A CN 106136779A
- Authority
- CN
- China
- Prior art keywords
- glaze
- cup
- color
- dual
- processing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The processing method that the invention discloses a kind of Dual-color cup, relate to cup processing method field, comprise the steps: that (1) cup base screens, (2) setting-out, (3) glaze spraying, (4) leaching glaze, (5) drag at the end, the ratio of glaze slip and waterproofing agent is 1:6 1:8, different glaze can be reduced inside and outside base substrate trickle in sintering process the phenomenon mutually adulterated, promote the aesthetics of cup, the temperature of line drawing machine is 20 24 DEG C, may insure that the block-water effect of setting-out serosity, improve the efficiency of setting-out, rim of a cup after glaze spraying carries out dipping in mouth on sponge and processes, the density of sponge is 26 30g/cm2, the later glaze of rim of a cup can be eliminated, improve aesthetics, the leaching glaze time controls at 12 14s/ parts, makes base substrate leaching glaze complete, and cup glaze thickness is uniform.Adopting this method the Dual-color cup uniform in color of processing, without sagging, without glaze heap phenomenon, market potential is huge, has a extensive future.
Description
Technical field
The invention belongs to cup processing method field, it is more particularly related to the processing method of a kind of Dual-color cup.
Background technology
Ceramic cup makes cup with pottery exactly, is used for drinking the vessel containing wine, water, tea etc..So-called " ceramic " is exactly clay
Make a kind of shape, by clay or other inorganic non-metallic raw material, through the PROCESS FOR TREATMENT such as molding, sintering, be used for decorating and protecting
Building wall and the tabular on ground or Bulk ceramic goods.It is made to harden, no longer through being heated to a certain degree after drying
It is dissolved in water, along with the socioeconomic Dual-color cup meeting developed rapidly with the continuous renewal of people's consumption idea, more cultural coloring
Increasingly by the generally favor of consumer, its market share also can constantly expand, and with its vigorous vitality and higher
Profit margin create more preferable economic benefit, promote Production of Ceramics sound development.
Summary of the invention
Problem to be solved by this invention is to provide a kind of cup uniform in color, without sagging, without the Dual-color cup of glaze heap phenomenon
Processing method.
To achieve these goals, the technical scheme that the present invention takes is:
The processing method of a kind of Dual-color cup, comprises the steps:
(1) cup base screening
The object that circular regular and base substrate cleaning the cup base of selected shape rule, oral area is processed as Dual-color cup；
(2) setting-out
The cup base of screening is placed on line drawing machine and at the uniform velocity rotates, dip glaze slip and waterproofing agent with the brush pen on line drawing machine
The mixed liquor being configured to, is drawn on base substrate, is then put in drying baker by the base substrate after setting-out and dries, and forms essence
Base, glaze slip proportion is 1.50-1.70g/cm3, the rotating speed of line drawing machine is 150-250r/min；
(3) glaze spraying
Essence base is put on glaze spraying device, the milky white glaze slip and color glaze glaze slip of adjusting ratio are sprayed by the nozzle of glaze spraying device
To base substrate inner surface, milky white glaze slip specific gravity control is at 1.65-1.75g/cm3, color glaze slurry controls at 1.70-1.76g/cm3；
(4) leaching glaze
In automatic infiltration glaze machine, adjust the ratio of opal glaze and color glaze, then the base substrate after glaze spraying is put into automatic infiltration glaze
Carrying out soaking glaze in machine to process, milky white glaze slip specific gravity control is at 1.50-1.60g/cm3, color glaze slurry specific gravity control is at 1.55-1.62g/
cm3；
(5) drag at the end
Cup after having soaked glaze is placed on 40-50 purpose and moves 2-4 time on the net, and the interval time moved is 5-10min, torr
Carry out at the end product inspection, qualified after product carry out packing, dispatching from the factory.
Preferably, in described step (2), the ratio of glaze slip and waterproofing agent is 1:6-1:8.
Preferably, in described step (2), the temperature of line drawing machine is 20-24 DEG C.
Preferably, in described step (3), rim of a cup after glaze spraying carries out dipping in mouth on sponge and processes.
Preferably, the density of described sponge is 26-30g/cm2。
Preferably, described step (4) the leaching glaze time controls at 12-14s/ part.
Beneficial effect: the ratio of the processing method that the invention provides a kind of Dual-color cup, glaze slip and waterproofing agent is 1:6-1:
8, it is possible to reduce inside and outside base substrate, different glaze trickles the phenomenon of mutually doping in sintering process, promote the aesthetics of cup, picture
The temperature of line machine is 20-24 DEG C, it can be ensured that the block-water effect of setting-out serosity, improves the efficiency of setting-out, and the rim of a cup after glaze spraying exists
Carrying out dipping in mouth on sponge to process, the density of sponge is 26-30g/cm2, the later glaze of rim of a cup can be eliminated, improve aesthetics, leaching
The glaze time controls at 12-14s/ part, makes base substrate leaching glaze complete, and the glaze thickness of cup is uniform.Adopt this method the double-colored of processing
Cup cup uniform in color, without sagging, without glaze heap phenomenon, market potential is huge, has a extensive future.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with
Detailed description of the invention, is expanded on further the technical step of the present invention:
Embodiment 1:
The processing method of a kind of Dual-color cup, comprises the steps:
(1) cup base screening
The object that circular regular and base substrate cleaning the cup base of selected shape rule, oral area is processed as Dual-color cup；
(2) setting-out
The cup base of screening is placed on line drawing machine and at the uniform velocity rotates, dip glaze slip and waterproofing agent with the brush pen on line drawing machine
The mixed liquor being configured to, is drawn on base substrate, is then put in drying baker by the base substrate after setting-out and dries, and forms essence
Base, glaze slip proportion is 1.50g/cm3, the ratio of glaze slip and waterproofing agent is 1:6, and the rotating speed of line drawing machine is 150r/min, line drawing machine
Temperature be 20 DEG C；
(3) glaze spraying
Essence base is put on glaze spraying device, the milky white glaze slip and color glaze glaze slip of adjusting ratio are sprayed by the nozzle of glaze spraying device
To base substrate inner surface, the rim of a cup after glaze spraying carries out dipping in mouth on sponge and processes, and the density of sponge is 26g/cm2, milky white glaze slip ratio
Heavily control at 1.65g/cm3, color glaze slurry controls at 1.70g/cm3；
(4) leaching glaze
In automatic infiltration glaze machine, adjust the ratio of opal glaze and color glaze, then the base substrate after glaze spraying is put into automatic infiltration glaze
Carrying out soaking glaze in machine to process, the leaching glaze time controls at 12s/ part, and milky white glaze slip specific gravity control is at 1.50g/cm3, color glaze slurry proportion
Control at 1.55g/cm3；
(5) drag at the end
Cup after having soaked glaze is placed on 40 purposes and moves on the net 2 times, and the interval time moved is 5min, carries out after backing
The inspection of product, qualified after product carry out packing, dispatching from the factory.
Embodiment 2:
The processing method of a kind of Dual-color cup, comprises the steps:
(1) cup base screening
The object that circular regular and base substrate cleaning the cup base of selected shape rule, oral area is processed as Dual-color cup；
(2) setting-out
The cup base of screening is placed on line drawing machine and at the uniform velocity rotates, dip glaze slip and waterproofing agent with the brush pen on line drawing machine
The mixed liquor being configured to, is drawn on base substrate, is then put in drying baker by the base substrate after setting-out and dries, and forms essence
Base, glaze slip proportion is 1.60g/cm3, the ratio of glaze slip and waterproofing agent is 1:7, and the rotating speed of line drawing machine is 200r/min, line drawing machine
Temperature be 22 DEG C；
(3) glaze spraying
Essence base is put on glaze spraying device, the milky white glaze slip and color glaze glaze slip of adjusting ratio are sprayed by the nozzle of glaze spraying device
To base substrate inner surface, the rim of a cup after glaze spraying carries out dipping in mouth on sponge and processes, and the density of sponge is 28g/cm2, milky white glaze slip ratio
Heavily control at 1.70g/cm3, color glaze slurry controls at 1.73g/cm3；
(4) leaching glaze
In automatic infiltration glaze machine, adjust the ratio of opal glaze and color glaze, then the base substrate after glaze spraying is put into automatic infiltration glaze
Carrying out soaking glaze in machine to process, the leaching glaze time controls at 12-14s/ part, and milky white glaze slip specific gravity control is at 1.55g/cm3, color glaze slurry ratio
Heavily control at 1.59g/cm3；
(5) drag at the end
Cup after having soaked glaze is placed on 45 purposes and moves on the net 3 times, and the interval time moved is 8min, carries out after backing
The inspection of product, qualified after product carry out packing, dispatching from the factory.
Embodiment 3:
The processing method of a kind of Dual-color cup, comprises the steps:
(1) cup base screening
The object that circular regular and base substrate cleaning the cup base of selected shape rule, oral area is processed as Dual-color cup；
(2) setting-out
The cup base of screening is placed on line drawing machine and at the uniform velocity rotates, dip glaze slip and waterproofing agent with the brush pen on line drawing machine
The mixed liquor being configured to, is drawn on base substrate, is then put in drying baker by the base substrate after setting-out and dries, and forms essence
Base, glaze slip proportion is 1.70g/cm3, the ratio of glaze slip and waterproofing agent is 1:8, and the rotating speed of line drawing machine is 250r/min, line drawing machine
Temperature be 24 DEG C；
(3) glaze spraying
Essence base is put on glaze spraying device, the milky white glaze slip and color glaze glaze slip of adjusting ratio are sprayed by the nozzle of glaze spraying device
To base substrate inner surface, the rim of a cup after glaze spraying carries out dipping in mouth on sponge and processes, and the density of sponge is 30g/cm2, milky white glaze slip ratio
Heavily control at 1.75g/cm3, color glaze slurry controls at 1.76g/cm3；
(4) leaching glaze
In automatic infiltration glaze machine, adjust the ratio of opal glaze and color glaze, then the base substrate after glaze spraying is put into automatic infiltration glaze
Carrying out soaking glaze in machine to process, the leaching glaze time controls at 14s/ part, and milky white glaze slip specific gravity control is at 1.60g/cm3, color glaze slurry proportion
Control at 1.62g/cm3；
(5) drag at the end
Cup after having soaked glaze is placed on 50 purposes and moves on the net 4 times, and the interval time moved is 10min, and backing is laggard
The inspection of row product, qualified after product carry out packing, dispatching from the factory.
After process above processes, taking out sample respectively, measurement result is as follows:
Can draw according to above table data, technical scheme substantially increases relevant relative to prior art
Performance indications, when embodiment 2 parameter, the cup uniform in color processed, without sagging, without glaze heap phenomenon, after having leaching glaze
Mouthful, bottom season sliding, between cup height and quality error little advantage, be now more beneficial for the processing of Dual-color cup.
The ratio of the processing method that the invention provides a kind of Dual-color cup, glaze slip and waterproofing agent is 1:6-1:8, it is possible to reduce
Inside and outside base substrate, different glaze trickles the phenomenon of mutually doping in sintering process, the aesthetics of lifting cup, the temperature of line drawing machine
For 20-24 DEG C, it can be ensured that the block-water effect of setting-out serosity, improving the efficiency of setting-out, the rim of a cup after glaze spraying is carried out on sponge
Dipping in mouth to process, the density of sponge is 26-30g/cm2, the later glaze of rim of a cup can be eliminated, improve aesthetics, the leaching glaze time controls
At 12-14s/ part, making base substrate leaching glaze complete, cup glaze thickness is uniform.The Dual-color cup cup color adopting this method processing is equal
Even, without sagging, without glaze heap phenomenon, market potential is huge, has a extensive future.
The foregoing is only embodiments of the invention, not thereby limit the scope of the claims of the present invention, every utilize this
Equivalent structure or equivalence flow process that bright description is made convert, or are directly or indirectly used in other relevant technology necks
Territory, is the most in like manner included in the scope of patent protection of the present invention.
Claims (6)
1. the processing method of a Dual-color cup, it is characterised in that comprise the steps:
(1) cup base screening
The object that circular regular and base substrate cleaning the cup base of selected shape rule, oral area is processed as Dual-color cup；
(2) setting-out
The cup base of screening is placed on line drawing machine and at the uniform velocity rotates, dip glaze slip and waterproofing agent preparation with the brush pen on line drawing machine
The mixed liquor become, is drawn on base substrate, is then put in drying baker by the base substrate after setting-out and dries, and forms essence base, glaze
Slurry proportion is 1.50-1.70g/cm3, the rotating speed of line drawing machine is 150-250r/min；
(3) glaze spraying
Essence base is put on glaze spraying device, the milky white glaze slip and color glaze glaze slip of adjusting ratio are sprayed onto base by the nozzle of glaze spraying device
Internal surface, milky white glaze slip specific gravity control is at 1.65-1.75g/cm3, color glaze slurry specific gravity control is at 1.70-1.76g/cm3；
(4) leaching glaze
In automatic infiltration glaze machine, adjust the ratio of opal glaze and color glaze, then the base substrate after glaze spraying is put in automatic infiltration glaze machine
Carrying out soaking glaze to process, milky white glaze slip specific gravity control is at 1.50-1.60g/cm3, color glaze slurry specific gravity control is at 1.55-1.62g/cm3；
(5) drag at the end
Cup after having soaked glaze is placed on 40-50 purpose and moves 2-4 time on the net, and the interval time moved is 5-10min, after backing
Carry out product inspection, qualified after product carry out packing, dispatching from the factory.
2. according to the processing method of a kind of Dual-color cup described in claim 1, it is characterised in that: in described step (2) glaze slip and
The ratio of waterproofing agent is 1:6-1:8.
3. according to the processing method of a kind of Dual-color cup described in claim 1, it is characterised in that: line drawing machine in described step (2)
Temperature be 20-24 DEG C.
4. according to the processing method of a kind of Dual-color cup described in claim 1, it is characterised in that: in described step (3) after glaze spraying
Rim of a cup on sponge, carry out dipping in mouth process.
5. according to the processing method of a kind of Dual-color cup described in claim 4, it is characterised in that: the density of described sponge is 26-
30g/cm2。
6. according to the processing method of a kind of Dual-color cup described in claim 1, it is characterised in that: described step (4) the leaching glaze time
Control at 12-14s/ part.