CN106116310A - A kind of containing slag powders with the thermal insulation mortar of polypropylene fibre - Google Patents
A kind of containing slag powders with the thermal insulation mortar of polypropylene fibre Download PDFInfo
- Publication number
- CN106116310A CN106116310A CN201610493944.6A CN201610493944A CN106116310A CN 106116310 A CN106116310 A CN 106116310A CN 201610493944 A CN201610493944 A CN 201610493944A CN 106116310 A CN106116310 A CN 106116310A
- Authority
- CN
- China
- Prior art keywords
- slag
- polypropylene fibre
- thermal insulation
- insulation mortar
- slag powders
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of containing slag powders with the thermal insulation mortar of polypropylene fibre, including the component of following weight: cement 200 300, slag micropowder 50 100, slag coarse aggregate 200 300, polypropylene fibre 35, starch ether 5 10, sodium gluconate 5 10, lauryl alcohol 35, arabic gum 8 12, sodium silicate 24, redispersable latex powder 24, water reducer 13；Water is appropriate.Compared with prior art, the invention has the beneficial effects as follows: the present invention contains the thermal insulation mortar of slag powders and polypropylene fibre, employing slag powders is raw material, is equipped with polypropylene fibre and modifying agent, has the premium properties such as intensity height, good toughness, insulation, antiseep, good dispersion.
Description
Technical field
The present invention relates to building material field, particularly relate to a kind of insulation sand containing slag powders and polypropylene fibre
Slurry.
Background technology
Concrete mortar is widely used in the engineerings such as bridge, building, power station, not only needs higher intensity, toughness
And stability requirement, and must have self certain water resistance, at northern area, in addition it is also necessary to possess cold-resistant freeze proof simultaneously
Performance.Especially extremely frigid zones, difference variation is big, concrete easily occur through the most repeatedly freezing, after melting process crackle,
Becoming crisp, infiltration phenomenon, the index such as its intensity, toughness and stability is severely impacted.
Slag powders is the garbage of metallurgy industry, if by slag powders in addition modification, making mortar, will have very well
Economic benefit, and solve the storage problem of slag powders.
It was verified that polypropylene fibre has good dispersibility in concrete.
Summary of the invention
The present invention provides a kind of containing slag powders with the thermal insulation mortar of polypropylene fibre, and employing slag powders is raw material, is equipped with
Polypropylene fibre and modifying agent, have intensity height, good toughness, insulation, the premium properties of antiseep.
In order to achieve the above object, the present invention realizes by the following technical solutions:
A kind of containing slag powders with the thermal insulation mortar of polypropylene fibre, including the component of following weight: cement
200-300, slag micropowder 50-100, slag coarse aggregate 200-300, polypropylene fibre 3-5, starch ether 5-10, sodium gluconate
5-10, lauryl alcohol 3-5, arabic gum 8-12, sodium silicate 2-4, redispersable latex powder 2-4, water reducer 1-3；Water is appropriate.
Compared with prior art, the invention has the beneficial effects as follows:
The present invention contains the thermal insulation mortar of slag powders and polypropylene fibre, and employing slag powders is raw material, is equipped with polypropylene fine
Peacekeeping modifying agent, has the premium properties such as intensity height, good toughness, insulation, antiseep, good dispersion.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1
A kind of containing slag powders with the thermal insulation mortar of polypropylene fibre, including the component of following weight: cement
260, slag micropowder 50-100, slag coarse aggregate 200, polypropylene fibre 4, starch ether 8, sodium gluconate 7, lauryl alcohol 4, I
Primary glue 10, sodium silicate 3, redispersable latex powder 2, polycarboxylate water-reducer 2；Water is appropriate.
The granularity requirements of described slag micropowder be fineness be that 45 μm square hole screens tail over≤25%, the specific surface of slag micropowder
Long-pending >=350m3/Kg；Described slag coarse aggregate is the most formulated by following grain size distribution:
Slag coarse aggregate 3 weight portion of granularity >=25mm
Slag coarse aggregate 25 weight portion of 16mm < granularity < 25mm
Slag coarse aggregate 25 weight portion of granularity≤16mm
The preparation method of described thermal insulation mortar: in addition to cement, stirs described raw material ratio by weight,
Rear addition cement, mix homogeneously makes product.
Embodiment 2
A kind of containing slag powders with the thermal insulation mortar of polypropylene fibre, including the component of following weight: cement
200, slag micropowder 60, slag coarse aggregate 250, polypropylene fibre 4, starch ether 6, sodium gluconate 8, lauryl alcohol 5, arabic gum
8, sodium silicate 2, redispersable latex powder 2, water reducer 1；Water is appropriate.
The granularity requirements of described slag micropowder be fineness be that 45 μm square hole screens tail over≤25%, the specific surface of slag micropowder
Long-pending >=350m3/Kg；Described slag coarse aggregate is the most formulated by following grain size distribution:
Slag coarse aggregate 5 weight portion of granularity >=25mm
Slag coarse aggregate 30 weight portion of 16mm < granularity < 25mm
Slag coarse aggregate 30 weight portion of granularity≤16mm
The preparation method of described thermal insulation mortar, with embodiment 1.
Embodiment 3
A kind of containing slag powders with the thermal insulation mortar of polypropylene fibre, including the component of following weight: cement
300, slag micropowder 100, slag coarse aggregate 260, polypropylene fibre 5, starch ether 10, sodium gluconate 8, lauryl alcohol 5, Arab
Glue 12, sodium silicate 4, redispersable latex powder 4, water reducer 3；Water is appropriate.
The granularity requirements of described slag micropowder be fineness be that 45 μm square hole screens tail over≤25%, the specific surface of slag micropowder
Long-pending >=350m3/Kg；Described slag coarse aggregate is the most formulated by following grain size distribution:
Slag coarse aggregate 1 weight portion of granularity >=25mm
Slag coarse aggregate 20 weight portion of 16mm < granularity < 25mm
Slag coarse aggregate 20 weight portion of granularity≤16mm
The preparation method of described thermal insulation mortar, with embodiment 1.
Embodiment 4
A kind of containing slag powders with the thermal insulation mortar of polypropylene fibre, including the component of following weight: cement
200, slag micropowder 50, slag coarse aggregate 200, polypropylene fibre 4, starch ether 6, sodium gluconate 5, lauryl alcohol 4, arabic gum
10, sodium silicate 2, redispersable latex powder 3, water reducer 2；Water is appropriate.
The granularity requirements of described slag micropowder be fineness be that 45 μm square hole screens tail over≤25%, the specific surface of slag micropowder
Long-pending >=350m3/Kg；Described slag coarse aggregate is the most formulated by following grain size distribution:
Slag coarse aggregate 5 weight portion of granularity >=25mm
Slag coarse aggregate 30 weight portion of 16mm < granularity < 25mm
Slag coarse aggregate 30 weight portion of granularity≤16mm
The preparation method of described thermal insulation mortar, with embodiment 1.
The performance testing index of products obtained therefrom such as following table:
Claims (1)
1. one kind contains slag powders and the thermal insulation mortar of polypropylene fibre, it is characterised in that include the group of following weight
Point: cement 200-300, slag micropowder 50-100, slag coarse aggregate 200-300, polypropylene fibre 3-5, starch ether 5-10, Fructus Vitis viniferae
Sodium saccharate 5-10, lauryl alcohol 3-5, arabic gum 8-12, sodium silicate 2-4, redispersable latex powder 2-4, water reducer 1-3；Water is fitted
Amount.