CN106118442A - A kind of blooming cold coating and application thereof - Google Patents
A kind of blooming cold coating and application thereof Download PDFInfo
- Publication number
- CN106118442A CN106118442A CN201610518705.1A CN201610518705A CN106118442A CN 106118442 A CN106118442 A CN 106118442A CN 201610518705 A CN201610518705 A CN 201610518705A CN 106118442 A CN106118442 A CN 106118442A
- Authority
- CN
- China
- Prior art keywords
- component
- blooming
- cold coating
- coating
- oligomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a kind of blooming cold coating, comprise the first component, second component, levelling agent antistatic additive, light trigger, diluent, the quality of described first component and second component is 1:3~1:1 than scope;Described first component in the first oligomer, the second oligomer and monomer arbitrarily both, described second component is to select remaining component after both in the first component, the present invention utilizes the compatibility difference between opposed polarity resin or resin and monomer, form the on-plane surface micro structure of particle-like effect on coated article surface after solidification, thus reach anti-stick, atomization, anti-scratch, the effect of delustring.
Description
Technical field:
The present invention relates to blooming cold coating, be specifically related to component and the application of blooming cold coating.
Background technology:
The method generally using chemosynthesis from matting resin the most on the market, i.e. introduces energy in coating building-up process
Light-absorbing structure or group play photoextinction.Chinese patent CN103163571A discloses a kind of blooming and system thereof
Make method, first manufacturing the mould with wavy pattern, more described mould is transferred on basement membrane, making described blooming have one
Determine mist degree;Chinese patent CN103740250A discloses a kind of preparation method from extinction type leather waterborne polyurethane coating agent,
First it is respectively synthesized A, B two component, remixes formulated;Chinese patent CN104530328A discloses a kind of from matting resin
Preparation method, first the synthesis Ludox containing double bond, is synthesized with methacrylate-based monomer with this Ludox the most again
From matting resin.Common problem existing for above patent is that method is relatively cumbersome, Expenses Cost.
It is little low with operation voltage etc. that liquid crystal display (liquid crystal display, LCD) has light weight, volume
Advantage, has been widely used in personal mobile communication and household appliances in recent years, owing to liquid crystal panel itself is the most luminous, so
Need to add backlight module, and general backlight film group includes: light source, light guide plate, optical diffusion film and prismatic lens, wherein light diffusion
Film merit can be that the point source of light emitting diode (light emitting diode, LED) is converted into uniform area source.
For the optical diffusion film in back lighting device, both require that there is good covering effect, it is also desirable to have good increasing
Bright effect.In order to meet requirements above, a lot of diffusion barrier manufacturing firms all resins or microgranule to diffusion layer are improved, but
Because the luminance raising for back lighting device is limited, so current back lighting device the most all includes prismatic lens, so pass through
Being applied in combination of prismatic lens and diffusion barrier both can solve covering problem and can also solve blast problem.
But, for back lighting device, when overlapping optical diffusion film, prismatic lens, light guide plate, the light diffusion layer of optical diffusion film and
Between prismatic lens back or front, the anti-stick layer of optical diffusion film and light guide plate surface, between prismatic lens front or light diffusion layer
Produce friction because contacting mutually, all can produce because contacting with making in transportation it addition, use in optical diffusion film superposition
Friction, either diffusion barrier diffusion layer or anti-stick layer, the positive back side of prismatic lens or light guide plate has scuffing, the most high-precision
In the liquid crystal display of refinement, its slight scratch will become the poor prognostic cause of liquid crystal display.
The existing optical diffusion film used in the back lighting device of liquid crystal display etc., typically by being just coated with light diffusion layer, base
Material (PET) and the back of the body are coated with anti-stick layer composition, and existing technology is mostly to be respectively coated with difference at PET basement membrane front and back
The resin of the diffusion particle of particle diameter.
Summary of the invention:
The purpose of the present invention is on the one hand, it is provided that a kind of blooming cold coating, solves coating and is not required to add the feelings of particle
Anti-stick is realized under condition, atomization, anti-scratch, the effect of delustring.
On the other hand, it is provided that the application of blooming cold coating.
For achieving the above object, the technical scheme is that
A kind of blooming cold coating, it is characterised in that comprise following components:
First component
Second component
Levelling agent
Antistatic additive
Light trigger
Diluent;
The quality of described first component and second component is 1:3~1:1 than scope;
Described first component in the first oligomer, the second oligomer and monomer arbitrarily both, described second component
It is that the first component is selected remaining component after both;
The most described first component is the first oligomer and the second oligomer, and the most described second component is monomer;
Described first component is the first oligomer and monomer, and the most described second component is the second oligomer;
Described first component is the second oligomer and monomer, and the most described second component is the first oligomer.
Further, and dissolubility difference DELTA SP of described first component and second component < 1, described group of the first component and
Dissolubility difference DELTA SP that two components meet is < when 1, in the micro structure size homogeneity of coated article surface formation after coating solidification
Good.
Further, the mist degree after the coating of described blooming cold coating > 3%.
Further, the surface roughness after the coating of described blooming cold coating > 0.25 μm.
Further, described first oligomer is aliphatic polyurethane dimethylacrylate.
Further, described second oligomer is aliphatic six acrylate.
Further, described monomer is that caprolactone modifies double pentaerythritol methacrylate.
Further, after the coating of described compositions, coating dry film thickness range is 2~8 μm.
Above-mentioned blooming cold coating is applied to diffusion barrier or brightness enhancement film by one.
Beneficial effect:
Present invention generally provides is a kind of blooming cold coating without particle, utilize opposed polarity resin or
Compatibility difference between resin and monomer, forms the on-plane surface micro structure of particle-like effect on coated article surface after solidification,
Thus reach anti-stick, and atomization, anti-scratch, the effect of delustring.
Detailed description of the invention:
In order to make the purpose of the present invention, technical scheme and advantage clearer, below in conjunction with embodiment, to invent into
Row further describes.Should be appreciated that specific embodiment described herein, only in order to explain the present invention, is not used to limit
Determine the present invention.
Comparative example 1
It is embodied as case as follows:
Embodiment 1
It is embodied as case 1 as follows:
Embodiment 2
It is embodied as case 2 as follows:
Embodiment 3
It is embodied as case 3 as follows:
Embodiment 4
It is embodied as case 4 as follows:
Embodiment 5
It is embodied as case 5 as follows:
Implementation process:
Being mixed successively by above-mentioned raw materials, high speed dispersor 1000r/min stirs 15min, by the coating fluid prepared 120 mesh
Gravure roll is spread evenly across PET base material layer (, below 2.5%, light transmittance is more than 88% for the mist degree of the PET base material layer) back side, dries
Dry, cross UV after form anti-stick layer semi-finished product (build 2~8 μm), dry temperature 80-100 DEG C, UV light strong 75%~
90%.
Specific embodiment properties test result:
The foregoing is only the preferred embodiment of invention, be not limiting as the present invention, all the spirit and principles in the present invention it
Interior made amendment, equivalent and improvement etc., should be included within the scope of the present invention.
The present invention is made any restriction in form by attempt according to this, therefore all have made to have under identical spirit
Close any modification or the change of the present invention, all must be included in the category that the invention is intended to protection.
Claims (9)
1. a blooming cold coating, it is characterised in that comprise following components:
First component
Second component
Levelling agent
Antistatic additive
Light trigger
Diluent;
The quality of described first component and second component is 1:3~1:1 than scope;
Described first component in the first oligomer, the second oligomer and monomer arbitrarily both, described second component is the
One component is selected remaining component after both.
Blooming cold coating the most according to claim 1, it is characterised in that described first component and second component
Dissolubility difference DELTA SP < 1.
Blooming cold coating the most according to claim 1, it is characterised in that described blooming cold coating is coated with
Mist degree after cloth > 3%.
Blooming cold coating the most according to claim 1, it is characterised in that described blooming cold coating is coated with
Cloth rear surface roughness > 0.25 μm.
Blooming cold coating the most according to claim 1, it is characterised in that described first oligomer is aliphatic poly
Urethane dimethylacrylate.
Blooming cold coating the most according to claim 1, it is characterised in that described second oligomer is aliphatic six
Acrylate.
Blooming cold coating the most according to claim 1, it is characterised in that described monomer is caprolactone modification double season
Penta tetrol six acrylate.
Blooming cold coating the most according to claim 1, it is characterised in that by coating dry film after described coatings
Thickness range is 2~8 μm.
9. blooming cold coating described in an any one of claim 1-8, it is characterised in that by described blooming resin
Coating is applied to diffusion barrier or brightness enhancement film.