CN106113801A - Fixed point coating aluminum foil-plastic-aluminum foil and preparation technology thereof - Google Patents
Fixed point coating aluminum foil-plastic-aluminum foil and preparation technology thereof Download PDFInfo
- Publication number
- CN106113801A CN106113801A CN201610408676.3A CN201610408676A CN106113801A CN 106113801 A CN106113801 A CN 106113801A CN 201610408676 A CN201610408676 A CN 201610408676A CN 106113801 A CN106113801 A CN 106113801A
- Authority
- CN
- China
- Prior art keywords
- aluminum foil
- layer
- fixed point
- coating
- plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
This case relates to a kind of fixed point coating aluminum foil-plastic-aluminum foil and preparation technology thereof, include: aluminium foil layer, this aluminium foil layer has relative first surface and second surface, and described first surface is provided with adhesive for polyurethane layer, and this adhesive for polyurethane layer surface is provided with aramid layer or polyester layer;Described second surface is provided with the VC glue-line of fixed point coating;Wherein, between described adhesive for polyurethane layer and described aramid layer or polyester layer, it is additionally provided with ink printing block.This case uses fixed point coating method, within the coating weight of VC glue being reduced to original 40%, save the gluing cost of more than 60%, VOCs discharge capacity decreases 60% simultaneously, energy consumption is greatly improved the feature of environmental protection during torrid zone aluminum produces while reducing, play the effect of energy-saving and emission-reduction, the features such as this method has simply, implementation cost is low, preservation and effect is good.
Description
Technical field
The present invention relates to drug packing material field, particularly to one fixed point coating aluminum foil-plastic-aluminum foil and preparation work thereof
Skill.
Background technology
Aluminum foil-plastic-aluminum foil paper tinsel is a kind of thermoforming plastic bubble-cap and the combination of cold forming clad aluminum, and blister package keeps bubble
Molded dimension is constant, and the area around bubble-cap is the most wider so that the hot belt type bubble-cap composite membrane after cold forming can steep with thermoforming
In cover sealing, compensate for the aluminum-plastic packaged middle printing opacity of tradition, the problem of water preventing ability difference, now the most progressively accepted by domestic manufacturer.
The composition of aluminum foil-plastic-aluminum foil (also referred to as aluminum-plastic-aluminum) is polyamide or polyester/aluminium/binding agent, and it is in certain temperature
A kind of sheet material by special equipment, this different materials being composited under degree and pressure, is specifically for strengthening tradition plastic-aluminum bag
The barrier of dress and a kind of packaged form of growing up, only need to add an aluminum in polrvinyl chloride (PVC) bubble-cap stiff sheet the most again
The lid moulding composite membrane is the formation of aluminum foil-plastic-aluminum foil packaging..
In the prior art, the usual structure of torrid zone bubble-cap aluminum is polyamide PA25/ aluminium foil AL60/ acrylic acid VC glue, its
Middle VC glue uses the full version coating method of aluminium foil surface, but actually VC glue simply plays heat sealing effect in heat-seal land, at other
The VC glue of position coating is not all used effectively.The working concentration of solvent-borne type heat-seal coating is usually 25%, and butt coating weight is
3.0g/m2, being computed often being coated with one square metre, then the organic solvent amount discharged in air is 2.25g.These are discharged into greatly
Organic solvent (being called for short VOCs) in gas, on the one hand can cause serious atmosphere light chemical combination to pollute, cause greenhouse effect, cause pole
Big environmental hazard, makes crop production reduction, is entered in human body by breathing, and liver and nervous system to human body cause damage,
Harm enterprise direct labor and the health of surrounding population;On the other hand the significant wastage of VOC raw material is caused.
Using fixed point coating method, be the most only just coated with VC glue at the position needing heat-sealing, remaining position is not coated with VC glue, this
Within the coating weight of VC glue just can be reduced to original 40% by sample, i.e. realize the gluing cost savings of more than 60%, simultaneously
VOCs discharge capacity decreases 60%, thus feature of environmental protection torrid zone aluminum produce in is greatly improved.But VC glue of the prior art
Heat seal strength can As time goes on dramatic decrease, the stability of this set point coating method brings no small challenge.
Summary of the invention
The deficiency existed for prior art, this case provides a kind of fixed point coating aluminum foil-plastic-aluminum foil and preparation work thereof
Skill.
For achieving the above object, this case is achieved through the following technical solutions:
A kind of fixed point coating aluminum foil-plastic-aluminum foil, it includes: aluminium foil layer, this aluminium foil layer have relative first surface and
Second surface, described first surface is provided with adhesive for polyurethane layer, and this adhesive for polyurethane layer surface is provided with aramid layer or poly-
Ester layer;Described second surface is provided with the VC glue-line of fixed point coating;Wherein, at described adhesive for polyurethane layer and described aramid layer
Or between polyester layer, it is additionally provided with ink printing block.
Preferably, described fixed point coating aluminum foil-plastic-aluminum foil, wherein, the thickness of described aramid layer or polyester layer is
15-40μm。
Preferably, described fixed point coating aluminum foil-plastic-aluminum foil, wherein, the thickness of described aluminium foil layer is 30-100 μm.
Preferably, described fixed point coating aluminum foil-plastic-aluminum foil, wherein, the coating thickness of described VC glue-line is 4-8 μm,
Coating width is 8-12mm.
Preferably, described fixed point coating aluminum foil-plastic-aluminum foil, wherein, described VC glue-line includes resin base material, should
Resin base material is selected from acrylic resin, vinyl chloride-vinyl acetate resin, polyester resin or a combination thereof.
Preferably, described fixed point coating aluminum foil-plastic-aluminum foil, wherein, described VC glue-line also includes modifying agent, institute
State modifying agent to include:
Preferably, described fixed point coating aluminum foil-plastic-aluminum foil, wherein, in parts by weight, described resin base material: described
Modifying agent=100: 10-20.
Preferably, described fixed point coating aluminum foil-plastic-aluminum foil, wherein, described ethylene-ethyl methacrylate copolymerization
In thing, ethylene contents is 31-33wt%, and surplus is ethyl methacrylate.
A kind of preparation technology of fixed point coating aluminum foil-plastic-aluminum foil as above, comprising:
Described aramid layer or polyester layer print described ink printing block;
Described adhesive for polyurethane layer paving is invested on described aluminium foil layer, and carries out bonding with described ink printing block, add
Heat cure, the coating weight of wherein said adhesive for polyurethane layer is 0.2-9.9g/m2;
Described VC glue-line is coated on described aluminium foil layer by the way of fixed point is coated with.
Preferably, the preparation technology of described fixed point coating aluminum foil-plastic-aluminum foil, wherein, the fixed point of described VC glue-line is coated with
Cloth technique is: pneumatic unreel → manually version → automatically is dried → gap receipts to version → precision coating → predrying → floated
Volume;
Wherein, the version molded dimension of coating mesh roller used during accurate coating can be detected and identify;
The described carved region of coating mesh roller and the edge in non-engraved district are respectively set to waveform, and are spaced,
With the expansion of reply site;
Described VC glue-line before coating, is configured to the liquid of concentration >=40wt%.
The invention has the beneficial effects as follows: this case uses fixed point coating method, is the most only just coated with VC at the position needing heat-sealing
Glue, remaining position is not coated with VC glue, within thus the coating weight of VC glue being reduced to original 40%, i.e. realize 60% with
On gluing cost savings, VOCs discharge capacity decreases 60% simultaneously, while energy consumption reduces and torrid zone aluminum is greatly improved
The features such as the feature of environmental protection in production, plays the effect of energy-saving and emission-reduction, and this method has simply, implementation cost is low, preservation and effect is good;
By the improvement to VC glue so that it has more stable and lasting heat seal strength.
Accompanying drawing explanation
Fig. 1 is the structural representation of fixed point coating aluminum foil-plastic-aluminum foil.
Detailed description of the invention
The present invention is described in further detail below in conjunction with the accompanying drawings, to make those skilled in the art with reference to description literary composition
Word can be implemented according to this.
As it is shown in figure 1, the fixed point coating aluminum foil-plastic-aluminum foil of an embodiment is listed in this case, it includes: aluminium foil layer 1, should
Aluminium foil layer 1 has relative first surface and second surface, and first surface is provided with adhesive for polyurethane layer 2, this polyurethane gluing
Oxidant layer 2 surface is provided with aramid layer 3 or polyester layer 3;Second surface is provided with the VC glue-line 4 of fixed point coating;Wherein, at polyurethane adhesive
Ink printing block 5 it is additionally provided with between adhensive layer and aramid layer or polyester layer.The effect of ink printing block 5 is beneficially at powder charge ring
Joint carries out photoelectric tracing.
In the above-described embodiments, the thickness of aramid layer 3 or polyester layer 3 is preferably 15-40 μm.
In the above-described embodiments, the thickness of aluminium foil layer 1 is preferably 30-100 μm.
In the above-described embodiments, the coating thickness of VC glue-line 4 is 4-8 μm, and coating width is 8-12mm.
In the above-described embodiments, VC glue-line 4 includes resin base material, and this resin base material is selected from acrylic resin, chlorine vinegar tree
Fat, polyester resin or a combination thereof.
As another embodiment of this case, wherein, in VC glue-line, 4 also include modifying agent, and this modifying agent includes:
The effect of modifying agent is to slow down the problem that VC glue elapses in time and the heat seal strength that produces drastically declines, to improve
The stability of VC glue heat seal strength and persistency so that even with the mode of fixed point coating, also will not subtracting because of spreading area
Little and affect the heat seal strength of VC glue.Above-mentioned formula is as an entirety, and its respective ratio should be severely limited.But research
Finding, the molecular weight of the polymer in above-mentioned formula is the least on the impact of its performance, it is therefore not necessary to polymer each in formula
Molecular weight defines.Carboxylic styrene butadiene latex and Polyethylene Glycol are mainly used in improving VC glue adhesion strength at high temperature, and
Antioxygen property to air;Isopropyl acid N-butyl is mainly used in regulating VC glue and is heat-sealed to the speed of solidification from high temperature, meanwhile, different
Another effect of n-butyl propionate is to reduce shrinkage stress when VC is gelled solid, to improve the stability of heat-sealing;Ethylene-methyl
The effect of ethyl acrylate copolymer is to reduce VC glue deformation amplitude at high temperature, increases VC glue viscosity at high temperature simultaneously
Coefficient, thus reduce its mobility, so that VC glue still can keep higher heat seal strength under less spreading area.
Except resin base material, modifying agent in VC glue, may preferably further comprise routine dispersant or surfactant, but this
A little dispersants or surfactant need to be only that adhesive field is conventional, and therefore this case no longer limits at this.
In the above-described embodiments, resin base material and modifying agent contain a preferred adding proportion, the most in parts by weight, tree
Aliphatic radical material: modifying agent=100: 10-20.
In the above-described embodiments, in ethylene-ethyl methacrylate copolymer, ethylene contents is preferably 31-33wt%, remaining
Amount is ethyl methacrylate.In order to ensure that the effect of ethylene-ethyl methacrylate copolymer is to reduce deformation amplitude and increasing
Add viscosity coefficient, need ethylene contents therein is defined.
The preparation technology of fixed point coating aluminum foil-plastic-aluminum foil as above, comprising:
Printing-ink printing block on aramid layer or polyester layer;
Adhesive for polyurethane layer paving is invested on aluminium foil layer, and carries out bonding with ink printing block, be heating and curing, Qi Zhongju
The coating weight of urethane adhesive layer is 0.2-9.9g/m2;
VC glue-line is coated on aluminium foil layer by the way of fixed point is coated with.
In the above-described embodiments, the fixed point coating process of VC glue-line is: pneumatic unreel → manually to version → automatically to version →
Accurate coating → predrying → floated dry → gap rolling;
Wherein, the version molded dimension of coating mesh roller used during accurate coating can be detected and identify;
The carved region of coating mesh roller is respectively set to waveform with the edge in non-engraved district, and is spaced, to answer
Site is expanded;
VC glue-line before coating, is configured to the liquid of concentration >=40wt%.
Although embodiment of the present invention are disclosed as above, but it is not restricted in description and embodiment listed
Using, it can be applied to various applicable the field of the invention completely, for those skilled in the art, and can be easily
Realizing other amendment, therefore under the general concept limited without departing substantially from claim and equivalency range, the present invention does not limit
In specific details with shown here as the legend with description.
Claims (10)
1. a fixed point coating aluminum foil-plastic-aluminum foil, it is characterised in that include: aluminium foil layer, this aluminium foil layer has relative the
One surface and second surface, described first surface is provided with adhesive for polyurethane layer, and this adhesive for polyurethane layer surface is provided with polyamides
Amine layer or polyester layer;Described second surface is provided with the VC glue-line of fixed point coating;Wherein, at described adhesive for polyurethane layer with described
Ink printing block it is additionally provided with between aramid layer or polyester layer.
2. fixed point coating aluminum foil-plastic-aluminum foil as claimed in claim 1, it is characterised in that described aramid layer or polyester layer
Thickness is 15-40 μm.
3. fixed point coating aluminum foil-plastic-aluminum foil as claimed in claim 1, it is characterised in that the thickness of described aluminium foil layer is 30-
100μm。
4. fixed point coating aluminum foil-plastic-aluminum foil as claimed in claim 1, it is characterised in that the coating thickness of described VC glue-line is
4-8 μm, coating width is 8-12mm.
5. fixed point coating aluminum foil-plastic-aluminum foil as claimed in claim 1, it is characterised in that described VC glue-line includes resin base
Material, this resin base material is selected from acrylic resin, vinyl chloride-vinyl acetate resin, polyester resin or a combination thereof.
6. fixed point coating aluminum foil-plastic-aluminum foil as claimed in claim 5, it is characterised in that described VC glue-line also includes modification
Agent, described modifying agent includes:
Above-mentioned each component sum is 100%.
7. fixed point coating aluminum foil-plastic-aluminum foil as claimed in claim 6, it is characterised in that in parts by weight, described resin base
Material: described modifying agent=100: 10-20.
8. fixed point coating aluminum foil-plastic-aluminum foil as claimed in claim 6, it is characterised in that described ethylene-methyl methacrylate second
In ester copolymer, ethylene contents is 31-33wt%, and surplus is ethyl methacrylate.
9. the preparation technology of a fixed point coating aluminum foil-plastic-aluminum foil as claimed in claim 1, it is characterised in that including:
Described aramid layer or polyester layer print described ink printing block;
Described adhesive for polyurethane layer paving is invested on described aluminium foil layer, and carries out bonding with described ink printing block, add thermosetting
Changing, the coating weight of wherein said adhesive for polyurethane layer is 0.2-9.9g/m2;
Described VC glue-line is coated on described aluminium foil layer by the way of fixed point is coated with.
10. the preparation technology of fixed point coating aluminum foil-plastic-aluminum foil as claimed in claim 9, it is characterised in that described VC glue-line
Fixed point coating process be: pneumatic unreel → manually to version → automatically to version → precision coating → predrying → floated dry →
Gap rolling;
Wherein, the version molded dimension of coating mesh roller used during accurate coating can be detected and identify;
The described carved region of coating mesh roller and the edge in non-engraved district are respectively set to waveform, and are spaced, to answer
Site is expanded;
Described VC glue-line before coating, is configured to the liquid of concentration >=40wt%.