CN106117646A - The formula and processing technology at the end in a kind of rubber pange - Google Patents
The formula and processing technology at the end in a kind of rubber pange Download PDFInfo
- Publication number
- CN106117646A CN106117646A CN201610602525.1A CN201610602525A CN106117646A CN 106117646 A CN106117646 A CN 106117646A CN 201610602525 A CN201610602525 A CN 201610602525A CN 106117646 A CN106117646 A CN 106117646A
- Authority
- CN
- China
- Prior art keywords
- rubber
- accelerator
- rubber pange
- pange
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides the formula at the end in a kind of rubber pange, it is characterised in that: this formula comprises following components: natural rubber 5000g, accelerator DM 95g, accelerator M 40g, accelerator D 30g, zinc oxide 400g, stearic acid 200g, PEG accelerator 150g, SPC accelerator 50g, paraffin 75g, Colophonium 130g, white factice 1000g, sodium bicarbonate 100g, foaming agent 200g, titanium dioxide 1250g, toner 1250g, Pulvis Talci 250g, sulfur 150g and anti-wear agent 20g;Present invention also offers the production technology at the end in a kind of rubber pange, this production technology includes raw material mixing, mixing process, tabletting process, foaming and setting and deburring.In the rubber pange that the present invention makes, end comfort level is high, resilience is good, ageing-resistant; in the rubber pange that will make, the end, is positioned between the big end and upper of a shoe; use the heating pressurization of automatic moulding footwear mould machine; in rubber pange, the big end, just can be bonded without glue by the end with upper of a shoe; bonding force is strong, and upper of a shoe is connected firmly with sole.
Description
Technical field
The present invention relates to the technical field of footwear material, particularly to the formula and processing technology at the end in a kind of rubber pange.
Background technology
Footwear on existing market, are substantially made up of the big end, the middle end and upper of a shoe three part, and its manufacturing process is usually first to be distinguished
Make the big end, the middle end and upper of a shoe, then with glue binding agent, the big end, the middle end and upper of a shoe be adhesively-bonded together to form complete shoes,
The middle end and upper of a shoe also can be connected by sewing type.Traditional shoe-making process is cumbersome, needs to use glue binding agent, glue
Binding agent volatilization produces harmful gas, threatens the health of human body, and easily pollutes environment, not environmentally, uses tradition
The footwear vamp in use for some time made of shoe-making process degumming phenomenon easily occurs, in the sky that temperature is relatively low with sole
, even easily there is the situation of fracture in gas;Additionally, many existing tradition shoemaking products on market, often due to the matter at the middle end
Feeling poor and resilience is the best, the sense comfortable and easy to wear causing shoes is the best, it addition, prior art has the middle end of many shoes
Resistance to ag(e)ing is the best, thus is necessary that the formula at the middle end to shoes and technique improve.
Summary of the invention
For the above-mentioned problems in the prior art, the technical problem to be solved is to provide a kind of rubber
The formula and processing technology at the end in foaming, in the rubber pange made, end comfort level is high, resilience is good, ageing-resistant, will make
Rubber pange in the end be positioned between the big end and upper of a shoe, use automatic moulding footwear mould machine heating pressurization, in rubber pange, the end, is just
Can be by the big end and upper of a shoe strong binding effectively, it is not necessary to use glue binding agent and bonding effect good, the shoes made
Comfortable and easy to wear, upper of a shoe is connected firmly with sole, the most easy to crack, is greatly improved the service life of shoes;Additionally, the rubber made is sent out
In bubble, the end, is conducive to the production process of shoes more environmentally-friendly.
Technical scheme is as follows: the formula at the end in a kind of rubber pange, and this formula comprises following components: natural rubber
Glue 5000g, accelerator DM 95g, accelerator M 40g, accelerator D 30g, zinc oxide 400g, stearic acid
200g, PEG accelerator 150g, SPC accelerator 50g, paraffin 75g, Colophonium 130g, white factice 1000g, sodium bicarbonate 100g, foaming
Agent 200g, titanium dioxide 1250g, toner 1250g, Pulvis Talci 250g, sulfur 150g and anti-wear agent 20g.
Further, described natural rubber is 3L natural rubber.
Further, described toner is white powder, uses as sulfuration filler.
The production technology at the end in a kind of rubber pange, this production technology uses the formula at the end in above-mentioned a kind of rubber pange
Produce, comprise the following steps:
(1) by natural rubber 5000g, accelerator DM 95g, accelerator M 40g, accelerator D 30g,
Zinc oxide 400g, stearic acid 200g, PEG accelerator 150g, SPC accelerator 50g, paraffin 75g, Colophonium 130g, white factice
1000g, sodium bicarbonate 100g, foaming agent 200g, titanium dioxide 1250g, toner 1250g, Pulvis Talci 250g, sulfur 150g and anti-wear agent
20g is sufficiently mixed;
(2) mixture that step (1) obtains is put into internal rubber mixer and carries out mixing, mixing pressure be 0.6~
1MPa, melting temperature under conditions of being 120~130 DEG C mixing 15~20 minutes, refine into film;
(3) film that step (2) is refined is put into opening rubber mixing machine and carry out tabletting process, by film tabletted
Material, cools down placement 20~24 hours in the environment of 10~15 DEG C by prepared sheet material;
(4) according to the requirement of bed die tool, the sheet material of cutting step (3) gained in rubber pange, the sheet material of well cutting is put
Enter bed die tool in rubber pange, then bed die tool in rubber pange is sent into foaming vulcanizer, under the conditions of 150~180 DEG C, send out
Bubble sizing 15~20 minutes;
(5) die sinking, takes out the end in the rubber pange prepared, carries out deburring, make the end in the rubber pange of finished product.
The invention has the beneficial effects as follows: the formula and processing technology at the end in a kind of rubber pange, in the rubber pange made
End comfort level is high, resilience is good, ageing-resistant, is conducive to improving wearing comfort;In the rubber pange that will make, the end, is positioned over
Big between the end and upper of a shoe, use the heating pressurization of automatic moulding footwear mould machine, in rubber pange, the end, just can be effective with upper of a shoe by the big end
Ground strong binding, it is not necessary to using glue binding agent and bonding effect good, the shoes made are comfortable and easy to wear, upper of a shoe is with sole even
Connect firmly, the most easy to crack, it is greatly improved the service life of shoes;Additionally, in the rubber pange made the end be conducive to the life of shoes
Product process is more environmentally-friendly.
Detailed description of the invention
To a preferred embodiment of the present invention will be described in detail.
The formula at the end in a kind of rubber pange, this formula comprises following components: natural rubber 5000g, accelerator DM
95g, accelerator M 40g, accelerator D 30g, zinc oxide 400g, stearic acid 200g, PEG accelerator 150g, SPC promote
Enter agent 50g, paraffin 75g, Colophonium 130g, white factice 1000g, sodium bicarbonate 100g, foaming agent 200g, titanium dioxide 1250g, toner
1250g, Pulvis Talci 250g, sulfur 150g and anti-wear agent 20g;Natural rubber in formula is preferably 3L natural rubber;In formula
Toner be preferably white powder, as sulfuration filler use.
The production technology at the end in a kind of rubber pange, this production technology uses the formula at the end in above-mentioned a kind of rubber pange
Produce, comprise the following steps:
(1) by natural rubber 5000g, accelerator DM 95g, accelerator M 40g, accelerator D 30g,
Zinc oxide 400g, stearic acid 200g, PEG accelerator 150g, SPC accelerator 50g, paraffin 75g, Colophonium 130g, white factice
1000g, sodium bicarbonate 100g, foaming agent 200g, titanium dioxide 1250g, toner 1250g, Pulvis Talci 250g, sulfur 150g and anti-wear agent
20g is sufficiently mixed;
(2) mixture that step (1) obtains is put into internal rubber mixer and carries out mixing, mixing pressure be 0.6~
1MPa, melting temperature under conditions of being 120~130 DEG C mixing 15~20 minutes, refine into film;Wherein, mixing pressure refers to
When internal rubber mixer carries out mixing, the certain pressure effect to mixture of the floating weight of internal rubber mixer, ram piston pressure
0.6~1MPa, the most mixing pressure is 0.6~1MPa;
(3) film that step (2) is refined is put into opening rubber mixing machine and carry out tabletting process, by film tabletted
Material, cools down placement 20~24 hours in the environment of 10~15 DEG C by prepared sheet material;
(4) according to the requirement of bed die tool, the sheet material of cutting step (3) gained in rubber pange, the sheet material of well cutting is put
Enter bed die tool in rubber pange, then bed die tool in rubber pange is sent into foaming vulcanizer, under the conditions of 150~180 DEG C, send out
Bubble sizing 15~20 minutes;
(5) die sinking, takes out the end in the rubber pange prepared, carries out deburring, make the end in the rubber pange of finished product.
The invention has the beneficial effects as follows: the formula and processing technology at the end in a kind of rubber pange, in the rubber pange made
End comfort level is high, resilience is good, ageing-resistant, is conducive to improving wearing comfort;In the rubber pange that will make, the end, is positioned over
Big between the end and upper of a shoe, use automatic moulding footwear mould machine (automatic moulding footwear mould machine is prior art, is no longer described in detail) to add
Heat pressurization, in rubber pange, the end, just can be by the big end and upper of a shoe strong binding effectively, it is not necessary to uses glue binding agent and glues
Closing respond well, the shoes made are comfortable and easy to wear, and upper of a shoe is connected firmly with sole, the most easy to crack, are greatly improved the use of shoes
Life-span;Additionally, in the rubber pange made the end be conducive to the production process of shoes more environmentally-friendly.
These are only the present invention preferably detailed description of the invention, but protection scope of the present invention be not limited thereto, all
Within the spirit and principles in the present invention, any modification, equivalent substitution and improvement etc. made, should be included in the protection of the present invention
Within the scope of.
Claims (4)
1. the formula at the end in a rubber pange, it is characterised in that: this formula comprises following components: natural rubber 5000g, sulfuration
Altax 95g, accelerator M 40g, accelerator D 30g, zinc oxide 400g, stearic acid 200g, PEG accelerator
150g, SPC accelerator 50g, paraffin 75g, Colophonium 130g, white factice 1000g, sodium bicarbonate 100g, foaming agent 200g, titanium dioxide
1250g, toner 1250g, Pulvis Talci 250g, sulfur 150g and anti-wear agent 20g.
The formula at the end in a kind of rubber pange the most according to claim 1, it is characterised in that: described natural rubber is 3L days
So rubber.
The formula at the end in a kind of rubber pange the most according to claim 1, it is characterised in that: described toner is white powder,
Use as sulfuration filler.
4. the production technology at the end in a rubber pange, it is characterised in that: this production technology uses any one of claims 1 to 3
In described a kind of rubber pange, the formula at the end produces, and comprises the following steps:
(1) by natural rubber 5000g, accelerator DM 95g, accelerator M 40g, accelerator D 30g, oxidation
Zinc 400g, stearic acid 200g, PEG accelerator 150g, SPC accelerator 50g, paraffin 75g, Colophonium 130g, white factice 1000g, little
Soda 100g, foaming agent 200g, titanium dioxide 1250g, toner 1250g, Pulvis Talci 250g, sulfur 150g and anti-wear agent 20g are abundant
Mixing;
(2) mixture that step (1) obtains is put into internal rubber mixer and carry out mixing, be 0.6~1MPa at mixing pressure, mix
Refining temperature be 120~130 DEG C under conditions of mixing 15~20 minutes, refine into film;
(3) film that step (2) is refined is put into opening rubber mixing machine and carry out tabletting process, film is pressed into sheet material, will
The sheet material prepared cools down placement 20~24 hours in the environment of 10~15 DEG C;
(4) according to the requirement of bed die tool, the sheet material of cutting step (3) gained in rubber pange, the sheet material of well cutting is put into rubber
Bed die tool in glue foaming, then sends bed die tool in rubber pange into foaming vulcanizer, and under the conditions of 150~180 DEG C, foaming is fixed
Type 15~20 minutes;
(5) die sinking, takes out the end in the rubber pange prepared, carries out deburring, make the end in the rubber pange of finished product.