CN106116223A - A kind of cement grinding aid - Google Patents
A kind of cement grinding aid Download PDFInfo
- Publication number
- CN106116223A CN106116223A CN201610440597.0A CN201610440597A CN106116223A CN 106116223 A CN106116223 A CN 106116223A CN 201610440597 A CN201610440597 A CN 201610440597A CN 106116223 A CN106116223 A CN 106116223A
- Authority
- CN
- China
- Prior art keywords
- parts
- grinding aid
- cement
- triethanolamine
- cellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to field of cement production, especially a kind of cement grinding aid;Its mass parts composition is as follows: modified triethanolamine 5 25 parts, propylene glycol 10 15 parts, unsaturated polyester resin 35 parts, 6 12 parts of sodium thiosulfate, calcium formate 28 parts, Tween 80 0.6 0.8 parts, alkyl polyglycoside 6 12 parts, maleic anhydride 10 30 parts, nano silicon 26 parts, sodium hexameta phosphate 2.4 5.6 parts, allyl polyethenoxy ether 26 parts, water conservation cellulose 1.8 4.8 parts;Under the conditions of grinding machine situation is immovable, mill output amplitude 10 30% can be improved, be effectively reduced grinding phenomenon simultaneously, optimize cement granules grating;Can improve the dispersibility of the interior material of mill, mill phenomenon stuck with paste by the Electrostatic Absorption and the bag ball that effectively eliminate cement subparticle.
Description
Technical field
The present invention relates to field of cement production, especially a kind of cement grinding aid.
Background technology
Cement grinding aid is a kind of chemical addition agent improving cement grinding effect and performance, can significantly improve cement platform
Time yield, each age strength of cement, improve its mobility.Cement grinding aid can be greatly lowered in grinding process the electrostatic formed
Absorption bag ball phenomenon, it is possible to reduce the coalescence trend again of the ultra-fine grain formed in grinding process.Cement grinding aid also can
Significantly improve cement fluidity, improve grinding effect and the grinding efficiency of powder concentrator of grinding machine, thus reduce grinding energy.Use
The cement that grinding aid produces has relatively low compacting coalescence trend, thus the handling of beneficially cement, and cement bunker can be reduced
Wall cling phenomenon.As a kind of chemical addition agent, grinding aid can improve concrete scroll and excite aquation power, thus improving water
Mud early strength and later strength.
Domestic most employing technical pure polymerization organic salt and inorganic salt are the main component of grinding aid, relatively costly, technology
Economic indicator is not suitable with practical condition, and product adaptation face is narrower, and the material higher especially for temperature is also the most suitable
Product.Identical product even for different manufacturers is applied to different manufacturers, there is also the situation that difference on effect is bigger.Existing
There is product cannot give full play to this product and improve grinding material adhesiving effect, and fail multiple effective grinding aid components matching one
Rising, thus play optimal grinding effect, cement or concrete can be brought harm by chlorine or alkali in the most existing grinding aid.
Summary of the invention
The technical problem to be solved in the present invention is: overcome deficiency of the prior art, it is provided that a kind of good water-retaining property, can improve
Cement specific surface area and the cement grinding aid of outward appearance.
For solving above-mentioned technical problem, the technical solution used in the present invention is as follows:
A kind of cement grinding aid, its mass parts composition is as follows: modified triethanolamine 5-25 part, propylene glycol 10-15 part, insatiable hunger
With polyester resin 3-5 part, sodium thiosulfate 6-12 part, calcium formate 2-8 part, tween 80 0.6-0.8 part, alkyl polyglycoside 6-12
Part, maleic anhydride 10-30 part, nano silicon 2-6 part, sodium hexameta phosphate 2.4-5.6 part, allyl polyethenoxy ether 2-6
Part, water conservation cellulose 1.8-4.8 part.
Further, the preparation method of described modified triethanolamine is as follows:
(1) configuration sulphuric acid and the sour mixed solution of phosphoric acid, the mol ratio of described sulphuric acid and phosphoric acid is 1:1.1-1.4;
(2) heating triethanolamine solution is to 130-140 DEG C, dropping acid mixed solution, triethanolamine and acid mixed solution
Mass ratio is 2-3:1;
(3), after maintaining 130-140 DEG C of stirring 3h, it is cooled to room temperature, obtains modified triethanolamine.
Further, the mol ratio of described sulphuric acid and phosphoric acid is 1:1.2.
Further, described triethanolamine is 2.5:1 with the mass ratio of acid mixed solution.
Further, at least one during described water conservation cellulose selects sodium carboxymethyl cellulose, hydroxyethyl cellulose.
Further, described water conservation cellulose selects sodium carboxymethyl cellulose, the mixture of hydroxyethyl cellulose, its quality
Ratio is 0.7-0.9:1.
Further, described sodium carboxymethyl cellulose, its mass ratio of hydroxyethyl cellulose are 0.8:1.
Further, described cement grinding aid mass parts composition as follows: modified triethanolamine 15 parts, propylene glycol 12 parts,
Unsaturated polyester resin 4 parts, 9 parts of sodium thiosulfate, calcium formate 5 parts, tween 80 0.7 part, alkyl polyglycoside 9 parts, maleic anhydride
20 parts, nano silicon 4 parts, sodium hexameta phosphate 4 parts, allyl polyethenoxy ether 4 parts, water conservation cellulose 3.2 parts.
Technical scheme is used to provide the benefit that:
The cement grinding aid of the present invention, has regulation effect to the grain diameter of cement, by increasing capacitance it is possible to increase in cement, particle diameter exists
Cement granules in 3-32 μ m, thus strengthen the specific surface area of cement;Cement specific surface area and outward appearance can be improved;The present invention
Cost of manufacture is relatively low, and energy consumption is low, and cement performance is good;
Under the conditions of grinding machine situation is immovable, mill output amplitude 10-30% can be improved, be effectively reduced powder simultaneously
Mill phenomenon, optimizes cement granules grating;The dispersibility of the interior material of mill can be improved, effectively eliminate the Electrostatic Absorption of cement subparticle
Mill phenomenon is stuck with paste with bag ball.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the invention will be further described.
Embodiment 1
A kind of cement grinding aid, its mass parts composition is as follows: modified triethanolamine 5 parts, propylene glycol 10 parts, unsaturated polyester (UP)
Resin 3 parts, 6 parts of sodium thiosulfate, calcium formate 2 parts, tween 80 0.6 part, alkyl polyglycoside 6 parts, maleic anhydride 10 parts, nanometer two
Silicon oxide 2 parts, sodium hexameta phosphate 2.4 parts, allyl polyethenoxy ether 2 parts, water conservation cellulose 1.8 parts.
Wherein, the preparation method of modified triethanolamine is as follows:
(1) configuration sulphuric acid and the sour mixed solution of phosphoric acid, the mol ratio of described sulphuric acid and phosphoric acid is 1:1.1;
(2) heating triethanolamine solution is to 130-135 DEG C, dropping acid mixed solution, triethanolamine and acid mixed solution
Mass ratio is 2:1;
(3), after maintaining 130-135 DEG C of stirring 3h, it is cooled to room temperature, obtains modified triethanolamine.
Wherein, water conservation cellulose selects sodium carboxymethyl cellulose.
Embodiment 2
A kind of cement grinding aid, its mass parts composition is as follows: modified triethanolamine 8 parts, propylene glycol 11 parts, unsaturated polyester (UP)
Resin 3.5 parts, 6.5 parts of sodium thiosulfate, calcium formate 3 parts, tween 80 0.65 part, alkyl polyglycoside 6.5 parts, maleic anhydride 12
Part, nano silicon 2.5 parts, sodium hexameta phosphate 2.8 parts, allyl polyethenoxy ether 3 parts, water conservation cellulose 2 parts.
Wherein, the preparation method of modified triethanolamine is as follows:
(1) configuration sulphuric acid and the sour mixed solution of phosphoric acid, the mol ratio of described sulphuric acid and phosphoric acid is 1:1.2;
(2) heating triethanolamine solution is to 130-135 DEG C, dropping acid mixed solution, triethanolamine and acid mixed solution
Mass ratio is 2.1:1;
(3), after maintaining 130-135 DEG C of stirring 3h, it is cooled to room temperature, obtains modified triethanolamine.
Wherein, water conservation cellulose selects sodium carboxymethyl cellulose, the mixture of hydroxyethyl cellulose, and its mass ratio is 0.7:
1。
Embodiment 3
A kind of cement grinding aid, its mass parts composition is as follows: modified triethanolamine 15 parts, propylene glycol 12 parts, unsaturated polyester
Ester resin 4 parts, 9 parts of sodium thiosulfate, calcium formate 5 parts, tween 80 0.7 part, alkyl polyglycoside 9 parts, maleic anhydride 20 parts, nanometer
Silicon dioxide 4 parts, sodium hexameta phosphate 4 parts, allyl polyethenoxy ether 4 parts, water conservation cellulose 3.2 parts.
Wherein, the preparation method of modified triethanolamine is as follows:
(1) configuration sulphuric acid and the sour mixed solution of phosphoric acid, the mol ratio of described sulphuric acid and phosphoric acid is 1:1.2;
(2) heating triethanolamine solution is to 135-140 DEG C, dropping acid mixed solution, triethanolamine and acid mixed solution
Mass ratio is 2.5:1;
(3), after maintaining 135-140 DEG C of stirring 3h, it is cooled to room temperature, obtains modified triethanolamine.
Wherein, sodium carboxymethyl cellulose, its mass ratio of hydroxyethyl cellulose are 0.8:1.
Embodiment 4
A kind of cement grinding aid, its mass parts composition is as follows: modified triethanolamine 22 parts, propylene glycol 13 parts, unsaturated polyester
Ester resin 4,11 parts of sodium thiosulfate, calcium formate 7 parts, tween 80 0.7 part, alkyl polyglycoside 11 parts, maleic anhydride 28 parts, nanometer
Silicon dioxide 5 parts, sodium hexameta phosphate 5.2 parts, allyl polyethenoxy ether 5 parts, water conservation cellulose 4.5 parts.
Wherein, the preparation method of modified triethanolamine is as follows:
(1) configuration sulphuric acid and the sour mixed solution of phosphoric acid, the mol ratio of described sulphuric acid and phosphoric acid is 1:1.3;
(2) heating triethanolamine solution is to 130-140 DEG C, dropping acid mixed solution, triethanolamine and acid mixed solution
Mass ratio is 2.8:1;
(3), after maintaining 135-140 DEG C of stirring 3h, it is cooled to room temperature, obtains modified triethanolamine.
Wherein, water conservation cellulose selects sodium carboxymethyl cellulose, the mixture of hydroxyethyl cellulose, and its mass ratio is 0.8:
1。
Embodiment 5
A kind of cement grinding aid, its mass parts composition is as follows: modified triethanolamine 25 parts, propylene glycol 15 parts, unsaturated polyester
Ester resin 5 parts, 12 parts of sodium thiosulfate, calcium formate 8 parts, tween 80 0.8 part, alkyl polyglycoside 12 parts, maleic anhydride 30 parts, receive
Rice silicon dioxide 6 parts, sodium hexameta phosphate 5.6 parts, allyl polyethenoxy ether 6 parts, water conservation cellulose 4.8 parts.
Wherein, the preparation method of modified triethanolamine is as follows:
(1) configuration sulphuric acid and the sour mixed solution of phosphoric acid, the mol ratio of described sulphuric acid and phosphoric acid is 1:1.4;
(2) heating triethanolamine solution is to 135-140 DEG C, dropping acid mixed solution, triethanolamine and acid mixed solution
Mass ratio is 3:1;
(3), after maintaining 135-140 DEG C of stirring 3h, it is cooled to room temperature, obtains modified triethanolamine.
Wherein, water conservation cellulose selects sodium carboxymethyl cellulose, the mixture of hydroxyethyl cellulose, and its mass ratio is 0.9:
1。
Embodiment 3 is preferred implementation, and before grinding, the addition of grinding aid is 0.06% in cement, comparative example without
Grinding aid, grinds 20min, 30min, 40min, 50min, 60min respectively, then contrasts 45 μm and tails over, and data are shown in Table.
With the above-mentioned desirable embodiment according to the present invention for enlightenment, by above-mentioned description, relevant staff is complete
Entirely can carry out various change and amendment in the range of without departing from this invention technological thought.The technology of this invention
The content that property scope is not limited in description, it is necessary to determine its technical scope according to right.
Claims (8)
1. a cement grinding aid, it is characterised in that its mass parts composition is as follows: modified triethanolamine 5-25 part, propylene glycol 10-
15 parts, unsaturated polyester resin 3-5 part, sodium thiosulfate 6-12 part, calcium formate 2-8 part, tween 80 0.6-0.8 part, alkyl
Many glycosides 6-12 part, maleic anhydride 10-30 part, nano silicon 2-6 part, sodium hexameta phosphate 2.4-5.6 part, pi-allyl polyoxy second
Alkene ether 2-6 part, water conservation cellulose 1.8-4.8 part.
A kind of cement grinding aid the most according to claim 1, it is characterised in that: the preparation method of described modified triethanolamine
As follows:
(1) configuration sulphuric acid and the sour mixed solution of phosphoric acid, the mol ratio of described sulphuric acid and phosphoric acid is 1:1.1-1.4;
(2) heating triethanolamine solution is to 130-140 DEG C, dropping acid mixed solution, triethanolamine and the quality of acid mixed solution
Ratio is 2-3:1;
(3), after maintaining 130-140 DEG C of stirring 3h, it is cooled to room temperature, obtains modified triethanolamine.
A kind of cement grinding aid the most according to claim 1, it is characterised in that: the mol ratio of described sulphuric acid and phosphoric acid is 1:
1.2。
A kind of cement grinding aid the most according to claim 1, it is characterised in that: described triethanolamine and acid mixed solution
Mass ratio is 2.5:1.
A kind of cement grinding aid the most according to claim 1, it is characterised in that: described water conservation cellulose selects carboxymethyl fine
At least one in dimension element sodium, hydroxyethyl cellulose.
A kind of cement grinding aid the most according to claim 5, it is characterised in that: described water conservation cellulose selects carboxymethyl fine
Dimension element sodium, the mixture of hydroxyethyl cellulose, its mass ratio is 0.7-0.9:1.
A kind of cement grinding aid the most according to claim 6, it is characterised in that: described sodium carboxymethyl cellulose, ethoxy
Its mass ratio of cellulose is 0.8:1.
A kind of cement grinding aid the most according to claim 1, it is characterised in that its mass parts composition is as follows: modified three ethanol
Amine 15 parts, propylene glycol 12 parts, unsaturated polyester resin 4 parts, 9 parts of sodium thiosulfate, calcium formate 5 parts, tween 80 0.7 part, alkane
Quito glycosides 9 parts, maleic anhydride 20 parts, nano silicon 4 parts, sodium hexameta phosphate 4 parts, allyl polyethenoxy ether 4 parts, water conservation
Cellulose 3.2 parts.