CN106123689B - The double anti-clothes of comfort type and its manufacturing method - Google Patents
The double anti-clothes of comfort type and its manufacturing method Download PDFInfo
- Publication number
- CN106123689B CN106123689B CN201610496066.3A CN201610496066A CN106123689B CN 106123689 B CN106123689 B CN 106123689B CN 201610496066 A CN201610496066 A CN 201610496066A CN 106123689 B CN106123689 B CN 106123689B
- Authority
- CN
- China
- Prior art keywords
- cloth
- double anti
- fiber
- clothes
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a kind of anti-clothes of comfort type pair and its manufacturing method, and double anti-clothes include housing and the double anti-materials being arranged in housing, and described pair of anti-materials include double anti-chips and padded coaming；Double anti-chips are formed by least 20 laminate cloth according to [0 °/90 °] orthogonal superposition, and the pressing plate cloth is suppressed by laminated cloth；The laminated cloth is formed by two layers of fiber cloth according to [0 °/90 °] orthogonal superposition；The fiber cloth is formed by filament through adhesive bond.Double anti-comfort levels that take of the present invention are good, and manufacturing process is simple and practicable, is not necessarily to multi parameters control.
Description
Technical field
The present invention relates to a kind of Protection Product more particularly to a kind of double anti-clothes of comfort type and its manufacturing methods.
Background technology
Double anti-clothes that is to say bulletproof stab-resistant clothes, and as its name suggests, not only the individual with bulletproof function but also with anti-stab function was anti-
Protect product.For flak jackets and stab-resistance body armor, the bullet-proof mechanism of material and anti-stab mechanism are not quite similar, shellproof mainly to rely on
The stretch-proof fracture strength of material, the tensile strength of material is bigger, and the projectiles such as bullet or fragmentation of high speed impact are in impact material
Expect, break/expanded material during its energy that dissipates it is more, to make projectile composition deformation, it is prevented to advance；And anti-stab process
In, since lancination is the process of a slow persistence, the shear strength of material is bigger, and point of a knife deformation is quicker, can hinder
Only sharp instrument continuation is advanced forward, achievees the purpose that protection.Under normal conditions, it is shellproof and it is anti-stab be contradictory, shellproof good material,
General anti-stab effect can be poor, and anti-stab good material, general bulletproof effect can be poor.In recent years, both at home and abroad in the research of double anti-clothes
Greater advance is achieved in terms of exploitation, but in view of the difference of mechanism, product is mostly that more structures of stab-resistant material and bullet resistant material are folded
Add, forms, this stack combinations by multiple material such as more combinations of materials often improve the complexity of process.Currently, open
Number for CN102788531A and CN 101881582A double anti-clothes, be by with bulletproof function material and anti-stab function
Material is combined, the difference is that double anti-clothes of Publication No. CN102788531 A are to be by bullet resistant material and stab-resistant material
By certain measure combination at one layer, double anti-clothes of Publication No. CN 101881582A are by bullet resistant material and stab-resistant material letter
It singly combines in a chip.
In addition, by the combination of bullet resistant material and stab-resistant material other than complex procedures, double anti-clothes that a combination thereof is formed exist
It is also tended in pliability not good enough.If the performance of flak jackets and stab-resistance body armor can be combined into one, effective protection, it is comfortable soft and
An equalization point is found between lightweight, it is possible to realize integrated protection efficiency on single structure and material, form softness
Comfort type Protection Product.And currently, only yet there are no report with a kind of soft double anti-clothes of comfort type that single structure and material manufactures
Road.
Invention content
In view of the foregoing drawbacks, the present invention provides a kind of anti-clothes of comfort type pair and its manufacturing method, for overcoming the prior art
Middle bullet resistant material and stab-resistant material are simply combined and manufacture complex process caused by double anti-clothes, what comfort level was not good enough lacks
It falls into.
The present invention provides a kind of double anti-clothes of comfort type, including housing and the double anti-materials being arranged in housing, and described pair anti-
Material includes double anti-chips and padded coaming；
Double anti-chips are formed by least 20 laminate cloth according to [0 °/90 °] orthogonal superposition, and the pressing plate cloth is by no latitude
Cloth is suppressed；
The laminated cloth is formed by two layers of fiber cloth according to [0 °/90 °] orthogonal superposition；
The fiber cloth is formed by filament through adhesive bond.
Double anti-clothes of the present invention refer to not only with bulletproof effect but also with the protective garment of anti-stab effect.Double anti-clothes of the present invention
Mainly double anti-effects are played by double anti-chips, wherein the manufacturing process of double anti-clothes is divided into three step process, first, by fiber
Silk obtains fiber cloth by adhesive bond；Then, two layers of fiber cloth is subjected to orthogonal superposition and obtains laminated cloth；Finally, by nothing
Latitude cloth obtains pressing plate cloth by compression process, and the Orthogonal Composite of multilayer pressing plate cloth obtains double anti-chips.
Pair anti-clothes of the invention are just prevented by the combination satisfaction pair of filament and adhesive when initially generating fiber cloth
Fundamental importance, to make it only need the orthogonal superposition of two layers of fiber cloth that can obtain no latitude in subsequent manufacturing process
Cloth, and the orthogonal superposition of at least 20 laminate cloth can obtain double anti-chips, therefore in the manufacturing process of double anti-clothes, both
The combined and spliced of multiple material is not needed, Special controlling need not be also carried out to the superposition angle of combination, therefore the present invention's is double
Not only comfort level is high but also simple and feasible in manufacturing process for anti-clothes.
Specifically, the effect that the number of plies of pressing plate cloth can protect as needed specifically determines.For example, it is double to meet the Ministry of Public Security
When -1 grade anti-, the number of plies of required pressing plate cloth is 28-45 layers；Meet the Ministry of Public Security it is -2 grades double anti-when, the number of plies of required pressing plate cloth is 45-
55 layers.In general, when the number of plies of pressing plate cloth is 20, so that it may to meet double anti-effects.And padded coaming can be selected from ethylene-vinegar
Sour ethylene copolymer, chemical crosslink polyethylene foam equivalent comfort elastomer.
Double anti-clothes of the present invention are not spliced and combined the material with anti-stab function and bulletproof function simply,
But be initial raw material by filament and adhesive, it is processed by special sequence, obtains the list with anti-stab bulletproof effect
The anti-material of a pair of, single double anti-materials can meet the effect demand of bulletproof anti-puncturing simultaneously.Meanwhile this pair of anti-material is not only
Make double anti-material more soft comfortables with double anti-effects, and due to having abandoned the combination of multiple functions material, hence it is evident that
Improve safety, flexibility and the comfortable row of user.
Further, the adhesive be selected from aqueous polyurethane, aqueous polyvinyl acetate, water polyolefin adhesive and
It is one or more in water-and acrylate.By the numerous studies of inventor, above-mentioned adhesive or a combination thereof object generating
After fiber cloth, extraneous energy can be absorbed, the anti-shock strength of fiber cloth is obviously improved.
Further, the mass percent that the filament accounts for the fiber cloth is 70-85%, and the adhesive accounts for described
The mass percent of fiber cloth is 15-30%.It, can be when manufacturing fiber cloth in order to further increase double anti-effects of double anti-clothes
Its manufacturing process is controlled, specifically, the use ratio of filament and adhesive can be controlled.When by filament
When controlling within the above range with the use ratio of adhesive, the use intensity of fiber cloth is significantly improved, so as to double
In the manufacturing process of anti-chip, it is only necessary to which the orthogonal superposition of two layers of fiber cloth can obtain laminated cloth, avoid the prior art
In improve density of material by multiple-layer stacked multi-angle is superimposed to achieve the effect that the overelaborated operation of protection.
Further, the solid content of the adhesive is 20-60%.In the adhesive of the present invention, in addition to having for adhesive
It imitates outside ingredient, remaining all water, by the way that the solid content control of adhesive within the above range, can be made the viscosity of adhesive
Reach 50mPas~300mPas, pH value reaches 6~9.Wherein, which can be further ensured that adhesive and filament
For gluing at the intensity of fiber cloth, which can ensure that adhesive to filametntary wellability, further enhances plybonding effect.
Further, the surface density of the pressing plate cloth is 130-350g/m2.By to adhesive, filametntary parameter control
System, can change the surface density of pressing plate cloth.By the research of inventor, within the above range by the surface density control of pressing plate cloth
When, double anti-effects of double anti-chips can significantly be enhanced.
Further, the filament of the fiber cloth is constituted in polyethylene fibre, aramid fiber and polyarylate fiber
It is one or more.In specifically manufacture fiber cloth, the preferable aramid fiber of filament.When filament is above-mentioned several fibers
When mixture, ratio of the present invention between each fiber is not limited.Preferably, polyethylene fibre, aramid fiber and polyarylate
Fibre strength is at least 25cN/dtex, and modulus is at least 1000cN/dtex.
The present invention selects specific adhesive uniformly to be combined with fiber, so that the impact energy of bullet is spread to fiber surrounding, has
Conducive to the absorption of energy, achieve the purpose that prevent bullet process, meanwhile, adhesive of the invention also has certain hardness, energy
Effective point of a knife piercing and the blade resisted realizes good anti-stab function to the dissection of material.With traditional double anti-materials
It compares, double anti-materials of the invention are homogenous material, rather than the overlapping with shellproof and anti-stab functional material, therefore are significantly improved
The comfort level of process operability and double anti-clothes.
The present invention also provides a kind of manufacturing methods of any of the above-described double anti-clothes of the comfort type, include the following steps：
1) filament is immersed in the adhesive, is fixed on arranging machine after opening up silk, when the adhesive is dried
Afterwards, the first fiber cloth is made；First fiber cloth is rotated by 90 °, is made in first fiber cloth according to aforesaid operations
Second fiber cloth；First fiber cloth and the second fiber cloth combine to obtain the laminated cloth；
2) laminated cloth progress compression process is obtained into the pressing plate cloth, the compression process includes the heat that sequence carries out
Pressure processing and cold pressing treatment；
3) at least 20 layers of pressing plate cloth are obtained into double anti-chips according to [0 °/90 °] orthogonal superposition, then uses waterproof
Cloth is by the padded coaming and double anti-chip portfolios and carries out edge sealing package, obtains double anti-materials；
4) double anti-materials are arranged in the housing, obtain the double anti-clothes of the comfort type.
Step 1) is the manufacturing method about laminated cloth, specifically, the adhesive that will be completed according to the configuration of target solid content
After being put into glue groove, by filament by glue groove impregnation, open up silk, be fixed on arranging machine, after adhesive drying, that is, form first
Fiber cloth.First fiber cloth is rotated by 90 °, manufactures the second fiber cloth in the first fiber cloth according to the method described above, to obtain
Laminated cloth.Wherein, the filament after impregnation is fixed on arranging machine at 80 DEG C about after twenty minutes, adhesive has just been dried
Finish.When opening up silk fixation, brushing processing can also be carried out to adhesive by scraper blade, adhesive is made to be evenly distributed on filament
On.
In step 2), according to the version type of housing, laminated cloth can be cut into the matched size of housing, then will be without latitude
Cloth is placed between two layers of isolation film, hot-pressing processing and cold pressing treatment using hydraulic power press to laminated cloth Jing Guo sequence, membrane
Afterwards, the pressing plate cloth with some strength is obtained.
In step 3), by multilayer pressing plate cloth after [0 °/90 °] orthogonal superposition obtains double anti-chips, padded coaming is pressed
Hindsight cun is put together with double anti-chips according to upper and lower relation after cutting, and edge sealing package is carried out to the two with waterproof cloth, i.e., complete
At the making of double anti-materials.
In step 4), double anti-materials are fixed on jacket internal according to set-up mode in the prior art, it specifically can root
According to precordial locations, the back position etc. for needing to select to be fixed on housing.Wherein, the padded coaming in double anti-materials, which is provided in, leans on
Double anti-chips of the side of person of modern times's body, double anti-materials are provided in the side far from body, i.e. external injury is prevented with double first
Double anti-chips in material contact at first.
Above-mentioned manufacturing method is simple and practicable, will not carry out group with two kinds of materials of anti-stab function and bulletproof function
It closes, but using filament and adhesive as raw material, manufacture is had a homogenous material of anti-stab bulletproof function simultaneously, and
It is not existing all only with simple controllable orthogonal superposition technique when fiber cloth is combined and when pressing plate cloth is combined
There is being layering for the multiple angles in technology, therefore not only further demonstrates significant double preventive effects of homogenous material of the present invention
Fruit, and it is effectively improved the comfort level of double anti-clothes.The present invention by adhesive with it is filametntary combine, the compacting of laminated cloth
The techniques such as processing, obtain the homogenous material with double anti-functions, and the easy manufacturing process of double anti-clothes has innovated the system of double anti-clothes
Make technique.
Further, in order to enhance double anti-effects, when filament impregnation generates the first fiber cloth and the second fiber cloth, control
It is 70-85% to make the filament and account for the mass percent of first fiber cloth, and the adhesive accounts for first fiber cloth
Mass percent be 15-30%；The mass percent that the filament accounts for second fiber cloth is 70-85%, the glue
The mass percent that stick accounts for second fiber cloth is 15-30%.The fiber cloth manufactured through the ratio can not only reach
To double anti-effects, and the bending resistance length of its pressing plate cloth subsequently obtained is 9cm~20cm, hence it is evident that improves the comfortable of double anti-clothes
Property.
Further, the hot-pressing processing includes：At 120-180 DEG C, the laminated cloth is suppressed at 1-10MPa
10-20min；
The cold pressing treatment includes：(25 DEG C) at room temperature, by the laminated cloth after hot-pressing processing in 1-10MPa
Lower compacting 1-3min.
The implementation of the present invention includes at least following advantage：
1, double anti-functional materials of the invention are single structure material, therefore avoid bullet resistant material in the prior art and prevent
The process complexity pierced the combined and spliced of material and brought, manufacture raw material is simple and easy to get, and manufacturing process is simple to operation, technique ginseng
Number degree of controllability is high.
2, it is of the invention it is double it is anti-take comfort levels height, bending resistance length is down to 9cm~20cm, hence it is evident that improves user of service's
Comfort level and flexibility.
Description of the drawings
Fig. 1 is the orthohormbic structure schematic diagram of the single layer pressing plate cloth of the double anti-clothes of comfort type of the present invention.
Specific implementation mode
Keep the purpose, technical scheme and advantage of the embodiment of the present invention clearer, it below will be in the embodiment of the present invention
Technical solution is clearly and completely described, it is clear that described embodiments are some of the embodiments of the present invention, rather than complete
The embodiment in portion.Based on the embodiments of the present invention, those of ordinary skill in the art are not under the premise of making the creative labor
The every other embodiment obtained, shall fall within the protection scope of the present invention.
The raw material of filament and adhesive that following embodiments use, specific producer and specification are as follows：
Filament:Aramid fiber, Dutch Aksu company, trade mark Twaron-2000, line density 1680dtex, fiber are straight
9~12gm of diameter；
Adhesive：Aqueous polyurethane, Beyer Co., Ltd.
Embodiment 1
The manufacturing step of the double anti-clothes of the present embodiment is：
1) manufacture of laminated cloth
Water-based polyurethane adhesive is prepared into the glue that solid content is 30%, is put into glue groove, aramid fiber passes through glue groove
Impregnation exhibition silk, is arranged and is fixed on arranging machine, while being smoothened glue with scraper blade, at 80 DEG C it is dry completely after, obtain the
One fiber cloth；First fiber cloth is rotated by 90 °, is then carried out filament with the first fiber cloth with same method orthogonal multiple
It closes to get the Aramid No-Woven Cloth to interlock to two layers；Wherein, the mass ratio of aramid fiber and adhesive is 3:1.
2) manufacture of pressing plate cloth
Laminated cloth is cut into 50cm × 50cm sizes, is put among two layers of isolation film, then places it in hydraulic power press,
Hot pressing 10min is carried out at 120 DEG C, 5MPa, 3min is then cold-pressed under room temperature 5MPa, membrane is to get aramid fiber pressing plate cloth.
3) manufacture of double anti-clothes
35 laminate cloth, then with padded coaming mounted on top, are packaged by [0 °/90 °] to overlapping with waterproof cloth
It fixes to get double anti-materials.
Double anti-materials are plugged to the precordial locations for being fixed on housing, manufacture obtains double anti-clothes of the present embodiment.
Bulletproof anti-puncturing performance tests are carried out to double anti-clothes that the present embodiment manufactures, wherein ballistic performance test according to
Ministry of Public Security GA141-2010《Police flak jackets》Standard is practiced shooting, that is, uses 54 formula 7.62mm pistols, 51 formula, 7.62 pistol cartridge
(lead for retractable pencil) is tested；Anti-stab performance test is according to Ministry of Public Security GA68-2008《Police stab-resistance body armor》Standard is tested, it is intended to be surveyed
The double anti-clothes manufactured in the examination present invention, with the requirement of this bulletproof stab-resistant clothes FDC-1, FDC-2 for meeting Ministry of Public Security's promulgation.
Meanwhile according to GB/T18318-2001《The measurement of textile fabric bending length》In the double anti-clothes of inclined plane method test
The bending resistance length of fiber pressing plate cloth, test principle be using the long and narrow sample of the fabric of certain size as cantilever beam, can according to it
Flexibility, can measuring and calculation its bending when length, as the index of fabric softness, the bending resistance length value of test is smaller, explanation
The pliability of fabric is better.
Above-mentioned test result is specifically shown in Table 1.
Embodiment 2
The manufacturing step of the double anti-clothes of the present embodiment is：
1) manufacture of laminated cloth
Water-based polyurethane adhesive is prepared into the glue that solid content is 40%, is put into glue groove, aramid fiber passes through glue groove
Impregnation exhibition silk, is arranged and is fixed on arranging machine, while being smoothened glue with scraper blade, at 80 DEG C it is dry completely after, obtain the
One fiber cloth；First fiber cloth is rotated by 90 °, is then carried out filament with the first fiber cloth with same method orthogonal multiple
It closes to get the Aramid No-Woven Cloth to interlock to two layers；Wherein, the mass ratio of aramid fiber and adhesive is 3:1.
2) manufacture of pressing plate cloth
Laminated cloth is cut into 50cm × 50cm sizes, is put among two layers of isolation film, then places it in hydraulic power press,
Hot pressing 10min is carried out at 120 DEG C, 5MPa, 3min is then cold-pressed under room temperature 5MPa, membrane is to get aramid fiber pressing plate cloth.
3) manufacture of double anti-clothes
35 laminate cloth, then with padded coaming mounted on top, are packaged by [0 °/90 °] to overlapping with waterproof cloth
It fixes to get double anti-materials.
Double anti-materials are plugged to the precordial locations for being fixed on housing, manufacture obtains double anti-clothes of the present embodiment.
Using test method same as Example 1, anti-stab shellproof and comfort is carried out to double anti-clothes of the present embodiment
Performance test, test result is specifically shown in Table 1.
Embodiment 3
The manufacturing step of the double anti-clothes of the present embodiment is：
1) manufacture of laminated cloth
Water-based polyurethane adhesive is prepared into the glue that solid content is 40%, is put into glue groove, aramid fiber passes through glue groove
Impregnation exhibition silk, is arranged and is fixed on arranging machine, while being smoothened glue with scraper blade, at 80 DEG C it is dry completely after, obtain the
One fiber cloth；First fiber cloth is rotated by 90 °, is then carried out filament with the first fiber cloth with same method orthogonal multiple
It closes to get the Aramid No-Woven Cloth to interlock to two layers；Wherein, the mass ratio of aramid fiber and adhesive is 2.8:1.
2) manufacture of pressing plate cloth
Laminated cloth is cut into 50cm × 50cm sizes, is put among two layers of isolation film, then places it in hydraulic power press,
Hot pressing 15min is carried out at 140 DEG C, 5MPa, 3min is then cold-pressed under room temperature 5MPa, membrane is to get aramid fiber pressing plate cloth.
3) manufacture of double anti-clothes
35 laminate cloth, then with padded coaming mounted on top, are packaged by [0 °/90 °] to overlapping with waterproof cloth
It fixes to get double anti-materials.
Double anti-materials are plugged to the precordial locations for being fixed on housing, manufacture obtains double anti-clothes of the present embodiment.
Using test method same as Example 1, anti-stab shellproof and comfort is carried out to double anti-clothes of the present embodiment
Performance test, test result is specifically shown in Table 1.
Embodiment 4
The manufacturing step of the double anti-clothes of the present embodiment is：
1) manufacture of laminated cloth
Water-based polyurethane adhesive is prepared into the glue that solid content is 40%, is put into glue groove, aramid fiber passes through glue groove
Impregnation exhibition silk, is arranged and is fixed on arranging machine, while being smoothened glue with scraper blade, at 80 DEG C it is dry completely after, obtain the
One fiber cloth；First fiber cloth is rotated by 90 °, is then carried out filament with the first fiber cloth with same method orthogonal multiple
It closes to get the Aramid No-Woven Cloth to interlock to two layers；Wherein, the mass ratio of aramid fiber and adhesive is 3.5:1.
2) manufacture of pressing plate cloth
Laminated cloth is cut into 50cm × 50cm sizes, is put among two layers of isolation film, then places it in hydraulic power press,
Hot pressing 15min is carried out at 180 DEG C, 3MPa, 3min is then cold-pressed under room temperature 5MPa, membrane is to get aramid fiber pressing plate cloth.
3) manufacture of double anti-clothes
35 laminate cloth, then with padded coaming mounted on top, are packaged by [0 °/90 °] to overlapping with waterproof cloth
It fixes to get double anti-materials.
Double anti-materials are plugged to the precordial locations for being fixed on housing, manufacture obtains double anti-clothes of the present embodiment.
Using test method same as Example 1, anti-stab shellproof and comfort is carried out to double anti-clothes of the present embodiment
Performance test, test result is specifically shown in Table 1.
Reference examples 1
The manufacturing step of the double anti-clothes of this reference examples is：
1) manufacture of laminated cloth
Water-based polyurethane adhesive is prepared into the glue that solid content is 40%, is put into glue groove, aramid fiber passes through glue groove
Impregnation exhibition silk, is arranged and is fixed on arranging machine, while being smoothened glue with scraper blade, at 80 DEG C it is dry completely after, obtain the
One fiber cloth；First fiber cloth is rotated by 90 °, is then carried out filament with the first fiber cloth with same method orthogonal multiple
It closes to get the Aramid No-Woven Cloth to interlock to two layers；Wherein, the mass ratio of aramid fiber and adhesive is 3:1.
2) manufacture of double anti-clothes
Laminated cloth is cut into 50cm × 50cm sizes, by 35 layers of laminated cloth by [0 °/90 °] to overlapping, then with padded coaming
Mounted on top is packaged fixed to get double anti-materials with waterproof cloth.
Double anti-materials are plugged to the precordial locations for being fixed on housing, manufacture obtains double anti-clothes of this reference examples.
Using test method same as Example 1, anti-stab shellproof and comfort is carried out to double anti-clothes of this reference examples
Performance test, test result is specifically shown in Table 1.
Reference examples 2
The manufacturing step of the double anti-clothes of this reference examples is：
1) manufacture of laminated cloth
By aqueous epoxy resins prepare solid content be 40% glue, be put into glue groove, aramid fiber by glue groove impregnation,
Exhibition silk is arranged and is fixed on arranging machine, while being smoothened glue with scraper blade, at 80 DEG C it is dry completely after, obtain the first fibre
Wei Bu；First fiber cloth is rotated by 90 °, then filament is carried out with the first fiber cloth with same method it is orthogonal compound, i.e.,
Obtain two layers of Aramid No-Woven Cloth staggeredly；Wherein, the mass ratio of aramid fiber and adhesive is 3:1.
2) manufacture of pressing plate cloth
Laminated cloth is cut into 50cm × 50cm sizes, is put among two layers of isolation film, then places it in hydraulic power press,
Hot pressing 15min is carried out at 180 DEG C, 3MPa, 3min is then cold-pressed under room temperature 5MPa, membrane is to get aramid fiber pressing plate cloth.
3) manufacture of double anti-clothes
35 laminate cloth, then with padded coaming mounted on top, are packaged by [0 °/90 °] to overlapping with waterproof cloth
It fixes to get double anti-materials.
Double anti-materials are plugged to the precordial locations for being fixed on housing, manufacture obtains double anti-clothes of this reference examples.
Using test method same as Example 1, anti-stab shellproof and comfort is carried out to double anti-clothes of this reference examples
Performance test, test result is specifically shown in Table 1.
Reference examples 3
The manufacturing step of the double anti-clothes of this reference examples is：
1) manufacture of laminated cloth
Water-based polyurethane adhesive is prepared into the glue that solid content is 30%, is put into glue groove, aramid fiber passes through glue groove
Impregnation exhibition silk, is arranged and is fixed on arranging machine, while being smoothened glue with scraper blade, at 80 DEG C it is dry completely after, obtain the
One fiber cloth；First fiber cloth is rotated by 90 °, is then carried out filament with the first fiber cloth with same method orthogonal multiple
It closes to get the fiber cloth interlocked to two layers；Then two layers of fiber cloth staggeredly is rotated 45 degree, with same method by filament
It is carried out with two layers of fiber cloth staggeredly compound to get the fiber cloth interlocked to three layers；Then three layers of fiber cloth staggeredly is rotated
135 degree, with same method by the fiber cloth of filament and three layers staggeredly carry out it is compound to get to four layers of aramid fiber staggeredly without latitude
Cloth, the wherein compound angle of this four layers of fiber cloths are [0 °/90 °/45 °/135 °], and the mass ratio of aramid fiber and adhesive is 3:
1。
2) manufacture of pressing plate cloth
Laminated cloth is cut into 50cm × 50cm sizes, is put among two layers of isolation film, then places it in hydraulic power press,
Hot pressing 10min is carried out at 120 DEG C, 5MPa, 3min is then cold-pressed under room temperature 5MPa, membrane is to get aramid fiber pressing plate cloth.
3) manufacture of double anti-clothes
35 laminate cloth, then with padded coaming mounted on top, are used into waterproof cloth by [0 °/90 °/45 °/135 °] to overlapping
It is packaged fixed to get double anti-materials.
Double anti-materials are plugged to the precordial locations for being fixed on housing, manufacture obtains double anti-clothes of this reference examples.
Using test method same as Example 1, anti-stab shellproof and comfort is carried out to double anti-clothes of this reference examples
Performance test, test result is specifically shown in Table 1.
Ballistic performance, anti-stab performance and the pliability Comparative result of 1 sample of table
Note：-- representing in practicing shooting shellproof test has penetration phenomenon, recess that can not calculate.
From the comparing result of table 1：Type and technological process of the present invention by control adhesive, can be made to
Double anti-functions to double anti-clothes with double anti-functions, this pair of anti-clothes only can be completed by simple function material, and comfortable
It spends good.
Finally it should be noted that：The above embodiments are only used to illustrate the technical solution of the present invention., rather than its limitations；To the greatest extent
Present invention has been described in detail with reference to the aforementioned embodiments for pipe, it will be understood by those of ordinary skill in the art that：Its according to
So can with technical scheme described in the above embodiments is modified, either to which part or all technical features into
Row equivalent replacement；And these modifications or replacements, various embodiments of the present invention technology that it does not separate the essence of the corresponding technical solution
The range of scheme.
Claims (5)
1. a kind of double anti-clothes of comfort type, which is characterized in that including housing and the double anti-materials being arranged in housing, double anti-materials
Material includes double anti-chips and padded coaming；
Double anti-chips are formed by least 20 laminate cloth according to [0 °/90 °] orthogonal superposition, and the pressing plate cloth is by laminated cloth pressure
It makes；
The laminated cloth is formed by two layers of fiber cloth according to [0 °/90 °] orthogonal superposition；
The fiber cloth is formed by filament through adhesive bond；
The mass percent that the filament accounts for the fiber cloth is 70-85%, and the adhesive accounts for the quality of the fiber cloth
Percentage is 15-30%；
The surface density of the pressing plate cloth is 130-350g/m2, the bending resistance length of the pressing plate cloth is 9cm~20cm；
The filament for constituting the fiber cloth is one or more in polyethylene fibre, aramid fiber and polyarylate fiber；
The intensity of the polyethylene fibre, aramid fiber and polyarylate fiber is at least 25cN/dtex, and modulus is at least
1000cN/dtex。
2. the double anti-clothes of comfort type according to claim 1, which is characterized in that the adhesive is selected from aqueous polyurethane, water
It is one or more in property polyvinyl acetate, water polyolefin adhesive and water-and acrylate.
3. the double anti-clothes of comfort type according to claim 1 or 2, which is characterized in that the solid content of the adhesive is 20-
60%.
4. the manufacturing method of the double anti-clothes of any comfort types of claim 1-3, which is characterized in that include the following steps：
1) filament is immersed in the adhesive, is fixed on arranging machine after opening up silk, after the adhesive is dried, system
Obtain the first fiber cloth；First fiber cloth is rotated by 90 °, it is fine described first according to the method operation for preparing the first fiber cloth
The second fiber cloth is made on Wei Bu；First fiber cloth and the second fiber cloth combine to obtain the laminated cloth；
2) laminated cloth progress compression process is obtained into the pressing plate cloth, the compression process includes at the hot pressing that sequence carries out
Reason and cold pressing treatment；
3) at least 20 layers of pressing plate cloth are obtained into double anti-chips according to [0 °/90 °] orthogonal superposition, it then will with waterproof cloth
The padded coaming and double anti-chip portfolios simultaneously carry out edge sealing package, obtain double anti-materials；
4) double anti-materials are arranged in the housing, obtain the double anti-clothes of the comfort type；
The mass percent that the filament accounts for first fiber cloth is 70-85%, and the adhesive accounts for first fiber
The mass percent of cloth is 15-30%；
The mass percent that the filament accounts for second fiber cloth is 70-85%, and the adhesive accounts for second fiber
The mass percent of cloth is 15-30%.
5. the manufacturing method of the double anti-clothes of comfort type according to claim 4, which is characterized in that the hot-pressing processing includes：
At 120-180 DEG C, the laminated cloth is suppressed into 10-20min at 1-10MPa；
The cold pressing treatment includes：At room temperature, the laminated cloth after hot-pressing processing is suppressed into 1-3min at 1-10MPa.